Smaller Ge Quantum Dots Obtained by ArF Excimer Laser Annealing

Ge self-assembled quantum dots (SAQDs) are grown with a self-assembled UHV/CVD epitaxy system. Then,the as-grown Ge quantum dots are annealed by ArF excimer laser. In the ultra-shot laser pulse duration,～20ns, bulk diffusion is forbidden, and only surface diffusion occurs, resulting in a laser induced quantum dot (LIQD). The diameter of the LIQD is 20～25nm which is much smaller than the as-grown dot and the LIQD has a higher density of about 6 × 10~(10)cm~(-2). The surface morphology evolution is investigated by AFM.

A High-Efficiency Fiber-to-Waveguide Coupler with Low Polarization Dependence Using a Diluted Waveguide in InP Substrate with a 1.55μm Wavelength

We propose a fiber-to-waveguide coupler for side-illuminated p-i-n photodiodes to obtain high responsivity and low polarization dependence that is grown on InP substrate and is suitable for surface hybrid integration in low cost modules. The fiber-to-waveguide coupler is based on a diluted waveguide,which is composed of ten periods of undoped 120nm InP/80nm InGaAsP （1.05μm bandgap） multiple layers. Using the semi-vectorial three dimensional beam propagation method （BPM） with the central difference scheme,the coupling efficiency of fiber-to-waveguide under different conditions is simulated and studied,and the optimized conditions for fiber-to-waveguide coupling are obtained. For TE-like and TM-like modes,the calculated maximum coupling efficiency is higher than 94% and 92% ,respectively. The calculated polarization dependence is less than 0. ldB,showing good polarization independence.

Low-Temperature Growth of ZnO Films on GaAs by Metal Organic Chemical Vapor Deposition

ZnO thin films were grown on GaAs （001） substrates by metal-organic chemical vapor deposition （MOCVD） at low temperatures ranging from 100 to 400℃. DEZn and 1-12 O were used as the zinc precursor and oxygen precursor, respectively. The effects of the growth temperatures on the growth characteristics and optical properties of ZnO films were investigated. The X-ray diffraction measurement （XRD） results indicated that all the thin films were grown with highly c- axis orientation. The surface morphologies and crystal properties of the films were critically dependent on the growth temperatures. Although there was no evidence of epitaxial growth, the scanning electron microscopy （SEM） image of ZnO film grown at 400℃ revealed the presence of ZnO microcrystallines with closed packed hexagon structure. The photoluminescence spectrum at room temperature showed only bright band-edge （3. 33eV） emissions with little or no deep-level e- mission related to defects.

Efficient Mode-locked and Q-switched Nd∶YVO_4 Laser with Semiconductor Saturable Absorber Mirror

We reported an efficient diode pumped Nd ! YVO, 1 064 nm laser passively mode-locked and Q-switched by a semiconductor saturable absorber mirror(SESAM). At the incident pump power of 7. 5 W, 2. 81 W average output power was obtained during stable CW mode locking with a repetition rate of 111 MHz. The optical conversion efficiency was 37. 5% , and the slope efficiency was 39%. So far as we know, this is the highest optical-optical conversion efficiency with a SESAM at home.

808-nm fiber coupled module with a CW output power up to 130 W

A fiber coupled module is fabricated with integrating the emitting light from four laser diode bars into multimode fiber bundle. The continuous wave (CW) output power of the module is about 130 W with a coupling efficiency of around 80%. The output power is very stable after the temperature cycling and vibration test. No apparent power decrease has been observed as the device working continuously for 500 h.

A Novel Power Supply Solution of a Passive RFID Transponder

This paper presents a power supply solution for fully integrated passive radio-frequency identification(RFID) transponder IC,which has been implemented in 0.35μm CMOS technology with embedded EEPROM from Chartered Semiconductor.The proposed AC/DC and DC/DC charge pumps can generate stable output for RFID applications with quite low power dissipation and extremely high pumping efficiency.An analytical model of the voltage multiplier,comparison with other charge pumps,simulation results,and chip testing results are presented.

1 GHz Repetition Rate CW Mode-locked Nd∶YVO_4 Laser

A diode-pumped CW mode-locked Nd

AIGaN/GaN HEMTs Power Amplifier MIC with Power Combining at C-Band

A power amplifier MIC with power combining based on AlGaN/GaN HEMTs was fabricated and measured. The amplifier consists of four 10×120μm transistors. A Wilkinson splitters and combining were used to divide and combine the power. By biasing the amplifier at V_(DS) =40V, I(DS)= 0. 9A, a maximum CW output power of 41. 4dBm with a maximum power added efficiency (PAE) of 32. 54% and a power combine efficiency of 69% was achieved at 5. 4GHz.

