RTD与PHEMT的集成研究

Submitted by zhangdi (zhangdi@red.semi.ac.cn) on 2009-04-13T11:45:31Z

Using photoluminescence as optimization criterion to achieve high-quality InGaAs/AlGaAs pHEMT structure

The single delta -doped InGaAs/AlGaAs pseudomorphic HEMT structure materials were grown by molecular beam epitaxy. The photoluminescence spectra of the materials were studied. There are two peaks in the photoluminescence spectra of the materials, corresponding to two sub energy levels of InGaAs quantum well. The ratio of the two peak's intensity was used as criterion to optimize the layer structures of the materials. The material with optimized layer ;tructures exhibits the 77 It mobility and two-dimensional electron gas density of 16 500 cm(2)/Vs and 2.58 x 10(12) cm(-2) respectively, and the 300 K mobility and two-dimensional electron gas density of 6800 cm(2)/Vs and 2.55 x 10(12) cm(-2) respectively. The pseudomorphic HEMT devices with gate length of 0.2 mum were fabricated using this material. The maximum transconductance of 650 mS/mm and the cut-off frequency of 81 GHz were achieved. (C) 2001 Elsevier Science B.V. All rights reserved.

RTD与PHEMT集成的几个关键工艺

在新型的共振隧穿二极管(RTD)器件与PHEMT器件单片集成材料结构上,研究和分析了分立器件的制作工艺,给出了分立器件的制作工艺参数.利用上述工艺成功制作了RTD和PHEMT器件,并在室温下分别测试了RTD器件和PHEMT器件的电学特性.测试表明:在室温下,RTD器件的峰电流密度与谷电流密度之比提高到1.78;PHEMT器件的最大跨导约为120mS/mm,在Vgs＝0.5V时的饱和电流约为270mA/mm.这将为RTD集成电路的研制奠定工艺基础.

MBE生长的高质量AlGaAs/InGaAs双δ掺杂PHEMT结构的材料

用MBE方法制备的PHEMT微结构材料，其2DEG浓度随材料结构的不同在2.0-4.0×10~(12)cm~(-2)之间，室温霍耳迁移率在5000-6500cm~2·V~(-1)·s~(-1)之间。制备的PHEMT器件，栅长为0.7μm的器件的直流特性：I_(dss)～280mA/mm,I_(max)～520-580mA/mm,g_m～320-400mS/mm,BV_(DS)>15V(I_(DS)=1mA/mm),BV_(GS)>10V,微波特性：P_0～600-900mW/mm,G～6-10dB,η_(add)～40-60%;栅长为0.4μm的器件的直流特性:I_(max)～800mA/mm,g_m>400mS/mm。

Using photoluminescence as optimization criterion to achieve high-quality InGaAs/AlGaAs pHEMT structure

The single delta -doped InGaAs/AlGaAs pseudomorphic HEMT structure materials were grown by molecular beam epitaxy. The photoluminescence spectra of the materials were studied. There are two peaks in the photoluminescence spectra of the materials, corresponding to two sub energy levels of InGaAs quantum well. The ratio of the two peak's intensity was used as criterion to optimize the layer structures of the materials. The material with optimized layer ;tructures exhibits the 77 It mobility and two-dimensional electron gas density of 16 500 cm(2)/Vs and 2.58 x 10(12) cm(-2) respectively, and the 300 K mobility and two-dimensional electron gas density of 6800 cm(2)/Vs and 2.55 x 10(12) cm(-2) respectively. The pseudomorphic HEMT devices with gate length of 0.2 mum were fabricated using this material. The maximum transconductance of 650 mS/mm and the cut-off frequency of 81 GHz were achieved. (C) 2001 Elsevier Science B.V. All rights reserved.

The keys to get high transconductance of AlGaAs/InGaAs/GaAs pseudomorphic HEMTs devices

There are two key points to get high transconductance of pseudomorphic HEMTS (pHEMTs) devices. From the point view of materials, the transfer efficiency of the electrons from the delta -doped AlGaAs layer to the InGaAs channel must be high. From the point view of device processing, the gate recess depth must be carefully controlled. In the present work, AlGaAs/InGaAs/GaAs pHEMTs structures were grown by molecular beam epitaxy. Layer structures of the pHEMTs were optimized to get high transfer efficiency of the electrons. Gate recess depth was also optimized. A 0.2 mum pHEMT was fabricated on the materials with optimized layer structure using the optimized gate recess depth. The maximum transconductance of 650 mS/mm and the cut-off frequency of 81 GHz were achieved. (C) 2001 published by Elsevier Science Ltd.

Growth and characterization of InGaAs/InAlAs/InP high-electron-mobility transistor structures towards high channel conductivity

High-quality InGaAs/InAlAs/InP high-electron-mobility transistor (HEMT) structures with lattice-matched or pseudomorphic channels have been grown by molecular-beam epitaxy (MBE). The purpose of this work is to enhance the channel conductivity by changing the epitaxial structure and growth process. With the use of pseudomorphic step quantum-well channel, the highest channel conductivity is achieved at x = 0.7, the corresponding electron mobilities are as high as 12300 (300 K) and 61000 cm(2)/V.s (77 K) with two-dimensional electron gas (2DEG) density of 3.3 x 10(12) cm(-2). These structures are comprehensively characterized by Hall measurements, photoluminescence, double crystal X-ray diffraction and transmission electron microscopy. Strong room-temperature luminescence is observed, demonstrating the high optical quality of the samples. We also show that decreasing the In composition in the InyAl1-yAs spacer is very effective to increase the 2DEG density of PHEMT structures. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

HEMT结构材料中二维电子气的输运性质研究

该文通过变温的Hall测量系统地研究了GaAs基HEMT和PHEMT以及InP基HEMT三种结构材料的电子迁移率μ_n和二维电子浓度n_s。仔细地分析了不同HEMT结构材料的散射机制对电子迁移率的影响以及不同HEMT材料结构对电子浓度的影响。研究结果表明InP基HEMT的n_s×μ_n值比GaAs基HEMT和PHEMT的n_s×μm值都大，说明可以用n_s×μ_0值来判断HEMT结构材料的性能好坏。