Al2O3 : Cr3+ nanotubes synthesized via homogenization precipitation followed by heat treatment

Cr3+-doped NH4Al(OH)(2)CO3 nanotubes, templated by surfactant assemblies, were successfully synthesized via the homogenization precipitation method, and various crystallographic phase Al2O3:Cr3+ nanotubes were also obtained by postannealing at different temperatures. The characteristic R-1, R-2 doublet line transitions of ruby can be observed in the high crystalline alpha-Al2O3 nanotubes calcined at temperatures higher than 1200 degrees C. The results also indicate that the formation mechanism of the tubular nanostructures should result from the self-rolling action of layered compound NH4Al(OH)(2)CO3 under the assistance of the surfactant soft-template. The convenient synthetic procedure, excellent reproducibility, clean reactions, high yield, and fine quality of products in this work make the present route attractive and significant. Aluminum oxide nanotubes with high specific surface area could be used as fabricating nanosized optical devices doped with different elements and stable catalyst supports of metal clusters.

Pt nanoparticles: Heat treatment-based preparation and Ru(bpy)(3)(2+)-mediated formation of aggregates that can form stable films on bare solid electrode surfaces for solid-state electrochemiluminescence detection

A simple thermal process for the preparation of small Pt nanoparticles is presented, carried out by heating a H-2-PtCl6/3- thiophenemalonic acid aqueous solution. The following treatment of such colloidal Pt solution with Ru( bpy)(3)(2+) causes the assembly of Pt nanoparticles into aggregates. Most importantly, directly placing such aggregates on bare solid electrode surfaces can produce very stable films exhibiting excellent electrochemiluminescence behaviors.

Study on the phase behavior of BaEu2Mn2O7 through heat treatment of a single crystal

A new orthorhombic phase of BaEu2Mn2O7 with the space group of Ccmm (no.63) was identified for single crystals after heat treatment and its Crystal Structure was determined by single crystal X-ray diffractometry. The volume Of the unit cell has twice the fundamental tetragonal cell and corner-shared MnO6 octahedra are slightly distorted and Mn-O-Mn angle between the neighboring octahedra tilts with an angle by around 3 degrees from b-axis. It is concluded from the results of the heat treatment of single crystals at various temperatures that this orthorhombic phase changes into a tetragonal One With superstructure (P4(2)/mnm) at 402 K and changes once more into the fundamental tetragonal phase (I4/mmm) above 552 K. The tetragonal phase with superstructure which has been expected to be an unstable one is stable between the two temperatures.

One-step synthesis and size control of dendrimer-protected gold nanoparticles: A heat-treatment-based strategy

Dendrimer-protected gold nanoparticles have been facilely obtained by heating an aqueous solution containing third generation poly(propyleneimine) dendrimers and HAuCl4 without the additional step of introducing other reducing agents. Transmission electron microscopy (TEM) and UV vis data indicate the size the nucleation and growth kinetics of gold nanoparticles thus formed which can be tuned by changing the initial molar ratio of dendrimer to gold.

Variation of crystallographic parameters in PEEKK with heat treatment temperature

Using the wide-angle X-ray diffraction method, the variation of crystallographic parameters of poly(aryl ether ether ketone ketone) (PEEKK) has been studied in different heat treatment temperatures. All the reflections and their intensities as well as their Miller indices are presented in detail according to an orthorhombic system. The investigation indicates that the unit cell parameters a, b, c and the unit cell volume V systematically decrease with increasing heat treatment temperature. This variation is interpreted by the change of conformation of polymer molecular chains during thermal treatment. The results calculated from the formula of degree of crystallinity (W-c,W-x) for PEEKK, which was derived based on X-ray scattering intensity theory and the graphic multipeak resolution method, are compatible with the density measurement (W-c,W-d) and calorimetry (W-c,W-h) values. (C) 1997 Elesevier Science Ltd.