Simultaneous three-photon-excited violet upconversion luminescence of Ce3+: Lu2Si2O7 single crystals by femtosecond laser irradiation

We found that Ce3+:Lu2Si2O7 single crystals could be excited at 800 nm by using a femtosecond Ti:sapphire laser. The emission spectra of Ce3+:Lu2Si2O7 crystals were the same for one-photon excitation at 267 nm as for excitation at 800 nm. The emission intensity of Ce3+: Lu2Si2O7 crystals was found to depend on the cube of the laser power at 800 nm, consistent with simultaneous absorption of three 800 nm photons. The measured value of the three-photon absorption cross section is sigma'(3) = 2.44 x 10(-77) cm(6) s(2). (c) 2006 Optical Society of America.

Thermal, spectroscopic and laser properties of Yb3+Na+: CaF2 single crystals

The effects of Na+ doping level on the thermal conductivities, absorption and emission spectra, and fluorescence lifetimes of Yb3+ ,Na+ :CaF2 crystals were systematically studied. Sites structure, covalent force, and crystal field strength of Yb3+ :CaF2 crystals were markedly varied by codoping Na+ as charge compensator. The 2.0at% Yb3+ and 3.0at% Na+-codoped CaF2 crystal was demonstrated to operate in diode-pumped passively mode-locking scheme. Transform-limited 1 ps laser pulses were obtained, showing the crystal capable of producing ultra-short laser pulses. (c) 2006 Elsevier B.V. All rights reserved.

Effect of annealing and gamma irradiation on undoped and Eu3+-doped Y2SiO5 single crystals

The absorption spectra of the undoped Y2SiO5 and Eu3+-doped Y2SiO5 crystals grown by the Czochralski technique were compared before and after annealing and, similarly, the unannealed and annealed crystals after gamma-ray irradiation. The absorption bands of Eu2+ ions with peaks at 300 and 390 nm were observed in the as-grown Y2SiO5:Eu3+ crystal. These peaks were more intense in H-2-annealed and irradiated Y2SiO5:Eu3+ crystals. The additional absorption peaks at 260 and 320-330 nm which were attributed to F color centers and O- hole centers were observed in irradiated undoped Y2SiO5 and Y2SiO5:Eu3+ crystals, respectively. (c) 2005 Elsevier B.V. All rights reserved.

Comparison of fluorescence spectra of Yb : Y3Al5O12 and Yb : YALO(3) single crystals

Yb:Y3Al5O12 (Yb:YAG) single crystals with Yb doping concentration 0.5 at.%, 5 at.%, 15 at.%, 25 at.%, 50 at.%, 100 at.% and Yb:YAlO3 (Yb:YAP) single crystals with Yb doping concentration 0.5 at.%, 5 at.%, 15 at.%, 30 at.% were grown by the Czochralski process. The fluorescence spectra of these crystals and the effects of self-absorption on the shape of the fluorescence spectra were studied. Through comparing the fluorescence spectra of Yb:YAG and Yb:YAP, all results indicate that the effects of self-absorption on the fluorescence spectra of Yb:YAP are remarkably stronger than that of Yb:YAG at the same Yb concentration. (c) 2006 Elsevier B.V. All rights reserved.

Influence of electron irradiation on hydrothermally grown zinc oxide single crystals

The resistivity of hydrothermally grown ZnO single crystals increased from similar to 10(3) Omega cm to similar to 10(6) Omega cm after 1.8 MeV electron irradiation with a fluence of similar to 10(16) cm(-2), and to similar to 10(9) Omega cm as the fluence increased to similar to 10(18) cm(-2). Defects in samples were studied by thermally stimulated current (TSC) spectroscopy and positron lifetime spectroscopy (PLS). After the electron irradiation with a fluence of 10(18) cm(-2), the normalized TSC signal increased by a factor of similar to 100. A Zn vacancy was also introduced by the electron irradiation, though with a concentration lower than expected. After annealing in air at 400 degrees C, the resistivity and the deep traps concentrations recovered to the levels of the as-grown sample, and the Zn vacancy was removed.

