Formation of self-assembly and the mechanism of Si nanoquantum dots prepared by low pressure chemical vapor deposition

Si nanoquantum dots have been formed by self-assembled growth on the both Si-O-Si and Si-OH bonds terminated SiO2 surfaces using the low-pressure chemical vapor deposition (LPCVD) and surface thermal decomposition of pure SiH4 gas. We have experimentally studied the variation of Si. dot density with Si-OH bonds density, deposition temperature and SiH4 pressure, and analyzed qualitatively the formation mechanism of the Si nanoquantum dots based on LPCVD surface thermal dynamics principle. The results are very. important for the control of the density and size of Si nanoquantum dots, and have potential applications in the new quantum devices.

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Two-dimensional ZnO nanowall networks were grown on ZnO-coated silicon by thermal evaporation at low temperature without catalysts or additives. All of the results from scanning electronic spectroscope, X-ray diffraction and Raman scattering confirmed that the ZnO nanowalls were vertically aligned and c-axis oriented. The room-temperature photoluminescence spectra showed a dominated UV peak at 378 nm, and a much suppressed orange emission centered at similar to 590 nm. This demonstrates fairly good crystal quality and optical properties of the product. A possible three-step, zinc vapor-controlled process was proposed to explain the growth of well-aligned ZnO nanowall networks. The pre-coated ZnO template layer plays a key role during the synthesis process, which guides the growth direction of the synthesized products. (C) 2007 Elsevier B.V. All rights reserved.

Optical anisotropy and strain evolution of GaAs surfaces at the onset of the formation of InAs quantum dots

By using reflectance difference spectroscopy we have studied the in-plane optical anisotropy of GaAs surfaces covered by ultrathin InAs layers. The strain evolution of the GaAs surface with the InAs deposition thickness can be obtained. It is found that the optical anisotropy and the surface tensile strain attain maximum values at the onset of the formation of InAs quantum dots (QDs) and then decrease rapidly as more InAs QDs are formed with the increase of InAs deposition. The origin of the optical anisotropy has been discussed.

Temperature dependence of the formation of nano-scale indium clusters in InAlGaN alloys on Si(111) substrates

The temperature dependence of the formation of nano-scale indium clusters in InAlGaN quaternary alloys, which are grown by metalorganic chemical vapour deposition on GaN/Si(111) epilayers, is investigated. Firm evidence is provided to support the existence of phase separation, or nano-scale In-rich clusters, by the combined results of high-resolution transmission electron microscopy (HRTEM), high-resolution x-ray diffraction (HRXRD) and micro-Raman spectra. The results of HRXRD and Raman spectra indicate that the degree of phase separation is strong and the number of In clusters in the InAlGaN layers on silicon substrate is higher at lower growth temperatures than that at higher growth temperatures, which limits the In and Al incorporated into the InAlGaN quaternary alloys. The detailed mechanism of luminescence in this system is studied by low temperature photoluminescence (LT-PL). We conclude that the ultraviolet (UV) emission observed in the quaternary InAlGaN alloys arises from the matrix of a random alloy, and the second emission peak in the blue-green region results from the nano-scale indium clusters.

Effects of annealing ambient on the formation of compensation defects in InP

Positron annihilation lifetime (PAL) and photoinduced current transient spectroscopies (PICTS) have been employed to study the formation of compensation defects in undoped InP under different annealing processes with pure phosphorus (PP) ambience and iron phosphide (IP) ambience, respectively. The different annealing ambiences convert the as-grown n-type undoped InP into two types of semi-insulating (SI) states. The positron average lifetimes of as-grown InP, PP SI-InP, and IP SI-InP are found to be 246, 251, and 243 ps, respectively, which are all longer than the bulk lifetime of 240 ps, indicating the existence of vacancy-type positron-trapping defects. For as-grown InP, VInH4 complexes are the dominant defects. They dissociate into VInHn(0less than or equal tonless than or equal to3) acceptor vacancies under PP ambience annealing, compensating the residual shallow donors and turning the material semi-insulating. In forming IP SI-InP, diffusion of iron into V-In complexes under IP ambience annealing produces the substitutional compensation defect Fe-In, causing a shorter positron average lifetime. The PICTS measurements show that a group of vacancy-type defects has been suppressed by iron diffusion during the annealing process, which is in good agreement with the PAL results. (C) 2003 American Institute of Physics.

