Annealing ambient controlled deep defect formation in InP

Deep defects in annealed InP have been investigated by deep level transient capacitance spectroscopy (DLTS), photo induced current transient spectroscopy (PICTS) and thermally stimulated current spectroscopy (TSC). Both DLTS results of annealed semiconducting InP and PICTS and TSC results of annealed semi-insulating InP indicate that InP annealed in phosphorus ambient has five defects, while lid? annealed in iron phospbide ambient has two defects. Such a defect formation phenomenon is explained in terms of defect suppression by the iron atom diffusion process. The correlation of the defects and the nature of the defects in annealed InP are discussed based on the results.

On the nature of iron in InP: A FTIR study

Fe is still the commonly used dopant to fabricate semi-insulating(SI) InP, a key material for high-speed electronic and optoelectronic devices. High resolved absorption spectra of the internal d-d shell transitions at Fe2+ in InP and the related phonon sidebands and a series of iron related absorption Lines are presented. Detailed infrared absorption study of the characteristic spectra of four zero-phonon lines(ZPLs), which are attributed to transitions within the 5D ground state of Fe2+ (3d(6)) on the indium site in a tetrahedral crystal field of phosphorus atoms and their temperature effects are given.

Dynamics of formation of defects in annealed InP

Dynamics of formation of defects in the annealed nominally undoped semi-insulating InP obtained by high pressure, high temperature annealing of high purity materials is proposed. Incorporated hydrogen passivates vacancy at indium site from annihilation forming fully hydrogenated indium vacancy which dissociates leaving large lattice relaxation behind, deep donors, mainly larger complexes involving phosphorus at indium site and isolated hydrogen defects are created in nominally undoped InP after annealing. Also created are acceptor levels such as vacancy at indium site. Carrier charge compensation mechanism in nominally undoped InP upon annealing at high temperature is given. Microscopic models of hydrogen related defects are given. Structural, electronic and vibrational properties of LVMs related to hydrogen as well as their temperature effect are discussed.

Formation mechanism of defects in annealed InP

Dynamical formation mechanism of defects in the annealed nominally undoped semi-insulating InP obtained by high pressure, high temperature annealing of high purity materials is proposed. Local vibrational modes in tenths of InP samples reveal clearly existence of complexes related to hydrogen. Complexes of vacancy at indium site with one to four hydrogen atoms and isolated hydrogen or hydrogen dimers, complexes of hydrogen with various impurities are investigated by FTIR. Hydrogen can acts as an actuator for generation of antistructure defects. Fully hydrogenated indium vacancy dissociates leaving large lattice relaxation behind, deep donors, mainly larger complexes involving phosphorus at indium site and isolated hydrogen defects are created in nominally undoped InP after annealing. Also created are acceptor levels such as vacancy at indium site. Carrier charge compensation mechanism in nominally undoped InP upon annealing at high temperature is given. Microscopic models of hydrogen related defects are given. Structural, electronic and vibrational properties of LVMs related to hydrogen as well as their temperature effect are discussed.

Space grown semi-insulating gallium arsenide single crystal and its application

Low noise field effect transistors and analogue switch integrated circuits (ICs) have been fabricated in semi-insulating gallium arsenide (SI-GaAs) wafers grown in space by direct ion-implantation. The electrical behaviors of the devices and the ICs have surpassed those fabricated in the terrestrially grown SI-GaAs wafers. The highest gain and the lowest noise of the transistors made from space-grown SI-GaAs wafers are 22.8 dB and 0.78 dB, respectively. The threshold back-gating voltage of the ICs made from space-grown SI-GaAs wafers is better than 8.5 V The con-elation between the characterizations of materials and devices is studied systematically. (C) 2002 COSPAR. Published by Elsevier Science Ltd. All rights reserved.

