Photoelectric characteristics of metal/InGaN/GaN heterojunction structure

A heterojunction structure photodetector was fabricated by evaporating a semitransparent Ni/Au metal film oil the InGaN/GaN structure. The photocurrent (PC) spectra show that both the Schottky junction (NiAu/InGaN) and the InGaN/GaN isotype heterojunction contribute to the PC signal which suggests that two junctions are connected in series and result in a broader spectral response of the device. Secondary electron, cathodoluminescence and electron-beam-induced current images measured from the same area of the edge surface clearly reveal the profile of the layer structure and distribution of the built-in electric field around the two junctions. A band diagram of the device is drawn based oil the consideration of the polarization effect at the InGaN/GaN interface. The analysis is consistent with the physical mechanism of a tandem structure of two junctions connected in series.

Effect of p-GaN layer thickness on the performance of p-i-n structure GaN ultraviolet photodetectors

We investigated the influence of thickness of p-GaN layer on the performance of p-i-n structure GaN ultraviolet photodetector. Through the simulation calculation, it was found that both the quantum efficiency and dark current of device decrease when employing thicker p-GaN layer, while both the quantum efficiency and dark current increase with decreasing thickness of p-GaN layer. It is suggested that the Schottky contact junction between the metal and p-GaN may be responsible for the incompatible effect. We has to make a suitable choice of the thickness of p-GaN in the device design according to the application requirement.

Tunneling magnetoresistance in CoFeB/GaAs/(Ga,Mn)As hybrid magnetic tunnel junctions

We reported the all electronic demonstration of spin injection and detection in the trilayers with hybrid structure of CoFeB/GaAs/(Ga,Mn)As (metal/insulator semiconductor) by probing the magnetoresistance at low temperature from 1.8 to 30 K. Tunneling magnetoresistance (TMR) ratios of 3.8%, 4.7%, 2.9%, and 1.4% at 1.8, 10, 20, and 30 K, respectively, were observed. Bias dependence of both the junction resistance and TMR ratio was studied systematically. V-half at which TMR drops to half of its maximum is 6.3 mV, being much smaller compared to that observed in (Ga,Mn)As/ZnSe/Fe and (Ga,Mn)As/AlAs/MnAs hybrid structures, indicating lower Fermi energy of (Ga,Mn)As.

High rate deposition of microcrystalline silicon films by high-pressure radio frequency plasma enhanced chemical vapor deposition (PECVD)

Hydrogenated microcrystalline silicon (mu c-Si:H) thin films were prepared by high-pressure radio-frequency (13.56 MHz) plasma enhanced chemical vapor deposition (rf-PECVD) with a screened plasma. The deposition rate and crystallinity varying with the deposition pressure, rf power, hydrogen dilution ratio and electrodes distance were systematically studied. By optimizing the deposition parameters the device quality mu c-Si:H films have been achieved with a high deposition rate of 7.8 angstrom/s at a high pressure. The V-oc of 560 mV and the FF of 0.70 have been achieved for a single-junction mu c-Si:H p-i-n solar cell at a deposition rate of 7.8 angstrom/s.

Single-electron tunneling depressing synapse for cellular neural networks

In this paper, a cellular neural network with depressing synapses for contrast-invariant pattern classification and synchrony detection is presented, starting from the impulse model of the single-electron tunneling junction. The results of the impulse model and the network are simulated using simulation program with integrated circuit emphasis (SPICE). It is demonstrated that depressing synapses should be an important candidate of robust systems since they exhibit a rapid depression of excitatory postsynaptic potentials for successive presynaptic spikes.

Photovoltaic effects in InGaN structures with p-n junctions

InGaN photovoltaic structures with p-n junctions have been fabricated by metal organic chemical vapour deposition. Using double-crystal X-ray diffraction measurements, it was found that the room temperature band gaps of p-InGaN and n-InGaN films were 2.7 and 2.8 eV, respectively. Values of 3.4 x 10(-2) mA cm(-2) short-circuit current, 0.43 V open-circuit voltage and 0.57 fill factor have been achieved under ultraviolet illumination (360 nm), which were related to p-n junction connected back-to-back with a Schottky barrier and many defects of the p-InGaN film. 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Fabrication and transport properties of ZnO/Nb-1 wt %-doped SrTiO3 epitaxial heterojunctions

(110) ZnO/(001) Nb-1 wt %-doped SrTiO3 n-n type heteroepitaxial junctions were fabricated using the pulse laser deposition method. A diodelike current behavior was observed. Different from conventional p-n junctions or Schottky diodes, the diffusion voltage was found to increase with temperature. At all temperatures, the forward current was perfectly fitted on the thermionic emission model. The band bending at the interface can qualitatively explain our results, and the extracted high ideality factor at low temperatures, as well as large saturation currents, is ascribed to the deep-level-assisted tunneling current through the junction. (C) 2008 American Institute of Physics.

