Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究

Nd3+-doped Y2-2x La-2x O-3 (x = 0.08) transparent ceramics were fabricated by conventional fabrication process. Spectroscopic properties of the samples were investigated. The absorption band of Nd3+ : Y1.84La0.16O3 was broad covering the wavelength range 780-850 nm. When doped with 1.5at% Nd3+, the cross sections of the sample at 820 nm and laser diode pumped 808 nm were 1.81 x 10(-20) cm(2) and 1.54 x 10(-20) cm(2), respectively. The strongest emission peak of the sample was centered at 1078 mn with long fluorescent lifetime, broad emission bandwidth and high quantum efficiency. Because of the additive La2O3, the spectroscopic quality parameter (X-Nd) of matrix was' decreased from 1.6 to 0.46, thus the fluorescence branch ratio of F-4(3/2) - (4) I-11/2 transition was increased to 56.82%. These properties of Nd3' : Y1.84La0.16O3 transparent ceramic are benefitial to achieve high efficient laser output and ultrashort modelocked pulse.

Yb:Y2-2xLa2xO3激光透明陶瓷的光谱性能

It was first reported the spectral properties of a low-temperature sintered transparent Yb: Y2-2x La-2x O-3 laser ceramics. Yb: Y2-2x La-2x O-3 laser ceramics have broad absorption band and large absorption cross- section of 4.0 x 10(-20) cm(2) at wavelengths 977nm of the highest absorption peak. Its fluorescence lifetime is 1.1 ms, and the emission cross-sections are 1.0 x 10(-20) cm(2) and 0.7 x 10(-20) cm(2) at wavelengths 1033nm and 1077nm, respectively. All the optical properties are similar to those of single crystals.

Growth and spectroscopic characteristics of Yb : LPS single crystal

For the first time, a high optical quality Yb3+-doped lutetium pyrosilicate laser crystal Lu2Si2O7 (LPS) was grown by the Czochralski (Cz) method. The segregation coefficient of ytterbium ion in Yb:LPS crystal detected by the inductively coupled plasma atomic emission spectrometer (TCP-AES) method is equal to 0.847. X-ray powder diffraction result confirms the C2/m phase monoclinic space group of the grown crystal and the peaks corresponding to different phases were indexed. The absorption and fluorescence spectra, as well as fluorescence decay lifetime of Yb3+ ion in LPS have been investigated. The absorption and fluorescence cross-sections of the transitions F-2(7/2) <-> F-2(5/2) of Yb3+ ion in LPS crystal have been determined. The advantages of the Yb:LPS crystal including high crystal quality, quasi-four-level laser operating scheme, high absorption cross-sections (1.33 x 10(-2) cm(2)) and particularly broad emission bandwidth (similar to 62 nm) indicated that the Yb:LPS crystal seemed to be a promising candidate used as compact, efficient thin chip lasers when LD is pumped at 940 and 980 nm due to its low-symmetry monoclinic structure and single crystallographic site. (c) 2007 Elsevier B.V. All rights reserved.

Visible luminescence in Yb3+-doped gadolinium gallium garnets

In this paper, some results on visible luminescence performed on Yb3+-doped gadolinium gallium garnets under 165 and 940 nm excitation were presented. The upconversion luminescence was ascribed to Yb3+ cooperative luminescence and the presence of rare earth impurity ions. The gain cross-sections of Yb:GGG crystal as a function of excited-state population fraction P were studied. Emission spectra under 165 nm at 20 K showed there was no charge transfer luminescence in Yb:GGG. (c) 2006 Elsevier B.V. All rights reserved.

La2O3对Yb：Y2O3透明陶瓷光谱性能的影响

研究了La2O3对Yb：Y2O3透明陶瓷光谱性能的影响，添加适量La2O3以后，Yb：Y2O3透明陶瓷的吸收峰和发射峰的位置不变，但由于La^3＋的离子半径大于Y^3＋的离子半径，在Y2O3中引入La^3＋离子后，导致Y2O3晶格常数变大，晶场强度变弱，同时降低了Y2O3晶体的有序度，致使发射峰强度有所下降，发射截面变小．过量的№La2O3（x=0．16）造成yb^3＋激活离子发射强度明显下降；其荧光寿命在添加La2O3后总体增大45％-60％.