Semi-insulating GaAs grown in outer space

A semi-insulating GaAs single crystal ingot was grown in a recoverable satellite, within a specially designed pyrolytic boron nitride crucible, in a power-traveling furnace under microgravity. The characteristics of a compound semiconductor single crystal depends fundamentally on its stoichiometry, i.e. the ration of two types of atoms in the crystal. a practical technique for nondestructive and quantitative measuring stoichiometry in GaAs single crystal was used to analyze the space-grown GaAs single crystal. The distribution of stoichiometry in a GaAs wafer was measured for the first time. The electrical, optical and structural properties of the space-grown GaAs crystal were studied systematically, Device fabricating experiments prove that the quality of field effect transistors fabricated from direct ion-implantation in semi-insulating GaAs wafers has a close correlation with the crystal's stoichiometry. (C) 2000 Elsevier Science S.A. All rights reserved.

PHOTOINDUCED CHANGES OF HYDROGEN-BONDING IN SEMIINSULATING IRON-DOPED INDIUM-PHOSPHIDE

After illumination with 1-1.3 eV photons during cooling-down, metastable PH modes are observed by IR absorption at 5 K in semi-insulating InP:Fe. They correlate with the photo-injection of holes, but not with a change of the charge state of the K-related centres present at equilibrium. They are explained by a change of the bonding of H, induced by hole trapping, from IR-inactive centres to PH-containing centres, stable only below 80 K. One metastable centre has well-defined geometrical parameters and the other one could be located in a region near from the interface with (Fe,P) precipitates.

Annihilation of deep level defects in InP through high temperature annealing

Deep level transient spectroscopy (DLTS) and thermally stimulated current spectroscopy (TSC) have been used to investigate defects in semi-conducting and semi-insulating (SI) InP after high temperature annealing, respectively. The results indicate that the annealing in iron phosphide ambient has an obvious suppression effect of deep defects, when compared with the annealing in phosphorus ambient. A defect annihilation phenomenon has also been observed in Fe-doped SI-InP materials after annealing. Mechanism of defect formation and annihilation related to in-diffusion of iron and phosphorus is discussed. Nature of the thermally induced defects has been discussed based on the results. (c) 2007 Elsevier Ltd. All rights reserved.

Microdefects and electrical uniformity of InP annealed in phosphorus and iron phosphide ambiances

Microdefects originating from impurity-dislocation interactions in undoped InP that had been annealed in phosphorus and iron phosphide ambiances have been studied using optical microscopy. The electrical uniformity of the annealed wafer is improved by removing impurity aggregation around dislocations and by eliminating impurity striations in the annealing process. Compared to as-grown Fe-doped semi-insulating (SI) material, SI wafers obtained by annealing undoped InP in iron phosphide ambiances have better uniformity. This is attributed to the avoidance of Fe aggregation around dislocations and dislocation clusters, Fe precipitation and impurity striations, and is related to the use of a low concentration of Fe in the annealed material. The influence of Fe diffusion on the migration of dislocations in the annealing process has been studied and reviewed. (C) 2003 Elsevier B.V. All rights reserved.

Effects of annealing ambient on the formation of compensation defects in InP

Positron annihilation lifetime (PAL) and photoinduced current transient spectroscopies (PICTS) have been employed to study the formation of compensation defects in undoped InP under different annealing processes with pure phosphorus (PP) ambience and iron phosphide (IP) ambience, respectively. The different annealing ambiences convert the as-grown n-type undoped InP into two types of semi-insulating (SI) states. The positron average lifetimes of as-grown InP, PP SI-InP, and IP SI-InP are found to be 246, 251, and 243 ps, respectively, which are all longer than the bulk lifetime of 240 ps, indicating the existence of vacancy-type positron-trapping defects. For as-grown InP, VInH4 complexes are the dominant defects. They dissociate into VInHn(0less than or equal tonless than or equal to3) acceptor vacancies under PP ambience annealing, compensating the residual shallow donors and turning the material semi-insulating. In forming IP SI-InP, diffusion of iron into V-In complexes under IP ambience annealing produces the substitutional compensation defect Fe-In, causing a shorter positron average lifetime. The PICTS measurements show that a group of vacancy-type defects has been suppressed by iron diffusion during the annealing process, which is in good agreement with the PAL results. (C) 2003 American Institute of Physics.

