The growth temperatures dependence of optical and electrical properties of InN films

InN films grown on sapphire at different substrate temperatures from 550 degrees C to 700 degrees C by metalorganic chemical vapor deposition were investigated. The low-temperature GaN nucleation layer with high-temperature annealing (1100 degrees C) was used as a buffer for main InN layer growth. X-ray diffraction and Raman scattering measurements reveal that the quality of InN films can be improved by increasing the growth temperature to 600 degrees C. Further high substrate temperatures may promote the thermal decomposition of InN films and result in poor crystallinity and surface morphology. The photoluminescence and Hall measurements were employed to characterize the optical and electrical properties of InN films, which also indicates strong growth temperature dependence. The InN films grown at temperature of 600 degrees C show not only a high mobility with low carrier concentration, but also a strong infrared emission band located around 0.7 eV. For a 600 nm thick InN film grown at 600 degrees C, the Hall mobility achieves up to 938 cm(2)/Vs with electron concentration of 3.9 x 10(18) cm(-3).

Effects of crystalline quality on the ultraviolet emission and electrical properties of the ZnO films deposited by magnetron sputtering

The ZnO films were deposited on c-plane sapphire, Si (0 0 1) and MgAl2O4 (1 1 1) substrates in pure Ar ambient at different substrate temperatures ranging from 400 to 750 degrees C by radio frequency magnetron sputtering. X-ray diffraction, photoluminescence and Hall measurements were used to evaluate the growth temperature and the substrate effects on the properties of ZnO films. The results show that the crystalline quality of the ZnO films improves with increasing the temperature up to 600 degrees C, the crystallinity of the films is degraded as the growth temperature increasing further, and the ZnO film with the best crystalline quality is obtained on sapphire at 600 degrees C. The intensity of the photoluminescence and the electrical properties strongly depend on the crystalline quality of the ZnO films. The ZnO films with the better crystallinity have the stronger ultraviolet emission, the higher mobility and the lower residual carrier concentration. The effects of crystallinity on light emission and electrical properties, and the possible origin of the n-type conductivity of the undoped ZnO films are also discussed. (C) 2009 Elsevier B. V. All rights reserved.

Defect evolution and accompanied change of electrical properties during the GaN growth by metalorganic chemical vapor deposition

The defect evolution and its correlation with electrical properties of GaN films grown by metalorganic chemical vapor deposition are investigated. It is found that the dislocation density decreases gradually during the growth process, and the dislocation reduction rate in the island coalescence process is especially rapid. The changes in electron mobility of GaN with the increase of growth time are mainly dependent on the dislocations acting as scattering centers. Furthermore, the variation of carrier concentration in GaN may be related with the point defects and their clusters. The quality of GaN could be improved by suitably increasing the film thickness. (C) 2009 Elsevier B.V. All rights reserved.

Influence of nitrogen annealing on electrical properties of lead zirconate titanate thin film deposited on titanium metal foil

We report on improved electrical properties of lead zirconate titanate (PZT) film deposited on titanium metal foil using nitrogen annealing. After nitrogen annealing of the PZT capacitors, symmetric capacitance-voltage (C-V) characteristics, higher dielectric constant and breakdown field, less change of dielectric constant with frequency, lower dielectric loss and leakage current are obtained. (C) 2003 Elsevier B.V. All rights reserved.

Electrical properties and electroluminescence of 4H-SiC p-n junction diodes

Homoepitaxial growth of 4H-SiC on off-oriented Si-face(0001) substrates was performed by using the step-controlled epitaxy technique in a newly developed low-pressure hot-wall CVD (LP-HWCVD) system with a horizontal air-cooled quartz tube at around 1500 degreesC and 1.33 x 10(4) Pa by employing SiH4 + C2H4 + H-2. In-situ doping during growth was carried out by adding NH3 gas into the precursor gases. It was shown that the maximum Hall mobility of the undoped 4H-SiC epilayers at room temperature is about 430 cm(2) (.) V-1 (.) s(-1) with a carrier concentration of similar to 10(16) cm(-3) and the highest carrier concentration of the N-doped 4H-SiC epilayer obtained at NH3 flow rate of 3 sccm is about 2.7 x 10(21) cm(-3) with a mobility of 0.75 cm(2) (.) V-1 (.) s(-1). SiC p-n junctions were obtained by epitaxially growing N-doped 4H-SiC epilayers on Al-doped 4H-SiC substrates. The C - V characteristics of the diodes were linear in the 1/C-3 - V coordinates indicating that the obtained p-n junctions were graded with a built-in voltage of 2.7 eV. The room temperature electroluminescence spectra of 4H-SiC p-n junctions are studied as a function of forward current. The D-A pair recombination due to nitrogen donors and the unintentional, deep boron center is dominant at low forward bias, while the D-A pair recombination due to nitrogen donors and aluminum acceptors are dominant at higher forward biases. The p-n junctions could operate at temperature of up to 400 degreesC, which provides a potential for high-temperature applications.

Effects of Ag on electrical properties of Ag/Ni/p-GaN ohmic contact

Properties of the Ag/Ni/p-GaN structure at different temperatures are studied by Auger electron spectroscopy, scanning electron microscopy and high resolution x-ray diffraction. The effect of Ag in ohmic contact on the crystalline quality is investigated and the optimized value of annealing temperature is reported. The lowest specific contact resistance of 2.5 x 10(-4) Omega cm(2) is obtained at annealing temperature of 550 degrees C.

