Degree of fourth-order coherence by double Hanbury Brown-Twiss detections

Photon quantum statistics of light can be shown by the high-order coherence. The fourth-order coherences of various quantum states including Pock states, coherent states, thermal states and squeezed vacuum states are investigated based on a double Banbury Brown Twiss (HBT) scheme. The analytical results are obtained by taking the overall efficiency and background into account.

Quantitative strain characterization of SiGe heterostructures by high-resolution transmission electron microscopy

We report the quantitative strain characterization in semiconductor heterostructures of silicon-germaniums (Si(0.76)Geo(0.24)) grown on Si substrate by an ultra-high vacuum chemical vapor deposition system. The relaxed SiGe virtual substrate has been achieved by thermal annealing of the SiGe film with an inserted Ge layer. Strain analysis was performed using a combination of high-resolution transmission electron microscopy and geometric phase analysis.

Promoting strain relaxation of Si0.72Ge0.28 film on Si (100) substrate by inserting a low-temperature Ge islands layer in UHVCVD

A flat, fully strain-relaxed Si0.72Ge0.28 thin film was grown on Si (1 0 0) substrate with a combination of thin low-temperature (LT) Ge and LT-Si0.72Ge0.28 buffer layers by ultrahigh vacuum chemical vapor deposition. The strain relaxation ratio in the Si0.72Ge0.28 film was enhanced up to 99% with the assistance of three-dimensional Ge islands and point defects introduced in the layers, which furthermore facilitated an ultra-low threading dislocation density of 5 x 10(4) cm (2) for the top SiGe film. More interestingly, no cross-hatch pattern was observed on the SiGe surface and the surface root-mean-square roughness was less than 2 nm. The temperature for the growth of LT-Ge layer was optimized to be 300 degrees C. (C) 2008 Elsevier B.V. All rights reserved.

High transmission of slow light in the photonic crystal waveguide bends

We present the research on the transmission characteristic of slow-light-mode in the photonic crystal line-defect waveguide bends on SOL After optimizing the structure parameters in the vicinity of the bends, the normalized transmission efficiency of slow-light-mode through the photonic crystal 60 degree and 120 degree waveguide bends are as high as 80% and 60% respectively, which are 10 times higher than that in the undeformed case. To slow down light further, we design novel coupled cavity waveguide bend structures with high quality-factor. High normalized transmission efficiency of 75% and low group velocity of c/170 ( c is the light velocity in vacuum) are realized. These results are beneficial to enhance the slow light effect of photonic crystal structures and improve the miniaturization and integration of photonic crystal slow light devices.

GaSb based midinfrared equilateral-triangle-resonator semiconductor lasers

Theoretical calculations of the mode characteristics of an equilateral-triangle resonator (ETR) with a 10 mu m cavity side length show that the fundamental mode, with longitudinal mode index of 25, has a wavelength of 2.185 mu m and a longitudinal mode separation of 100 nm. This mode has a quality factor (similar to 2x10(5)) that is much larger than the first (similar to 5x10(4)) and second (similar to 3x10(4)) order modes, indicating that single fundamental mode lasing should be accessible over a broad wavelength tuning range. An electrically injected ETR based on this design is fabricated from an InGaAsSb/AlGaAsSb/GaSb, graded-index separate-confinement heterostructure, laser diode wafer with a 2.1 mu m emission wavelength. This device achieved single mode, continuous wave operation at 77 K with a threshold current of 0.5 mA and a single mode wavelength tuning range of 3.25 nm, which is accomplished by varying the injection current from 0.5 to 6.0 mA. (C) 2008 American Vacuum Society.

