STRUCTURAL DEFECTS AND THEIR ELECTRICAL-ACTIVITY IN GERMANIUM IMPLANTED SILICON

The electrical and structural characteristics of secondary defects in regrown amorphous layers formed in n-type Si(100) with a resistivity of 2 OMEGA cm and 6 OMEGA cm using Ge+ ions, has been studied. The amorphous layers with a thickness of 460 nm are formed by implantation of 1 x 10(15) Ge+ cm-2 at an energy of 400 keV. Both conventional furnace and rapid thermal annealing were used to regrow the amorphous layer and the residual defects have been characterised in terms of their concentration depth distribution and activation energies using C-V and DLTS. Structural information has been obtained from RBS and XTEM. By choosing suitable anneal conditions it is possible to eliminate extended defects, apart from a low concentration of end of range dislocation loops. However, a substantial population of electrically active point defects remain after simple low thermal budget anneals. In a sample implanted with 1 x 10(15) Ge+ cm-2 at 400 keV a region of deep donors approximately 460 nm from the surface is always present When the samples are annealed at higher temperatures (> 850-degrees the total deep donor concentration is reduced by one order of magnitude. Other electrically active defects not observable in the low (750-degrees-C) temperature annealed layers become apparent during anneals at intermediate temperatures.

HYDROGEN-RELATED DONOR IN SILICON-CRYSTALS GROWN IN A HYDROGEN ATMOSPHERE

Neutron transmutation doped (NTD) silicon crystals grown in a hydrogen atmosphere have been investigated by infrared absorption spectroscopy at a low temperature (10 K). An effective-mass-like donor state HD0/+ has been found at 110.8 me V below the conduction band bottom after rapid thermal annealing (RTA). The HD0/+ formation mechanism after NTD and RTA is briefly discussed, and tentatively attributed to H atoms present in the vicinity of some residual irradiation defects, like a complex of a H atom and a H-saturated vacancy.

INTERFACIAL REACTIONS IN THE CO/SI/GAAS AND SI/CO/GAAS SYSTEMS

The interfacial reactions between thin films of cobalt and silicon and (100)-oriented GaAs substrates in two configurations, Co/Si/GaAs and Si/Co/GaAs, were studied using a variety of techniques including Auger electron spectroscopy, x-ray diffraction, and transmission electron microscopy. The annealing conditions were 200, 300, 400, 600-degrees-C for 30 min, and rapid thermal annealing for 15 s. It was found that Si layer in the Co/Si/GaAs system acts as a barrier at the interface between Co and GaAs when annealed up to 600-degrees-C. The interfacial reaction between Co and Si is faster than that between Co and GaAs in the system of Si/Co/GaAs. The sequence of compound formation for the two metallizations studied (Co/Si/GaAs and Si/Co/GaAs) depends strongly on the sample configuration as well as the layer thickness of Si and Co (Co/Si atomic ratio). From our results, it is promising to utilize Co/Si/GaAs multilayer film structure to make a CoSi2/GaAs contact, and this CoSi2 may offer an alternative to the commonly used W silicides as improved gate metallurgies in self-aligned metal-semiconductor field effect transistor (MESFET) technologies.

IMPLANTATION ENERGY SELECTION IN MOLECULAR-BEAM EPITAXY GAAS FILMS ON SI SUBSTRATES

GaAs films made by molecular beam epitaxy with thicknesses ranging from 0.9 to 1.25-mu-m on Si have been implanted with Si ions at 1.2 MeV to dose of 1 x 10(15)/cm2. A rapid infrared thermal annealing and white light annealing were then used for recrystallization. Crystalline quality was analysed by using backscattering channeling technique with Li ion beam of 4.2 MeV. The experimental results show that energy selection is important for obtaining better and uniform recrystallized GaAs epilayers.

CERIUM SILICIDE FORMATION IN THIN CE SI MULTILAYER FILMS

Alternating layers of Si(200 angstrom thick) and Ce(200 angstrom thick) up to 26 layers altogether were deposited by electron evaporation under ultrahigh vacuum conditions on Si(100) substrate held at 150-degrees-C. Isothermal, rapid thermal annealing has been used to react these Ce-Si multilayer films. A variety of analytical techniques has been used to study these multilayer films after annealing, and among these are Auger electron spectroscopy, Rutherford backscattering, X-ray diffraction, and high resolution transmission electron microscopy. Intermixing of these thin Ce-Si multilayer films has occurred at temperatures as low as 150-degrees-C for 2 h, when annealed. Increasing the annealing temperature from 150 to 400-degrees-C for 1 h, CeSi2 forms gradually and the completion of reaction occurs at approximately 300-400-degrees-C. During the formation of CeSi2 from 150-400-degrees-C, there is some evidence for small grains in the selected area diffraction patterns, indicating that CeSi2 crystallites were present in some regions. However, we have no conclusive evidence for the formation of epitaxial CeSi2 layers, only polycrystals were formed when reacted in the solid phase even after rapid thermal anneal at 900-degrees-C for 10 s. The formation mechanism has also been discussed in combining the results of the La-Si system.

