INVESTIGATION OF NEGATIVE TRANSIENT CURRENT OF ARGON-IMPLANTED GAAS USING PHOTOINDUCED TRANSIENT-CURRENT SPECTROSCOPY

The investigation of deep levels of argon-implanted LEC-grown semi-insulating GaAs with implantation dosages ranging from 1 x 10(11) to 1 x 10(15) cm-2 has been performed. Using a photoinduced transient-current spectroscopy (PITCS) it was demonstrated that, for implantation dosages below 1 X 10(13) cm-2, a negative peak or negative transient current (NTC) was observed in the temperature range from 330 to 350 K. The magnitude of this negative peak increased with dosage up to a level of 1 X 10(12) cm-2, beyond which it decreased with dosage. The dosage dependence of the EL3 peak height and the resistance of the specimen have also been investigated. It was observed that the variation of the EL3 peak height with dosage was similar to the variation of the magnitude of the negative peak, that is the EL3 peak height likewise increased with dosage up to 1 X 10(12) cm-2, and then decreased. The resistance of the original high-resistivity specimen dropped abruptly when the dosage reached 1 X 10(12) cm-2. This critical dosage (1 X 10(12) cm-2) was found to be a threshold for the generation of a highly disordered state.

Shubnikov de Haas oscillations of a two-dimensional electron gas in a modulation-doped Zn0.80Cd0.20Se/ZnS0.06Se0.94 single quantum well

The magnetotransport properties of the two-dimensional (2D) electron gas confined in a modulation-doped Zn0.80Cd0.20Se/ZnS0.06Se0.94 single quantum well structure were studied at temperatures down to 0.35 K in magnetic fields up to 7.5 T. Well resolved 2D Shubnikovde Haas (SdH) oscillations were observed, although the conductivity of the sample in the as grown state was dominated by a bulk parallel conduction layer. After removing most of the parallel conduction layer by wet chemical etching the amplitude and number of SdH oscillations increased. From the temperature dependence of the amplitude the effective mass of the electrons was estimated as 0.17 m(0). Copyright (C) 1996 Published by Elsevier Science Ltd

259W准连续无铝808nm激光二极管线列阵

通过优化张应变量子阱外延结构和设计线列阵双沟道深隔离槽腐蚀工艺,采用低压金属有机化学气相沉积法(LP-MOCVD)生长了GaAsP/GalnP/AlGaInP单量子阱分别限制异质结激光器材料,并利用该材料制备r填充因子为50%的lcm宽线列阵激光巴条,用扫描电子显微镜(SEM)分析了隔离槽的形貌.在准连续工作条件(200μs脉宽,2%占空比)下,封装在被动制冷标准铜热沉上的器件在测试设备允许的最大驱动电流300A时可获得259W的输出功率,未观察到腔面光学灾变性损伤的发生.最高功率转换效率在工作电流为104A时达52%,此时输出功率为100W,激射光谱的中心波长为807.8nm,半高宽为2.4nm,快慢轴远场发散角分别为29.3°和7.5°.

Efficient Mode-locked and Q-switched Nd∶YVO_4 Laser with Semiconductor Saturable Absorber Mirror

We reported an efficient diode pumped Nd ! YVO, 1 064 nm laser passively mode-locked and Q-switched by a semiconductor saturable absorber mirror(SESAM). At the incident pump power of 7. 5 W, 2. 81 W average output power was obtained during stable CW mode locking with a repetition rate of 111 MHz. The optical conversion efficiency was 37. 5% , and the slope efficiency was 39%. So far as we know, this is the highest optical-optical conversion efficiency with a SESAM at home.

一种模拟倾斜折射率界面光波导的新方法

针对传统离散格式下，束传播方法（BPM）模拟倾斜折射率界面出现的问题，提出了一种简明且易于编程实现的改进方案．在横向上，通过坐标系变换和插值处理，以新颖的7点差分格式代替传统的5点差分方式；在纵向上，以四阶显式Runge-Kutta方法（RKBPM）代替二阶Crank-Nicholson算法（CNBPM），避免了求解不规则矩阵方程，从而使计算效率显著提高．

