Native deep level defects in ZnO single crystal grown by CVT method - art. no. 68410I

Hall effect, photoluminescence (PL), infrared absorption, deep level transient spectroscopy (DLTS), and Raman scattering have been used to study property and defects of ZnO single crystal grown by a chemical vapor transport method (CVT). As-grown ZnO is N type with free electron density Of 10(16)-10(17)cm(-3). It has a slight increase after 900 degrees C annealing in oxygen ambient. The DLTS measurement revealed four deep level defects with energy at 0.30eV, 0.50eV, 0.68eV and 0.90eV in the as-grown ZnO sample, respectively. After the high temperature annealing, only the 0.5eV defect survive and has a concentration increase. PL results of the as-grown and annealed ZnO indicate that the well-known green emission disappear after the annealing. The result suggests a correlation between the 0.68eV defect and the green PL peak. Results of P-doped ZnO were also compared with the undoped ZnO sample. The nature of the defects and their influence on the material property have been discussed.

Recent research results on deep level defects in semi-insulating InP - Application to improve material quality

An apparent defect suppression effect has been observed in InP through an investigation of deep level defects in different semi-insulating (SI) InP materials. Quality improvement of SI-InP based on the defect suppression mechanism is presented.

Deep levels in high resistivity GaN epilayers grown by MOCVD

Undoped high resistivity (HR) GaN epilayers were grown on (0001) sapphire substrate by metalorganic chemical vapor deposition (MOCVD). Thermally stimulated current (TSC) and resistivity measurements have been carried out to investigate deep level traps. Deep levels with activation energies of 1.06eV and 0.85eV were measured in sample 1. Gaussian fitting of TSC spectra showed five deep levels in different samples. (c) 2006 WILEY VCH Vertag GmbH & Co. KGaA, Weinheim

DETERMINATION OF THE SUBBAND ENERGY IN THE V-SHAPED POTENTIAL WELL OF DELTA-DOPED GAAS BY DEEP-LEVEL TRANSIENT SPECTROSCOPY

Using deep level transient spectroscopy (DLTS) the conduction-subband energy levels in a V-shaped potential well induced by Si-delta doping in GaAs were determined. Self-consistent calculation gives four subbands in the well below the Fermi level. Experimentally, two DLTS peaks due to electron emission from these subbands were observed. Another two subbands with low electron concentration are believed to be merged into the adjacent DLTS peak. A good agreement between self-consistent calculation and experiment was obtained. (C) 1994 American Institute of Physics.

CHARACTERIZATION OF HIGH FLUENCE NEUTRON-INDUCED DEFECT LEVELS IN HIGH-RESISTIVITY SILICON DETECTORS USING A LASER DEEP-LEVEL TRANSIENT SPECTROSCOPY (L-DLTS)

Neutron irradiated high resistivity (4-6 kOMEGA-cm) silicon detectors in the neutron fluence (PHI(n)) range of 5 X 10(11) n/cm2 to 1 X 10(14) n/cm2 have been studied using a laser deep level transient spectroscopy (L-DLTS). It has been found that the A-center (oxygen-vacancy, E(c) = 0.17 eV) concentration increases with neutron fluence, reaching a maximum at PHI(n) almost-equal-to 5 X 10(12) n/cm2 before decreasing with PHI(n). A broad peak has been found between 200 K and 300 K, which is the result of the overlap of three single levels: the V-V- (E(c) = 0.38 eV), the E-center (P-V, E(c) = 0.44 eV), and a level at E(c) = 0.56 eV that is probably V-V0. At low neutron fluences (PHI(n) < 5 X 10(12) n/cm2), this broad peak is dominated by V-V- and the E-centers. However, as the fluence increases (PHI(n) greater-than-or-equal-to 5 X 10(12) n/cm2), the peak becomes dominated by the level of E(c) = 0.56 eV.

THEORETICAL CALCULATION FOR SHUBNIKOV-DEHAAS OSCILLATIONS IN DEEP MESA STRUCTURES

We have used the rectangular confinement potential to describe Shubnikov-deHaas oscillations produced by one-dimensional electrons confined in deep mesa structures. The edge distortion of the confinement potential caused by electrostatic image forces is taken into account. The model contains no fitting parameters and relates well with experimental data. The comparison with earlier reported parabolic model is presented,

EFFECTS OF DEEP CENTERS AT PT SI INTERFACES AND HYDROGENATION

Electrical measurements were combined with surface techniques to study the Pt/Si interfaces at various silicide formation temperatures. Effects of deep centers on the Schottky barrier heights were studied. Hydrogen plasma treatment was used to passivate the impurity/defect centers at the interfaces, and the effects of hydrogenation on the Schottky barrier heights were also examined. Combining our previous study on the Pt/Si interfacial reaction, factors influencing the PtSi/Si Schottky barrier diode are discussed.