Effects of annealing on properties of spin-valve pinned with FeMn alloy

The magnetic properties of spin-valve pinned by FeMn layer were investigated after it was annealed at different temperatures. Its property was dependent on the vacuum annealing temperature. The pinning field could be increased through annealing at a temporature lower than 200degreesC;the pinning field would reduce and other properties be deteriorated as the annealing temperature was higher than 200degreesC; the pinning effect lost and giantmagnetic resistance disappeared at 300degreesC. Based on the results of AES analysis it was concluded that the diffusion in spin-valve multilayer was along grain boundary.

Strain relaxation of GeSi alloy with low dislocation density grown on low-temperature Si buffers

We have developed a low-temperature (LT) growth technique. Even with Ge fraction x upto 90%, the total thickness of fully relaxed GexSi1-x buffers can he reduced to 1.7 mu m with dislocation density lower than 5 x 10(6) cm(-2). The surface roughness is no more than 6 nm. The strain relaxation is quite inhomogeneous From the beginning. Stacking faults generate and form the mismatch dislocations in the interface of GeSi/LT-Si. (C) 1999 Elsevier Science B.V. All rights reserved.

Laser irradiation cell photothermal therapy assisted by gold nanoparticles

The strong absorption of gold nanoparticles in the visible spectral range allows the localized generation of heat in a volume of only a few tens of nanometer. The efficient conversion of strongly absorbed light by plasmonic gold nanoparticles to heat energy and their easy bioconjugation suggest that the gold nanoparticles can be used as selective photothermal agents in molecular cell targeting. The selective destruction of alkaline phosphatase, the permeabilization of the cell membrane and the selective killing of cells by laser irradiating gold nanoparticles were demonstrated. The potential of using this selective technique in molecularly targeted photothermal therapy and transfection is discussed.

Near-Infrared Femtosecond Laser for Studying the Strain in Si1-xGex Alloy Films via Second-Harmonic Generation

The second-harmonic generation (SHG) from Si1-xGex alloy films has been investigated by near-infrared femtosecond laser. Recognized by s-out polarized SHG intensity versus rotational angle of sample, the crystal symmetry of the fully strained Si0.83Ge0.17 alloy is found changed from the O-h to the C-2 point group due to the inhomogeneity of the strain. Calibrated by double crystal X-ray diffraction, the strain-induced chi((2)) is estimated at 5.7 x 10(-7) esu. According to the analysis on p-in/s-out SHG, the strain-relaxed Si0.10Ge0.90 alloy film is confirmed to be not fully relaxed, and the remaining strain is quantitatively determined to be around 0.1%.

EMPIRICAL PSEUDOPOTENTIAL BAND-STRUCTURE CALCULATION FOR ZN1-XCDXSYSE1-Y QUATERNARY ALLOY

The band structure of the Zn1-xCdxSySe1-y quaternary alloy is calculated using the empirical pseudopotential method and the virtual crystal approximation. The alloy is found to be a direct-gap semiconductor for all x and y composition. Polynomial approximation is obtained for the energy gap as a function of the composition x and y. Electron and hole effective masses are also calculated along various symmetry axes for different compositions and the results agree fairly well with available experimental values.

INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AU AND HYDROGENATED AMORPHOUS SI STUDIED BY XPS AND AES

Interfacial formation processes and reactions between Au and hydrogenated amorphous Si have been studied by photoemission spectroscopy and Auger electron spectroscopy. A three-dimensional growth of Au metal cluster occurs at initial formation of the Au/a-Si:H interface. When Au deposition exceeds a critical time, Au and Si begin interdiffusing and react to create an Au-Si alloy region. Annealing enhances interdiffusion and a Si-rich region exists on the topmost surface of Au films on a-Si:H.

INFLUENCES OF ALLOY DISORDER AND INTERFACE ROUGHNESS ON OPTICAL-SPECTRA OF INGAAS/GAAS STRAINED-LAYER QUANTUM-WELLS

We present studies of alloy composition and layer thickness dependences of excitonic linewidths in InGaAs/GaAs strained-layer quantum wells grown by MBE, using both photoluminescence and optical absorption. It is observed that linewidths of exciton spectra increase with indium content and well size. Using the virtual crystal approximation, the experimental data are analyzed. The results obtained show that the alloy disorder is the dominant mechanism for line broadening at low temperature. In addition, it is found that the absorption spectra related to light hole transitions have varied from a peak to a step-like structure as temperature increases. This behavior can be understood by the indirect space transitions of light holes.

Aggregation and precipitation in high dose as ion implanted Ge0.5Si0.5 alloy

Thermally stimulated redistribution and precipitation of excess arsenic in Ge0.5Si0.5 alloy has been studied by X-ray photoelectron spectroscopy (XPS), cross sectional transmission electron microscopy (XTEM) and X-ray energy disperse spectrometry (EDS). Samples were prepared by the implantation of 6 X 10(6) As+ cm(-2) and 100 keV with subsequent thermal processing at 800 degrees C and 1000 degrees C for 1 h. The XPS depth profiles from the implanted samples before and after the thermal annealing indicate that there is marked redistribution of the elements in heavily arsenic-implanted Ge0.5Si0.5 alloys during the annealing, including: (1) diffusion of As from the implanted region to the surface; (2) aggregation of Ge in the vicinity of the surface. A high density of precipitates was observed near the surface which were by XTEM and EDS identified as an arsenide. It is suggested that most of the implanted As in Ge0.5Si0.5 alloy exists in the form of GeAs.

