Interface as the origin of ferromagnetism in cobalt doped ZnO film grown on silicon substrate

We have investigated the magnetic properties of Co-doped zinc oxide (ZnO) film deposited on silicon substrate by magnetron sputtering. Co ions have a valence of 2+ and substitute for Zn sites in the lattice. By using a chemical etching method, an extrinsic ferromagnetism was demonstrated. The observed ferromagnetism is neither associated with magnetic precipitates nor with contamination, but originates from the silicon/silicon oxide interface. This interface ferromagnetism is characterized by being temperature independent and by having a parallel magnetic anisotropy. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.2989128]

Effect of the oxygen concentration on the properties of Gd2O3 thin films

Gd2O3 thin films were deposited on Si (100) substrates at 650degreesC by a magnetron sputtering system under different Ar/O-2 ratios of 6:1, 4:1 and 2:1. The effect of the oxygen concentration on the properties of oxide thin films was investigated by X-ray diffraction, X-ray photoelectron spectroscopy, atomic force microscopy and capacitance-voltage (C-V)measurement. X-ray diffraction shows that the structure of oxide films changed from the monoclinic Gd2O3 phase to cubic Gd2O3 phase when the oxygen concentration increased. According to C-V measurement, the dielectric constant value of the samples deposited at different Ar/O-2 ratios is about 12. (C) 2004 Elsevier B.V. All rights reserved.

Structural, magnetic properties and photoemission study of Ni-doped ZnO

Nickel-doped ZnO (Zn1-xNixO) have been produced using rf magnetron sputtering. X-ray diffraction measurements revealed that nickel atoms were successfully incorporated into ZnO host matrix without forming any detectable secondary phase. Ni 2p core-level photoemission spectroscopy confirmed this result and suggested Ni hits it chemical valence of 2 +. According to the . We studied the electronic magnetization measurements, no ferromagnetic but paramagnetic behavior was found for Zn0.86Ni0.14O. We studied the electronic structure of Zn0.86Ni0.14O by valence-band photoemission spectroscopy. The spectra demonstrate a structure at similar to 2 eV below the Fermi energy E-F, which is of Ni 3d origin. No emission was found at E-A, suggesting the insulating nature of the film. (c) 2005 Elsevier Ltd. All rights reserved.

Influence of nitridation time on the morphology of GaN nanorods synthesized by nitriding Ga2O3/ZnO films

Gallium nitride (GaN) nanorods were synthesized by nitriding Ga2O3/ZnO films which were deposited in turn on Si (111) substrates using radio frequency (RF) magnetron sputtering system. In the nitridation process, ZnO was reduced to Zn and Zn sublimated at 950 degrees C. Ga2O3 was reduced to Ga2O and Ga2O reacted with NH3 to synthesize GaN nanorods with the assistance of the sublimation of Zn. The morphology and structure of the nanorods were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and selected-area electron diffraction (SAED). The composition of GaN nanorods was studied by Fourier-transform infrared spectrophotometer (FTIR). The synthesized nanorods is hexagonal wurtzite structured. Nitridation time of the samples has an evident influence on the morphology of GaN nanorods synthesized by this method. (c) 2006 Elsevier B.V. All rights reserved.

Structural and photoluminescent properties of ternary Zn1-xCdxO crystal films grown on Si(111) substrates

The ternary Zn1-xCdxO (0less than or equal toxless than or equal to0.6) alloying films with highly c-axis orientation have been deposited on Si(111) substrates by direct current reactive magnetron sputtering method. X-ray diffraction measurement indicates that the wurtzite-type structure of ZnO can be stabilized up to nominal Cd content x similar to 0.6 without cubic CdO phase separation. The lattice parameter c of Zn1-xCdxO increases almost linearly from 5.229 Angstrom (x = 0) to 5.247 Angstrom (x = 0.6), indicating that Cd substitution takes place on the Zn lattice sites. The photoluminescence spectra of the Zn1-xCdxO thin films measured at 12 K display a substantial red shift (similar to0.3 eV) in the near-band-edges (NBEs) emission of ZnO: from 3.39 eV of ZnO to 3.00 eV of Zn0.4Cd0.6O. The direct modulation of band gap caused by Zn/Cd substitution is responsible for the red shift effect in NBE emission of ZnO. (C) 2003 Elsevier Science B.V. All rights reserved.