Nd：YbVO4晶体的拉曼光谱和荧光光谱研究

用群论的方法计算了Nd：YbVO4晶体的拉曼活性振动模数目，在室温下测得了其极化拉曼谱线，并指认了在不同几何配置下，各振动模式所对应的频率。同时，测得了室温下晶体的吸收谱，得到了中心波长为808am吸收峰的半高宽为12nm，并在J-O理论的基础上计算了晶体的光学参数，其三个晶场参数分别为Ω2=6．88945×10^-20cm^2。Ω4=4．13394×10^-20cm^2、Ω6=4．54503×10^-20cm^2，并由此得到^4F3／2能级的荧光寿命为178．69炉，1062nm处的荧光分支比为48．85％，积分发射截面为2．786710^-18cm^2。分别在808nm、940nm激发下测得晶体室温发射谱，观察到了Nd→Yb以及Nd←Yb间的能量传递现象。

Sm:GdVO_4晶体的生长及光谱性能研究

应用中频感应提拉法生长出掺杂浓度为2%原子分数的Sm:GdVO4晶体,研究了室温下c轴方向Sm:GdVO4晶体的吸收和荧光光谱。通过J-O理论计算出强度参数(Ωt),同时计算了对应于4G5/2能级的自发跃迁几率、荧光分支比和辐射寿命。通过荧光光谱计算了对应于566、604和646nm三个发射峰对应的发射截面,结果表明,Sm:GdVO4在604nm的发射截面最大,是掺Sm:YAP在607nm处发射截面的4.4倍。

Growth and spectral properties of Yb,Tm:YAG crystal

The YAG crystal codoped with Yb3+ and Tm3+ has been grown by Czochralski (Cz) method. The crystal structure of the crystal has been determined by X-ray diffraction analysis. The absorption and emission spectra of Yb,Tm:YAG crystal at room temperature have also been studied. The emission cross-sections have been calculated by Fuechtbauer-Ladenburg formula and reciprocity method. (C) 2007 Elsevier B.V. All rights reserved.

Intense upconversion and infrared emissions in Er3+;Yb3+ codoped Lu2 Si O5 and (Lu0.5 Gd0.5)2 Si O5 crystals

High optical quality Lu2SiO5 (LSO) and (Lu0.5Gd0.5)(2)SiO5 (LGSO) laser crystals codoped with Er3+ and Yb3+ have been fabricated by the Czochralski method. Intense upconversion (UC) and infrared emission (1543 nm) are observed under excitation of 975 nm. The luminescence processes are explained and the emission efficiencies are quantitatively obtained by measuring the UC efficiency and calculating the emission cross section. The temperature-dependent optical properties of the crystals are also investigated. Our study indicates that Er3+-Yb3+ : LSO and Er3+-Yb3+: LGSO crystals are promising gain media for developing the solid-state 1.5 mu m optical amplifiers and tunable UC lasers. (c) 2008 American Institute of Physics.

Spectral investigation of Yb-doped calcium pyroniobate crystal

Ytterbium-doped calcium pyroniobate single crystal has been grown for the first time. Spectral properties of Yb: Ca2Nb2O7 were investigated by emission and absorption spectra. Its cooperative luminescence and fluorescence lifetime were also studied. Yb ions in Ca2Nb2O7 showed very broad absorption and emission bandwidth and relatively large absorption and emission cross-sections. Along with other optical properties, this Yb-doped crystal would be a potential self-frequency doubling femtosecond laser gain material. (C) 2007 Published by Elsevier B.V.