Growth of 0.55eV-GaInAsSb Quaternary Alloy Films for a Thermophotovoltaic Device by Liquid Phase Epitaxy

Lattice matched Ga_(1-x)In_xAs_ySb_(1-y) quaternary alloy films for thermophotovoltaic cells were successfully grown on n-type GaSb substrates by liquid phase epitaxy. Mirror-like surfaces for the epitaxial layers were achieved and evaluated by atomic force microscopy. The composition of the Ga_(1-x)In_xAs_ySb_(1-y) layer was characterized by energy dispersive X-ray analysis with the result that x = 0.2, y = 0.17. The absorption edges of the Ga_(1-x)In_xAs_ySb_(1-y) films were determined to be 2. 256μm at room temperature by Fourier transform infrared transmission spectrum analysis, corresponding to an energy gap of 0.55eV. Hall measurements show that the highest obtained electron mobility in the undoped p-type samples is 512cm2~/(V·s) and the carrier density is 6. 1×10~(16)cm~(-3) at room temperature. Finally, GaInAsSb based thermophotovoltaic cells in different structures with quantum efficiency values of around 60% were fabricated and the spectrum response characteristics of the cells are discussed.

Resonant Raman Scattering and Photoluminescence Emissions from Above Bandgap Levels in Dilute GaAsN Alloy

The transitions of E0 ,E0 ＋A0, and E＋ in dilute GaAs（1-x） Nx alloys with x = 0.10% ,0.22% ,0.36% ,and 0.62% are observed by micro-photoluminescence. Resonant Raman scattering results further confirm that they are from the intrinsic emissions in the studied dilute GaAsN alloys rather than some localized exciton emissions in the GaAsN alloys. The results show that the nitrogen-induced E E＋ and E0 ＋ A0 transitions in GaAsN alloys intersect at a nitrogen content of about 0.16%. It is demonstrated that a small amount of isoelectronic doping combined with micro-photoluminescence allows direct observation of above band gap transitions that are not usually accessible in photoluminescence.

Metalorganic Chemical Vapor Deposition of GaNAs Alloy Using Dimethylhydrazine as Nitrogen Precursor

GaNAs alloy is grown by metalorganic chemical vapor deposition (MOCVD) using dimethylhydrazine (DMHy) as the nitrogen precursor. High-resolution X-ray diffraction (HRXRD) and secondary ion mass spectrometry (SIMS) are combined in determining the nitrogen contents in the samples. Room temperature photoluminescence (RTPL) measurement is also used in characterizing. The influence of different Ga precursors on GaNAs quality is investigated. Samples grown with triethylgallium (TEGa) have better qualities and less impurity contamination than those with trimethylgallium (TMGa). Nitrogen content of 5.688% is achieved with TEGa. The peak wavelength in RTPL measurement is measured to be 1278.5nm.

Characterization of Ga N_x As_(1 - x) Alloy Grownon Ga As by Molecular Beam Epitaxy

集成光电子学国家重点实验室基金,国家863计划,国家自然科学基金,中科院项目

Effect of rapid thermal annealing on the Raman spectrum of Si0.33Ge0.67/Si (100) alloy

The effect of thermal annealing on the Raman spectrum of Si0.33Ge0.67 alloy grown on Si (100) by molecular beam epitaxy is investigated in the temperature range of 550-800 degrees C. For annealing below 700 degrees C, interdiffusion at the interface is negligible and the residual strain plays the dominant role in the Raman shift. The strain-shift coefficients for Si-Ge and Ge-Ge phonon modes are determined to be 915 +/- 215 cm(-1) and 732 +/- 117 cm(-1), respectively. For higher temperature annealing, interdiffusion is significant and strongly affects the Raman shift and the spectral shape.

Pressure behavior of Te isoelectronic centers in S-rich ZnS1-xTex alloy

The photoluminescence from ZnS1-xTex alloy with 0 < x < 0.3 was investigated under hydrostatic pressure up to 7 GPa. Two peaks were observed in the alloys with x < 0.01, which are related to excitons bound to isolated Te isoelectronic impurities (Te-1 centers) and Te pairs (Te-2 centers), respectively. Only the Te-2 related emissions were observed in the alloys with 0.01 < x < 0.03. The emissions in the alloys with 0.03 < x < 0.3 are attributed to the excitons bound to the Te-n (n greater than or equal to 3) cluster centers. The pressure coefficient of the Te-1 related peak is 89(4) meV/GPa, about 40% larger than that of the band gap of ZnS. On the other hand, the pressure coefficient of the Te-2 related emissions is only 52(4) meV/GPa, about 15% smaller than that of the ZnS band gap. A simple Koster-Slater model has been used to explain the different pressure behavior of the Te-1 and Te-2 centers. The pressure coefficient of the Te-3 centers is 62(2) meV/GPa. Then the pressure coefficients of the Te-n centers decrease rapidly with further increasing Te composition.

Strain relaxation of GeSi alloy with low dislocation density grown on low-temperature Si buffers

We have developed a low-temperature (LT) growth technique. Even with Ge fraction x upto 90%, the total thickness of fully relaxed GexSi1-x buffers can he reduced to 1.7 mu m with dislocation density lower than 5 x 10(6) cm(-2). The surface roughness is no more than 6 nm. The strain relaxation is quite inhomogeneous From the beginning. Stacking faults generate and form the mismatch dislocations in the interface of GeSi/LT-Si. (C) 1999 Elsevier Science B.V. All rights reserved.