IDENTIFICATION OF THE ENERGY-LEVELS OF SI-RH

Two thermostable levels E(0.31) and E(0.58) related to Rh in Si were observed using deep level transient spectroscopy and double correlation deep level transient spectroscopy techniques. By means of thermal annealing and electron irradiation, the microscopic natures of these levels were identified for the first time. The levels E(0.31) and E(0.58) arise from by the same impurity center but have different charge states. Their microstructures are not related to a pure substitutional Rh atom, but correspond to a complex. This result is compared to our self-consistent theoretical calculation.

Damage removal and strain relaxation in As+-implanted Si0.57Ge0.43 epilayers grown by gas source molecular beam epitaxy

The damage removal and strain relaxation in the As+-implanted Si0.57Ge0.43 epilayers were studied by double-crystal x-ray diffractometry and transmission electron microscopy. The results presented in this paper indicate that rapid thermal annealing at temperatures higher than 950 degrees C results in complete removal of irradiation damage accompained by the formation of GeAs precipitates which enhance the removal process of dislocations.

Aggregation and precipitation in high dose as ion implanted Ge0.5Si0.5 alloy

Thermally stimulated redistribution and precipitation of excess arsenic in Ge0.5Si0.5 alloy has been studied by X-ray photoelectron spectroscopy (XPS), cross sectional transmission electron microscopy (XTEM) and X-ray energy disperse spectrometry (EDS). Samples were prepared by the implantation of 6 X 10(6) As+ cm(-2) and 100 keV with subsequent thermal processing at 800 degrees C and 1000 degrees C for 1 h. The XPS depth profiles from the implanted samples before and after the thermal annealing indicate that there is marked redistribution of the elements in heavily arsenic-implanted Ge0.5Si0.5 alloys during the annealing, including: (1) diffusion of As from the implanted region to the surface; (2) aggregation of Ge in the vicinity of the surface. A high density of precipitates was observed near the surface which were by XTEM and EDS identified as an arsenide. It is suggested that most of the implanted As in Ge0.5Si0.5 alloy exists in the form of GeAs.

Photoluminescence studies of GaAs/AlGaAs single quantum well intermixed by Ga+ ion implantation

Ga(+)ion implantation followed by rapid thermal annealing (RTA) was used to enhance the interdiffusion in GaAs/AlGaAs single Quantum Wells(SQWs). The extent of intermixing was found to be dependent on the well depth, number of implanted ions and annealing time. A very fast interdiffusion process occurs at the initial annealing stage. After that, the enhanced diffusion coefficient goes back to the umimplanted value. We propose a two-step model to explain the diffusion process as a function of the annealing time : a fast diffusion process and a saturated diffusion process. The interdiffusion coefficient of the fast diffusion was found to be of well depth dependence and estimated to be in the range of 5.4x10(-16) similar to 1.5x10(-15)cm(2)s(-1). Copyright (C) 1996 Published by Elsevier Science Ltd

A new structure of In-based ohmic contacts to n-type GaAs

Electrical, structural and reaction characteristics of In-based ohmic contacts to n-GaAs were studied. Attempts were made to form a low-band-gap interfacial phase of InGaAs to reduce the barrier height at the metal/semiconductor junction, thus yielding low-resistance, highly reliable contacts. The contacts were fabricated by e-beam sputtering Ni, NiIn and Ge targets on VPE-grown n(+)-GaAs film (approximate to 1 mu m, 2 x 10(18) cm(-3)) in ultrahigh vacuum as the structure of Ni(200 Angstrom)/NiIn(100 Angstrom)/Ge(40 Angstrom)/n(+)-GaAs/SI-GaAs, followed by rapid thermal annealing at various temperatures (500-900 degrees C). In this structure, a very thin layer of Ge was employed to play the role of heavily doping donors and diffusion limiters between In and the GaAs substrate. Indium was deposited by sputtering NiIn alloy instead of pure In in order to ensure In atoms to be distributed uniformly in the substrate; nickel was chosen to consume the excess indium and form a high-temperature alloy of Ni3In. The lowest specific contact resistivity (rho(c)) of (1.5 +/- 0.5)x 10(-6) cm(2) measured by the Transmission Line Method (TLM) was obtained after annealing at 700 degrees C for 10 s. Auger sputtering depth profile and Transmission Electron Microscopy (TEM) were used to analyze the interfacial microstructure. By correlating the interfacial microstructure to the electronical properties, InxGa1-xAs phases with a large fractional area grown epitaxially on GaAs were found to be essential for reduction of the contact resistance.

