POWER DEPENDENCE OF THE RECOMBINATION PROCESSES IN THE INXGA1-XAS/GAAS SINGLE-QUANTUM-WELL

We have measured the power dependence of the photoluminesence spectra from a set of strained InxGa1-xAs/GaAs single quantum wells. The result shows that the excitation power has important effect on the carrier recombination processes. When the power increases from 0.5 to 14 mW, the photoluminescence from the barrier becomes more intense than that from the well and the trapping efficiency decreases. At high excitation level, the ratio of the radiative recombination rate to the nonradiative recombination rate of the barrier increases ten times than that at lower excitation level, while it only doubles for the well.

RADIATIVE RECOMBINATION IN N-TYPE AND P-TYPE GAAS COMPENSATED WITH LI

We report fundamental changes of the radiative recombination in a wide range of n-type and p-type GaAs after diffusion with the group-I element Li. These optical properties are found to be a bulk property and closely related to the electrical conductivity of the samples. In the Li-doped samples the radiative recombination is characterized by emissions with excitation-dependent peak positions which shift to lower energies with increasing degree of compensation and concentration of Li. These properties are shown to be in qualitative agreement with fluctuations of the electrostatic potential in strongly compensated systems. For Li-diffusion temperatures above 700-800-degrees-C semi-insulating conditions with electrical resistivity exceeding 10(7) OMEGA cm are obtained for all conducting starting materials. In this heavy Li-doping regime, the simple model of fluctuating potentials is shown to be inadequate for explaining the. experimental observations unless the number of charged impurities is reduced through complexing with Li. For samples doped with low concentrations of Li, on the other hand, the photoluminescence properties are found to be characteristic of impurity-related emissions.

LITHIUM PASSIVATION OF ZN AND CD ACCEPTORS IN P-TYPE GAAS

We report lithium passivation of the shallow acceptors Zn and Cd in p-type GaAs which we attribute to the formation of neutral Li-Zn and Li-Cd complexes. Similar to hydrogen, another group-I element, lithium strongly reduces the concentration of free holes when introduced into p-type GaAs. The passivation is inferred from an increase of both the hole mobility and the resisitivity throughout the bulk of the sample. It is observed most clearly for Li concentrations comparable to the shallow-acceptor concentration. In addition, compensation of shallow acceptors by randomly distributed donors is present in varying degree in the Li-diffused samples. Unlike hydrogenation of n-type GaAs, Li doping shows no evidence of neutralizing shallow donors in GaAs.

WANNIER-STARK LOCALIZATION IN INGAAS/GAAS SUPERLATTICES AND ITS APPLICATION TO ELECTROOPTICAL DEVICES

We have observed Wannier-Stark localization in strained In0.2Ga0.8As/GaAs superlattices by low- and room-temperature photocurrent spectra measurements. The experimental results are well in agreement with the theoretical predictions. A large field-induced modulation response of the absorption edge of the superlattices at room temperature suggests the possibilities of the application to the design of various kinds of electro-optical devices operating at a wavelength of 0.98 mum, based on Wannier-Stark localization effects.

OPTICAL CHARACTERISTICS OF GAAS/ALGAAS RIDGE-QUANTUM-WELL-WIRES GROWN BY MBE ON NONPLANAR SUBSTRATES

With conventional photolithography and wet chemical etching, we have realized GaAs/AlGaAs buried ridge-quantum-well-wires (RQWWs) with vertically stacked wires in lateral arrays promising for device application, which were grown in situ by a single-step molecular beam epitaxy growth and formed at the ridge tops of mesas on nonplanar substrates. Confocal photoluminescence (CPL) and polarization-dependent photoreflectance (PR) are applied to study optical characteristics of RQWWs. Lateral bandgap modulation due to lateral variation of QW layer thickness is demonstrated not only by CPL but also by PR. As one evidence for RQWWs, a large blue shift is observed at the energy level positions for electronic transitions corresponding to quantum wells (QWs) at the ridge tops of mesas compared with those corresponding to QWs on nonpatterned areas of the same sample. The blue shift is in contradiction with the fact that the GaAs QW layers at the tops of the mesas are thicker than those on nonpatterned areas. The other evidence for RQWWs, optical anisotropy is provided by the polarization-dependent PR, which results from lateral quantum size effect existing at the tops of the mesas.

