掺入有机硅提高溶胶-凝胶二氧化硅减反膜的稳定性研究

膜层稳定性对于激光器能否长期稳定使用极为重要。多孔SiO。减反膜经热处理后，结构中还存在许多Si—OH亲水基团，透过率稳定性受环境相对湿度的影响较大。向膜层中掺入有机硅，添加疏水基团，提高了膜层的疏水性，增强了膜层的透过率稳定性。膜层中加了Si-CH3疏水基团，膜层的疏水性大大提高；当Si-CH3与二氧化硅悬胶体中的Si的摩尔比为1／5．7时，即Si—CH3质量分数为0．35％时的二氧化硅膜层，其减反效果好，疏水性也高，从而大幅度提高了膜层的透过率稳定性，延长了膜层的寿命，对二氧化硅膜层具有高激光损伤阈值

磷酸盐激光玻璃凝胶防潮膜和减反膜

采用溶胶-凝胶方法制备（CH3）2Si（OC2H5）2预聚体涂膜液以及掺入SiO2悬胶体涂膜液改性，采用旋转法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，热处理后膜层固化。SiO2改性的CH3O防潮膜，热处理后的膜层耐摩擦性能明显改善。然后旋转涂制第二层多空性SiO2减反膜，涂膜胶体通过硅酸乙脂碱催化水解缩聚制得，减反膜的折射率为约1．25，玻璃棒涂膜后激光波长1053nm减少表面反射率6．5％-7．5％，双层膜激光破坏阈值12J／cm^2，1053nm／1ns，膜层表面粗糙度（RMS）2．523nm。直径20

高激光损伤阈值溶胶-凝胶ZrO2薄膜

采用醇热法水解氧氯化锆（ZrOCl2·8H2O）制备ZrO2溶胶，提拉法涂膜。采用粘度、粒度分布、折射率、IR、DSC、AFM等测试手段对溶胶和薄膜性能进行表征。结果表明，ZrO2溶胶颗粒的平均粒径为18．9nm，薄膜经300℃热处理后折射率可高达1．95，膜层表面均匀平整，表面平均粗糙度仅为0．561nm，膜层的激光损伤阈值为14J／cm^2（1064nm，1ns）。

甲基化对多孔SiO_2增透薄膜光学稳定性能的影响

分别通过引入甲基三乙氧基硅烷(MTES)、二甲基二乙氧基硅烷(DMDES)以及六甲基二硅氮烷(HMDS)组分对SiO2悬胶体进行改性,得到不同甲基化的多孔SiO2改性薄膜。研究了改性薄膜的光学稳定性,抗激光破坏性能以及机械抗擦性能。结果表明,HMDS改性薄膜的光学稳定性最好而机械抗擦性较弱,MTES与DMDES改性薄膜的光学稳定性较低而机械抗擦性良好且均与改性组分的含量有关,甲基化改性薄膜的抗激光破坏性能比未改性薄膜的有所降低。

Análise molecular vibracional da interface adesivo-dentina após aplicação de múltiplas camadas de sistemas adesivos convencionais de dois passos

O propósito do presente estudo foi analisar o efeito da aplicação de múltiplas camadas consecutivas de dois sistemas adesivos convencionais de dois passos na difusão resinosa e padrão de distribuição dos componentes monoméricos resinosos. Dezesseis terceiros molares humanos hígidos foram tratados com os sistemas adesivos convencionais de dois passos de acordo com as instruções dos fabricantes ou com aplicações em múltiplas camadas consecutivas. Os espécimes foram seccionados paralelamente aos túbulos dentinários e as superfícies submetidas ao polimento com lixas 600, 1200, 1800, 2000 e 4000. Os espectros Raman foram coletados ao longo de uma linha perpendicular a interface adesivo-resina em intervalos de 1 ou 2 m. As medidas de difusão da resina adesiva e distribuição dos componentes monomériccos foram avaliadas pelos picos Raman de 1113 cm-1, 1609 cm-1 e 1454 cm-1. O gradiente de desmineralização usado na determinação da região de hibridização foi avaliado pelo pico de 960 cm-1 da apatita. De acordo com os resultados obtidos, a aplicação de múltiplas camadas apresentou uma tendência de homogeneização dos componentes poliméricos, dependente da composição química da resina adesiva.

Structure and properties of amorphous thin film for optical data storage

In this paper the magnetic and magneto-optical properties of amorphous rare earth-transition metal (RE-TM) alloys as well as the magnetic coupling in the multi-layer thin films for high density optical data storage are presented. Using magnetic effect in scanning tunneling microscopy the clusters structure of amorphous RE-TM thin films has been observed and the perpendicular magnetic anisotropy in amorphous RE-TM thin films has been interpreted. Experimental results of quick phase transformation under short pulse laser irradiation of amorphous semiconductor and metallic alloy thin films for phase change optical recording are reported. A step-by-step phase transformation process through metastable states has been observed. The waveform of crystallization propagation in micro-size spot during laser recording in amorphous semiconductor thin films is characterized and quick recording and erasing mechanism for optical data storage with high performance are discussed. The nonlinear optical effects in amorphous alloy thin films have been studied. By photo-thermal effect or third order optical nonlinearity, the optical self-focusing is observed in amorphous mask thin films. The application of amorphous thin films with super-resolution near field structure for high-density optical data storage is performed. (c) 2007 Elsevier B.V. All rights reserved.

Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

ZrO2, films were deposited by electron-beam evaporation with the oxygen partial pressure varying from 3 X 10(-3) Pa to I I X 10(-3) Pa. The phase structure of the samples was characterized by x-ray diffraction (XRD). The thermal absorption of the films was measured by the surface thermal lensing technique. A spectrophotometer was employed to measure the refractive indices of the samples. The laser-induced damage threshold (LIDT) was assessed using a 1064, nm Nd: yttritium-aluminium-garnet pulsed laser at pulse width of 12 ns. The influence of oxygen partial pressure on the microstructure and LIDT of ZrO2 films was investigated. XRD data revealed that the films changed from polycrystalline to amorphous as the oxygen partial pressure increased. The variation of refractive index at 550 nm wavelength indicated that the packing density of the films decreased gradually with increasing oxygen partial pressure. The absorptance of the samples decreased monotonically from 125.2 to 84.5 ppm with increasing oxygen partial pressure. The damage threshold, values increased from 18.5 to 26.7 J/cm(2) for oxygen partial pressures varying from 3 X 10(-3) Pa to 9 X 10(-3) Pa, but decreased to 17.3 J/cm(2) in the case of I I X 10(-3) Pa. (C) 2005 American Vacuum Society.

双源共蒸法制备非均匀膜的模型分析

探讨了双源共蒸法制备非均匀薄膜的堆积模型，并给出了非均匀膜的沉积速率与两种膜料沉积速率的关系．当两种膜料的沉积单分子大小近似相等或者小分子沉积速率远大于大分子时，可以近似认为混合介质膜的沉积速率等于两种膜料的沉积速率之和；当两种膜料的沉积单分子大小不满足近似相等且两种膜料的沉积速率可比较时，非均匀膜的沉积速率不能简单地用两种膜料的沉积速率之和来近似，它将随两种膜料沉积单分子的大小不同和沉积速率比不同按照不同的规律变化，并在文中给出了不同情况下的非均匀膜的沉积速率变化规律。

The study on the interface adhesion comparison of the MgF2, Al2O3, SiO2 and Ag thin films

Adhesion between the interface of pure silver thin film and three kinds of low refractive index coatings MgF2, Al2O3, SiO2 were compared in this article. The results indicated that the adhesion of Al2O3 and Ag was evidently superior to that of MgF2 and Ag, and the adhesion of MgF2 and Ag was evidently superior to that Of SiO2 and Ag. Reasons were analyzed accordingly. On the other hand, we compared the effect on the optical characteristic of Ag film when these three kinds of films were used as protective coatings and enhanced coatings. Considering the difference of the adhesion between Ag and MgF2, Al2O3, SiO2, suited uses are given for each other. © 2004 Elsevier B.V. All rights reserved.

Extended bidirectional reflectance distribution function for polarized light scattering from subsurface defects under a smooth surface

By introducing the scattering probability of a subsurface defect (SSD) and statistical distribution functions of SSD radius, refractive index, and position, we derive an extended bidirectional reflectance distribution function (BRDF) from the Jones scattering matrix. This function is applicable to the calculation for comparison with measurement of polarized light-scattering resulting from a SSD. A numerical calculation of the extended BRDF for the case of p-polarized incident light was performed by means of the Monte Carlo method. Our numerical results indicate that the extended BRDF strongly depends on the light incidence angle, the light scattering angle, and the out-of-plane azimuth angle. We observe a 180 degrees symmetry with respect to the azimuth angle. We further investigate the influence of the SSD density, the substrate refractive index, and the statistical distributions of the SSD radius and refractive index on the extended BRDF. For transparent substrates, we also find the dependence of the extended BRDF on the SSD positions. (c) 2006 Optical Society of America.

Effect of microstructure of TiO2 thin films on optical band gap energy

TiO2 coatings are prepared on fused silica with conventional electron beam evaporation deposition. After annealed at different temperatures for four hours, the spectra and XRD patterns of TiO2 thin film are obtained. XRD patterns reveal that only anatase phase can be observed in TiO2 coatings regardless of the different annealing temperatures, and with the increasing annealing temperature, the grain size gradually increases. The relationship between the energy gap and microstructure of anatase is determined and discussed. The quantum confinement effect is observed that with the increasing grain size of TiO2 thin film, the band gap energy shifts from 3.4 eV to 3.21 eV. Moreover, other possible influence of the TiO2 thin-film microstructure, such as surface roughness and thin film absorption, on band gap energy is also expected.