Stress analysis of ZrO2/SiO2 multilayers deposited on different substrates with different thickness periods

The effects of repeating thickness periods on stress are studied in ZrO2/SiO2 multilayers deposited by electron-beam evaporation on BK7 glass and fused-silica substrates. The results show that the residual stress is compressive and decreases with an increase of the periods of repeating thickness in the ZrO2/SiO2 multilayers. At the same time, the residual stress in multilayers deposited on BK7 glass is less than that of samples deposited on fused silica. The variation of the microstructure examined by x-ray diffraction shows that microscopic deformation does not correspond to macroscopic stress, which may be due to variation of the interface stress. (c) 2005 Optical Society of America.

ZrO2／SiO2多层膜中膜厚组合周期数及基底材料对残余应力的影响

ZrO2／SiO2多层膜由相同沉积条件下的电子束蒸发方法制备而成，通过改变多层膜中高(ZrO2)、低(SiO2)折射率材料膜厚组合周期数的方法，研究了沉积在熔石英和BK7玻璃基底上多层膜中残余应力的变化．用ZYGO光学干涉仪测量了基底镀膜前后曲率半径的变化，并确定了薄膜中的残余应力．结果发现，该多层膜中的残余应力为压应力，随着薄膜中膜厚组合周期数的增加，压应力值逐渐减小．而且在相同条件下，石英基底上所沉积多层膜中的压应力值要小于BK7玻璃基底上所沉积多层膜中的压应力值．用X射线衍射技术测量分析了膜厚组合周

Laser conditioning and multi-shot laser damage accumulation effects of HfO2/SiO2 antireflective coatings

Laser conditioning effects of the HfO2/SiO2 antireflective (AR) coatings at 1064 nm and the accumulation effects of multishot laser radiation were investigated. The HfO2/SiO2 AR coatings were prepared by E-beam evaporation (EBE). The singleshot and multi-shot laser induced damage threshold was detected following ISO standard 11254-1.2, and the laser conditioning was conducted by three-step raster scanning method. It was found that the single-shot LIDT and multi-shot LIDT was almost the same. The damage mostly > 80% occurred in the first shot under multi-shot laser radiation, and after that the damage occurring probability plummeted to < 5%. There was no obvious enhancement of the laser damage resistance for both the single-shot and multi-shot laser radiation of the AR coatings after laser conditioning. A Nomarski microscope was employed to map the damage morphology, and it found that the damage behavior is defect-initiated for both unconditioned and conditioned samples. © 2004 Elsevier B.V. All rights reserved.

The study on the interface adhesion comparison of the MgF2, Al2O3, SiO2 and Ag thin films

Adhesion between the interface of pure silver thin film and three kinds of low refractive index coatings MgF2, Al2O3, SiO2 were compared in this article. The results indicated that the adhesion of Al2O3 and Ag was evidently superior to that of MgF2 and Ag, and the adhesion of MgF2 and Ag was evidently superior to that Of SiO2 and Ag. Reasons were analyzed accordingly. On the other hand, we compared the effect on the optical characteristic of Ag film when these three kinds of films were used as protective coatings and enhanced coatings. Considering the difference of the adhesion between Ag and MgF2, Al2O3, SiO2, suited uses are given for each other. © 2004 Elsevier B.V. All rights reserved.

Effects of CO2 laser conditioning of the antireflection Y2O3/SiO2 coatings at 351 nm

Y2O3/SiO2 coatings were deposited on fused silica by electron beam evaporation. A continuous wave CO2 laser was used to condition parts of the prepared samples at different scanning speeds in the air. LAMBDA 900 spectrometer was used to investigate the changes of the transmittance and residual reflection spectrum. A Nomarski microscope under dark field was used to examine the changes of the micro defect density. The changes of the surface roughness and the microstructure of the film before and after conditioning were investigated by AFM and X-ray diffraction, respectively. We found that laser-induced damage threshold (LIDT) of the films conditioning at 30 mm/s scanning speed was increased by more than a factor of 3 over the thresholds of the as-deposited films. The conditioning effect was correlated with an irradiation-induced decrease of the defect density and absorption of the films. (c) 2005 Elsevier B.V. All rights reserved.

沉积参量及时效时间对SiO2薄膜残余应力的影响

SiO2薄膜由电子束蒸发方法沉积而成。用GPI数字波面光学干涉仪测量了不同沉积条件下玻璃基底镀膜前后曲率半径的变化，并确定了SiO2薄膜中的残余应力。在其他条件相同的情况下，当沉积温度由190℃升高到350℃时，SiO2薄膜中的压应力由一156MPa增大为-289MPa。氧分压由3．0×10^-3Pa升高到13．0×10^-3Pa时，SiO2薄膜中的应力由-223．5MPa变为20．4MPa。通过对薄膜折射率的测量，发现薄膜的堆积密度随沉积条件的改变也发生了规律性的变化。应力的变化主要是由于沉积时蒸发粒子