GaN外延膜厚度的x射线双晶衍射测量

提出了一种利用x射线双晶衍射测量GaN厚度的新方法．该方法采用GaN积分强度和衬底积分强度的比值与样品厚度的关系来测量GaN外延膜厚度，此比值与GaN样品厚度在t＜2μm为线性关系．该方法消除了因GaN吸收造成的影响，比单纯用GaN积分强度与样品厚度的关系推算GaN外延膜厚度精度更高，更方便可靠．

RF-MBE生长AlN/GaN超晶格结构二维电子气材料

用射频等离子体辅助分子束外延技术（RF-MBE）在c面蓝宝石衬底上外延了高质量的GaN膜以及AlN/GaN超晶格结构极化感应二维电子气材料。所获得的掺Si的GaN膜室温电子浓度为2.2 * 10~(18)cm~(-3)，相应的电子迁移率为221cm~2/(V·s);1μm厚的GaN外延膜的（0002）X射线衍射摇摆曲线半高宽（FWHM）为7’；极化感应产生的二维电子气室温电子迁移率达到1086cm~2/(V·s)，相应的二维电子气面密度为7.5 * 10~(12)cm~(-2)。

铯对GaAs（100）表面氧化的催化作用

于2010-11-23批量导入

Investigation on integrated high speed DFB light source and narrow bandwidth RCE photodetector for WDM fiber communication network application

Electroabsorption (EA) modulator integrated with partially gain coupling distributed feedback (DFB) lasers have been fabricated and shown high single mode yield and wavelength stability. The small signal bandwidth is about 7.5 GHz. Strained Si1-chiGechi/Si multiple quantum well (MQW) resonant-cavity enhanced (RCE) photodetectors with SiO2/Si distributed Bragg reflector (DBR) as the mirrors have been fabricated and shown a clear narrow bandwidth response. The external quantum efficiency at 1.3 mum is measured to be about 3.5% under reverse bias of 16 V. A novel GaInNAs/GaAs MQW RCE p-i-n photodetector with high reflectance GaAs/ALAs DBR mirrors has also been demonstrated and shown the selectively detecting function with the FWHM of peak response of 12 nm.

安全策略模型聚合性评估方法

动态策略支持与授权粒度是访问控制的关键问题.现有的研究只关注安全策略的描述能力,却忽略了对策略结构与授权粒度的分析,从而无法全面满足动态策略支持与最小授权要求.指出Lampson访问矩阵模型是对最细粒度访问控制的抽象,普通安全策略则根据应用安全需求对Lampson访问矩阵进行聚合.基于安全标签的聚合性描述框架(a descriptive framework of groupability basing on security labels,简称GroSeLa)可将普通安全策略映射为Lampson访问矩阵,该框架分为基本组件与扩展两部分:前者分析用于实现矩阵聚合的安全策略结构;后者则指出实现全面动态策略支持必须支持的7类管理性需求.在此基础上,提出5项聚合性指标:聚合因子、动态因子、策略规模、授权粒度与职责隔离支持.对4类经典安全策略ACL,BLP,DTE与RBAC的评估,是从矩阵聚合的角度分析不同的安全策略在表达性、可用性与授权粒度上的差异.

