Damage on HfO2/SiO2 high-reflecting coatings under single and multiple Nd:YAG laser pulse irradiation

The single- and multi-shot damage behaviors of HfO2/SiO2 high-reflecting (HR) coatings under Nd:YAG laser exposure were investigated. Fundamental aspects of multi-shot laser damage, such as the instability due to pulse-to-pulse accumulation of absorption defect and structural defect effect, and the mechanism of laser induced defect generation, are considered. It was found in multi-shot damage, the main factors influencing laser-induced damage threshold (LIDT) are accumulation of irreversible changes of structural defects and thermal stress that induced by thermal density fluctuations.

不同沉积参量下ZrO_2薄膜的微结构和激光损伤阈值

ZrO2采用X射线衍射(XRD)技术分析了不同充氧条件和沉积温度对ZrO2溥膜组成结构的影响，并对不同工艺下制备的薄膜的表面粗糙度和激光损伤阈值进行了测量。结果发现随着氧压的升高，ZrO2溥膜将由单斜相多晶态逐渐转变为非晶态结构，而随着基片温度的增加，溥膜将由非晶态逐渐转变为单斜相多晶态。同时发现随着氧压升高晶粒尺寸减小，而随着沉积温度增加，晶粒尺寸增大。氧压增加时工艺对表面粗糙度有一定程度的改善，而沉积温度升高，工艺对表面粗糙度的改善不明显。晶粒尺寸大小变化与表面粗糙度变化存在对应关系。激光损伤测量表明

脉冲激光辐照光学薄膜的缺陷损伤模型

建立了缺陷吸收升温致薄膜激光损伤模型，该模型从热传导方程出发，考虑了缺陷内部的温度分布以及向薄膜的传导过程，通过引入散射系数简化了Mie散射理论得出的吸收截面．对电子束蒸发沉积的ZrO2：Y2O3单层膜进行了激光破坏实验，薄膜样品的损伤是缺陷引起的，通过辉光放电质谱法对薄膜制备材料的纯度分析发现材料中的主要杂质元素为铂，其含量为0．9％．利用缺陷损伤模型对损伤过程进行了模拟，理论模型和实验结果取得了较好的一致性．

ZrO2／SiO2棱镜偏振膜的膜系优化设计与制备

对以K9玻璃为基底，采用ZrO2和SiO2为高低膜料来制备棱镜偏振膜，并进行膜系优化设计。设计指标为：波长540nm处满足Tp>99％，Ts<1％。优化结果表明，膜系以H3L(HL)^13 H3LH为最佳膜系。测试结果表明，此膜系完全满足设计指标，偏振性能优良。探讨了参考波长对偏振膜工作带宽的影响。

LBO晶体上ZrO2薄膜的显微结构和光学性质

用电子柬蒸发方法在三种不同取向的三硼酸锂（LiB3O3，简称LBO）晶体上沉积了ZrO2薄膜。采用分光光度计和X射线衍射技术对LBO晶体基底结构对薄膜光学性质和显微结构的影响进行了研究。实验结果表明：基底结构对薄膜的显微结构和光学性质具有明显影响，即X-LBO，Y-LBO和Z-LBO上沉积的ZrO3薄膜分别沿m（-212），m（021）和o（130）择优生长，且m（021）择优取向的ZrO3薄膜具有最高的折射率和最小的晶格不匹配。

Graded index 532HR/1064HT filter by glancing angle deposition

Glancing angle deposition is a novel method to prepare graded index coatings. By using this method and physical vapour deposition, ZrO2 is used to engineer graded index filter on BK7 glass substrate. Controlling the deposition rate and the periodic oscillation of oblique angle of deposited material, a 10-period graded index ZrO2 filter with high reflection near 532 nm and high transmittance at wavelength 1064 nm is fabricated. The causes of difference between the theoretical and experimental results are discussed in detail. The material properties and electron gun nonlinearity are possibly the main origins of the difference, which result in the variations in both thickness control and deposition rate of the Elm material.