氧分压对电子束蒸发SiO2薄膜机械性质和光学性质的影响

采用ZYGO MarkⅢ-GPI数字波面干涉仪、NamoScopeⅢa型原子力显微镜对不同氧分压下电子束蒸发方法制备的SiO2薄膜中的残余应力及表面形貌进行了研究，结果发现：随着氧分压的增大，薄膜中的压应力值逐渐减小，最后变为张应力状态；同时薄膜的表面粗糙度也随着氧分压的增大而逐渐增大，另外，折射率对氧分压也非常敏感，随着氧分压的增大呈现出了减小的趋势，这些现象主要是由于氧分压的改变使得SiO2薄膜结构发生了变化引起的。

Laser conditioning of ZrO2 : Y2O3/SiO2 mirror coatings prepared by E-beam evaporation

Laser conditioning effects of the dielectric mirror coatings with different designs were investigated. Simple quarter-wave ZrO2:Y2O3/SiO2 mirrors and half-wave SiO2 over-coated ZrO2:Y2O3/SiO2 mirror coatings were fabricated by E-beam evaporation (EBE). The absorbance of the samples before and after laser conditioning was measured by surface thermal lensing (STL) technology and the defects density was detected under Nomarski microscope. The enhancement of the laser damage resistance was found after laser conditioning. The dependence of the laser conditioning on the coating design was also observed and the over-coated sample obtained greatest enhancement, whereas the absorbance of the samples did not change obviously. During the sub-threshold fluence raster scanning, the minor damage about defects size was found and the assumption of pre-damage mechanism, based on the functional damage concept, was put forward. The improvement of the laser induced damage threshold (LIDT) was attributed to the benign damage of the defects and the dependence on the coating design owed to the damage growth behavior of different coating designs. (C) 2004 Elsevier B.V. All rights reserved.

Negative dispersion mirrors in Ta2O5/: SiO2 for femtosecond Ti : Sapphire lasers by using gires-tournois interferometers

We design and experimentally demonstrate some negative dispersion mirrors with optimized Gires-Tournois interferometers. The mirror structure is composed of 38 alternating Ta2O5 and SiO2 layers and could be regarded as two sections: high-reflectivity section consisting of a series of quarter-wavelength optical thickness stacks and negative-dispersion section consisting of only 13 layers. The designed mirrors exhibit the expected performance. These mirrors were fabricated by using ion beam sputtering. By adopting such mirrors, dispersion of a mode-locked femtosecond Ti:sapphire laser has been compensated for mostly. With two series of the mirrors, 32 fs and 15 fs pulses have been obtained respectively.

Damage on HfO2/SiO2 high-reflecting coatings under single and multiple Nd:YAG laser pulse irradiation

The single- and multi-shot damage behaviors of HfO2/SiO2 high-reflecting (HR) coatings under Nd:YAG laser exposure were investigated. Fundamental aspects of multi-shot laser damage, such as the instability due to pulse-to-pulse accumulation of absorption defect and structural defect effect, and the mechanism of laser induced defect generation, are considered. It was found in multi-shot damage, the main factors influencing laser-induced damage threshold (LIDT) are accumulation of irreversible changes of structural defects and thermal stress that induced by thermal density fluctuations.

ZrO2／SiO2棱镜偏振膜的膜系优化设计与制备

对以K9玻璃为基底，采用ZrO2和SiO2为高低膜料来制备棱镜偏振膜，并进行膜系优化设计。设计指标为：波长540nm处满足Tp>99％，Ts<1％。优化结果表明，膜系以H3L(HL)^13 H3LH为最佳膜系。测试结果表明，此膜系完全满足设计指标，偏振性能优良。探讨了参考波长对偏振膜工作带宽的影响。

Ta2O5／SiO2硬膜双腔滤光片激光损伤特性研究

研究了Ta2O5／SiO2硬膜双腔干涉滤光片带内、带边及带外的吸收和激光损伤特性。实验发现，对于作用激光，带通滤光片的驻波场分布、吸收率和损伤阈值在带内、带边和带外的响应特性对作用激光波长均呈现出明显的选择性。根据实验结果，结合滤光片的驻波场分析，给出了带通滤光片的损伤机理。

真空中有机污染物对TiO2/SiO2介质膜损伤阈值的影响

本文主要研究了真空中有机污染物对薄膜阈值的影响。采用电子枪蒸镀的方式制备了由TiO2/SiO2两种材料组合而成的1064nm高反膜，分别在大气和真空中对其损伤阈值进行了测量。发现在真空中污染物易黏附于光学元件表面，导致损伤；真空中的氧分子会加速损伤过程，根据破斑形貌的分析认为是由于在激光作用下氧分子与有机污染物发生反应造成的；真空中的有机污染物被去除后，真空和大气中的损伤阈值差别不大，破斑形貌相似。结果表明有机污染物是真空中损伤阈值降低的主要原因。

Comparison of femtosecond and nanosecond laser-induced damage in HfO2 single-layer film and HfO2-SiO2 high reflector

HfO2 single layers, 800 run high-reflective (HR) coating, and 1064 ran HR coating were prepared by electron-beam evaporation. The laser-induced damage thresholds (LIDTs) and damage morphologies of these samples were investigated with single-pulse femtosecond and nanosecond lasers. It is found that the LIDT of the HfO2 single layer is higher than the HfO2-SiO2 HR coating in the femtosecond regime, while the situation is opposite in the nanosecond regime. Different damage mechanisms are applied to study this phenomenon. Damage morphologies of all samples due to different laser irradiations are displayed. (c) 2007 Optical Society of America.