Effect of in situ thermal treatment during growth on crystal quality of GaN epilayer grown on sapphire substrate by MOVPE

GaN epilayers on sapphire substrate grown by metalorganic vapor-phase epitaxy (MOVPE) in a horizontal-type low-pressure two-channel reactor were investigated. Samples were characterized by X-ray diffraction (XRD), Raman scattering, atomic force microscopy (AFM) and photoluminescence (PL) measurements. The influence of the temperature changes between low temperature (LT) deposited GaN buffer and high temperature (WT) grown GaN epilayer on crystal quality of epilayer was extensively studied. The effect of in situ thermal annealing during the growth on improving the GaN layer crystal quality was demonstrated and the possible mechanism involved in such a growth process was discussed. (C) 2001 Elsevier Science B.V. All rights reserved.

Studies of high DC current induced degradation in III-V nitride based heterojunctions

We report experiments on high de current stressing in commercial III-V nitride based heterojunction light-emitting diodes. Stressing currents ranging from 100 mA to 200 mA were used. Degradations in the device properties were investigated through detailed studies of the current-voltage (I-V) characteristics, electroluminescence, deep-level transient Fourier spectroscopy and flicker noise. Our experimental data demonstrated significant distortions in the I-V characteristics subsequent to electrical stressing. The room temperature electro-luminescence of the devices exhibited a 25% decrement in the peak emission intensity. Concentration of the deep-levels was examined by deep-level transient Fourier spectroscopy, which indicated an increase in the density of deep-traps from 2.7 x 10(13) cm(-3) to 4.2 x 10(13) cm(-3) at E-1 = E-C - 1.1 eV. The result is consistent with our study of 1/f noise, which exhibited up to three orders of magnitude increase in the voltage noise power spectra. These traps are typically located at energy levels beyond the range that can be characterized by conventional techniques including DLTS. The two experiments, therefore, provide a more complete picture of trap generation due to high dc current stressing.

Hydrogen-dependent lattice dilation in GaN

Using Raman spectroscopy we have analysed the strain status of GaN films grown on sapphire substrates by NH3 source molecular beam epitaxy (MBE). In addition to the expected compressive biaxial strain, in some cases GaN films grown on c-face sapphire substrates suffer from serious tensile biaxial strain. This anomalous behaviour has been well interpreted in terms of interstitial hydrogen-dependent lattice dilation. The hydrogen concentration in the films is measured by nuclear reaction analysis (NRA). With increasing hydrogen incorporation, the residual compressive biaxial strain is first further relaxed, and then turns into tensile strain when the hydrogen contaminant exceeds a critical concentration. The hydrogen incorporation during the growth process is found to be growth-rate dependent, and is supposed to be strain driven. We believe that the strain-induced interstitial incorporation is another way for strain relaxation during heteroepitaxy, besides the two currently well known mechanisms: formation of dislocations and growth front roughening.

The content calculation of hexagonal phase inclusions in cubic GaN films on GaAs(001) substrates grown by metalorganic chemical vapor deposition

Cubic GaN(c-GaN) films are grown on GaAs(001) substrates by metalorganic chemical vapor deposition (MOCVD). Two GaN samples were grown with different buffer layer, the deposition time of each was 1 and 3 min, respectively. 4-circle X-ray double crystal diffraction (XRDCD) was used to study the secondary crystallographic phases presented in the c-GaN films. The phase composition of the epilayers was determined by X-ray reciprocal space mapping. The intensities of the c-GaN(002) and h-GaN(10 (1) over bar 1) planes detected in the mapping were investigated by omega scans. The content of the hexagonal phase inclusions in the c-GaN films was calculated to about 1.6 and 7.9%, respectively. The thicker buffer layer is not preferable for growing high quality pure c-GaN films. (C) 2000 Elsevier Science S.A. All rights reserved.

Room-temperature optical transitions in Mg-doped cubic GaN/GaAs(100) grown by metalorganic chemical vapor deposition

The mechanism of room-temperature optical transitions in a Mg-doped cubic GaN epilayer grown on GaAs(100) by metalorganic chemical vapor deposition has been investigated. By examining the dependence of photoluminescence on the excitation intensity (which varied over four orders) at room temperature, four different emissions with different origins were identified. A blue emission at similar to 3.037 eV was associated with a shallow Mg acceptor, while three different lower-energy emissions at similar to 2.895, similar to 2.716, and similar to 2.639 eV were associated with a deep Mg complex. In addition to a shallow acceptor at E congruent to 0.213 eV, three Mg-related deep defect levels were also found at around 215, 374, and 570 meV (from the conduction band). (C) 2000 American Institute of Physics. [S0021-8979(00)01904-6].

