Mg，Ti共掺Al2O3透明多晶陶瓷光谱性能研究

Transparent polycrystalline MgO and TiO2 codoped Al2O3 ceramics were fabricated by conventional solid-state pressureless processing. The absorption, emission and excitation spectra of ( Mg, Ti : Al2O3 ceramics were measured. Owing to charge compensation of Mg2+, only UV absorption around 250nm was observed due to O2- -> Ti4+ charge transfer transitions (CT) when Ti content was low. As a result, the emission peaks of isolated Ti4+ ion located at 280-290nm and 410-420nm were observed. Besides absorption peak of V, ion, the characteristic absorption peak of V, ion centered at 490nm was observed in Mg, Ti) : Al2O3 ceramics when Ti content was high. The emission spectra of Ti3+, ion in polycrystalline Al2O3 ceramics coincide with that of Ti: Al2O3 single crystal.