Low threshold lasing of GaN-based vertical cavity surface emitting lasers with an asymmetric coupled quantum well active region

We have fabricated and characterized GaN-based vertical cavity surface emitting lasers (VCSELs) with a unique active region structure, in which three sets of InGaN asymmetric coupled quantum wells are placed in a half-wavelength (0.5 lambda) length. Lasing action was achieved under optical pumping at room temperature with a threshold pumping energy density of about 6.5 mJ/cm(2). The laser emitted a blue light at 449.5 nm with a narrow linewidth below 0.1 nm and had a high spontaneous emission factor of about 3.0x10(-2). The results indicate that this active region structure is useful in reducing the process difficulties and improving the threshold characteristics of GaN-based VCSELs.

Synthesis of MDMO-PPV capped PbS quantum dots and their application to solar cells

Poly[2-methoxy-5-(3',7'-dimethyloctyloxy)-1,4-phenylenevinylene] (MDMO-PPV) capped PbS quantum dots about 3-6 nm in diameter were synthesized with a novel method. Unlike the synthesis of oleic acid capped PbS quantum dots, the reactions were carried out in solution at room temperature, with the presence of a capping ligand species, MDMO-PPV. The quantum dots were used to fabricate bulk heterojunction solar cells with an indium tin oxide (ITO)/polyethylenedioxythiophene/polystyrenesulphonate (PEDOT: PSS)/MDMO-PPV: PbS/Al structure. Current density-voltage characterization of the devices showed that after the addition of the MDMO-PPV capped PbS quantum dots to MDMO-PPV film, the performance was dramatically improved compared with pristine MDMO-PPV solar cells. (C) 2008 Elsevier Ltd. All rights reserved.

Spin states in semiconductor quantum dot with a single magnetic ion

We investigate theoretically CdTe quantum dots containing a single Mn2+ impurity, including the sp-d exchange interaction between carriers and the magnetic ion and the short-range exchange interaction between electron and hole. We find anticrossing behaviors in the energy spectrum of the electron-hole (e-h) pair that arise from the interplay between exchange interactions and the magnetic field. In addition to the s-d exchange interaction, we find that other mechanisms inducing the anticrossings become important in the strong heavy hole-light hole (hh-lh) mixing regime. The transition strengths between the states with spin projection of Mn2+ ion S-z not equal -5/2 (S-z = -5/2) decrease (increase) with increasing magnetic fields due to the alignment of the Mn2+ spin. The spin splitting of the e-h pair states depends sensitively on the external magnetic and electric field, which reveals useful information about the spin orientation and position of the magnetic ion. Meanwhile, the manipulation of the position of the magnetic ion offers us a way to control the spin splitting of the carriers. (C) 2008 Elsevier B.V. All rights reserved.

Single-photon emission at liquid nitrogen temperature from a single InAs/GaAs quantum dot

We report on the single photon emission from single InAs/GaAs self-assembled Stranski-Krastanow quantum dots up to 80K under pulsed and continuous wave excitations. At temperature 80 K, the second-order correlation function at zero time delay, g((2))(0), is measured to be 0.422 for pulsed excitation. At the same temperature under continuous wave excitation, the photon antibunching effect is observed. Thus, our experimental results demonstrate a promising potential application of self-assembled InAs/GaAs quantum dots in single photon emission at liquid nitrogen temperature.

Small SiGe quantum dots obtained by excimer laser annealing

In this paper, we obtain SiGe quantum dots with the diameters and density of 15-20 nm and 1.8 x 10(11) cm(-2), respectively, by 193 nm excimer laser annealing of Si0.77Ge0.23 strained films. Under the excimer laser annealing, only surface atoms diffusion happens. From the detailed statistical information about the size and shape of the quantum dots with different annealing time, it is shown that the as-grown self-assembled quantum dots, especially the {105}-faceted dots, are not stable and disappear before the appearance of the laser-induced quantum dots. Based on the calculation of surface energy and surface chemical potential, we show that the {103}-faceted as-grown self-assembled quantum dots are more heavily strained than the {105}-faceted ones, and the heavy strain in the dot can decrease the surface energy of the dot facets. The formation of the laser-induced quantum dots, which is also with heavy strain, is attributed to kinetic constraint. (c) 2008 Elsevier B.V. All rights reserved.

Electronic states of InAs/GaAs tyre-shape quantum ring

In the framework of the effective mass theory, this paper calculates the electron energy levels of an InAs/GaAs tyre-shape quantum ring (TSQR) by using the plane wave basis. The results show that the electron energy levels are sensitively dependent on the TSQR's section thickness d, and insensitively dependent on TSQR's section inner radius R-1 and TSQR's inner radius R-2. The model and results provide useful information for the design and fabrication of InAs/GaAs TSQRs.

Optical study of lateral carrier transfer in (In,Ga)As/GaAs quantum-dot chains

We have studied the lateral carrier transfer in a specially designed quantum dot chain structure by means of time-resolved photoluminescence (PL) and polarization PL. The PL decay time increases with temperature, following the T-1/2 law for the typical one-dimensional quantum system. The decay time depends strongly on the emission energy: it decreases as the photon energy increases. Moreover, a strong polarization anisotropy is observed. These results are attributed to the efficient lateral transfer of carriers along the chain direction. (c) 2008 American Institute of Physics.

