La2O3对Yb:Y2O3透明陶瓷光谱性能的影响
Data(s) |
2007
|
---|---|
Resumo |
研究了La2O3对Yb:Y2O3透明陶瓷光谱性能的影响,添加适量La2O3以后,Yb:Y2O3透明陶瓷的吸收峰和发射峰的位置不变,但由于La^3+的离子半径大于Y^3+的离子半径,在Y2O3中引入La^3+离子后,导致Y2O3晶格常数变大,晶场强度变弱,同时降低了Y2O3晶体的有序度,致使发射峰强度有所下降,发射截面变小.过量的№La2O3(x=0.16)造成yb^3+激活离子发射强度明显下降;其荧光寿命在添加La2O3后总体增大45%-60%. The effect of La2O3 doping on the spectroscopic properties of transparent Yb: Y2O3 ceramics was studied. After doping La2O3, the shapes and positions of the absorption and emission peaks of transparent (Yb0.05Y0.95-x La-x)(2)O-3 ceramics were almost the same as those of Yb:Y2O3. When La2O3 was added into Yb:Y2O3, the lattice constant of (Yb0.05Y0.95-xLax)(2)O-3 became large and the crystal field strength weaker due to introducing of larger radius of La3+ ion, simultaneously its degree of order is decreased, which results in the decrease of the emission intensities and the emission cross-sections. The emission intensities were reduced greatly for the excessive doping of La2O3 ( 16at%) in (Yb0.05Y0.95-x La-x)(2)O-3 ceramics. On the whole the fluorescent lifetimes of the samples are increased by 45%-60% after doping La2O3. |
Identificador | |
Idioma(s) |
中文 |
Fonte |
杨秋红;徐军;豆传国;张红伟;丁君;唐在峰.La2O3对Yb:Y2O3透明陶瓷光谱性能的影响,物理学报,2007,56(7):3961-3965 |
Palavras-Chave | #光学材料;晶体 #氧化镧 #氧化钇 #透明陶瓷 #光谱性能 #lanthanum oxide #yttrium oxide #transparent ceramics #spectroscopic property |
Tipo |
期刊论文 |