Structural, morphological and optical properties of ZnO thin films grown on gamma-LiAlO2 substrate by pulsed laser deposition

ZnO thin films were deposited on the substrates of (100) gamma-LiAlO2 at 400, 550 and 700 degrees C using pulsed laser deposition (PLD) with the fixed oxygen pressure of 20 Pa, respectively. When the substrate temperature is 400 degrees C, the grain size of the film is less than 1 mu m observed by Leitz microscope and measured by X-ray diffraction (XRD). As the substrate temperature increases to 550 degrees C, highly-preferred c-orientation and high-quality ZnO film can be attained. While the substrate temperature rises to 700 degrees C, more defects appears on the surface of film and the ZnO films become polycrystalline again possibly because more Li of the substrate diffused into the ZnO film at high substrate temperature. The photoluminescence (PL) spectra of ZnO films at room temperature show the blue emission peaks centered at 430 nm. We suggest that the blue emission corresponds to the electron transition from the level of interstitial Zn to the valence band. Meanwhile, the films grown on gamma-LiAlO2 (LAO) exhibit green emission centered at 540 nm, which seemed to be ascribed to excess zinc and/or oxygen vacancy in the ZnO films caused by diffusion of Li. from the substrates into the films during the deposition.

Deposition of ZnO thin films on (100) γ-LiAlO2 substrate

Optical properties for ZnO thin films grown on (100) γ-LiAlO2 (LAO) substrate by pulsed laser deposition method were investigated. The c-axis oriented ZnO films were grown on (100) γ-LiAlO2 substrates at the substrate temperature of 550 Celsius degrees. The transmittance of the films was over 85%. Peaks attributed to excitons were shown in absorption spectra, which indicated that thin films had high crystallinity. Photoluminescence spectra with the maximum peak at 540 nm were observed at room temperature, which seemed to be ascribed to oxygen vacancy in the ZnO films caused by diffusion of Li from the substrates into the films during the deposition.

Nonpolar m-plane thin film GaN and InGaN/GaN light-emitting diodes on LiAlO2(100) substrates

The nonpolar m-plane (1 (1) over bar 00) thin film GaN and InGaN/GaN light-emitting diodes (LEDs) grown by metal-organic chemical vapor deposition on LiAlO2 (100) substrates are reported. The LEDs emit green light with output power of 80 mu W under a direct current of 20 mA for a 400x400 mu m(2) device. The current versus voltage (I-V) characteristic of the diode shows soft rectifying properties caused by defects and impurities in the p-n junction. The electroluminescence peak wavelength dependence on injection current, for currents in excess of 20 mA, saturates at 515-516 nm. This proves the absence of polarization fields in the active region present in c-plane structures. The light output intensity versus current (L-I) characteristic of the diode exhibits a superlinear relation at low injection current caused by nonradiative centers providing a shunt path and a linear light emission zone at high current level when these centers are saturated. (c) 2007 American Institute of Physics.

Defects in LPE-grown beta-barium borate (beta-BaB2O4) thin films

Morphological defects in beta-barium borate (beta-BBO) thin films grown on Sr2+ -doped alpha-BBO substrates by liquid phase epitaxy (LPE) technique were studied by scanning electron micrograph (SEM), atomic force microscopy (AFM) and optical spectroscopy. The present results indicate that the main defects exit in beta-BBO thin films are microcracks and hollow structure. The formation of microcrack is due to the lattice mismatch and the difference of thermal expansion coefficients between substrate and film. The hollow structure might be caused during the combination of islands, which formed in the initial stage. (C) 2006 Elsevier GmbH. All rights reserved.

Structural and optical properties of a-plane ZnO thin films synthesized on γ-LiAlO2 (302) substrates by low pressure metal-organic chemical vapor deposition

Nonpolar a-plane (1120) ZnO thin films have been fabricated on gamma-LiAlO2 (302) substrates via the low-pressure metal-organic chemical vapor deposition. An obvious intensity variation of the E-2 mode in the Raman spectra indicates that there exhibits in-plane optical anisotropy in the a-plane ZnO thin films. Highly-oriented uniform grains of rectangular shape can be seen from the atomic force microscopy images, which mean that the lateral growth rate of the thin films is also anisotropic. It is demonstrated experimentally that a buffer layer deposited at a low temperature (200 degrees C) can improve the structural and optical properties of the epilayer to a large extent. (c) 2007 Elsevier B.V. All rights reserved.

Characterization of m-plane ZnO thin film on gamma-LiAlO2 (100) substrate by metal-organic chemical vapor deposition

Non-polar (1 (1) over bar 00)m-plane ZnO thin film has been prepared on gamma-LiAlO2 (100)substrate via the low pressure metal organic chemical vapor deposition. Obvious intensity variation of the E-2 mode in the polarized Raman spectra and the absorption edge shift in the polarized optical transmission spectra indicate that the m-plane film exhibits optical anisotropy, which have applications in certain optical devices, such as the UV modulator and polarization-dependent beam switch. From the atomic force microscopy images, highly-oriented uniform-sized grains of rectangular shape were observed. (c) 2008 Elsevier B.V. All rights reserved.

Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

ZrO2, films were deposited by electron-beam evaporation with the oxygen partial pressure varying from 3 X 10(-3) Pa to I I X 10(-3) Pa. The phase structure of the samples was characterized by x-ray diffraction (XRD). The thermal absorption of the films was measured by the surface thermal lensing technique. A spectrophotometer was employed to measure the refractive indices of the samples. The laser-induced damage threshold (LIDT) was assessed using a 1064, nm Nd: yttritium-aluminium-garnet pulsed laser at pulse width of 12 ns. The influence of oxygen partial pressure on the microstructure and LIDT of ZrO2 films was investigated. XRD data revealed that the films changed from polycrystalline to amorphous as the oxygen partial pressure increased. The variation of refractive index at 550 nm wavelength indicated that the packing density of the films decreased gradually with increasing oxygen partial pressure. The absorptance of the samples decreased monotonically from 125.2 to 84.5 ppm with increasing oxygen partial pressure. The damage threshold, values increased from 18.5 to 26.7 J/cm(2) for oxygen partial pressures varying from 3 X 10(-3) Pa to 9 X 10(-3) Pa, but decreased to 17.3 J/cm(2) in the case of I I X 10(-3) Pa. (C) 2005 American Vacuum Society.

Study of thin-film SO2 gas sensors by photometric and ellipsometric methods

Pt-, Pd-, and Zr-doped SnO2 thin films and dopant-free VOx films were fabricated by planar magnetron sputtering. Tests for sensitivity to SO2 for all samples were conducted at 180 degreesC, and the sensitivities were investigated ex situ with photometric and ellipsometric methods at room temperature. It was found that the optical sensitivities as well as the sensitive wavelength region for SnO2 films could be tuned by doping. The Pd-doped SnO2 films had good sensitivity in the visible range, and the Zr-doped in the near IR. The dominant sensitive wavelength region for VOx films fell into the visible range, and the ratio of the sensitivity in the visible to that in the near IR increased with O-2/Ar in the depositing atmosphere. (C) 2001 society of Photo-Optical instrumentation Engineers .

Analysis of electromagnetic propagation in birefringent thin film

In general, the propagating behavior of extraordinary wave in anisotropic materials is different from that in isotropic materials. With the tangential continuity of Maxwell's equations, the electromagnetic propagating behaviors have been investigated at the incident and exit interfaces of the uniaxial anisotropic thin film. The emphasis was placed on two interesting optical phenomena such as homolateral refraction behavior and wide-angle Brewster's phenomenon, which occurred at the interfaces of uniaxial anisotropic thin film.

Simulation of growth process of thin film on non-planar substrate

In (2 + 1) dimension, growth process of thin film on non-planar substrate in Kuramoto-Sivashinsky model is studied with numerical simulation approach. 15 x 15 semi-ellipsoids arranged orderly on the surface of substrate are used to represent initial rough surface. The results show that at the initial stage of growth process, the surface morphology of thin film appears to be grid-structure, and the interface width constantly decreases with the growth time, then reaches minimum. However, the grid-structure becomes ambiguous, and granules of different sizes distribute evenly on the surface of thin film with the increase of growth time. Thereafter, the average size of granules and the interface width gradually increase, and the surface morphology of thin film presents fractal properties. The numerical results of height-height correlation functions of thin film verify the surface morphology of thin film to be fractal for a longer growth time. By fitting of the height-height correlation functions of thin film with different growth times, the growth process is described quantitatively. (c) 2004 Elsevier B.V. All rights reserved.

Matrix analysis of an anisotropic optical thin film

Based on Maxwell's equations, standard boundary conditions are imposed on resultant electric- and magnetic-field vectors at interfaces, and the propagating characteristics of extraordinary waves, such as the forward- and backward-propagating directions of wave vectors, rays and their corresponding refractive indices are determined in a uniaxially birefringent thin film. Furthermore, 2 x 2 characteristic matrices of a birefringent thin film are derived including multiple reflections for the extraordinary wave.

Enhancement of near-band edge photoluminescence of ZnO thin films by employing MgF2 buffer layer

ZnO/MgF2/ZnO sandwich structure films were fabricated. The effects of a buffer layer on structure and optical properties of ZnO films were investigated by X-ray diffraction, photoluminescence, optical transmittance and absorption measurements. Measurement results showed that the buffer layer had the effects of improving the quality of ZnO films and releasing the residual stresses in the films. The near-band edge emissions of ZnO films deposited on the MgF2 buffer layer were significantly enhanced compared with those deposited on bare substrate due to the smaller lattice mismatch between MgF2 and ZnO than that between fused silica and ZnO. (c) 2006 Elsevier B.V. All rights reserved.

Enhancement of near-band-edge photoluminescence of ZnO thin films in sandwich configuration at room temperature

ZnO/ITO/ZnO sandwich structure films were fabricated. The effects of buffer layer on the structure and optical properties of ZnO films were investigated by x-ray diffraction (XRD), photoluminescence, optical transmittance, and absorption measurements. XRD spectra indicate that a buffer layer has the effects of lowering the grain orientation of ZnO films and increasing the residual stresses in the films. The near-band-edge emissions of ZnO films deposited on both single indium tin oxide (ITO) buffer and ITO/ZnO double buffers are significantly enhanced compared with that deposited on a bare substrate due to the quantum confinement effect. (C) 2006 American Institute of Physics.

The study on the interface adhesion comparison of the MgF2, Al2O3, SiO2 and Ag thin films

Adhesion between the interface of pure silver thin film and three kinds of low refractive index coatings MgF2, Al2O3, SiO2 were compared in this article. The results indicated that the adhesion of Al2O3 and Ag was evidently superior to that of MgF2 and Ag, and the adhesion of MgF2 and Ag was evidently superior to that Of SiO2 and Ag. Reasons were analyzed accordingly. On the other hand, we compared the effect on the optical characteristic of Ag film when these three kinds of films were used as protective coatings and enhanced coatings. Considering the difference of the adhesion between Ag and MgF2, Al2O3, SiO2, suited uses are given for each other. © 2004 Elsevier B.V. All rights reserved.