Optical and structural properties of ZnO films grown on Si(100) substrates by MOCVD - art. no. 60290G

High quality ZnO films have been successfully grown on Si(100) substrates by Metal-organic chemical vapor deposition (MOCVD) technique. The optimization of growth conditions (II-VI ratio, growth temperature, etc) and the effects of film thickness and thermal treatment on ZnO films' crystal quality, surface morphology and optical properties were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), and photoluminescence (PL) spectrum, respectively. The XRD patterns of the films grown at the optimized temperature (300 degrees C) show only a sharp peak at about 34.4 degrees corresponding to the (0002) peak of hexagonal ZnO, and the FWHM was lower than 0.4 degrees. We find that under the optimized growth conditions, the increase of the ZnO films' thickness cannot improve their structural and optical properties. We suggest that if the film's thickness exceeds an optimum value, the crystal quality will be degraded due to the large differences of lattice constant and thermal expansion coefficient between Si and ZnO. In PL analysis, samples all displayed only ultraviolet emission peaks and no observable deep-level emission, which indicated high-quality ZnO films obtained. Thermal treatments were performed in oxygen and nitrogen atmosphere, respectively. Through the analysis of PL spectra, we found that ZnO films annealing in oxygen have the strongest intensity and the low FWHM of 10.44 nm(106 meV) which is smaller than other reported values on ZnO films grown by MOCVD.

PASSIVATION OF THE INP(100) SURFACE USING (NH4)(2)S-X

InP(100) surface treated with (NH4)(2)S-x has been investigated by using photoluminescence(PL), Auger electron spectroscopy and X-ray photoelectron spectroscopy. It is found that PL intensity increased by a factor of 3.3 after (NH4)(2)S-x passivation and the sulfur remained on the surface only bonded to indium, not to phosphorus. This suggests that the sulfur atoms replace the phosphorus atoms on the surface and occupy the phosphorus vacancies.

Growth of Space Ordered on GaAs（100） Vicinal 1.3μm InAs Quantum Dots Substrates by MOCVD

Space ordered 1.3μm self-assembled InAs QDs are grown on GaAs（100） vicinal substrates by MOCVD. Photoluminescence measurements show that the dots on vicinal substrates have a much higher PL intensity and a narrower FWHM than those of dots on exact substrates, which indicates better material quality. To obtain 1.3μm emissions of InAs QDs, the role of the so called InGaAs strain cap layer （SCL） and the strain buffer layer （SBL） in the strain relaxation process in quantum dots is studied. While the use of SBL results only in a small change of emission wavelength,SCL can extend the QD＇s emission over 1.3μm due to the effective strain reducing effect of SCL.

立方相 Al_xGa_(1-x)N/GaAs(100)的MOVCD外延生长

利用MOCVD生长技术在GaAs(100)衬底上生长了高质量的立方相AlGaN薄膜。通过光致发光（PL）、扫描电镜（SEM）分析了不同NH_3流量、不同生长温度对AlGaN外延层的结晶质量和表面形貌的影响。发现相对高的NH_3流量和相对高的生长温度可以提高AlGaN外延层的结晶质量。

在p-Si(100)上溅射法生长ZnO的结构和光学特性

室温下在p-Si(100)上采用直流反应磁控溅射法外延生长了ZnO薄膜。XRD测量表明了ZnO是高度c轴单一取向生长的，XRC测量则表明了ZnO的高质量。在室温下的PL测量中见到了带边发射，其强度与晶体质量有关。

Optical properties of self-assembled ternary In(GA/Al)As quantum dots on (100) and (N 1 1)B InP substrates

In this paper, we investigated the self-assembled quantum dots formed on (100) and (N11)B (N = 2, 3, 4, 5) InP substrates by molecular beam epitaxy (MBE). Two kinds of ternary QDs (In0.9Ga0.1As and In0.9Al0.1As QDs) are grown on the above substrates; Transmission electron microscopy (TEM) and photoluminescence (PL) results confirm QDs formation for all samples. The PL spectra reveal obvious differences in integral luminescence, peak position, full-width at half-maximum and peak shape between different oriented surfaces. Highest PL integral intensity is observed from QDs on (411)B surfaces, which shows a potential for improving the optical properties of QDs by using high-index surface. (C) 2000 Elsevier Science B.V. All rights reserved.

Investigation of PL properties of C-doped SiO2/Si samples after high energy Pb ion irradiation

Amorphous SiO2 thin films with about 400-500 nm in thickness were thermally grown on single crystalline silicon. These SiO2/Si samples were firstly implanted at room temperature (RT) with 100 keV carbon ions to 2.0 x 10(17),5.0 X 10(17) or 1.2 x 10(18) ions/cm(2), then irradiated at RT by 853 MeV Pb ions to 5.0 x 10(11), 1.0 X.10(12) 2.0 x 10(12) or 5.0 x 10(12) ions/cm(2), respectively. The variation of photoluminescence (PL) properties of these samples was analyzed at RT using a fluorescent spectroscopy. The obtained results showed that Pb-ion irradiations led to significant changes of the PL properties of the carbon ion implanted SiO2 films. For examples, 5.0 x 10(12) Pb-ions/cm(2) irradiation produced huge blue and green light-emitters in 2.0 x 10(17) C-ions/cm(2) implanted samples, which resulted in the appearance of two intense PL peaks at about 2.64 and 2.19 eV. For 5.0 x 10(17) carbon-ions/cm(2) implanted samples, 2.0 x 10(12) Pb-ions/cm(2) irradiation could induce the formation of a strong and wide violet band at about 2.90 eV, whereas 5.0 x 10(12) Pb-ionS/cm(2) irradiation could,create double peaks of light emissions at about 2.23 and 2.83 eV. There is no observable PL peak in the 1.2 x 10(18) carbon-ions/cm(2) implanted samples whether it was irradiated with Pb ions or not. All these results implied that special light emitters could be achieved by using proper ion implantation and irradiation conditions, and it will be very useful for the synthesis of new type Of SiO2-based light-emission materials.