Detection of Terahertz Photon by GaAs-Based Single Electron Transistor at Low Temperatures

A reproducible terahertz (THz) photocurrent was observed at low temperatures in a Schottky wrap gate single electron transistor with a normal-incident of a CH_3OH gas laser with the frequency 2. 54THz.The change of source-drain current induced by THz photons shows that a satellite peak is generated beside the resonance peak. THz photon energy can be characterized by the difference of gate voltage positions between the resonance peak and satellite peak. This indicates that the satellite peak exactly results from the THz photon-assisted tunneling. Both experimental results and theoretical analysis show that a narrow spacing of double barriers is more effective for the enhancement of THz response.

A Multi-Finger Si_(1-x)Ge_x/Si Heterojunction Bipolar Transistor for Wireless Power Amplifier Applications

A large area multi-finger configuration power SiGe HBT device(with an emitter area of about 880μm~2)was fabricated with 2μm double-mesa technology.The maximum DC current gain β is 214.The BV_(CEO) is up to 10V,and the BV_(CBO) is up to 16V with a collector doping concentration of 1×10~(17)cm~(-3) and collector thickness of 400nm.The device exhibits a maximum oscillation frequency f_(max) of 19.3GHz and a cut-off frequency f_T of 18.0GHz at a DC bias point of I_C=30mA and V_(CE)=3V.MSG(maximum stable gain)is 24.5dB,and U(Mason unilateral gain)is 26.6dB at 1GHz.Due to the novel distribution layout,no notable current gain fall-off or thermal effects are observed in the I-V characteristics at high collector current.

Uniformity Investigation in 3C-SiC Epitaxial Layers Grown on Si Substrates by Horizontal Hot-Wall CVD

50mm 3C-SiC epilayers are grown on （100） and （111） Si substrates in a newly developed horizontal lowpressure hot-wall CVD reactor under different growth pressures and flow rates of H_2 carrier gas. The structure,electrical properties, and thickness uniformity of the 3C-SiC epilayers are investigated by X-ray diffraction （XRD） ,sheet resistance measurement, and spectroscopic ellipsometry. XRD patterns show that the 3C-SiC films have excellent crystallinity. The narrowest full widths at half maximum of the SIC（200） and （111） peaks are 0.41° and 0.21°, respectively. The best electrical uniformity of the 50mm 3C-SiC films obtained by sheet resistance measurement is 2.15%. A σ/mean value of ± 5.7% in thickness uniformity is obtained.

High power red-light GaInP/AlGaInP laser diodes with nonabsorbing windows based on Zn diffusion-induced quantum well intermixing

The layer structure of GaInP/AlGaInP quantum well laser diodes (LDs) was grown on GaAs substrate using low-pressure metalorganic chemical vapor deposition (LP-MOCVD) technique. In order to improve the catastrophic optical damage (COD) level of devices, a nonabsorbing window (NAW), which was based on Zn diffusion-induced quantum well intermixing, was fabricated near the both ends of the cavities. Zn diffusions were respectively carried out at 480, 500, 520, 540, and 580 Celsius degree for 20 minutes. The largest energy blue shift of 189.1 meV was observed in the window regions at 580 Celsius degree. When the blue shift was 24.7 meV at 480 Celsius degree, the COD power for the window LD was 86.7% higher than the conventional LD.

360-nm Photoluminescence from Silicon Oxide Films Embedded with Silicon Nanocrystals

Si-rich silicon oxide films were deposited by RF magnetron sputtering onto composite Si/SiO2 targets. After annealed at different temperature, the silicon oxide films embedded with silicon nanocrystals were obtained. The photoluminescenee（PL） from the silicon oxide films embedded with silicon nanocrystals was observed at room temperature. The strong peak is at 360 nm, its position is independent of the annealing temperature. The origin of the 360-nm PL in the silicon oxide films embedded with silicon nanoerystals was discussed.

An All-E-Beam Lithography Process for the Patterning of 2D Photonic Crystal Waveguide Devices

We present an all-e-beam lithography (EBL) process for the patterning of photonic crystal waveguides.The whole device structures are exposed in two steps. Holes constituting the photonic crystal lattice and defects are first exposed with a small exposure step size (less than 10nm). With the introduction of the additional proximity effect to compensate the original proximity effect, the shape, size, and position of the holes can be well controlled.The second step is the exposure of the access waveguides at a larger step size (about 30nm) to improve the scan speed of the EBL. The influence of write-field stitching error can be alleviated by replacing the original waveguides with tapered waveguides at the joint of adjacent write-fields. It is found experimentally that a higher exposure efficiency is achieved with a larger step size;however,a larger step size requires a higher dose.

Comparison of Loss and Crosstalk Characteristics of SOI Based Intersecting Waveguides with Different Bend Structures

By means of two dimension beam propagation method (2D-BPM) with high order Pade approximation, behaviors of SOI waveguide based bend intersections with variant bending radius are simulated and analized. The result shows that crosstalk of intersections decreases with the increase of bending radius and intersecting angle. Furthermore, loss and crosstalk characteristics of bend intersections formed by sine bend, cosine bend and arc bend are compared. Sine bend based structures are proved that it can present lowest loss and smallest crosstalk properties among the three and may find their wide application in the design of bend intersections and other more complicated photonic devices and circuits.