Growth of composite sapphire/Ti : sapphire by the hydrothermal method

Composite sapphire/Ti:sapphire crystals for high-power laser application were grown by the hydrothermal method. The results of the X-ray rocking curve analysis indicate high crystalline quality of the surface Al2O3 material. The strong bonding between the overgrown Al2O3 and seed Ti:Al2O3 crystals is indispensable for withstanding high thermal stresses produced by intense optical pumping. The optical loss at the boundary of the composite crystal is considerably low, indicating the lack of scattering centers. (c) 2005 Elsevier B.V. All rights reserved.

Ti：LiAlO2新型晶体的结构分析

通过研究提拉法生长的掺杂Ti浓度为0.2at%的LiAlO2晶体吸收光谱,荧光光谱和红外光谱,来分析此新型晶体的结构.分析发现光谱中仅出现了四价Ti离子的196nm的特征吸收峰,用235nm光激发得到384nm的特征发射峰;针对吸收光谱中660-820nm出现的四个弱小吸收峰提出了一个色心模型,从而解释了空气和富Li气氛处理后吸收峰消失的现象;对比纯LiAlO2晶体的红外光谱发现,Ti的掺入仅影响了[AlO4]键强,而[LiO4]及相关键强几乎不变;结合ICP测试估算出直径50mm,厚1mm的Ti：LiA

Mg，Ti共掺Al2O3透明多晶陶瓷光谱性能研究

Transparent polycrystalline MgO and TiO2 codoped Al2O3 ceramics were fabricated by conventional solid-state pressureless processing. The absorption, emission and excitation spectra of ( Mg, Ti : Al2O3 ceramics were measured. Owing to charge compensation of Mg2+, only UV absorption around 250nm was observed due to O2- -> Ti4+ charge transfer transitions (CT) when Ti content was low. As a result, the emission peaks of isolated Ti4+ ion located at 280-290nm and 410-420nm were observed. Besides absorption peak of V, ion, the characteristic absorption peak of V, ion centered at 490nm was observed in Mg, Ti) : Al2O3 ceramics when Ti content was high. The emission spectra of Ti3+, ion in polycrystalline Al2O3 ceramics coincide with that of Ti: Al2O3 single crystal.

Ti:sapphire laser pumped high average power laser crystal Nd:GGG with high efficiency output

High-quality neodymium doped GGG laser crystals have been grown by Czochralski (Cz) method. Results of Nd:GGG thin chip laser operating at 1.064 μm pumped by Ti:sapphire laser operating at 808 nm were reported. The slop efficiency was as high as 20%.

Spectra analysis of a novel Ti-doped LiAlO2 single crystal

LiAlO2 single crystals doped with Ti at concentration 0.2 at.% are grown by the Czochralskl technique with dimensions Phi 42 x 55 mm. Ti ions in the crystal are quadrivalence proven by comparing the absorption and fluorescence spectra of pure LiAlO2 and Ti: LiAlO2. After air and Li-rich atmosphere annealing, the absorption peaks in the range of 600-800nm disappear. We conclude that 682 and 756nm absorption peaks are attributed to the V-Li and V-O absorptions, respectively. The peaks at 716nm and 798nm may stem from the V-Li(+) and F+ absorptions. The colour-centre model can be applied to explain the experimental phenomena. Ti4+-doping produces more lithium vacancies in the LiAlO2 crystal. The intensities of [LiO4] and the associated bonds remain unchanged, which improves the anti-hydrolyzation and thermal stability of LiAlO2 crystals.

温梯法生长的Ti：Al2O3晶体的光谱分析

本文研究了不同掺Ti^3＋浓度对温梯法生长的Ti：Al2O3晶体吸收光谱、荧光光谱和X射线衍射光谱的影响。根据吸收光谱提出了一个色心模型。对比了样品各处420nm荧光谱，发现掺Ti^3＋浓度越大，该处荧光强度越弱，同时解释了420肿处荧光峰的起源。对比了样品各处720nm处的荧光谱，发现掺Ti^3＋浓度越大，该处荧光强度越强。X射线衍射谱（XRD）表明，衍射峰强度随掺Ti^3＋浓度的增大而逐渐增强。

Ti：Al2O3透明多晶陶瓷光谱特性分析

采用传统无压烧结工艺制备出透明性良好的掺Ti氧化铝陶瓷；测定了该陶瓷的吸收光谱、荧光光谱和激发光谱。结果表明，掺Ti氧化铝透明陶瓷样品在Mg与Ti掺入离子的摩尔比（NMg／NTi）较小时，表现出Ti^3＋离子的490nm特征吸收峰，即^2T2→^2E跃迁产生的宽带吸收；NMg／NTi较大时，陶瓷样品吸收光谱中不存在Ti^3＋离子吸收，其250nm处吸收为O^2-→Ti^4＋的转移吸收。掺Ti氧化铝透明陶瓷样品Ti^3＋离子的发射谱线与单晶的相吻合，同时Ti^3＋在氧化铝陶瓷中分布很均匀，且Ti^3＋浓度较