Investigation of filling factor in In0.53Ga0.47As/In0.52Al0.48As quantum wells with two occupied subbands

The magnetic field dependence of filling factors has been investigated on InP based In-0.53 Ga0.47As/In-0.52 Al-0.48 As quantum well samples with two occupied subbands by means of magnetotransport measurements at the temperature of 1.5 K in a magnetic field range of 0 to 13 T. Under the condiction that Laundau-level broadening is larger than the spin splitting of each subband, filling factors are even when the splitting energy of two subbands is an integer multiple of the cyclotron energy, i. e. Delta E-21 = khw(c). If the splitting energy of two subbands is half of an odd interger multiple of the cyclotron erergy, i. e. Delta E-21 = (2 k + 1) hw(c) /2, the filling factor is odd.

Fabrication and excitation-power-density-dependent micro-photoluminescence of hexagonal nanopillars with a single InGaAs/GaAs quantum well

Hexagonal nanopillars with a single InGaAs/GaAs quantum well (QW) were fabricated on a GaAs (111) B substrate by selective-area metal-organic vapor phase epitaxy. The standard deviations in diameter and height of the nanopillars are about 2% and 5%, respectively. Zincblende structure and rotation twins were identified in both the GaAs and the InGaAs layers by electron diffraction. The excitation-power-density-dependent micro-photoluminescence (mu-PL) of the nanopillars was measured at 4.2, 50, 100 and 150 K. It was shown that, with increasing excitation power density, the mu-PL peak's positions shift to a higher energy, and their intensity and width increase, which were rationalized using a model that includes the effects of piezoelectricity, photon-screening and band-filling. It was also revealed that the rotation twins significantly reduce the diffusion length of the carriers in the nanopillars, compared to that in the regular semiconductors.

Quantum teleportation via a two-qubit Heisenberg XXZ chain - effects of anisotropy and magnetic field

We study quantum teleportation via a two-qubit Heisenberg XXZ, chain under an inhomogeneous magnetic field. We first consider entanglement teleportation, and then focus on the teleportation fidelity under different conditions. The effects of anisotropy and the magnetic field, both uniform and inhomogeneous, are discussed. We also find that, though entanglement teleportation does require an entangled quantum channel, a nonzero critical value of minimum entanglement is not always necessary.

Low threshold current density 1.3 mu m metamorphic InGaAs/GaAs quantum well laser diodes

Very low threshold current density InGaAs/ GaAs quantum well laser diodes grown by molecular beam epitaxy on InGaAs metamorphic buffers are reported. The lasing wavelength of the ridge waveguide laser diode with cavity length of 1200 mm is centred at 1337.2 nm; the threshold current density is 205 A/cm(2) at room temperature under continuous-wave operation.

Continuous-wave operation of GaN based multi-quantum-well laser diode at room temperature

Room-temperature operation of cw GaN based multi-quantum-well laser diodes (LDs) is demonstrated. The LD structure is grown on a sapphire (0001) substrate by metalorganic chemical vapour deposition. A 2.5 mu m x 800 mu m ridge waveguide structure is fabricated. The electrical and optical characteristics of the laser diode under direct current injection at room temperature are investigated. The threshold current and voltage of the LD under cw operation are 110mA and 10.5V, respectively. Thermal induced series resistance decrease and emission wavelength red-shift are observed as the injection current is increased. The full width at half maximum for the parallel and perpendicular far field pattern (FFP) are 12 degrees and 32 degrees, respectively.

High-density and narrow size-distribution InAs quantum dots formed by a modified two-step growth

We develop a modified two-step method of growing high-density and narrow size-distribution InAs/GaAs quantum dots (QDs) by molecular beam epitaxy. In the first step, high-density small InAs QDs are formed by optimizing the continuous deposition amount. In the second step, deposition is carried out with a long growth interruption for every 0.1 InAs monolayer. Atomic force microscope images show that the high-density (similar to 5.9x 10(10) CM-2) good size-uniformity InAs QDs are achieved. The strong intensity and narrow linewidth (27.7 meV) of the photoluminescence spectrum show that the QDs grown in this two-step method have a good optical quality.

Electronic structure in GaAs/AlxGa1-xAs spherical quantum dots

In this paper, how the dots' radius, At concentration and external electric field affect the single electron energy states in GaAs/AlxGa1-xAs spherical quantum dots are discussed in detail. Furthermore, the modification of the energy states is calculated when the difference in effective electron mass in GaAs and AlxGa1-xAs are considered. In addition, both the analytical method and the plane wave method are used in calculation and the results are compared, showing that they are in good agreement with each other. The results and methods can provide useful information for the future research and potential applications of quantum dots.

Single-photon emission from a single InAs quantum dot

Excitation power-dependent micro-photoluminescence spectra and photon-correlation measurement are used to study the optical properties and photon statistics of single InAs quantum dots. Exciton and biexciton emissions, whose photoluminescence intensities have linear and quadratic excitation power dependences, respectively, are identified. Under pulsed laser excitation, the zero time delay peak of second order correlation function corresponding to exciton emission is well suppressed, which is a clear evidence of single photon emission.