The effects of pre-irradiation on the formation of Si1-xCx alloys

Carbon ions were implanted into crystal Si to a concentration of (0.6-1.5)at% at room temperature. Some samples were pre-irradiated with S-29(i)+ ions, while others were not pre-irradiated. Then the two kinds of samples were implanted with C-12(+) ions simultaneously, and Si1-xCx alloys were grown by solid phase epitaxy with high-temperature annealing. The effects of preirradiation on the formation of Si1-xCx alloys were studied. If the dose of implanted C ion was less than that for amorphizing Si crystals, the implanted C atoms would like to combine with defects produced during implantation, and then it was difficult for Si1-xCx alloys to form after annealine, at 950 degreesC. Pre-irradiation was advantageous for Si1-xCx alloy formation. With the increase of C ion dose, the damage produced by C ions increased. Pre-irradiation was unfavorable for Si1-xCx, alloy formation. If the implanted C concentration was higher than that for solid phase epitaxy solution, only part of the implanted C atoms form Si1-xCx alloys and the effects of pre-irradiation could be neglected. As the annealing temperature was increased to 1050 degreesC, Si1-xCx alloys in both pre-irradiated and unpreirradiated samples of low C concentration remained, whereas most part of Si1-xCx alloys in samples with high C concentration vanished.

Atomic-force-microscopy investigation of the formation and evolution of Ge islands on GexSi1-x strained layers

A constant amount of Ge was deposited on strained GexSi1-x layers of approximately the same thickness but with different alloy compositions, ranging from x = 0.06 to x = 0.19. From their atomic-force-microscopy images, we found that both the size and density of Ge islands increased with the Ge composition of the strained layer. By conservation of mass, this implies that these islands must incorporate material from the underlying strained layer. (C) 2000 American Institute of Physics. [S0003-6951(00)03529-4].

Effects of annealing treatment on the formation of CO2 in ZnO thin films grown by metal-organic chemical vapor deposition

Post-growth annealing was carried out on ZnO thin films grown by metal-organic chemical vapor deposition (MOCVD). The grain size of ZnO thin film increases monotonically with annealing temperature. The ZnO thin films were preferential to c-axis oriented after annealing as confirmed by Xray diffraction (XRD) measurements. Fourier transformation infrared transmission measurements showed that ZnO films grown at low temperature contains CO2 molecules after post-growth annealing. A two-step reaction process has been proposed to explain the formation mechanism of CO2, which indicates the possible chemical reaction processes during the metal-organic chemical vapor deposition of ZnO films.

PHOTOEMISSION-STUDY OF THE INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AL AND HYDROGENATED AMORPHOUS SI

Using photoemission spectroscopy and Auger electron spectroscopy, the interfacial formation process and the reactions between Al and hydrogenated amorphous Si are probed, and annealing behaviors of the Al/a-Si:H system are investigated as well. It is found that a three-dimensional growth of Al metal clusters which includes reacted Al and non-reacted metal Al occurs at the initial Al deposition time, reacted Al and Si alloyed layers exist in the Al/a-Si:H interface, and non-reacted Al makes layer-by-layer growth forming a metal Al layer on the sample surface. The interfacial reactions and element interdiffusion of Al/a-Si:H are promoted under the vacuum annealing.

An investigation of the formation mechanisms of electric field domains in GaAs/AlAs superlattices

We have studied the vertical transport and formation mechanisms of electric field domains in doped weakly-coupled GaAs/AlAs superlattices. Under hydrostatic pressure two kinds of sequential resonant tunneling are observed within the pressure range from 0 to 4.5 kbar. A transition from Gamma-Gamma to Gamma-X sequential resonant tunneling occurs at P-t approximate to 1.6 kbar. For P < P-t, the high electric field domain is formed by the Gamma-Gamma process, while for P > P-t it is preferentially formed by the Gamma-X process.