CONTROLLING OF SCHOTTKY-BARRIER HEIGHTS FOR AU/N-GAAS AND TI/N-GAAS WITH HYDROGEN INTRODUCED AFTER METAL-DEPOSITION BY BIAS ANNEALING

Up to now, in most of the research work done on the effect of hydrogen on a Schottky barrier, the hydrogen was introduced into the semiconductor before metal deposition. This letter reports that hydrogen can be effectively introduced into the Schottky barriers (SBs) of Au/n-GaAs and Ti/n-GaAs by plasma hydrogen treatment (PHT) after metal deposition on [100] oriented n-GaAs substrates. The Schottky barrier height (SBH) of a SB containing hydrogen shows the zero/reverse bias annealing (ZBA/RBA) effect. ZBA makes the SBH decrease and RBA makes it increase. The variations in the SBHs are reversible. In order to obtain obvious ZBA/RBA effects, selection of the temperature for plasma hydrogen treatment is important, and it is indicated that 100-degrees-C for Au/n-GaAs and 150-degrees-C for Ti/n-GaAs are suitable temperatures. It is concluded from the analysis of experimental results that only the hydrogen located at or near the metal-semiconductor interface, rather than the hydrogen in the bulk of either the semiconductor or the metal, is responsible for the ZBA/RBA effect on SBH.

SHIFTING PHOTOLUMINESCENCE BANDS IN HIGH-RESISTIVITY LI-COMPENSATED GAAS

It is shown that Li diffusion of GaAs can give rise to semi-insulating samples with electrical resistivity as high as 10(7) OMEGAcm in undoped, n-type, and p-type starting materials. The optical properties of the compensated samples are correlated with the depletion of free carriers caused by the Li diffusion. The radiative recombination of the Li-compensated samples is dominated by emissions with excitation-dependent peak positions that shift to lower energies with increasing compensation. The photoluminescence properties are characteristic of fluctuations of the electrostatic potential in strongly doped, compensated crystals.

NEAR-RESONANT RAMAN-SCATTERING FROM GAAS/ALAS SUPERLATTICES

This article presents the results of near-resonant Raman scattering measurements on GaAs/AlAs superlattices at room temperature. A strong enhancement of GaAs LO phonon-even modes resulted owing to a dipole-allowed Frohlich interaction in superlattices. Similar to the previous results, the LO phonon-even modes in a polarized configuration are observed. In contrast to previous work, however, what we observed in depolarized configurations is the LO phonon-odd modes instead of even modes. It is confirmed that the selection rules for near-resonant Raman scattering from LO phonons in this kind of superlattices are the same as those for off-resonant scattering. From the second-order Raman scattering, it is confirmed that polarized second-order Raman scattering spectra consist of overtones and combinations of two even modes, and depolarized second-order Raman scattering spectra consist of combinations of an even mode and an odd mode. Our experimental results coincide with the predictions using the recently developed Huang-Zhu model. A brief discussion on interface modes and their combination with confined modes is also presented.

PHOTOREFLECTANCE SPECTROSCOPY OF SEMIINSULATING GAAS

Clear observations of photoreflectance (PR) spectra due to excitonic transitions in semi-insulating GaAs bulk materials are reported. The modulation mechanism is attributed to the electromodulation induced by the Dember effect. This study indicates that the PR spectroscopy provides an important method for characterizing the crystal quality of high-resistivity GaAs.

OXYGEN IN INXGA1-XASYP1-Y GROWN ON GAAS

The measurement of DLTS on the alloy InxGa1-xAsyP1-y (0 less-than-or-equal-to y less-than-or-equal-to 0.3; 0.5 greater-than-or-equal-to x greater-than-or-equal-to 0.35) shows a new signal, labeled as E2, with an activation energy of E(c) - 0.61 eV and the SIMS signals show a large number of oxygen. To clarify is further, the energy of the deep level E2 is quantitatively calculated by using Vogl's tight-binding theory and Hjalmarson's deep level theory. As a result, the deep A1-symmetric level associated with an oxygen on the anion site of InxGa1-xAsyP1-y locates deeply in the band gap. Thus, the level E2 is considered to be induced by the oxygen impurity.

INTERFACIAL REACTIONS IN THE CO/SI/GAAS AND SI/CO/GAAS SYSTEMS

The interfacial reactions between thin films of cobalt and silicon and (100)-oriented GaAs substrates in two configurations, Co/Si/GaAs and Si/Co/GaAs, were studied using a variety of techniques including Auger electron spectroscopy, x-ray diffraction, and transmission electron microscopy. The annealing conditions were 200, 300, 400, 600-degrees-C for 30 min, and rapid thermal annealing for 15 s. It was found that Si layer in the Co/Si/GaAs system acts as a barrier at the interface between Co and GaAs when annealed up to 600-degrees-C. The interfacial reaction between Co and Si is faster than that between Co and GaAs in the system of Si/Co/GaAs. The sequence of compound formation for the two metallizations studied (Co/Si/GaAs and Si/Co/GaAs) depends strongly on the sample configuration as well as the layer thickness of Si and Co (Co/Si atomic ratio). From our results, it is promising to utilize Co/Si/GaAs multilayer film structure to make a CoSi2/GaAs contact, and this CoSi2 may offer an alternative to the commonly used W silicides as improved gate metallurgies in self-aligned metal-semiconductor field effect transistor (MESFET) technologies.