Silicon waveguide modulator based on carrier depletion in periodically interleaved PN junctions

We present the design and numerical simulation results for a silicon waveguide modulator based on carrier depletion in a linear array of periodically interleaved PN junctions that are oriented perpendicular to the light propagation direction. In this geometry the overlap of the optical waveguide mode with the depletion region is much larger than in designs using a single PN junction aligned parallel to the waveguide propagation direction. Simulations predict that an optimized modulator will have a high modulation efficiency of 0.56 V.cm for a 3V bias, with a 3 dB frequency bandwidth of over 40 GHz. This device has a length of 1.86 mm with a maximum intrinsic loss of 4.3 dB at 0V bias, due to free carrier absorption. (C) 2009 Optical Society of America

Tunneling magnetoresistance in (Ga,Mn)As/Al-O/CoFeB hybrid structures

Tunneling magnetoresistance (TMR) in Ga(0.9)2Mn(0.08)As/Al-O/Co40Fe40B20 trilayer hybrid structure as a function of temperature from 10 to 50 K with magnetic field vertical bar H vertical bar <= 2000 Oe has been studied. TMR ratio of 1.6% at low fields at 10 K was achieved with the applied current of 1 mu A. The behavior of junction resistance was well explained by the tunneling resistance across the barrier. Strong bias dependences of magnetoresistance and junction resistance were presented. (C) 2009 American Institute of Physics. [DOI 10.1063/1.3068418]

An Anomalous Gain Mechanism in GaN Schottky Barrier Ultraviolet Photodetectors

The gain mechanism in GaN Schottky barrier ultraviolet photodetectors is investigated by focused light beam. When the incident light illuminates the central region of the Schottky contact electrode, the responsivity changes very little with the increase of reverse bias voltage. However, when the incident light illuminates the edge region of the electrode, the responsivity increases remarkably with the increase of reverse bias voltage, and the corresponding quantum efficiency could be even higher than 100%. It is proposed that the surface states near the edge of the electrode may lead to a reduction of effective Schottky barrier height and an enhancement of electron injection, resulting in the anomalous gain.

Temperature dependent spectral response characteristic of III-V compound tandem cell

The GaInP/GaAs/Ge triple-junction tandem cells with a conversion efficiency of 27.1% were fabricated using metalorganic chemical vapor deposition (MOCVD) technique. Temperature dependence of the spectral response measurements of the GaInP/GaAs/Ge tandem cell was performed by a quantum efficiency system at temperatures ranging from 25A degrees C to 160A degrees C. The red-shift phenomena of the absorption limit for all subcells were observed with increasing temperature, which is dued to the energy gap narrowing with temperature. The short-circuit current densities (J (sc)) of GaInP, GaAs and Ge subcells at room temperature calculated based on the spectral response data were 12.9, 13.7 and 17 mA/cm(2), respectively. The temperature coefficient of J (sc) for the tandem cell was determined to be 8.9 mu A/(cm(2) center dot A degrees C), and the corresponding temperature coefficient of the open-circuit voltage deduced from the series-connected model was -6.27 mV/A degrees C.

Molecular Beam Epitaxy of GaSb on GaAs Substrates with AlSb Buffer Layers

We investigate the molecular beam epitaxy growth of GaSb films on GaAs substrates using AlSb buffer layers. Optimization of AlSb growth parameter is aimed at obtaining high GaSb crystal quality and smooth GaSb surface. The optimized growth temperature and thickness of AlSb layers are found to be 450 degrees C and 2.1 nm, respectively. A rms surface roughness of 0.67 nm over 10 x 10 mu m(2) is achieved as a 0.5 mu m GaSb film is grown under optimized conditions.

Stable multiplication gain in GaN p-i-n avalanche photodiodes with large device area

Visible-blind p-i-n avalanche photodiodes (APDs) were fabricated with high-quality GaN epilayers deposited on c-plane sapphire substrates by metal-organic chemical vapour deposition. Due to low dislocation density and a sophisticated device fabrication process, the dark current was as small as similar to 0.05 nA under reverse bias up to 20V for devices with a large diameter of 200 mu m, which was among the largest device area for GaN-based p-i-n APDs yet reported. When the reverse bias exceeded 38V the dark current increased sharply, exhibiting a bulk avalanche field-dominated stable breakdown without microplasma formation or sidewall breakdown. With ultraviolet illumination (360 nm) an avalanche multiplication gain of 57 was achieved.

1 x 4 Ge-on-SOI PIN Photodetector Array for Parallel Optical Interconnects

High-quality Ge film was epitaxially grown on silicon on insulator using the ultrahigh vacuum chemical vapor deposition. In this paper, we demonstrated that the efficient 1 4 germanium-on-silicon p-i-n photodetector arrays with 1.0 mu m Ge film had a responsivity as high as 0.65 A/W at 1.31 mu m and 0.32 A/W at 1.55 mu m, respectively. The dark current density was about 0.75 mA/cm(2) at 0 V and 13.9 mA/cm(2) at 1.0 V reverse bias. The detectors with a diameter of 25 mu m were measured at 1550 nm incident light under 0 V bias, and the result showed that the 3-dB bandwidth is 2.48 GHz. At a reverse bias of 3 V, the bandwidth is about 13.3 GHz. The four devices showed a good consistency.

Influence of penetrating V-pits on leakage current of GaN based p-i-n UV detector

The leakage mechanism of GaN-based p-i-n (p-AlGaN/i-GaN/n-GaN) UV detector has been investigated. With the same dislocation density, devices made from material with higher density of V-pits on surface produce larger leakage current. SEM images show that some V-pits penetrate into i-GaN layer, sometimes even the n-GaN layer. If p-ohmic contact metal (Ni/Au) deposits in the V-pits, Schottky contact would be formed at the interface of metal and i-GaN, or form ohmic contact at the interface of metal and n-GaN. The existence of parallel Schottky junction and ohmic contact resistance enhances the leakage current greatly.