提拉法Ti:LiAlO_2晶体的生长、缺陷及N_2退火研究

本文采用提拉法成功地生长了钛掺杂浓度为0.1%原子分数的LiAlO2单晶体,借助光学显微镜,结合化学腐蚀法,对Ti:LiAlO2晶体(100)面空气退火前后的缺陷特征进行了研究,用AFM观测了(100)面晶片在不同温度下流动N2气氛退火过的表面形貌。结果表明:Ti:LiAlO2晶体(100)面的位错腐蚀坑是底面为平行四边形的锥形坑,位错密度约为5.0×104cm-2,900℃空气退火后晶片表面的位错腐蚀坑变大;N2退火能显著影响晶片的表面形貌,当退火温度为900℃时,晶片的均方根粗糙度(RMS)达到最低值

射频磁控溅射法制备TiO2-xNX薄膜的结构性能研究

利用射频磁控溅射法室温下在Si（100）衬底上制备了N掺杂的TiO2薄膜，并且采用x射线衍射（XRD）、X射线光电子能谱（XPS）和透射光谱对薄膜进行了表征。XRD结果表明在纯Ar和N2（33．3％）／Ar气氛下制备的TiO2-xNx薄膜均为单一的金红石相，薄膜结晶性良好，呈高度（211）择优取向，而在N2（50．0％）／Ar下制备的薄膜结晶性明显变差；对于N掺杂的TiO2薄膜，XPS表明部分N原子进入TiO2晶格，并且以N—Ti—O、N—O键以及间隙式N原子形式存在；透射光谱表明掺N后的TiO2薄膜吸收边发生了红移。

Newly designed multilayer thin film mirror for dispersion compensation in Ti:sapphire femtosecond lasers

There are two different effects to generate group delay dispersion by multilayer thin film mirrors: chirper effect and Gires-Tournois effect. Both effects are employed to introduce desired dispersion in the designed mirror. Thus the designed mirror provides large dispersion throughout broad waveband. Such mirror can be used for dispersion compensation in Ti:sapphire femtosecond lasers. Most group delay dispersion of a 5-mm Ti:sapphire crystal can be compensated perfectly with only four bounces of the designed mirror.

Negative dispersion mirrors in Ta2O5/: SiO2 for femtosecond Ti : Sapphire lasers by using gires-tournois interferometers

We design and experimentally demonstrate some negative dispersion mirrors with optimized Gires-Tournois interferometers. The mirror structure is composed of 38 alternating Ta2O5 and SiO2 layers and could be regarded as two sections: high-reflectivity section consisting of a series of quarter-wavelength optical thickness stacks and negative-dispersion section consisting of only 13 layers. The designed mirrors exhibit the expected performance. These mirrors were fabricated by using ion beam sputtering. By adopting such mirrors, dispersion of a mode-locked femtosecond Ti:sapphire laser has been compensated for mostly. With two series of the mirrors, 32 fs and 15 fs pulses have been obtained respectively.

Sol-Gel法制备生物玻璃／Ti涂层参数的确定

采用溶胶-凝胶（Sol-Gel）法在已经预涂了一层过渡层的纯钛基体上制备生物玻璃（BG）涂层。试验以正硅酸乙酯（TEOS）、硝酸钙（Ca（NO3）2·4H2O）、氯化镁（MgCl2·6H2O）等为原料，并采用正交试验设计，所得涂层均通过SEM和EDS进行分析，并利用空间几何模型折算绝对偏差，从而确定出最优的试验参数为：[Si]=1M，水酯比（Rω）=4，pH=4．5，浸涂粘度（η）为3．55mPa·s。

Optical and electrical properties of TiOx thin films deposited by electron beam evaporation

The TiOx thin films were prepared by electron beam evaporation using TiO as the starting material. The effect of the annealing temperature on the optical and electrical properties was investigated. The spectra of X-ray photoelectron spectroscopy reveal that Ti in the films mainly exist in the forms of Ti2+ and Ti3+ below 400 degrees C 24h annealing. The charge transfer between different titanium ion contribute greatly to the color, absorption, and electrical resistance of the films. (c) 2006 Elsevier Ltd. All rights reserved.

Laser-induced damage of Ti O2 Si O2 high reflector at 1064 nm

A high laser-induced damage threshold (LIDT) TiO2/SiO2 high reflector (HR) at 1064 nm is deposited by e-beam evaporation. The HR is characterized by optical properties, surface, and cross section structure. LIDT is tested at 1064 nm with a 12 ns laser pulse in the one-on-one mode. Raman technique and scanning electron Microscope are used to analyze the laser-induced modification of HR. The possible damage mechanism is discussed. It is found that the LIDT of HR is influenced by the nanometer precursor in the surface, the intrinsic absorption of film material, the compactness of the cross section and surface structure, and the homogeneity of TiO2 layer. Three typical damage morphologies such as flat-bottom pit, delamination, and plasma scald determine well the nanometer defect initiation mechanism. The laser-induced crystallization consists well with the thermal damage nature of HR. (C) 2008 American Institute of Physics.

Hole-Phonon Relaxation and Photocatalytic Properties of Titanium Dioxide and Zinc Oxide: First-Principles Approach

First-principles calculations for the temporal characteristics of hole-phonon relaxation in the valence band of titanium dioxide and zinc oxide have been performed. A first-principles method for the calculations of the quasistationary distribution function of holes has been developed. The results show that the quasistationary distribution of the holes in TiO2 extends to an energy level approximately 1eV below the top of the valence band. This conclusion in turn helps to elucidate the origin of the spectral dependence of the photocatalytic activity of TiO2. Analysis of the analogous data for ZnO shows that in this material spectral dependence of photocatalytic activity in the oxidative reactions is unlikely.