线性共蒸法制备非均匀膜的误差特性模拟分析

对双源线性共蒸法制备的非均匀薄膜折射率分布与光学特性的关系作了探讨，并与均匀介质膜的光学特性作了对比；从折射率正变和负变两个方面．讨论了混合介质膜折射率不同变化规律对光学性能带来的影响；讨论了厚度误差和折射率极值误差对非均匀膜光学性能的影响。结果发现：折射率变化规律误差主要对非均匀膜的应用波段范围产生影响，而膜层厚度误差和折射率极值误差超过一定值时，将对薄膜光学特性产生重要影响。

沉积温度对HfO2薄膜残余应力的影响

用电子柬蒸发方法制备了HfO2薄膜，根据镀膜前后基片曲率半径的变化，用Stoney公式计算了薄膜应力。讨论了沉积温度对薄膜残余应力的影响。结果发现，HfO2薄膜的残余应力均为张应力，应力值随沉积温度的升高先增大后减小，在280℃左右出现极大值。对样品进行了XRD测试，从微观结构上对实验结果进行了分析，发现微结构演变引起的内应力变化是引起薄膜残余应力改变的主要因素，HfO2薄膜在所选沉积温度60～350℃内出现了晶态转变，堆积密度随温度升高而增大。

高真空室中的水蒸气对HfO2薄膜性能的影响

本文研究了在镀膜过程中真空室内水蒸气的含量对HfO2薄膜物理性能的影响。用电子束蒸发和光电极值监控的方法在BK7基底上制备HfO2薄膜。利用残余气体分析仪在线监测了真空室内的残余气氛组成。分别用Lambda 900光谱仪、X射线衍射方法、表面热透镜技术和1064nm的激光器测试了薄膜的光学性能、微结构、吸收和激光损伤阈值。实验发现，附加冷阱装置有助于我们有效控制镀膜过程中的水汽含量，且在水蒸气含量较少的真空室内镀制的薄膜具有较高的折射率，较小的晶粒尺寸，较低的弱吸收值和较高的损伤阈值。

Control of polarization for a broadband dichroic filter at 45 degrees incidence

A method for the control of polarization for a broadband dichroic filter was reported and some design examples were elaborated. This method could be applied over a wide range of wavelengths and a wide range of polarizations in the transmission region. A nonpolaiizing broadband dichroic filter and a broadband dichroic filter with certain polarization were designed and fabricated by electron beam evaporation with ion beam assisted deposition. The experimental spectral performances showed good agreement with their theoretical curves. In addition, the application of the method was discussed. (c) 2007 Optical Society of America

用于掺钛蓝宝石激光系统的高反膜的激光损伤

用电子束蒸发制备了用于掺钛蓝宝石啁啾脉冲放大激光系统的TiO2/HfO2/SiO2高反膜，其带宽约为176nm（R>98%, λ0=800nm），激光损伤阈值（LIDT）为2.4 J/cm2。通过TiO2和HfO2单层膜的透过光谱计算了这两种材料的折射率和消光系数。高反膜的性能主要由高折射率材料决定：折射率越高，反射带越宽；消光系数越小，薄膜吸收越小，LIDT越高。最后，讨论了高反膜的激光损伤机制。

Ta2O5膜在532, 800 和 1064 nm波长的n-on-1体系下的激光损伤阈值研究

Ta2O5膜采用传统的电子束蒸发方法制备，并在氧气中673 K的条件下进行了退火12 h处理。首先在1-on-1体系下对Ta2O5膜进行了532和1064 nm波长下的激光损伤阈值（LIDT） 研究，然后在n-on-1体系下分别对532，800和1064 nm三种波长下的激光损伤阈值进行了研究。结果表明在n-on-1体系下Ta2O5膜在532和1064 nm波长下的阈值均高于1-on-1体系下的阈值。此外，在n-on-1体系下，薄膜的阈值随波长增加而增大。同时发现，在氧气中进行退火对Ta2O5膜的光学性能

Influences of annealing on residual stress and structure of HfO2 films

HfO2 Elms are deposited on BK7 glass substrates by electron beam evaporation. The influences of annealing between 100 degrees C and 400 degrees C on residual stresses and structures of HfO2 films are studied. It is found that little differences of spectra, residual stresses and structures are obtained after annealing at lower temperatures. After annealing at higher temperatures, the spectra shift to short wavelength, the residual stress increases with the increasing annealing temperature. At the same time, the crystallite size increases and interplanar distance decreases. The variations of optical spectra and residual stress correspond to the evolutions of structures induced by annealing.