Hydrogen contaminant and its correlation with background electrons in GaN

GaN epilayers grown by molecular beam epitaxy using NH3 as the nitrogen source were found to contain hydrogen. We further notice that the background electron concentration in GaN can be correlated with the amount of hydrogen contaminant. X-ray photoelectron spectroscopy (XPS) measurements of the N Is peak reveal that hydrogen is bound to nitrogen. This will make the corresponding Ga atom see insufficient N counterpart, as can be inferred from the XPS Ga 3d spectrum. We then think that nitrogen in the lattice terminated by hydrogen is an effective nitrogen vacancy and hence a donor accounting for the background electrons.

Energy bands and acceptor binding energies of GaN

The energy bands of zinc-blende and wurtzite GaN are calculated with the empirical pseudopotential method, and the pseudopotential parameters for Ga and N atoms are-given. The calculated energy bands are in agreement with those obtained by the ab initio method. The effective-mass theory for the semiconductors of wurtzite structure is established, and the effective-mass parameters of GaN for both structures are given The binding energies of acceptor states are calculated by solving strictly the effective-mass equations. The binding energies of donor and acceptor are 24 and 142 meV for the zinc-blende structure, 20 and 131, and 97 meV for the wurtzite structure, respectively, which are consistent with recent experimental results. It is proposed that there are two kinds of acceptor in wurtzite GaN. One kind is the general acceptor such as C, which substitutes N, which satisfies the effective-mass theory. The other kind of acceptor includes Mg, Zn, Cd, etc., the binding energy of these accepters is deviated from that given by the effective mass theory. In this report, wurtzite GaN is grown by the molecular-beam epitaxy method, and the photoluminescence spectra were measured. Three main peaks are assigned to the donor-acceptor transitions from two kinds of accepters. Some of the transitions were identified as coming from the cubic phase of GaN, which appears randomly within the predominantly hexagonal material. [S0163-1829(99)15915-0].

Cubic InGaN grown by MOCVD

We report on the growth of high-quality cubic phase InGaN on GaAs by MOCVD. The cubic InGaN layers are grown on cubic GaN buffer layers on GaAs (001) substrates. The surface morphology of the films are mirror-like. The cubic nature of the InGaN films is obtained by Xray diffraction (XRD) measurements. The InGaN layers show strong photoluminescence (PL) at room temperature. Neither emission peak from wurtzite GaN nor yellow luminescence is observed in our films. The highest In content as determined by XRD is about 17% with an PL emission wavelength of 450 nm. The FWHM of the cubic InGaN PL peak are 153 meV and 216 meV for 427 nm and 450 nm emissions, respectively. It is found that the In compositions determined from XRD are not in agreement with those estimated from PL measurements. The reasons for this disagreement are discussed.

p-type co-doping study of GaN by photoluminescence

Photoluminescence measurements were performed on p-type co-doping effects of C, As, and Mg in GaN. The dopants were incorporated into GaN by ion implantation performed at 77 K. We find that the 3.42 eV luminescence line is sensitive to hole concentration, and propose that after cartful calibration the 3.42 eV line may be used as a probe to measure hole concentration in GaN. Simply doping one kind of accepters will not result in holes, while co-doping can substantially improve p-type doping efficiency. As + C and As + Mg co-doping induce an acceptor level of 180 meV above the valence band. Mg + C co-doping is the most promising method for p-type doping, the related acceptor level is determined to be as shallow as 130 meV. The improvement of the doping efficiency by co-doping is probably due to the decrease of the acceptor ionization energy. (C) 1999 Elsevier Science B.V. All rights reserved.