Polarized spectral analysis of Ho3+ ions in biaxial YAlO3 crystal for 2 mu m lasers

An Ho3+-doped YAlO3 (Ho : YAP) single crystal has been grown by the Czochralski technique. The polarized absorption spectra, polarized fluorescence spectra and fluorescence decay curve of the crystal are measured at room temperature. The spectroscopic parameters are calculated based on Judd-Ofelt theory, and the effective phenomenological intensity parameters Omega(2,eff), Omega(4,eff) and Omega(6,eff) are obtained to be 2.89 x 10(-20), 2.92 x 10(-20) and 1.32 x 10(-20) cm(2), respectively. The room-temperature fluorescence lifetime of the Ho3+ 5I(7) -> I-5(8) transition is measured to be 8.1 ms. Values of the absorption and emission cross-sections with different polarizations are presented for the I-5(7) manifold, and the polarized gain cross-section curves are also provided and discussed.

Crystal growth and spectral properties of Sm:GdVO4

The 2 at.% Sm:GdVO4 crystal was grown by the Czochralski method. The segregation coefficient of Sm3+ ion in this crystal is 0.98. The crystal structure of the Sm:GdVO4 crystal was determined by X-ray diffraction analysis. Judd-Ofelt theory was used to calculate the intensity parameters (Omega(i)), the spontaneous emission probability, the luminary branching ratio and the radiative lifetime of the state (4)G(5/2). The stimulated emission cross-sections at 567, 604 and 646 nm are calculated to be 5.92 x 10(-21), 7.62 x 10(-21) and 5.88 x 10(-21) cm(2), respectively. The emission cross-section at 604 nm is 4.4 times lager than that in Sm: YAP at 607 nm. (C) 2007 Elsevier B.V. All rights reserved.

Luminescence behavior of Yb(3+)heavy-doped yttrium lanthanum oxide transparent ceramics

Yb3+ heavy-doped yttrium lanthanum oxide transparent ceramics were fabricated and their spectroscopic properties were investigated. The absorption bands of (YbxY0.9-xLa0.1)(2)O-3 (x = 0.05-0.15) ceramics are broad at wavelength of 900-1000 nm. The absorption cross-sections centered at 974 nm and the emission cross-sections at 1031 nm of Yb3+ ion are 0.89-1.12 x 10(-20) cm(2) and 1.05 x 10(-20) cm(2) respectively. The up-conversion luminescence intensity of Yb3+-doped yttrium lanthanum oxide ceramics increased firstly, then decreased with the increase of Yb3+ ion content. (C) 2008 Elsevier B.V. All rights reserved.

Characteristics of oxide-free InGaAlAs layers grown by narrow stripe selective MOVPE

Narrow stripe selective MOVPE has been used to grow high quality oxide-free InGaAlAs layers on an InP substrate patterned with SiO2 masks at optimized growth conditions. Mirror-like surface morphologies and abrupt cross sections are obtained in all samples without spike growth at the mask edge. For the narrow stripe selectively grown InGaAlAs layers with a mesa width of about 1.2 mu m, a bandgap wavelength shift of 70 nm, a photoluminescence (PL) intensity of more than 80% and a PL full width at half maximum (FWHM) of less than 60 meV are obtained simultaneously with a small mask width variation from 0 to 40 mu m. The characteristics of the thickness enhancement ratio and the PL spectrum dependence on the mask width are presented and explained by considering both the migration effect from a masked region and the lateral vapour diffusion effect.

Fabrication of InGaAlAs MQW buried heterostructure lasers by narrow stripe selective MOVPE

Fabrication of InGaAlAs MQW buried heterostructure (BH) lasers by narrow stripe selective MOVPE is demonstrated in this paper. High quality InGaAlAs MQWs were first grown by narrow stripe selective MOVPE without any etching process and assessed by analysing the cross sections and PL spectrums of the InGaAlAs MQWs. Furthermore, BHs were fabricated for the InGaAlAs MQW lasers by a developed unselective regrowth method, instead of conventional selective regrowth. The InGaAlAs MQW BH lasers exhibit good device characteristics, with a high internal differential quantum efficiency of 85% and a low internal loss of 6.7 cm(-1). Meanwhile, narrow divergence angles of the far field pattern are obtained for the fabricated lasers.