Lifetime study of N impurity states in GaAs1-xNx (x=0.1%) under hydrostatic pressure

The lifetimes of a series of N-related photoluminescence lines (A(2)-A(6)) in GaAs1-xNx (x=0.1%) were studied under hydrostatic pressures at similar to 30 K. The lifetimes of A(5) and A(6) were found to increase rapidly with increasing pressure: from 2.1 ns at 0 GPa to more than 20 ns at 0.92 GPa for A(5) and from 3.2 ns at 0.63 GPa to 10.8 ns at 0.92 GPa for A(6). The lifetime is found to be closely correlated with the binding energy of the N impurity states, which is shown either in the pressure dependence for a given emission line or in the lifetime variation from A(2) to A(6). (c) 2006 American Institute of Physics.

Fabrication process and power and lifetime characteristics of very-small-aperture laser

High output power very-small-aperture laser has been created on 650 nm edge emitting laser diodes. The far-field output power is 0.4 mW at the 25 mA driving current, and the highest output power exceeds 1 mW. The special fabrication process is described and the failure mechanism leading to the short lifetime of the devices is discussed.

Gallium vacancy and the residual acceptor in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Positron lifetime, photoluminescence (PL), and Hall measurements were performed to study undoped p-type gallium antimonide materials. A 314 ps positron lifetime component was attributed to Ga vacancy (V-Ga) related defect. Isochronal annealing studies showed at 300 degreesC annealing, the 314 ps positron lifetime component and the two observed PL signals (777 and 797 meV) disappeared, which gave clear and strong evidence for their correlation. However, the hole concentration (similar to2x10(17) cm(-3)) was observed to be independent of the annealing temperature. Although the residual acceptor is generally related to the V-Ga defect, at least for cases with annealing temperatures above 300 degreesC, V-Ga is not the acceptor responsible for the p-type conduction. (C) 2002 American Institute of Physics.

High-power and long-lifetime InAs/GaAs quantum-dot laser at 1080 nm

High power and long lifetime have been demonstrated for a semiconductor quantum-dot (QD) laser with five-stacked InAs/GaAs QDs separated by an InGaAs strain-reducing layer (SRL) and a GaAs spacer layer as an active medium. The QD lasers exhibit a peak power of 3.6 W at 1080 nm, a quantum slope efficiency of 84.6%, and an output-power degradation rate of 5.6%/1000 h with continuous-wave constant-current operation at room temperature. A comparative reliability investigation indicates that the lifetime of the InAs/GaAs QD laser with the InGaAs SRL is much longer than that of a QD laser without the InGaAs SRL. This improved lifetime of the QD laser could be explained by the reduction of strain in and around InAs QDs induced by the InGaAs SRL. (C) 2001 American Institute of Physics.

Short range scattering mechanism of type-II GaSb/GaAs quantum dots on the transport properties of two-dimensional electron gas

We have studied the scattering process of AlGaAs/GaAs two-dimensional electron gas with the nearby embedded GaSb/GaAs type-II quantum dots (QDs) at low temperature. Quantum Hall effect and Shubnikov-de Haas oscillation were performed to measure the electron density n(2D), the transport lifetime tau(t) and the quantum lifetime tau(q) under various biased gate voltage. By comparing measured results of QDs sample with that of reference sample without embedded QDs, mobilities (transport mobility mu(t) and quantum mobility mu(q)) dominated by GaSb QDs scattering were extracted as functions of n(2D). It was found that the ratios of tau(t) to tau(q) were varying within the range of 1-4, implying the scattering mechanism belonging to the sort of short-range interaction. In the framework of Born approximation, a scattering model considering rectangular-shaped potential with constant barrier height was successfully applied to explain the transport experimental data. In addition, an oscillating ratio of tau(t)/tau(q) with the increasing n(2D) was predicted in the model.

Broad-spectrum and long-lifetime emissions of Nd3+ ions in lead fluorosilicate glass

A novel Nd3+-doped lead fluorosilicate glass (NPS glass) is prepared by a two-step melting process. Based on the absorption spectrum a Judd-Ofelt theory analysis is made. The emission line width of NPS glass is 44.2nm. The fluorescence decay lifetime of the 4F3/2 level is 586±20μsec, and the stimulated emission cross-section is 0.87×10-20cm2 at 1056nm. A laser oscillation is occurred at 1062nm when pumped by 808nm Diode Laser. The slope efficiency is 23.7% with a 415mJ threshold. It is supposed that NPS glass is a good candidate for using in ultra-short pulse generation and amplification by the broad emission bandwidth and long fluorescence lifetime.

Room-Temperature Continuous-Wave Operation of InGaN-Based Blue-Violet Laser Diodes with a Lifetime of 15.6 Hours

We report our recent progress of investigations on InGaN-based blue-violet laser diodes (LDs). The room-temperature (RT) cw operation lifetime of LDs has extended to longer than 15.6 h. The LD structure was grown on a c-plane free-standing (FS) GaN substrate by metal organic chemical vapor deposition (MOCVD). The typical threshold current and voltage of LD under RT cw operation are 78 mA and 6.8 V, respectively. The experimental analysis of degradation of LD performances suggests that after aging treatment, the increase of series resistance and threshold current can be mainly attributed to the deterioration of p-type ohmic contact and the decrease of internal quantum efficiency of multiple quantum well (MQW), respectively.

WELL-WIDTH DEPENDENCE OF THE EXCITON LIFETIME IN GAAS/ALGAAS QUANTUM-WELLS

The dependence of the excitonic lifetime on the well width has been studied in conventional GaAs/AlGaAs quantum wells. Two clearly different variations of the measured excitonic lifetime have been observed. For wide well widths, we find a nearly linear decrease of the lifetime with decreasing well width. However, when the well is further decreased, a saturation and even increase of the lifetime with decreasing well width are observed. The experimental data are compared with the theory of radiative excitonic recombination, and show that well width dependence of the measured photoluminescence lifetime can be attributed mainly to the change of the excitonic effective volume and the overlap integral as well.

WELL WIDTH DEPENDENCE OF THE EXCITON LIFETIME IN NARROW GAAS/GAALAS QUANTUM-WELLS

We have studied the radiative excitonic lifetime as a function of the well width in GaAs/GaAlAs quantum wells. An increasing lifetime with decreasing well width has been observed in very narrow and high quality GaAs/GaAlAs quantum wells, and attributed to the reduced overlap of the electron and hole wave functions and the increase of the exciton effective volume. This is the first observation of its kind in the conventional GaAs/GaAlAs quantum wells.