Fatigue-free behavior of Bi3.25La0.75Ti3O12 thin films grown on several bottom eletrodes by the polymeric precursor method

Fatigue-free Bi3.25La0.75Ti3O12 (BLT) thin films were grown on LaNiO3,RuO2, and La0.5Sr0.5CoO3 bottom electrodes in a microwave furnace at 700 degreesC for 10 min. The remanent polarization (P-r) and the drive voltage (V-c) were in the range of 11-23 muC/cm(2) and 0.86-1.56 V, respectively, and are better than the values found in the literature. The BLT capacitors did not show any significant fatigue up to 10(10) read/write switching cycles. (C) 2004 American Institute of Physics.

a-b axis-oriented lanthanum doped Bi4Ti3O12 thin films grown on a TiO2 buffer layer

a-b axis-oriented, lanthanum doped Bi4Ti3O12 (BLT) thin films with a TiO2 rutile buffer layer deposited on Pt/Ti/SiO2/Si substrates were grown by the soft chemical method. Butterfly dielectric behavior has been achieved and can be ascribed to the ferroelectric domain switching. The remanent polarization and the coercive voltage for the film deposited on TiO2 buffer layer were 22.2 mu C/cm(2) and 1.8 V, respectively. Random-oriented BLT films showed a reduction in switching polarization when compared to the a-b axis-oriented films. Due to the excellent physical properties, these films are a promising candidate for use in lead-free applications in ferroelectric devices. (c) 2006 American Institute of Physics.

Efficient flotation of yeast cells grown in batch culture

A fast flotation assay was used to select new floating yeast strains. The flotation ability did not seem to be directly correlated to total extracellular protein concentration of the culture. However, the hydrophobicity of the cell was definitely correlated to the flotation capacity. The Saccharomyces strains (FLT strains) were highly hydrophobic and showed an excellent flotation performance in batch cultures without additives (flotation agents) and with no need for a special flotation chamber or flotation column. A stable and well-organized structure was evident in the dried foam as shown by scanning electron microscopy which revealed its unique structure showing mummified cells (dehydrated) attached to each other. The attachment among the cells and the high protein concentration of the foams indicated that proteins might be involved in the foam formation. The floating strains (strains FLT) which were not flocculent and showed no tendency to aggregate, were capable of growing and producing ethanol in a synthetic medium containing high glucose concentration as a carbon source. The phenomenon responsible for flotation seems to be quite different from the flocculation phenomenon. (C) 1996 John Wiley & Sons, Inc.

Low temperature annealing of amorphous gallium arsenide films

This work reports the changes in the optical properties produced by annealing of amorphous GaAs at temperatures smaller than or just sufficient to produce crystallization of the material. The films were grown by the flash evaporation technique on glass substrates at room temperature. Optical and structural changes of our samples were monitored through photothermal deflection spectroscopy, optical transmittance and reflectance and X-ray diffraction (XRD). The structural results from XRD detected no crystallization of the films for temperatures up to 240 degreesC. We have observed consistent changes in the optical gap and Urbach energy of the annealed film. The optical gap increases with increasing annealing temperature from 1.17 to 1.32 eV. The Urbach energy decrease from 120 meV (as-grown film) to 105 meV (anneal at 200 degreesC). We propose that these changes are due to a diminution of the tail state defects and/or the relaxation of strained bonds. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Optical properties of Mg doped LiNbO3 thin films grown by polymeric precursor method.

Polymeric precursor solution was used to deposit by spin-coating pure and Mg doped LiNbO3 thin films on sapphire substrates. The effects of magnesium addition on crystallinity, morphology and optical properties of the annealed films were investigated. X-ray diffraction patterns indicate the oriented growth of the films. AFM studies show that the films are very homogeneous, dense and present smooth surfaces. The refractive index and optical losses obtained by the prism coupling method were influenced by the magnesium addition.

