Role of interface absorption in laser-induced local heating of optical coatings

Considering the interface absorption in optical coatings, we propose a model to simulate interface absorption. Calculations are made and the temperature field of several kinds of thin film multilayers, including those of partial reflectivity, high-reflectivity, and antireflectivity coatings are analyzed. The interface absorption is found to greatly influence the temperature distribution within multilayer coatings and to weaken the laser damage resistance of the samples. The real-time results of the photothermal deflection technique for laser induced damage to samples supports the model. (C) 1997 Society of Photo-Optical Instrumentation Engineers.

氧分压对ZrO2薄膜激光损伤阈值的影响

在不同的氧分压下用电子束热蒸发的方法制备了ZrO2薄膜。分别通过X射线衍射、光学光谱、热透镜技术、抗激光辐照等测试，对所制备样品的微结构、折射率、吸收率及激光损伤阈值进行了测量。实验结果表明，薄膜中晶粒主要是四方相为主的多晶结构，并且随着氧分压的增加，结晶度、折射率以及弱吸收均逐渐降低。薄膜的激光损伤阈值开始随着氧分压增加从18．5J／cm^2逐渐增加，氧分压为9×10^-3Pa时达到最大，值为26．7J／cm^2，氧分压再增加时则又降低到17．5J／cm^2。由此可见，氧分压引起的薄膜微结构变化是ZrO

Influence of oxygen partial pressure on the structure and photoluminescence of direct current reactive magnetron sputtering ZnO thin films

The effects of oxygen partial pressure on the structure and photoluminescence (PL) of ZnO films were studied. The films were prepared by direct current (DC) reactive magnetron sputtering with various oxygen concentrations at room temperature. With increasing oxygen ratio, the structure of films changes from zinc and zinc oxide phases, single-phase ZnO, to the (002) orientation, and the mechanical stresses exhibit from tensile stress to compressive stress. Films deposited at higher oxygen pressure show weaker emission intensities, which may result from the decrease of the oxygen vacancies and zinc interstitials in the film. This indicates that the emission in ZnO film originates from the oxygen vacancy and zinc interstitial-related defects. From optical transmittance spectra of ZnO films, the plasma edge shifts towards the shorter wavelength with the improvement of film stoichiometry. (C) 2004 Elsevier B.V. All rights reserved.

The effects of oxygen partial pressure on the optical absorption edge and the UV emission energy of ZnO films

The optical absorption edge and ultraviolet (UV) emission energy of ZnO films deposited by direct current (DC) reactive magnetron sputtering at room temperature have been investigated. With the oxygen ratio increasing, the structure of films changes from zinc and zinc oxide coexisting phase to single-phase ZnO and finally to the highly (002) orientation. Both the grain size and the stress of ZnO film vary with the oxygen partial pressure. Upon increasing the oxygen partial pressure in the growing ambient, the visible emission in the room-temperature photoluminescence spectra was suppressed without sacrificing the band-edge emission intensity in the ultraviolet region. The peaks of photoluminescence spectra were located at 3.06---3.15 eV. From optical transmittance spectra of ZnO films, the optical band gap edge was observed to shift towards shorter wavelength with the increase of oxygen partial pressure.

不同沉积参量下ZrO_2薄膜的微结构和激光损伤阈值

ZrO2采用X射线衍射(XRD)技术分析了不同充氧条件和沉积温度对ZrO2溥膜组成结构的影响，并对不同工艺下制备的薄膜的表面粗糙度和激光损伤阈值进行了测量。结果发现随着氧压的升高，ZrO2溥膜将由单斜相多晶态逐渐转变为非晶态结构，而随着基片温度的增加，溥膜将由非晶态逐渐转变为单斜相多晶态。同时发现随着氧压升高晶粒尺寸减小，而随着沉积温度增加，晶粒尺寸增大。氧压增加时工艺对表面粗糙度有一定程度的改善，而沉积温度升高，工艺对表面粗糙度的改善不明显。晶粒尺寸大小变化与表面粗糙度变化存在对应关系。激光损伤测量表明

Effects of oxygen partial pressure on packing density and laser damage threshold of TiO2 thin films

TiO2 films are deposited by electron beam evaporation as a function of oxygen partial pressure. The packing density, refractive index, and extinction coefficient all decrease with the increase of pressure, which also induces the change of the film's microstructure, such as the increase of voids and H2O concentration in the film. The laser-induced damage threshold (LIDT) of the film increases monotonically with the rise of pressure in this experiment. The porous structure and low nonstoichiometric defects absorption contribute to the film's high LIDT. The films prepared at the lowest and the highest pressure show nonstoichiometric and surface-defects-induced damage features, respectively.(C) 2007 American Institute of Physics.