Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究
Data(s) |
2006
|
---|---|
Resumo |
Nd3+-doped Y2-2x La-2x O-3 (x = 0.08) transparent ceramics were fabricated by conventional fabrication process. Spectroscopic properties of the samples were investigated. The absorption band of Nd3+ : Y1.84La0.16O3 was broad covering the wavelength range 780-850 nm. When doped with 1.5at% Nd3+, the cross sections of the sample at 820 nm and laser diode pumped 808 nm were 1.81 x 10(-20) cm(2) and 1.54 x 10(-20) cm(2), respectively. The strongest emission peak of the sample was centered at 1078 mn with long fluorescent lifetime, broad emission bandwidth and high quantum efficiency. Because of the additive La2O3, the spectroscopic quality parameter (X-Nd) of matrix was' decreased from 1.6 to 0.46, thus the fluorescence branch ratio of F-4(3/2) - (4) I-11/2 transition was increased to 56.82%. These properties of Nd3' : Y1.84La0.16O3 transparent ceramic are benefitial to achieve high efficient laser output and ultrashort modelocked pulse. |
Identificador | |
Idioma(s) |
中文 |
Fonte |
Ding Jun;杨秋红;Tang Zai-Feng;徐军;苏良碧.Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究,物理学报,2006,55(12):6414-6418 |
Palavras-Chave | #光学材料;晶体 #yttrium lanthanum oxide transparent ceramics #spectroscopic characteristics #Nd3+ |
Tipo |
期刊论文 |