SiO2/Ta interface reaction in magnetic multilayers and its influence on Ta buffer layers

Ta is often used as a buffer layer in magnetic multilayers. In this study, Ta/Ni81Fe19/Ta multilayers were deposited by magnetron sputtering on sing-crystal Si with a 300-nm-thick SiO2 film. The composition and chemical states at the interface region of SiO2/Ta were studied using the X-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that there is an 'inter-mixing layer" at the SiO2/Ta interface due to a thermodynamically favorable reaction: 15 SiO2 + 37 Ta = 6 Ta2O5 + 5 Ta5Si3. Therefore, the Ta buffer layer thickness used to induce NiFe (111) texture increases.

Electroluminescence from Au/(SiO2/Si/SiO2) nanometer double barrier/p-Si structures and its mechanism

SiO2/Si/SiO2 nanometer double barriers (SSSNDB) with Si layers of twenty-seven different thicknesses in a range of 1-5 nm with an interval of 0.2 nm have been deposited on p-Si substrates using two-target alternative magnetron sputtering. Electroluminescence (EL) from the semitransparent Au film/SSSNDB/p-Si diodes and from a control diode without any Si layer have been observed under forward bias. Each EL spectrum of all these diodes can be fitted by two Gaussian bands with peak energies of 1.82 and 2.25 eV, and full widths at half maximum of 0.38 and 0.69 eV, respectively. It is found that the current, EL peak wavelength and intensities of the two Gaussian bands of the Au/SSSNDB/p-Si structure oscillate synchronously with increasing Si layer thickness with a period corresponding to half a de Broglie wavelength of the carriers. The experimental results strongly indicate that the EL originates mainly from two types of luminescence centres with energies of 1.82 and 2.25 eV in the SiO2 barriers, rather than from the nanometer Si well in the SSSNDB. The EL mechanism is discussed in detail.

Determination of the interdiffusion coefficients of liquid Zn and Sn using Ta/Zn-Sn/Si trilayers

In this paper we present a new method for measuring diffusion coefficients in liquid metals under convection-less conditions with solid/liquid-liquid/solid trilayer. The advantage of this kind of trilayer is that effects from gravity-induced convection and Marangoni-convection can be omitted, so that the diffusion coefficient is determined more accurately. The Ta/Zn-Sn/Si trilayer were prepared with a multi-target ion-beam sputtering deposition technique and annealed in an electric furnace under an argon atmosphere. The interdiffusion of liquid zinc and tin at 500 degrees degree C was investigated. The diffusion concentration profiles were determined by energy dispersive spectroscopy. The interdiffusion coefficients range from 1.0x10(-6)cm(2)/s to 2.8x10(-6)cm(2)/s, which is less than previous values measured by capillary reservoir technique under 1g-environment where various convection exist. The precise interdiffusion coefficients of liquid zinc and tin result from the removing of disturbances of various kinds of convection.

Magnetic property and interface structure of Ta/NiO/NiFe/Ta

Ta/NiO/NiFe/Ta multilayers, utilizing Ta as buffer layer, were prepared by rf reactive and de magnetron sputtering. The exchange coupling field between NiO and NiFe reached a maximum value of 9.6x10(3) A/m at a NiO film thickness of 50 nm. The composition and chemical states at interface region of Ta/NiO/Ta were studied by using the X-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that there is an "intermixing layer" at the Ta/NiO land NiO/Ta) interface due to a thermodynamically favorable reaction 2Ta + 5NiO = 5Ni + Ta2O5. This interface reaction has a great effect on exchange coupling. The thickness of Ni+NiO estimated by XPS depth. profiles is about 8-10 nm.

Low Temperature Deposited Nano-structured Vanadium Oxide Thin Films for Uncooled Infrared Detectors

A novel process of room temperature ion beam sputtering deposition of vanadium oxide films and low temperature post annealing for uncooled infrared detectors was proposed in this work. VOx thin films with relatively low square resistance (70 K Omega / square) and large temperature coefficient of resistance (more than 3%/K) at room temperature were fabricated using this low temperature process which was very compatible with the process of uncooled infrared detectors based on micromachined technology. Furthermore, chemical composition and film surface have been characterized using X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) respectively. The results showed that the main composition of the processed thin films was V2O5 and the thin films were in the process of crystallization.