Study on the perfection of in situ P-injection synthesis LEC-InP single crystals

Undoped, S-doped and Fe-doped InP crystals with diameter up to 4-inch have been pulled in drop 10 0 drop -direction under P-rich condition by a rapid P-injection in situ synthesis liquid encapsulated Czochralski (LEC) method. High speed photoluminescence mapping, etch-pit density (EPD) mapping and scanning electron microscopy have been used to characterize the samples of the single crystal ingots. Dislocations and electrical homogeneity of these samples are investigated and compared. By controlling the thermal field and the solid-liquid interface shape, 4-inch low-EPD InP single crystals have been successfully grown by the rapid P-injection synthesis LEC method. The EPD across the wafer of the ingots is less than 5 x 10(4) cm(-2). Cluster defects with a pore center are observed in the P-rich LEC grown InP ingots. These defects are distributed irregularly on a wafer and are surrounded by a high concentration of dislocations. The uniformity of the PL intensity across the wafer is influenced by these defects. (C) 2004 Elsevier B.V. All rights reserved.

Comparison of space- and ground-grown Ce: Bi12SiO20 single crystals

Ce doped Bi12SiO20 single crystals were grown either on board of the Chinese Spacecraft-Shenzhou No.3 (SZ-3) or on the ground at the same conditions with the exception of microgravity. The surface morphology of crystals clearly showed significant differences between the space- and ground-grown portions. The space- and ground-grown crystals have been measured by X-ray rocking curve, Cc concentration distribution in growth direction, dislocation density, absorption spectrums. These results show that the compositional homogeneity and structural perfection of Ce doped crystal grown in space are obviously improved.

Raman-forbidden mode and oxygen ordering in Bi2Sr2-xLaxCuO6+gamma single crystals annealed in oxygen

A Raman-forbidden phonon mode at about 840 cm(-1) is observed popularly on the surface of pun and La-doped Bi2Sr2-xLaxCuO6+y (0 less than or equal to x less than or equal to 0.8) single crystals annealed in oxygen. A remarkable excitation dependence of this additional line is found. Based on the properties of the structure of the Bi-O layer with excess oxygen atoms and the similarity in the appearance of the Raman-forbidden modes between RBa2Cu3Ox (R = Y, Nd, Gd, Pr) and Bi2Sr2-xLaxCuO6+y systems, we attribute the manifestation of this additional line to the ordering of the interstitial oxygen in the Bi-O layers. Our results provide Raman evidences for confirming that the ordering of the movable oxygen may exist universally in high-temperature superconductors.

Properties of GaAs single crystals grown by molecular beam epitaxy at low temperatures

Properties of GaAs single crystals grown at low temperatures by molecular beam epitaxy (LTMBE GaAs) have been studied. The results shaw that excessive arsenic atoms of about 10(20) cm(-3) exist in LTMBE GaAs in the form of arsenic interstitial couples, and cause the dilation in lattice parameter of LTMBE GaAs, The arsenic interstitial couples will be decomposed, and the excessive arsenic atoms will precipitate during the annealing above 300 degrees C. Arsenic precipitates accumulate in the junctions of epilayers with the increase in the temperature of annealing. The depletion regions caused by arsenic precipitates overlap each other in LTMBE GaAs, taking on the character of high resistivity, and the effects of backgating or sidegating are effectively restrained.

Wet etching and infrared absorption of AlN bulk single crystals

The defects and the lattice perfection of an AlN (0001) single crystal grown by the physical vapor transport (PVT) method were investigated by wet etching, X-ray diffraction (XRD), and infrared absorption, respectively. A regular hexagonal etch pit density (EPD) of about 4000 cm~(-2) is observed on the (0001) A1 surface of an AlN single crystal. The EPD exhibits a line array along the slip direction of the wurtzite structure, indicating a quite large thermal stress born by the crystal in the growth process. The XRD full width at half maximum (FWHM) of the single crystal is 35 arcsec, suggesting a good lattice perfection. Pronounced infrared absorption peaks are observed at wave numbers of 1790, 1850, 2000, and 3000 cm~(-1), respectively. These absorptions might relate to impurities O, C, Si and their complexes in AlN single crystals.

Characterization of Phosphorus Diffused ZnO Bulk Single Crystals

Phosphorus was diffused into CVT grown undoped ZnO bulk single crystals at 550 and 800℃ in a closed quartz tube. The P-diffused ZnO single crystals were characterized by the Hall effect, X-ray photoelectron spectroscopy （XPS）, photoluminescence spectroscopy （PL）, and Raman scattering. The P-diffused ZnO single crystals are n-type and have higher free electron concentration than undoped ZnO, especially for the sample diffused at 800℃. The PL measurement reveals defect related visible broad emissions in the range of 420-550nm in the P-diffused ZnO samples. The XPS result suggests that most of the P atoms substitute in the Zn site after they diffuse into the ZnO single crystal at 550℃ ,while the P atom seems to occupy the O site in the ZnO samples diffused at 800℃. A high concentration of shallow donor defect forms in the P-diffused ZnO,resulting in an apparent increase of free electron concentration.