ENHANCEMENT EFFECT OF PLASMA-ENHANCED CHEMICAL-VAPOR-DEPOSITED SIN CAPPING LAYER ON DIELECTRIC CAP QUANTUM-WELL DISORDERING

Quantum well disordering of GaAs/AlGaAs multiple quantum well(MQW) has been accomplished with only plasma enhanced chemical vapor deposited (PECVD) SiN cap layer growth. The amount of blue shift increases with SiN growing time. This result has been explained by the vacancy indiffusion during PECVD SiN growth. Rapid thermal annealing (RTA) of the sample after SiN cap layer growth at 850 degrees C for 35 s caused a larger amount of blue shift than those obtained without RTA. By considering the model of Al diffusion from AlGaAs barrier into GaAs QWs together with the result from photoluminescence (PL) measurement, Al diffusion coefficients were calculated. The Al diffusion coefficient due to PECVD SiN was estimated at about 3 x10(-17) cm(2)/s. It was possible to extract the effect of RTA on the QW disordering, which showed that the amount of the blue shift and the Al diffusion coefficient due only to RTA increases with SiN cap layer thickness as reported by Chi et al.(10))

OPTICAL AND STRUCTURAL-PROPERTIES OF AP-MOVPE GAINP/GAAS HETEROSTRUCTURES

Lattice matched GaInP/GaAs heterostructures were grown by atmospheric pressure-metal organic vapor phase epitaxy (AP-MOVPE). Compositional intermixing of As/P and Ga/In near the heterointerfaces was studied by photoluminescence (PL) spectroscopy. Indium segregation, memory effect of In into GaAs and the carry-over of As in the GaInP layer during the growth process were considered as three major factors giving rise to the anomalous emissions in the PL spectra. Both thermal annealing and zinc doping strongly enhanced the compositional interdiffusion near the heterointerfaces.

The influence of nitrogen clustering effect on optical transitions in GaInNAs/GaAs quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells and GaInNAs epilayers grown on GaAs substrate show an apparent "S-shape" temperature-dependence of the of dominant luminescence peak. At low temperature and weak excitation conditions, a PL peak related to nitrogen cluster-induced bound states can be well resolved in the PL spectra. It displays a remarkable red shift of up to 60 meV and is thermally quenched below 100 K with increasing temperature, being attributed to N-cluster induced bound states. The indium incorporation exhibits significant effect on the cluster formation. The rapid thermal annealing treatment at 750 C can essentially remove the bound states-induced peak.

Effect of SiO2 encapsulation on the nitrogen reorganization in GaNAs/GaAs single quantum well

Effects of SiO2, encapsulation and rapid thermal annealing (RTA) on the optical properties of GaNAs/GaAs single quantum well (SQW) were studied by low temperature photoluminescence (PL). A blueshift of the PL peak energy for both the SiO2-capped region and the bare region was observed. The results were attributed to the nitrogen reorganization in the GaNAs/GaAs SQW. It was also shown that the nitrogen reorganization was obviously enhanced by SiO2 cap-layer. A simple model [1] was used to describe the SiO2-enhanced blueshift of the low temperature PL peak energy.

Optical study of localized and delocalized states in GaAsN/GaAs

Taking advantages of short pulse excitation and time-resolved photoluminescence (PL), we have studied the exciton localization effect in a number of GaAsN alloys and GaAsN/GaAs quantum wells (QWs). In the PL spectra, an extra transition located at the higher energy side of the commonly reported N-related emissions is observed. By measuring PL dependence on temperature and excitation power along with PL dynamics study, the new PL peak has been identified as a transition of the band edge-related recombination in dilute GaAsN alloy and delocalized transition in QWs. Using selective excitation PL we further attribute the localized emission in QWs to the excitons localized at the GaAsN/GaAs interfaces. This interface-related exciton localization could be greatly reduced by a rapid thermal annealing.