Fe-diffusion-induced defects in InP annealed in iron phosphide ambient

Photoluminescence (PL) and photo induced current transient spectroscopy (PICTS) have been used to study deep levels in semi-insulating (SI) InP prepared by annealing undoped InP in pure phosphorus (PP) and iron phosphide (IP) ambient. Defects are much fewer in IP SI-InP than in PP SI-InP. Deep-level-related PL emission could only be detected in IP SI-InP. The results indicate that Fe diffusion inhibits the thermal formation of a number of defects in annealed InP. A complex defect has been formed in the annealing process in the presence of Fe.

Creation and suppression of point defects through a kick-out substitution process of Fe in InP

Indium antisite defect In-P-related photoluminescence has been observed in Fe-diffused semi-insulating (SI) InP. Compared to annealed undoped or Fe-predoped SI InP, there are fewer defects in SI InP obtained by long-duration, high-temperature Fe diffusion. The suppression of the formation of point defects in Fe-diffused SI InP can be explained in terms of the complete occupation by Fe at indium vacancy. The In-P defect is enhanced by the indium interstitial that is caused by the kick out of In and the substitution at the indium site of Fe in the diffusion process. Through these Fe-diffusion results, the nature of the defects in annealed undoped SI InP is better understood. (C) 2002 American Institute of Physics.

Positron-annihilation study of compensation defects in InP

Positron-annihilation lifetime and positron-annihilation Doppler-broadening (PADB) spectroscopies have been employed to investigate the formation of vacancy-type compensation defects in n-type undoped liquid encapsulated Czochrolski grown InP, which undergoes conduction-type conversions under high temperature annealing. N-type InP becomes p-type semiconducting by short time annealing at 700 degreesC, and then turns into n-type again after further annealing but with a much higher resistivity. Long time annealing at 950 degreesC makes the material semi-insulating. Positron lifetime measurements show that the positron average lifetime tau(av) increases from 245 ps to a higher value of 247 ps for the first n-type to p-type conversion and decreases to 240 ps for the ensuing p-type to n-type conversion. The value of tau(av) increases slightly to 242 ps upon further annealing and attains a value of 250 ps under 90 h annealing at 950 degreesC. These results together with those of PADB measurements are explained by the model proposed in our previous study. The correlation between the characteristics of positron annihilation and the conversions of conduction type indicates that the formation of vacancy-type defects and the progressive variation of their concentrations during annealing are related to the electrical properties of the bulk InP material. (C) 2002 American Institute of Physics.

High-speed and high-power 1.3 mu m InGaAsP/InP selective proton-bombarded buried crescent lasers with optical field attenuation regions

High-speed and high-power InGaAsP/lnP selective proton-bombarded buried crescent (SPB-BC) lasers with optical field attenuation regions were reported. The defect of proton bombardment can not affect the lifetime of the SPB-BC laser because the optical field attenuation region obstructs the growth and propagation of defects. A CW light output over 115 mW was achieved at room temperature using a 500 mu m long cavity SPB-BC laser. The 3 dB bandwidth was 8.5 GHz, and the lifetime was about 8.5 x 10(5) h. The capacitance of four kinds of current blocking structures was first measured in our experiment, and the results shown that the capacitance of proton-bombarded pnpn structure was not only less than that of pnpn current blocking structure, but also less than that of semi-insulating Fe-InP structure.

InP-base resonant tunneling diodes

We have fabricated In_0.53Ga_0.47As/AlAs/InP resonant tunneling diodes (RTDs) based on the air-bridge technology by using electron beam lithography processing.The epitaxial layers of the RTD were grown on semi-insulating (100) InP substrates by molecular beam epitaxy.RTDs with a peak current density of 24.6 kA/cm~2 and a peak-to-valley current ratio of 8.6 at room temperature have been demonstrated.