The growth of an AlGaN/GaN modulation-doped heterostructure by NH3 source molecular beam epitaxy

Using NH3 cracked on the growing surface as the nitrogen precursor, an AlGaN/GaN modulation-doped (MD) heterostructure without a buffer layer was grown on a nitridated sapphire substrate in a home-made molecular beam epitaxy (MBE) system. Though the Al composition is as low as 0.036, as deduced from photoluminescence (PL) measurements, the AlGaN barrier layer can be an efficient carrier supplier for the formation of a two-dimensional electron gas (2DEG) at the heterointerface. The 2DEG characteristics are verified by the variable temperature Hall measurements down to 7 K. Using a parallel conduction model, we estimate the actual mobility of the 2DEG to be 1100 cm(2)/V s as the sheet carrier density to be 1.0 x 10(12) cm(-2). Our results show that the AlGaN/GaN system is very suitable for the fabrication of high electron mobility transistors (HEMTs). (C) 1998 Elsevier Science B.V. All rights reserved.

High-concentration hydrogen in unintentionally doped GaN

We use nuclear reaction analysis to study hydrogen in unintentionally doped GaN, and high-concentration hydrogen, nearly 10(21) cm(-3), is detected. Accordingly, a broad but intense infrared absorption zone with a peak at 2962 cm(-1) is reported, which is tentatively assigned to the stretch mode of NH: Ga complex. The complex is assumed to be one candidate answering for background electrons in unintentionally doped GaN. (C) 1998 Elsevier Science B.V. All rights reserved.

Properties of GaN epilayers with various growth conditions grown by gas source molecular beam epitaxy

GaN epilayers on sapphire (0001) substrates were grown by the gas source molecular beam epitaxy (GSMBE) method using ammonia (NH,) gas as the nitrogen source. Properties of gallium nitride (GaN) epilayers grown under various growth conditions were investigated. The growth rate is up to 0.6 mu m/h in our experiments. Cathodoluminescence, photoluminescence and Hall measurements were used to characterize the films. It was shown that the growth parameters have a significant influence on the GaN properties. The yellow luminescence was enhanced at higher growth temperature. And a blue emission which maybe related to defects or impurity was observed. Although the emission at 3.31 eV can be suppressed by a low-temperature buffer layer, a high-quality GaN epilayer can be obtained without the buffer layer. (C) 1998 Elsevier Science B.V. All rights reserved.

Alignment of misfit dislocations in the In0.52Al0.48As/InxGa1-xAs/In0.52Al0.48As/InP heterostructure

It was observed with transmission electron microscopy in the In0.52Al0.48As/InxGa1-xAs/In0.52Al0.48As system grown on the (001) InP substrate that misfit dislocation lines deviate [110] directions at an angle with its value depending on the gallium content. Such an abnormal alignment of misfit dislocations is explained in terms of an alloy effect on the formation of single jogs on misfit dislocations in the interface between the III-V ternary compounds. (C) 1998 American Institute of Physics.

Structural identification of a cubic phase in hexagonal GaN films grown on sapphire by gas-source molecular beam epitaxy

The structural characteristics of gallium nitride (GaN) films grown on sapphire(0001) substrates by gas source molecular beam epitaxy (GSMBE) have been investigated using high-resolution synchrotron irradiation X-ray diffraction and cathodoluminescence with a variable energy electron beam. Besides the well-known GaN hexagonal structure, a small portion of cubic phase GaN was observed. The X-ray measurements provide an essential means for the structural identification of the GaN layers. Arising from the variable penetration depth of the electron beam in the cathodoluminescence measurements, it was found that the fraction of the GaN cubic-phase typically increased as the probing depth was increased. The results suggest that the GaN cubic phase is mostly located near the interface between the substrate and GaN layer due to the initial nucleation.

Wurtzite GaN epitaxial growth on a Si(001) substrate using gamma-Al2O3 as an intermediate layer

Wurtzite GaN films have been grown on (001) Si substrates using gamma-Al2O3 as an intermediate layer by low pressure (similar to 76 Torr) metalorganic chemical vapor deposition. Reflection high energy electron diffraction and double crystal x-ray diffraction measurements revealed that the thin gamma-Al2O3 layer of "compliant" character was an effective intermediate layer for the GaN film grown epitaxially on Si. The narrowest linewidth of the x-ray rocking curve for (0002) diffraction of the 1.3 mu m GaN sample was 54 arcmin. The orientation relationship of GaN/gamma-Al2O3/Si was (0001) GaN parallel to(001) gamma-Al2O3 parallel to(001) Si, [11-20] GaN parallel to[110] gamma-Al2O3 parallel to[110] Si. The photoluminescence measurement for GaN at room temperature exhibited a near band-edge peak of 365 nm (3.4 eV). (C) 1998 American Institute of Physics.