半干旱区沙质草地关键生态系统过程对水肥添加的响应

制约半干旱区生态系统恢复的主要因素是什么？一直是生态学界争论的问题，水分或养分或二者的联合限制是现存的3种观点，但是利用野外实验结合生态化学计量比，分析和判断半干旱区自然生态系统生产力恢复的限制因子还未见报道。 本论文以科尔沁沙地东南缘退耕后自然恢复的沙质草地为研究对象，通过析因设计的水、氮、磷添加实验，研究与碳循环、氮循环、磷循环等有关的生态系统关键过程，及其对人为干扰（灌溉和施肥）及全球变化（气候变化和氮沉降）的响应。从2004年到2005年采用3因素2水平析因设计进行水（0, 80mm）、氮（0, 20 g N m-2 yr-1）、磷（0, 10 g P2O5 m-2 yr-1）添加实验。2005年增加了0、2.5、5、7.5、10、30、40 g N m-2 yr-1的氮梯度添加实验。通过两年的实验，得出主要结论如下： 1）该沙质草地生态系统生产力主要受氮素养分的限制，水分与磷素并不是主要限制因素。施氮量达到7.5 g N m-2 yr-1时生物量明显提高，当氮素添加量达到40 g N m-2 yr-1时，生产力最高为1607.3 g m-2，但是并未找出氮肥添加量的上限。禾本科生物量与Shannon-Wiener多样性指数间呈指数负相关，拟合方程为：y = 1318.3e-0.2421x（R2 = 0.6887）。 2）添加水增加了土壤CO2排放速率，而施氮肥的影响并不明显。在较干旱的年份（降水量低于450 mm）干旱期（4月15日-6月15日）添加磷肥明显抑制了土壤呼吸，而在较湿润的年份（降水量高于450 mm）干旱期添加磷肥则显著增加了土壤呼吸。土壤呼吸与表层0-10 cm土壤含水量存在显著的正相关关系；土壤呼吸与土壤温度之间呈显著的指数正相关（R2 = 0.6798），拟合方程为：y = 0.1832e0.1299x。 3）氮素添加对半干旱区沙质草地生态系统氮有效性具有明显的增强作用，可提高土壤氮的矿化速率。该沙质草生态系统土壤有效氮主要由NO3--N组成，并具有明显的季节变化，NH4+-N和NO3--N含量在表层0-10 cm有高于10-20 cm的趋势。植物地上部分和凋落物的C:N比极低。土壤全量的C:N比明显受添加水的影响，与氮、磷添加无关。 4）添加磷素改善了半干旱区沙质草地生态系统土壤磷的有效性，添加氮和水则没有影响。0-10 cm层土壤相对有效磷有高于10-20 cm层的趋势，这说明土壤中的有效磷淋溶作用不强或者是植物主要利用了表土层10 cm以下的土壤有效磷。第一次提出P:N比的概念，利用相对有效磷和相对矿质氮的比值作为土壤相对P:N比，相对P:N比与生物量、ANPP、非禾本科ANPP之间呈显著的线性相关关系。相对P:N比与生物量的线性负相关程度最高，拟合方程为：y = -52.333x + 1356.2（R2 = 0.7263）。 5）水、肥添加对该沙质草地土壤含水量的影响并不显著，不同处理之间以及相同处理的不同层次之间土壤含水量的差异主要源自土壤的空间异质性。根据2005年4-7月的土壤含水量的方差分析结果，可以将表层0-10 cm划分为多变层，10-30 cm划分为过渡层，30-100 cm划分为稳变层。单独添加磷肥或水磷结合可以显著降低白草的蒸腾速率，而且添加磷肥可以抵消添加氮肥所导致的蒸腾速率增加。 6）添加水提高了物种丰富度和均匀度，而施氮肥降低了物种丰富度和均匀度，施磷肥也相应地增加了物种丰富度和均匀度，但幅度不大。本项研究的结果不支持单调上升格局，多样性与生产力呈负相关关系，单调下降和单峰关系两种格局都存在。10-20 cm土层相对矿质氮与物种丰富度、Shannon-Wiener指数、Shannon-Wiener均匀度指数均呈显著的负相关关系。物种丰富度与土壤相对矿质氮之间负相关关系最显著，可以用幂函数进行拟合方程：y = 348.58x-2.1236（n = 8; R2 = 0.8576）。 综合以上的研究结果，建议适量施用氮肥，加速退化沙质草地生态系统生产力的恢复；干旱年份辅以磷肥，以降低温室气体的排放速率。

稠油废水处理中优势微生物种群组成及变化规律

针对辽河油田锦采污水处理厂稠油废水，利用传统培养方法和PCR-DGGE诊断技术，对稠油废水处理过程中优势微生物种群组成和多样性进行全面系统的研究。结果表明，微生物对稠油废水生物处理的作用为细菌>真菌>放线菌。细菌数量、基因多样性指数与废水中TPH、CODCr均正相关，可以作为稠油废水水质评价的生物指标。 对影响稠油废水生物降解的主要因子进行优化表明，当30℃，pH值7.5，HRT为216h，添加N、P营养盐使N:P比为5.63:1时，CODCr去除率最高，去除后CODCr值满足污水综合排放一级标准（GB8978-1996）。利用GC-MS技术分析降解前后稠油废水中主要有机成分表明，微生物对饱和烃类化合物降解率最高，其次是低分子量芳香烃，而高分子量芳香烃、胶质和沥青质最低。 以稠油为唯一碳源，对筛选出的菌株进行摇瓶实验表明，各菌株对稠油均具有一定的降解能力，其中F0504除油能力最强，56d去除率可达63.3%；动力学方程拟合表明稠油生物降解过程符合一级动力学方程。降解后残油组分分析表明，B0505和F0501对烷烃、B0510、F0505和F0507对芳香烃、B0501和F0504对胶质、沥青质的去除率均较高，去除率都在30c%之间。 经鉴定，优势菌株B0501和B0505分别为液化金杆菌（Aureobaterium liquefaciens）和弗氏丙酸杆菌（Propionibacterium freuclenreichii），主要真菌有青霉（Penicillium）、曲霉（Aspergillus）、木霉（Trichoderma）和交链孢霉（Alternaria）。