Mullite whiskers grown from erbia-doped aluminum hydroxide-silica gel

Mullite whiskers and anisotropic grains that were derived from erbia-doped aluminum hydroxide-silica gel were studied. Firing 3.0-mol%-erbia-doped isostatically pressed pellets at 1600 degrees C for 1.0-8.0 h resulted in a high surface concentration of mullite whiskers. Their c-axes were aligned preferentially along the pellet surface; the maximum length was 50 mu m, and the maximum aspect ratio was 23. The pellet surface was fully covered by mullite whiskers, and small anisotropic grains with a low aspect ratio were observed in the bulk. The voids that were observed in the fracture surfaces were covered fully by mullite whiskers. The large number of voids resulted in an apparent density of 1.60 g/cm(3) in the sintered pellets. The molar ratio of alumina to silica in the whiskers was in the range of 1.30-1.45 tan average value of 1.31), regardless of whether the alumina/silica powder compositions were mixed in a 3:2 or 2:1 ratio.

Raman phonon modes of zinc blende InxGa1-xN alloy epitaxial layers

Transverse-optical (TO) and longitudinal-optical (LO) phonons of zinc blende InxGa1-xN (0 less than or equal to x less than or equal to 0.31) layers are observed through first-order micro-Raman scattering experiments. The samples are grown by molecular-beam epitaxy on GaAs (001) substrates, and x-ray diffraction measurements are performed to determine the epilayer alloy composition. Both the TO and LO phonons exhibit a one-mode-type behavior, and their frequencies display a linear dependence on the composition. The Raman data reported here are used to predict the A(1) (TO) and E-1 (TO) phonon frequencies of the hexagonal InxGa1-xN alloy. (C) 1999 American Institute of Physics. [S0003-6951(99)01234-6].

Tin-doped indium oxide nanobelts grown by carbothermal reduction method

This communication discusses the formation of doped nanobelts produced by a simple route. Tin-doped indium oxide (ITO) nanobelts were obtained by a carbothermal reduction method. The nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX) and wavelength-dispersive X-ray spectroscopy (WDX). The results show that the nanobelts have a cubic structure, are single crystalline and doped with tin and grow in the [400] direction.

Analysis of tolerance to copper and zinc in Aechmea blanchetiana grown in vitro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Magnetophotoluminescence study of GaAs/AlGaAs coupled double quantum wells with bimodal heterointerface roughness

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sulfonation and anticoagulant activity of botryosphaeran from Botryosphaeria rhodina MAMB-05 grown on fructose

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nucleation and growth evolution of InP dots on InGaP/GaAs

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Piezoelectric behavior of SrRuO(3) buffered lanthanum modified bismuth ferrite thin films grown by chemical method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Photodesorption and electron trapping in n-type SnO2 thin films grown by dip-coating technique

Thin films of undoped and Sb-doped (2 atg%) SnO2 have been prepared by sol-gel dip-coating technique on borosilicate glasses. Variation of photoconductivity excitation with wavelength and optical absorption indicate indirect bandgap transition with energy of ≅ 3.5 eV. Conductance as function of temperature indicates two levels of capture with 39 and 81 meV as activation energies, which may be related to an Sb donor and oxygen vacancy respectively. Electron trapping by these levels are practically destroyed by UV photoexcitation (305 nm) and heating in vacuum to 200°C. Gas analysis using a mass spectrometer indicates an oxygen related level, which may not be desorbed in the simpler O2 form.

Structural and surface morphology characterizations of oriented LiNbO3 thin films grown by polymeric precursor method

Polymeric precursor solution was used to deposit LiNbO3 thin films by dip coating on sapphire substrates. The effects of processing variables, such as heat treatment conditions and number of deposited layers, on crystallinity and morphology of the final films were investigated. X-ray diffraction patterns show the oriented growth of the films. The rocking curves, obtained around the (006) LiNbO3 peak, revealed that the shape peak and the FWHM value were influenced by the processing variables. According to these parameters, some films presented very homogeneous dense and smooth surfaces, as shown by the SEM and AFM studies.