Tunable Ag surface-plasmon-resonance wavelength and its application on the photochromic behavior of TiO2-Ag films

Surface and bulk plasmon resonance of noble metal particles play an essential role in the multicolor photochromism of semiconductor systems containing noble metal particles, Here we examined several key parameters affecting surface plasmon resonance wavelength (SPRW) of Ag particles and investigated the relation between surface plasmon and photochromic reaction wavelength. From the transmission spectra of sandwiched (TiO2/Ag/TiO2) and overcoated (Ag/TiO2) films deposited on quartz substrates at room temperature by rf helicon magnetron sputtering, we demonstrated that the SPRW can be made tunable by changing the surrounding media and thickness of the metal layer. The coloration and bleaching in visible light region due to photochromism were clearly observed for the films inserted with a 0.55 nm Ag layer.

Spectroscopic ellipsometry study of In2O3 thin films

In2O3 films grown by helicon magnetron sputtering with different thicknesses were characterized by spectroscopic ellipsometry in the energy range from 1.5 to 5.0 eV. Aside from one amorphous sample prepared at room substrate temperature, polycrystalline In2O3 films with cubic crystal structure were confirmed for other four samples prepared at the substrate temperature of 450 A degrees C. Excellent SE fittings were realized by applying 1 and/or 2 terms F&B amorphous formulations, building double layered film configuration models, and further taking account of void into the surface layer based on Bruggeman effective medium approximation for thinner films. Spectral dependent refractive indices and extinction coefficients were obtained for five samples. The curve shapes were well interpreted according to the applied dispersion formulas. Almost similar optical band gap values from 3.76 to 3.84 eV were obtained for five samples by Tauc plot calculation using extinction coefficients under the assumption of direct allowed optical transition mode.

EFFECT OF A SI LAYER ON THE SUPERCONDUCTIVE PROPERTIES OF A BIPBSRCACUO THIN-FILM

The Pb-doped BiSrCaCuO superconducting films were grown by the single source mixed evaporation technique. The microbridges of dimensions 50 mum x 40 mum were fabricated by standard photolithography technologies. Si films with a thickness of 2500 angstrom were deposited on the microbridge area surfaces of BiPbSrCaCuO superconducting films by rf-magnetron sputtering. A greatly lowered zero resistance temperature of the microbridge area of the BiPbSrCaCuO film after Si sputtering was found. A non-linear effect of the current-voltage (I-V) characteristics at 78 K was shown. The high-frequency capacitance-voltage (C-V) curve of this structure at 78 K was symmetrical with the maximum capacitance at V = 0, and the capacitance decreased with increasing applied bias voltage. Afl experimental results are discussed.

Structural studies of NixFe100-x/Mo magnetic multilayers by x-ray small-angle reflection and high-angle diffraction

Magnetic multilayers [NixFe100-x/Mo-30] grown by dc-magnetron sputtering were investigated by x-ray small-angle reflection and high-angle diffraction. Structural parameters of the multilayers such as the superlattice periods, the interfacial roughness, and interplane distance were obtained. It was found that for our NixFe100-x/Mo system, the Mo layer has bcc structure with [110] preferential orientation, while the preferential orientation of the NixFe100-x layer changes from a fee structure with [111] preferential orientation to a bcc structure with [110] preferential orientation with decreasing values of x. An intermixing layer located in the interlayer region between the NixFe100-x and Mo layers exists in the multilayers, and its thickness is almost invariant with respect to an increase of Mo layer thickness and/or a decrease of x in the region of x greater than or equal to 39. The thickness of the intermixing layer falls to zero when x less than or equal to 23.

360-nm Photoluminescence from Silicon Oxide Films Embedded with Silicon Nanocrystals

Si-rich silicon oxide films were deposited by RF magnetron sputtering onto composite Si/SiO2 targets. After annealed at different temperature, the silicon oxide films embedded with silicon nanocrystals were obtained. The photoluminescenee（PL） from the silicon oxide films embedded with silicon nanocrystals was observed at room temperature. The strong peak is at 360 nm, its position is independent of the annealing temperature. The origin of the 360-nm PL in the silicon oxide films embedded with silicon nanoerystals was discussed.