The effects of substrate temperature on the structure and properties of ZnO films prepared by pulsed laser deposition

ZnO thin films were prepared by pulsed laser deposition (PLD) on glass substrates with growth temperature from room temperature (RT) to 500 degrees C. The effects of substrate temperature on the structural and optical properties of ZnO films have been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission spectra, and RT photoluminescence (PL) measurements. The results showed that crystalline and (0 0 2)-oriented ZnO films were obtained at all substrate temperatures. As the substrate temperature increased from RT to 500 degrees C, the ratio of grain size in height direction to that in the lateral direction gradually decreased. The same grain size in two directions was obtained at 200 degrees C, and the size was smallest in all samples, which may result in maximum E, and E-0 of the films. UV emission was observed only in the films grown at 200 degrees C, which is probably because the stoichiometry of ZnO films was improved at a suitable substrate temperature. It was suggested that the UV emission might be related to the stoichiometry in the ZnO film rather than the grain size of the thin film. (c) 2007 Elsevier Ltd. All rights reserved.

Electroluminescence from Ge on Si substrate at room temperature

A Ge/Si heterojunction light emitting diode with a p(+)-Ge/i-Ge/N+-Si structure was fabricated using the ultrahigh vacuum chemical vapor deposition technology on N+-Si substrate. The device had a good I-V rectifying behavior. Under forward bias voltage ranging from 1.1 to 2.5 V, electroluminescence around 1565 nm was observed at room temperature. The mechanism of the light emission is discussed by the radiative lifetime and the scattering rate. The results indicate that germanium is a potential candidate for silicon-based light source material. (C) 2009 American Institute of Physics. [DOI 10.1063/1.3216577]

Photoluminescence from heterogeneous SiGe/Si nanostructures prepared via a two-step approach strategy

A two-step approach of preparation for SiGe/Si heterogeneous nanostructures, which combined with ultra-high vacuum chemical deposition and electrochemical anodization techniques, is demonstrated. Uniformly distributed nanostructures with a quite uniform distribution of size and morphology are obtained. A strong room-temperature photoluminescence from the nanostructures was observed with a narrow full-width at half-maximum of around 110 meV. The possible origins of the two main peaks at around 1.6 and 1.8 eV have been discussed in detail. The two-step approach is proved to be a promising method to fabricate new Si-based optoelectronic materials. (C) 2009 Elsevier B.V. All rights reserved.

Inductively coupled plasma etching in fabrication of 2D InP-based photonic crystals

The authors developed an inductively coupled plasma etching process for the fabrication of hole-type photonic crystals in InP. The etching was performed at 70 degrees C using BCl3/Cl-2 chemistries. A high etch rate of 1.4 mu m/min was obtained for 200 nm diameter holes. The process also yields nearly cylindrical hole shape with a 10.8 aspect ratio and more than 85 degrees straightness of the smooth sidewall. Surface-emitting photonic crystal laser and edge emitting one were demonstrated in the experiments.

Zero biased Ge-on-Si photodetector with a bandwidth of 4.72 GHz at 1550 nm

High quality Ge was epitaxially grown on Si using ultrahigh vacuum/chemical vapor deposition (UHV/CVD). This paper demonstrates efficient germanium-on-silicon p-i-n photodetectors with 0.8 mu m Ge, with responsivities as high as 0.38 and 0.21 A/W at 1.31 and 1.55 mu m, respectively. The dark current density is 0.37 mA/cm(2) and 29.4 mA/cm(2) at 0 V and a reverse bias of 0.5 V. The detector with a diameter of 30 mu m, a 3 dB-bandwidth of 4.72 GHz at an incident wavelength of 1550 nm and zero external bias has been measured. At a reverse bias of 3 V, the bandwidth is 6.28 GHz.

Room temperature photoluminescence of tensile-strained Ge/Si0.13Ge0.87 quantum wells grown on silicon-based germanium virtual substrate

We report a room temperature study of the direct band gap photoluminescence of tensile-strained Ge/Si0.13Ge0.87 multiple quantum wells grown on Si-based germanium virtual substrates by ultrahigh vacuum chemical vapor deposition. Blueshifts of the luminescence peak energy from the Ge quantum wells in comparison with the Ge virtual substrate are in good agreement with the theoretical prediction when we attribute the luminescence from the quantum well to the c Gamma 1-HH1 direct band transition. The reduction in direct band gap in the tensile strained Ge epilayer and the quantum confinement effect in the Ge/Si0.13Ge0.87 quantum wells are directly demonstrated by room temperature photoluminescence.