Structural and PL properties of Cu-doped ZnO films

Cu-doped ZnO films with hexagonal wurtzite structure were deposited on silicon (1 1 1) substrates by radio frequency (RF) sputtering technique. An ultraviolet (UV) peak at similar to 380nm and a blue band centered at similar to 430nm were observed in the room temperature photoluminescent (PL) spectra. The UV emission peak was from the exciton transition. The blue emission band was assigned to the Zn interstitial (Zn-i) and Zn vacancy (V-Zn) level transition. A strong blue peak (similar to 435 nm) was observed in the PL spectra when the alpha(Cu) (the area ratio of Cu-chips to the Zn target) was 1.5% at 100 W, and ZnO films had c-axis preferred orientation and smaller lattice mismatch. The influence of alpha(Cu) and the sputtering power on the blue band was investigated.

Magnetron Sputtering Growth of InAs0.3Sb0.7 Films on (100) GaAs Substrates: Strong Effect of Growth Conditions on Film Structure

The growth of highly lattice-mismatched InAs0.3Sb0.7 films on (100) GaAs Substrates by magnetron Sputtering has been investigated and even epitaxial lnAs(0.3)Sb(0.7) films have been successfully obtained. A strong effect of the growth conditions on the film structure was observed, revealing that there was a growth mechanism transition from three-dimensional nucleation growth to epitaxial layer-by-layer growth mode when increasing the substrate temperature. A qualitative explanation for that transition was proposed and the critical conditions for the epitaxial layer-by-layer growth mode were also discussed.

Properties of high k gate dielectric gadolinium oxide deposited on Si(100) by dual ion beam deposition (DIBD)

Gadolinium oxide thin films have been prepared on silicon (100) substrates with a low-energy dual ion-beam epitaxial technique. Substrate temperature was an important factor to affect the crystal structures and textures in an ion energy range of 100-500 eV. The films had a monoclinic Gd2O3 structure with preferred orientation ((4) over bar 02) at low substrate temperatures. When the substrate temperature was increased, the orientation turned to (202), and finally, the cubic structure appeared at the substrate temperature of 700 degreesC, which disagreed with the previous report because of the ion energy. The AES studies found that Gadolinium oxide shared Gd2O3 structures, although there were a lot of oxygen deficiencies in the films, and the XPS results confirmed this. AFM was also used to investigate the surface images of the samples. Finally, the electrical properties were presented. (C) 2004 Elsevier B.V. All rights reserved.

InAs0.3Sb0.7 films grown on (100) GaSb substrates with a buffer layer by liquid-phase epitaxy

The growth of InAsxSb1-x films on (100) GaSb substrates by liquid-phase epitaxy (LPE) has been investigated and epitaxial InAs0.3Sb0.7 films with InAs0.9Sb0.09 buffer layers have been successfully obtained. The low X-ray rocking curve FHWM values of InAs0.3Sb0.7 layer shows the high quality of crystal-orientation structure. Hall measurements show that the highest electron mobility in the samples obtained is 2.9 x 10(4) cm(2) V-1 s(-1) and the carrier density is 2.78 x 10(16)cm(-3) at room temperature (RT). The In As0.3Sb0.7 films grown on (10 0) GaSb substrates exhibit excellent optical performance with a cut-off wavelength of 12 mu m. (c) 2007 Elsevier B.V. All rights reserved.

Adsorption of His-tagged peptide to Ni, Cu and Au (100) surfaces: Molecular dynamics simulation

Molecular dynamics (MD) simulations are performed to study the interaction of His-tagged peptide with three different metal surfaces in explicit water. The equilibrium properties are analyzed by using pair correlation functions (PCF) to give an insight into the behavior of the peptide adsorption to metal surfaces in water solvent. The intermolecular interactions between peptide residues and the metal surfaces are evaluated. By pulling the peptide away from the peptide in the presence of solvent water, peeling forces are obtained and reveal the binding strength of peptide adsorption on nickel, copper and gold. From the analysis of the dynamics properties of the peptide interaction with the metal surfaces, it is shown that the affinity of peptide to Ni surface is the strongest, while on Cu and An the affinity is a little weaker. In MD simulations including metals, the His-tagged region interacts with the substrate to an extent greater than the other regions. The work presented here reveals various interactions between His-tagged peptide and Ni/Cu/Au surfaces. The interesting affinities and dynamical properties of the peptide are also derived. The results give predictions for the structure of His-tagged peptide adsorbing on three different metal surfaces and show the different affinities between them, which assist the understanding of how peptides behave on metal surfaces and of how designers select amino sequences in molecule devices design. (c) 2007 Elsevier Ltd. All rights reserved.

简单金属在[100]单轴应力下的理论强度

本文讨论了利用赝势理论,按照Born稳定性判据,计算简单金属理论强度的方法。然后计算了六种简单金属(Li,Na,K,Rb,Cs和Pb)在0K和[100]单轴应力下的理论拉伸与压缩强度。

Single sub-100 attosecond pulse generation in a two-colour time-gating laser field

We theoretically propose a method of generating a single sub-100 attosecond (as) pulse with a two-colour time-gating laser field. The field is synthesized by an 8 fs/800 nm (three optical cycles) pulse and a 24 fs/2400 nm (three optical cycles) pulse with an optimal time delay between them. In our simulation, we obtain a supercontinuum with an extremely broad spectrum of 150 eV and generate an isolated attosecond pulse with 96 as pulse duration without any dispersion compensation.