Influence of annealing temperature on structure, optical loss and laser-induced damage threshold of TiO2 thin films

TiO2 thin films are prepared on fused silica with conventional electron beam evaporation deposition. After annealed at different temperatures for 4h, the spectra and XRD patterns of the TiO2 thin film are obtained. Weak absorption of coatings is measured by the surface thermal lensing technique, and laser-induced damage threshold (LIDT) is determined. It is found that with the increasing annealing temperature, the transmittance of TiO2 films decreases. Especially when coatings are annealed at high temperature over 1173K, the optical loss is very serious. Weak absorption detection indicates that the absorption of coatings decreases firstly and then increases, and the absorption and defects play major roles in the LIDT of TiO2 thin films.

Structural and optical properties of nanostructured TiO2 thin films fabricated by glancing angle deposition

TiO2 films deposited by electron beam evaporation with glancing angle deposition (GLAD) technique were reported. The influence of flux angle on the surface morphology and the microstructure was investigated by scanning electron microscopy. The GLAD TiO2 films are anisotropy with highly orientated nanostructure of the slanted columns. With the increase of flux angle, refractive index and packing density decrease. This is caused by the shadowing effect dominating film growth. The anisotropic structure of TiO2 films results in optical birefringence, which reaches its maximum at the flux angle alpha = 65 degrees. The maximum birefringence of GLAD TiO2 films is higher than that of common bulk materials. It is suggested that glancing angle deposition may offer an effective method to obtain tailorable refractive index and birefringence in a large continuous range. (c) 2006 Elsevier B.V. All rights reserved.

Effects of oxygen partial pressure on packing density and laser damage threshold of TiO2 thin films

TiO2 films are deposited by electron beam evaporation as a function of oxygen partial pressure. The packing density, refractive index, and extinction coefficient all decrease with the increase of pressure, which also induces the change of the film's microstructure, such as the increase of voids and H2O concentration in the film. The laser-induced damage threshold (LIDT) of the film increases monotonically with the rise of pressure in this experiment. The porous structure and low nonstoichiometric defects absorption contribute to the film's high LIDT. The films prepared at the lowest and the highest pressure show nonstoichiometric and surface-defects-induced damage features, respectively.(C) 2007 American Institute of Physics.

Comparison of femtosecond and nanosecond laser-induced damage in HfO2 single-layer film and HfO2-SiO2 high reflector

HfO2 single layers, 800 run high-reflective (HR) coating, and 1064 ran HR coating were prepared by electron-beam evaporation. The laser-induced damage thresholds (LIDTs) and damage morphologies of these samples were investigated with single-pulse femtosecond and nanosecond lasers. It is found that the LIDT of the HfO2 single layer is higher than the HfO2-SiO2 HR coating in the femtosecond regime, while the situation is opposite in the nanosecond regime. Different damage mechanisms are applied to study this phenomenon. Damage morphologies of all samples due to different laser irradiations are displayed. (c) 2007 Optical Society of America.

Preparation of high laser induced damage threshold antireflection film using interrupted ion assisted deposition

Single layers and antireflection films were deposited by electron beam evaporation, ion assisted deposition and interrupted ion assisted deposition, respectively. Antireflection film of quite high laser damage threshold (18J/cm(2)) deposited by interrupted ion assisted deposition were got. The electric field distribution, weak absorption, and residual stress of films and their relations to damage threshold were investigated. It was shown that the laser induced damage threshold of film was the result of competition of disadvantages and advantages, and interrupted ion assisted deposition was one of the valuable methods for preparing high laser induced damage threshold films. (c) 2007 Optical Society of America

Effect of SiO2 protective layer on the femtosecond laser-induced damage of HfO2/SiO2 multilayer high-reflective coatings

Two kinds of HfO2/SiO2 800 nm high-reflective (HR) coatings, with and without SiO2 protective layer were deposited by electron beam evaporation. Laser-induced damage thresholds (LIDT) were measured for all samples with femtosecond laser pulses. The surface morphologies and the depth information of all samples were observed by Leica optical microscopy and WYKO surface profiler, respectively. It is found that SiO2 protective layer had no positive effect on improving the LIDT of HR coating. A simple model including the conduction band electron production via multiphoton ionization and impact ionization is used to explain this phenomenon. Theoretical calculations show that the damage occurs first in the SiO2 protective layer for HfO2/SiO2 HR coating with SiO2 protective layer. The relation of LIDT for two kinds of HfO2/SiO2 HR coatings in calculation agrees with the experiment result. (c) 2006 Elsevier B.V. All rights reserved.

Influence of deposition conditions on the microstructure of oxides thin films

Thin films of ZrO2, HfO2 and TiO2 were deposited on kinds of substrates by electron beam evaporation (EB), ion assisted deposition (IAD) and dual ion beam sputtering (DIBS). Then some of them were annealed at different temperatures. X-ray diffraction (XRD) was applied to determine the crystalline phase and the grain size of these films, and the results revealed that their microstructures strongly depended on the deposition conditions such as substrate, deposition temperature, deposition method and annealing temperature. Theory of crystal growth and migratory diffusion were applied to explain the difference of crystalline structures between these thin films deposited and treated under various conditions. (c) 2007 Elsevier B.V. All rights reserved.

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.