Electrical properties and electroluminescence of 4H-SiC p-n junction diodes

Homoepitaxial growth of 4H-SiC on off-oriented Si-face(0001) substrates was performed by using the step-controlled epitaxy technique in a newly developed low-pressure hot-wall CVD (LP-HWCVD) system with a horizontal air-cooled quartz tube at around 1500 degreesC and 1.33 x 10(4) Pa by employing SiH4 + C2H4 + H-2. In-situ doping during growth was carried out by adding NH3 gas into the precursor gases. It was shown that the maximum Hall mobility of the undoped 4H-SiC epilayers at room temperature is about 430 cm(2) (.) V-1 (.) s(-1) with a carrier concentration of similar to 10(16) cm(-3) and the highest carrier concentration of the N-doped 4H-SiC epilayer obtained at NH3 flow rate of 3 sccm is about 2.7 x 10(21) cm(-3) with a mobility of 0.75 cm(2) (.) V-1 (.) s(-1). SiC p-n junctions were obtained by epitaxially growing N-doped 4H-SiC epilayers on Al-doped 4H-SiC substrates. The C - V characteristics of the diodes were linear in the 1/C-3 - V coordinates indicating that the obtained p-n junctions were graded with a built-in voltage of 2.7 eV. The room temperature electroluminescence spectra of 4H-SiC p-n junctions are studied as a function of forward current. The D-A pair recombination due to nitrogen donors and the unintentional, deep boron center is dominant at low forward bias, while the D-A pair recombination due to nitrogen donors and aluminum acceptors are dominant at higher forward biases. The p-n junctions could operate at temperature of up to 400 degreesC, which provides a potential for high-temperature applications.