Influence of AlN interfacial layer on electrical properties of high-Al-content Al0.45Ga0.55N/GaN HEMT structure

Unintentionally doped high-Al-content Al0.45Ga0.55N/GaN high electron mobility transistor (HEMT) structures with and without AlN interfacial layer were grown by metal-organic chemical vapor deposition (MOCVD) on two-inch sapphire substrates. The effects of AlN interfacial layer on the electrical properties were investigated. At 300 K, high two-dimensional electron gas (2DEG) density of 1.66 x 10(11) cm(-2) and high electron mobility of 1346 cm(2) V-1 s(-1) were obtained for the high Al content HEMT structure with a 1 nm AlN interfacial layer, consistent with the low average sheet resistance of 287 Omega/sq. The comparison of HEMT wafers with and without AlN interfacial layer shows that high Al content AlGaN/AlN/GaN heterostructures are potential in improving the electrical properties of HEMT structures and the device performances. (c) 2006 Elsevier B.V. All rights reserved.

Electrical properties of undoped In0.53Ga0.47As grown on InP substrates by molecular beam epitaxy

A series of 1-mu m-thick undoped In0.53Ga0.47As with different substrate growth temperature (T-g) or different beam flux pressure (BFP) of As were grown on lattice-matched semi-insulating InP (001) substrates by molecular beam epitaxy (MBE). Van der Pauw Hall measurements were carried out for these In0.53Ga0.47As samples. The residual electron concentration decreased with increasing temperature from 77 to 140 K, but increased with increasing temperature from 140 to 300 K. Rapid thermal annealing (RTA) can reduce the residual electron concentration. The residual electron mobility increased with increasing temperature from 77 to 300 K. All these electrical properties are associated with As antisite defects. (c) 2006 Elsevier B.V. All rights reserved.

Correlation between optical and electrical properties in In0.52Al0.48As/InxGa1-xAs metamorphic high-electron-mobility-transistor structures on GaAs substrates

4.2 K photoluminescence (PL) and 77 K standard Hall-effect measurements were performed for In0.52Al0.48As/InxGa1-xAs metamorphic high-electron-mobility-transistor (HEMT) structures grown on GaAs substrates with different indium contents in the InxGa1-xAs well or different Si delta-doping concentrations. It was found that electron concentrations increased with increasing PL intensity ratio of the "forbidden" transition (the second electron subband to the first heavy-hole subband) to the sum of the "allowed" transition (the first electron subband to the first heavy-hole subband) and the forbidden transition. And electron mobilities decreased with increasing product of the average full width at half maximum of allowed and forbidden transitions and the electron effective mass in the InxGa1-xAs quantum well. These results show that PL measurements are a good supplemental tool to Hall-effect measurements in optimization of the HEMT layer structure. (c) 2006 American Institute of Physics.

The effect of AlN growth time on the electrical properties of Al0.38Ga0.62N/AlN/GaN HEMT structures

Al0.38Ga0.62N/AIN/GaN HEMT structures have been grown by metal-organic chemical vapor deposition (MOCVD) on 2-inch sapphire substrates. Samples with AIN growth time of 0s (without AIN interlayer), 12, 15, 18 and 24s are characterized and compared. The electrical properties of two-dimensional electron gas (2DEG) are improved by introducing AIN interlayers. The AIN growth time in the range of 12-18s, corresponding to the AIN thickness of 1-1.5 nm, is appropriate for the design of Al0.38Ga0.62N/AIN/GaN HEMT structures. The lowest sheet resistance of 277 Omega sq(-1) and highest room temperature 2DEG mobility of 1460 cm(2)V(-1) s(-1) are obtained on structure with AIN growth time of 12s. The structure with AIN growth time of 15s exhibits the highest 2DEG concentration of 1.59 x 10(13) cm(-2) and the smallest RMS surface roughness of 0.2 nm. (c) 2006 Elsevier B.V. All rights reserved.

Electrical properties of B-doped polycrystalline silicon thin films prepared by rapid thermal chemical vapour deposition

In this paper, about 30 mu m thick B-doped polycrystalline silicon (poly-Si) thin films were deposited on quartz substrates, n-type single crystalline silicon wafers and p(++)-type poly-Si ribbons by a rapid thermal chemical vapour deposition system in a temperature range from 1000 to 1150 degrees C. Activation energy measurement and room temperature/temperature dependent Hall effect measurement were performed on the poly-Si thin films prepared on the former two kinds of substrates, respectively. It seems that the electrical properties of as-prepared poly-Si thin films could be qualitatively explained by Seto's grain boundary (GB) trapping theory although there is a big difference between our samples and Seto's in gain size and film thickness etc. The experimental results reconfirm that GB itself is a kind of most effective recombination center with trapping level near the midgap and trapping state density in the order of 1012 cm(-2) magnitude. Electron beam induced current measurements on the poly-Si thin films prepared on the poly-Si ribbons also show that severe recombination occurs at the positions of GBs. (c) 2005 Elsevier B.V All rights reserved.

Electrical properties of GaN deposited on nitridated sapphire by molecular beam epitaxy using NH3 cracked on the growing surface

We have found that GaN epilayers grown by NH3-source molecular beam epitaxy (MBE) contain hydrogen. Dependent on the hydrogen concentration, GaN on (0001) sapphire can be either under biaxially compressive strain or under biaxially tensile strain. Furthermore, we notice that background electrons in GaN increase with hydrogen incorporation. X-ray photoelectron spectroscopy (XPS) measurements of the N1s region indicate that hydrogen is bound to nitrogen. So, the microdefect Ga...H-N is an effective nitrogen vacancy in GaN, and it may be a donor partly answering for the background electrons. (C) 1999 Elsevier Science B.V. All rights reserved.