In0.25Ga0.75As films growth on the thin GaAs/AlAs buffer layer on the GaAs(001) substrate

Thin GaAs/AlAs and GaAs/GaAs buffer layer structure have been fabricated on the GaAs(001) substrate. The top GaAs buffer layer is decoupled from the host substrate by introduction of a low temperature thin interlayer (AlAs or GaAs), which was mechanically behaved like the compliant substrate. Four hundred nanometer In0.25Ga0.75As films were grown on these substrates and the traditional substrate directly. Photoluminescence (PL), double-crystal X-ray diffraction (DCXRD) and atomic force microscopy (AFM) measurements were used to estimate the quality of the In0.25Ga0.75As layer and the compliant effects of the low temperature buffer layer. All the measurements shown that the qualities of epilayer have been improved and the substrate have been deteriorated severely. The growth technique of the thin GaAs/AlAs structure was found to be simple but very powerful for heteroepitaxy. (C) 2003 Elsevier Science B.V All rights reserved.

X-ray diffraction analysis of MOCVD grown GaN buffer layers on GaAs(001) substrates

In order to understand the growth feature of GaN on GaAs (0 0 1) substrates grown by metalorganic chemical vapor deposition (MOCVD), the crystallinity of GaN buffer layers with different thicknesses was investigated by using double crystal X-ray diffraction (DCXRD) measurements. The XRD results showed that the buffer layers consist of predominantly hexagonal GaN (h-GaN) and its content increases with buffer layer thickness. The nominal GaN (111) reflections with chi at 54.74degrees can be detected easily, while (0 0 2) reflections are rather weak. The integrated intensity of reflections from (111) planes is 4-6 times that of (0 0 2) reflections. Possible explanations are presented. (C) 2003 Elsevier Science B.V. All rights reserved.

Effects of seed dot layer and thin GaAs spacer layer on the structure and optical properties of upper In(Ga)As quantum dots

The structure and optical properties of In(Ga)As with the introduction of InGaAlAs or InAlAs seed dot layers are investigated. The area density and size homogeneity of the upper InGaAs dots are efficiently improved by the introduction of a buried layer of high-density dots. Our explanation for the realization of high density and size homogeneity dots is presented. When the GaAs spacer layer is too thin to cover the seed dots, the upper dots exhibit some optical properties like those of a quantum well. By analyzing the growth dynamics, we refer to this kind of dot as an empty-core dot. (C) 2003 American Institute of Physics.

Surface morphology and optical property of 1.3 mu m In0.5Ga0.5As/GaAs self-organized quantum dots grown by MBE

Surface morphology and optical properties of 1.3 mum self-organized InGaAs/GaAs quantum dots structure grown by molecular beam epitaxy have been investigated by atomic force microscopy and photoluminescence measurements. It has been shown that the surface morphology evolution and emission wavelengths of InGaAs/GaAs QDs can be controlled effectively via cycled monolayer deposition methods due to the reduction of the surface strain. Our results provide important information for optimizing the epitaxial parameters for obtaining 1.3 mum long wavelength emission quantum dots structures. (C) 2002 Elsevier Science B.V. All rights reserved.

Structure and photoluminescence study of InGaAs/GaAs quantum dots grown via cycled (InAs)(n)/(GaAs)(n) monolayer deposition

We report the morphology of an InGaAs nanostructure grown by molecular beam epitaxy via cycled (InAs)(n)/(GaAs)(n) monolayer deposition. Atomic force microscopy images clearly show that varying monolayer deposition per cycle has significant influence on the size, density and shape of the InGaAs nanostructure. Low-temperature photoluminescence spectra show the effect of n on the optical quality, and 1.35mum photoluminescence with a linewidth of only 19.2meV at room temperature has been achieved in the (InAs)(1)/(GaAs)(1) structure.

Selective area growth of GaN on GaAs(001) substrates by metalorganic vapor-phase epitaxy

Selective area growth (SAG) of GaN on SiO2 stripe-patterned GaN/GaAs(001) substrates was carried out by metalorganic vapor-phase epitaxy. The SAG samples were investigated by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). SEM observations showed that the morphology of SAG GaN is strongly dependent on the window stripe orientation and slightly affected by the orientation relationship between the window stripes and the gas flow. The (I 1 1)B sidewalls formed on the SAG GaN stripes are found to be stable. XRD measurements indicated the full-widths at half-maximum (FWHMs) of cubic GaN (0 0 2) rocking curves are reduced after SAG. The measured FWHMs with omega-axis parallel to [1(1) over bar 0] are always larger than the FWHM values obtained with omega-axis parallel to [I 10], regardless of the orientation relationship between the w-axis and the GaN stripes. (C) 2003 Elsevier Science B.V. All rights reserved.

Effect of InAs quantum dots on the Fermi level pinning of undoped-n(+) type GaAs surface studied by contactless electroreflectance

Self-assembled InAs quantum dots (QDs) have been fabricated by depositing 1.6, 1.8, 2.0 and 2.5 monolayer (ML) InAs on surfaces of the undoped-n(+) (UN+) type GaAs structure. Room temperature contactless electroreflectance (CER) was employed to study the built-in electric field and the surface Fermi level pinning of these QD-covered UN+ GaAs samples. The CER results show that 1.6 ML InAs QDs on GaAs do not modify the Fermi level, whereas for samples with more than 1.6 ML InAs coverage, the surface Fermi level is moved to the valence band maximum of GaAs by about 70 meV (which is independent of the InAs deposition thickness) compared to bare GaAs. It is concluded that the modification of InAs coverage on the Fermi level on the GaAs surface is due to the QDs, rather than to the wetting layer. (C) 2003 American Institute of Physics.