Enhanced charge storage characteristics of silicon nanocrystals fabricated by electron-beam coevaporation of Si and SiOx(x=1 or 2)

In this article, a simple and flexible electron-beam coevaporation (EBCE) technique has been reported of fabrication of the silicon nanocrystals (Si NCs) and their application to the nonvolatile memory. For EBCE, the Si and SiOx(x=1 or 2) were used as source materials. Transmission electron microscopy images and Raman spectra measurement verified the formation of the Si NCs. The average size and area density of the Si NCs can be adjusted by increasing the Si:O weight ratio in source material, which has a great impact on the crystalline volume fraction of the deposited film and on the charge storage characteristics of the Si NCs. A memory window as large as 6.6 V under +/- 8 V sweep voltage was observed for the metal-oxide-semiconductor capacitor structure with the embedded Si NCs.

1 x 4 Ge-on-SOI PIN Photodetector Array for Parallel Optical Interconnects

High-quality Ge film was epitaxially grown on silicon on insulator using the ultrahigh vacuum chemical vapor deposition. In this paper, we demonstrated that the efficient 1 4 germanium-on-silicon p-i-n photodetector arrays with 1.0 mu m Ge film had a responsivity as high as 0.65 A/W at 1.31 mu m and 0.32 A/W at 1.55 mu m, respectively. The dark current density was about 0.75 mA/cm(2) at 0 V and 13.9 mA/cm(2) at 1.0 V reverse bias. The detectors with a diameter of 25 mu m were measured at 1550 nm incident light under 0 V bias, and the result showed that the 3-dB bandwidth is 2.48 GHz. At a reverse bias of 3 V, the bandwidth is about 13.3 GHz. The four devices showed a good consistency.

Preferred growth of nanocrystalline silicon in boron-doped nc-Si : H Films

Preferred growth of nanocrystalline silicon (nc-Si) was first found in boron-doped hydrogenated nanocrystalline (nc-Si:H) films prepared using plasma-enhanced chemical vapor deposition system. The films were characterized by high-resolution transmission electron microscope, X-ray diffraction (XRD) spectrum and Raman Scattering spectrum. The results showed that the diffraction peaks in XRD spectrum were at 2theta approximate to 47degrees and the exponent of crystalline plane of nc-Si in the film was (220). A considerable reason was electric field derived from dc bias made the bonds of Si-Si array according to a certain orient. The size and crystalline volume fraction of nc-Si in boron-doped films were intensively depended on the deposited parameters: diborane (B2H6) doping ratio in silane (SiH4), silane dilution ratio in hydrogen (H-2), rf power density, substrate's temperature and reactive pressure, respectively. But preferred growth of nc-Si in the boron-doped nc-Si:H films cannot be obtained by changing these parameters. (C) 2004 Elsevier Ltd. All rights reserved.

Synthesis of GaN nanowires and nano-pyramids in a two-hot-boat chemical vapor deposition system via an in-doping technique

A two-hot-boat chemical vapor deposition system was modified from a thermal evaporation equipment. This system has the advantage of high vacuum, rapid heating rate and temperature separately controlled boats for the source and samples. These are in favor of synthesizing compound semiconducting nano-materials. By the system, we have synthesized high-quality wurtzite single crystal GaN nanowires and nanotip triangle pyramids via an in-situ doping indium surfactant technique on Si and 3C-SiC epilayer/Si substrates. The products were analyzed by x-ray diffraction, field emission scanning electron microscopy, highresolution transmission electron microscopy, energy- dispersive x-ray spectroscopy, and photoluminescence measurements. The GaN nanotip triangle pyramids, synthesized with this novel method, have potential application in electronic/ photonic devices for field-emission and laser.