Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Effect of gamma-irradiation on spectral properties of undoped Y2SiO5 crystals

The absorption spectra of undoped Y2SiO5 crystals were studied before and after gamma-irradiation. After gamma-irradiation, the additional absorption peaks at 260-270 and 320nm were observed in as-grown and H,annealed Y2SiO5 crystal, but it did not occur in air-annealed Y2SiO5 crystal. These absorption peaks were attributed to F color centers and O- hole centers, respectively. Owing to more oxygen vacancies and color centers in H-2-annealed Y2SiO5 crystal than that in as-grown Y2SiO5 crystal after gamma-irradiation, the additional absorption peaks were more intense in the former than that in the latter. With the irradiation dose increasing from 20 to 220kGy, the intensity of additional absorption peaks increased.

Effect of process parameters on laser damage threshold of TiO2 coatings

We investigate the laser damage behaviour of an electron-beam-deposited TiO2 monolayer at different process parameters. The optical properties, chemical composition, surface defects, absorption and laser-induced damage threshold (LIDT) of Elms are measured. It is found that TiO2 Elms with the minimum absorption and the highest LIDT can be fabricated using a TiO2 starting material after annealing. LIDT is mainly related to absorption and is influenced by the non-stoichiometric defects for TiO2 films. Surface defects show no evident effects on LIDT in this experiment.