Effect of process parameters on laser damage threshold of TiO2 coatings

We investigate the laser damage behaviour of an electron-beam-deposited TiO2 monolayer at different process parameters. The optical properties, chemical composition, surface defects, absorption and laser-induced damage threshold (LIDT) of Elms are measured. It is found that TiO2 Elms with the minimum absorption and the highest LIDT can be fabricated using a TiO2 starting material after annealing. LIDT is mainly related to absorption and is influenced by the non-stoichiometric defects for TiO2 films. Surface defects show no evident effects on LIDT in this experiment.

Influence of vacuum organic contaminations on laser-induced damage of 1064 nm anti-reflective coatings

We investigate the influence of vacuum organic contaminations on laser-induced damage threshold (LIDT) of optical coatings. Anti-reflective (AR) coatings at 1064 nm made by Ta2O5/SiO2 are deposited by the ion beam sputtering method. The LIDTs of AR coatings are measured in vacuum and in atmosphere, respectively. It is exhibited that contaminations in vacuum are easily to be absorbed onto optical surface because of lower pressure, and they become origins of damage, resulting in the decrease of LIDT from 24.5 J/cm(2) in air to 15.7 J/cm(2) in vacuum. The LIDT of coatings in vacuum has is slightly changed compared with the value in atmosphere after the organic contaminations are wiped off. These results indicate that organic contaminations are the main reason of the LIDT decrease in vacuum. Additionally, damage morphologies have distinct changes from vacuum to atmosphere because of the differences between the residual stress and thermal decomposability of filmy materials.

Effect of SiO2 protective layer on the femtosecond laser-induced damage of HfO2/SiO2 multilayer high-reflective coatings

Two kinds of HfO2/SiO2 800 nm high-reflective (HR) coatings, with and without SiO2 protective layer were deposited by electron beam evaporation. Laser-induced damage thresholds (LIDT) were measured for all samples with femtosecond laser pulses. The surface morphologies and the depth information of all samples were observed by Leica optical microscopy and WYKO surface profiler, respectively. It is found that SiO2 protective layer had no positive effect on improving the LIDT of HR coating. A simple model including the conduction band electron production via multiphoton ionization and impact ionization is used to explain this phenomenon. Theoretical calculations show that the damage occurs first in the SiO2 protective layer for HfO2/SiO2 HR coating with SiO2 protective layer. The relation of LIDT for two kinds of HfO2/SiO2 HR coatings in calculation agrees with the experiment result. (c) 2006 Elsevier B.V. All rights reserved.

Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

Influences of oxygen partial pressure on structure and related properties of ZrO2 thin films prepared by electron beam evaporation deposition

ZrO2 thin films were prepared by electron beam evaporation at different oxygen partial pressures. The influences of oxygen partial pressure on structure and related properties of ZrO2 thin films were studied. Transmittance, thermal absorption, structure and residual stress of ZrO2 thin films were measured by spectrophotometer, surface thermal lensing technique (STL), X-ray diffraction and optical interferometer, respectively. The results showed that the structure and related properties varied progressively with the increase of oxygen partial pressure. The refractive indices and the packing densities of the thin films decreased when the oxygen partial pressure increased. The tetragonal phase fraction in the thin films decreased gradually as oxygen partial pressure increased. The residual stress of film deposited at base pressure was high compressive stress, the value decreased with the increase of oxygen partial pressure, and the residual stress became tensile with the further increase of oxygen pressure, which was corresponding to the evolution of packing densities and variation of interplanar distances. (c) 2007 Elsevier B.V. All rights reserved.

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.

LBO晶体上1064，532nm倍频增透膜的镀制及性能分析

用电子束蒸发沉积方法在X切LBO（X-LBO）晶体上镀制了两种不同膜系结构的1064和532nm倍频增透膜，其中一种膜系结构为基底／ZrO2／Y2O3／A12O3／SiO2／空气，另一种为基底／0．5Al2O3／ZrO2／Y2O3／A12O3／SiO2／空气，两种膜系结构的主要差别在于有无氧化铝过渡层。测量了薄膜的反射率光谱曲线，发现两种增透膜在1064和532nm处的反射率均小于0．5％，实际镀制结果与理论设计曲线的差异主要是由材料折射率的变化引起的。且对样品在空气环境中进行了温度为473K的退火处理，