The effect of inserting strain-compensated GaNAs layers on the luminescence properties of GaInNAs/GaAs quantum well

Photoluminescence (PL) properties of GaInNAs/GaAs quantum wells (QWs) with strain-compensated GaNAs layers grown by molecular beam epitaxy are investigated. The temperature-dependent PL spectra of GaInNAs/GaAs QW with and without GaNAs layers are compared and carefully studied. It is shown that the introduction of GaNAs layers between well and barrier can effectively extend the emission wavelength, mainly due to the reduction of the barrier potential. The PL peak position up to 1.41 mum is observed at the room temperature. After adding the GaNAs layers into QW structures, there is no essential deterioration of luminescence efficiency. N-induced localization states are also not remarkably influenced. It implies that with optimized growth condition, high-quality GaInNAs/GaAs QWs with strain-compensated GaNAs layers can be achieved. (C) 2003 Elsevier Science B.V. All rights reserved.

Method for measurement of lattice parameter of cubic GaN layers on GaAs (001)

An extended technique derived from triple-axis diffraction setup was proposed to measure lattice parameters of cubic GaN(c-GaN) films. The fully relaxed lattice parameters of c-GaN are determined to be 4.5036+0.0004 Angstrom, which is closer to the values of a hypothetical perfect crystal. The speculated zero setting correction (Deltatheta) is very slight and within the range of the accuracy of measurement. Additionally, we applied this method to analyze strain of four different kinds of c-GaN samples. It is found that in-plane strain caused by large lattice mismatch and thermal expansion coefficients mismatch directly influence the epilayer growth at high temperatures, indicating that the relaxation of tensile strain after thermal annealing helps to improve the crystalline quality of c-GaN films and optical properties. (C) 2003 Elsevier Science B.V. All rights reserved.

The effects of rapid thermal annealing on the optical properties of Zn1-xMnxSe epilayer grown by MOCVD on GaAs substrate

Zn1-xMnxSe thin films with different Mn compositions are grown by metal-organic chemical vapor deposition on GaAs substrate. Good crystallinity of sample is evidenced by X-ray diffraction and rocking-curve measurements. Photoluminescence (PL) properties were carefully studied. A dominant PL peak close to the band edge is observed at low temperature for samples with higher Mn concentration. The temperature-dependent PL and time-resolved photoluminescence show that this emission peak is associated with the recombination of exciton bound to Mn-induced impurity bound states. It is found that rapid thermal annealing can induce reorganization of Mn composition in alloys and significantly reduce the density of impurity induced by Mn incorporation and improve the intrinsic interband transition. (C) 2002 Elsevier Science B.V. All rights reserved.

Structure and optical properties of upper In(Ga)As quantum dots on a different seed layer with a thin GaAs spacer layer

The structure and optical properties of In(Ga)As grown with the introduction of InGaAlAs or InAlAs seed dots layers are investigated. The area density and size homogeneity of the upper InGaAs dots are efficiently improved with the introduction of a layer of high-density buried dots. When the GaAs spacer layer is too thin to cover the seed dots, the upper dots exhibit the characterization of a quantum well. By analyzing the growth dynamics, we refer to it as an empty-core structure dot. (C) 2002 Elsevier Science B.V. All rights reserved.

In0.25Ga0.75As growth on low-temperature thin buffer layers formed on GaAs (001) substrate

High-quality In0.25Ga0.75As films were grown on low-temperature (LT) ultra-thin GaAs buffer layers formed on GaAs (0 0 1) substrate by molecular beam epitaxy. The epilayers were studied by atomic force microscopy (AFM), photo luminescence (PL) and double crystal X-ray diffraction (DCXRD), All the measurements indicated that LT thin buffer layer technique is a simple but powerful growth technique for heteroepitaxy. (C) 2002 Elsevier Science B.V. All rights reserved.

Interface-related in-plane optical anisotropy in GaAs/AlxGa1-xAs single-quantum-well structures studied by reflectance difference spectroscopy

The in-plane optical anisotropies of a series of GaAs/AlxGa1-xAs single-quantum-well structures have been observed at room temperature by reflectance difference spectroscopy. The measured degree of polarization of the excitonic transitions is inversely proportional to the well width. Numerical calculations based on the envelope function approximation incorporating the effect of C-2v-interface symmetry have been performed to analyze the origin of the optical anisotropy. Good agreement with the experimental data is obtained when the optical anisotropy is attributed to anisotropic-interface structures. The fitted interface potential parameters are consistent with predicted values.

Structural characterization of epitaxial lateral overgrown GaN on patterned GaN/GaAs(001) substrates

Epitaxial lateral overgrown (ELO) cubic GaN (c-GaN) on SiO2 patterned GaN/GaAs(0 0 1) substrates by metalorganic vapor phase epitaxy was investigated using transmission electron microscopy and X-ray diffraction (XRD) measurements. The density of stacking faults (SFs) in ELO c-GaN was similar to6 x 10(8) cm(-2), while that in underlying GaN template was similar to5 x 10(9) cm(-2). XRD measurements showed that the full-width at half-maximum of c-GaN (0 0 2) rocking curve decreased from 33 to 17.8 arcmin, indicating the improved crystalline quality of ELO c-GaN. The mechanism of SF reduction in ELO c-GaN was also discussed. (C) 2002 Elsevier Science B.V. All rights reserved.

Storage of photoexcited electron-hole pairs in an AlAs/GaAs heterostructure created by electron transfer in real and kappa spaces

The storage of photoexcited electron-hole pairs is experimentally carried out and theoretically realized by transferring electrons in both real and k spaces through resonant Gamma - X in an AlAs/GaAs heterostructure. This is proven by the peculiar capacitance jump and hysteresis in the measured capacitance-voltage curves. Our structure may be used as a photonic memory cell with a long storage time and a fast retrieval of photons as well.