抗菌不锈钢抗菌性能和机理初步研究

由于近年来有害微生物的肆虐和人们防病抗菌意识的增强，社会对各种新型抗菌材料的需求越来越迫切。抗菌不锈钢是一种兼具良好机械和抗菌性能的新型功能材料，具有广泛的应用前景。开发和推广抗菌不锈钢，具有重要的经济和社会意义。 本文以中科院金属研究所研制的两种抗菌不锈钢为研究对象，对其抗菌性能和抗菌机理进行了研究，以期为抗菌不锈钢的深入研发和推广提供理论依据。 本文获得了如下主要结论： 1．采用覆膜法研究了抗菌不锈钢的抗菌广谱性，铁素体和奥氏体抗菌不锈钢对供试的17株菌（除产气肠杆菌外），均显示了较强的杀灭作用，证明其具有抗菌广谱性。两种材料对非孢子（或芽孢）产生菌的杀灭作用强于孢子（或芽孢）产生菌。但是，两种材料对产气肠杆菌均无杀灭作用。 2．考察了铁素体和奥氏体的杀菌率随时间和菌浓度的变化情况。两种材料分别在作用3h时和9h时，对菌体浓度为1×107CFU/mL的大肠杆菌（ATCC25922）的杀菌率均达到99.5%。对菌体浓度≤1×107CFU/mL的大肠杆菌在24h内均可全部杀灭。 3．随打磨次数的增加，抗菌率没有变化，表明打磨不影响铁素体和奥氏体抗菌不锈钢的抗菌性能；抗菌率不受温度的影响，0～37℃之间，未观察到抗菌率受温度变化的明显影响。 4．从抗菌不锈钢中溶出的铜在杀菌过程中可能起重要作用。铁素体和奥氏体抗菌不锈钢与添加了终浓度为1mmol/L的EDTA的菌液作用后，杀菌率分别降为46.8%和38.8%，因为EDTA络合了溶液中的金属离子，间接表明铜离子在杀菌过程中起重要作用。 5．两种抗菌不锈钢中O2-的产生速率分别为0.117 nmol•min-1•g-1和0.107nmol•min-1•g-1，显著高于普通不锈钢（0.062 nmol•min-1•g-1）。细胞膜不饱和脂肪酸过氧化的终产物丙二醛含量分别为1.96 nmol/g和1.93 nmol/g。显著高于普通对照的1.08 nmol/g，表明存在脂肪酸被氧化的现象。这些结果为抗菌过程中存在O2-的氧化杀菌作用提供了间接证据。 6．通过透射电镜和原子力显微镜观察，与抗菌不锈钢作用后的细胞外形多发生变化，细胞壁和细胞膜破裂，细胞内容物漏出，有的菌体完全溶解为碎片，显示两种不锈钢对细胞膜和细胞壁形态的显著影响。随作用时间延长，菌液中钾离子浓度亦显著升高，在3h时，分别达到2.57mg/L和2.79mg/L（普通对照为1.61mg/L）。 7．在巯基氧化实验中，添加终浓度为5 mmol/L的L-cys，作用8h，铁素体的抗菌率降为11.1%,薄层层析结果显示，半胱氨酸可能被氧化成胱氨酸，表明抗菌不锈钢可能对还原性酶具有氧化作用。 8．提取与抗菌不锈钢作用后菌的DNA，凝胶电泳观察并未出现smear现象。表明在本实验条件下尚不能检测到抗菌不锈钢对细菌遗传物质的氧化切割作用。 关键词： 抗菌材料 抗菌不锈钢 抗菌性能 抗菌机理 O2-