Effect of rapid thermal annealing on GaInNAs/GaAs quantum wells grown by plasma-assisted molecular-beam epitaxy

We have studied the effect of rapid thermal annealing (RTA) on GaInNAs/GaAs quantum wells (QWs) grown by molecular-beam epitaxy using a dc plasma as the N source. It was found that RTA at low temperature (LT, 650 degrees C) and high temperature (HT, 900 degrees C) could both improve the QW quality significantly. To clarify the mechanism of quality improvement by RTA, a magnetic field perpendicular to the path of the N plasma flux was applied during the growth of the GaInNAs layers for the sake of comparison. It was found that LT-RTA mainly removed dislocations at interfaces related to the ion bombardment, whereas, HT-RTA further removed dislocations originating from the growth. LT-RTA caused only a slight blueshift of photoluminescence peak wavelength, probably due to defect-assisted interdiffusion of In-Ga at the QW interfaces. The blueshift caused by HT-RTA, on the other hand, was much larger. It is suggested that this is due to the fast defect-assisted diffusion of N-As at the QW interfaces. As defects are removed by annealing, the diffusion of In-Ga at interfaces would be predominant. (C) 2000 American Institute of Physics. [S0003- 6951(00)01535-7].

Kinetic modeling of N incorporation in GaInNAs growth by plasma-assisted molecular-beam epitaxy

We have studied the growth of GaInNAs by a plasma-assisted molecular-beam epitaxy (MBE). It was found that the N-radicals were incorporated into the epitaxial layer like dopant atoms. In the range of 400-500 degrees C, the growth temperature (T-g) mainly affected the crystal quality of GaInNAs rather than the N concentration. The N concentration dropped rapidly when T-g exceeded 500 degrees C. Considering N desorption alone is insufficient to account for the strong falloff of the N concentration with T-g over 500 degrees C, the effect of thermally-activated N surface segregation must be taken into account. The N concentration was independent of the arsenic pressure and the In concentration in GaInNAs layers, but inversely proportional to the growth rate. Based on the experimental results, a kinetic model including N desorption and surface segregation was developed to analyze quantitatively the N incorporation in MBE growth. (C) 2000 American Institute of Physics. [S0003-6951(00)00928-1].

Optical characterization of high-purity cubic GaN grown on GaAs (001) substrate by metalorganic chemical vapor deposition

The optical properties of cubic GaN films have been investigated in the temperature range of 10-300 K. Five peaks were observed at 10 K. From the dependence of photoluminescence emissions on the temperature and excitation intensity, we have assigned two of the five peaks (2.926 and 2.821 eV) to donor-acceptor pair (DAP) transitions. Furthermore, these two peaks were found to be related to a common shallow donor involved in the peak position previously reported at 3.150 eV. The intensities of DAP transitions were much weaker than that of excitonic emission even at low temperature, indicating a relatively high purity of our samples. (C) 2000 American Institute of Physics. [S0003-6951(00)00921-9].

Relaxed GexSi1-x layer formation with reduced dislocation density grown by ultrahigh vacuum chemical vapor deposition

A new alternative method to grow the relaxed Ge0.24Si0.76 layer with a reduced dislocation density by ultrahigh vacuum chemical vapor deposition is reported in this paper. A 1000-Angstrom Ge0.24Si0.76 layer was first grown on a Si(100) substrate. Then a 500-Angstrom Si layer and a subsequent 5000-Angstrom Ge0.24Si0.76 overlayer followed. All these three layers were grown at 600 degrees C. After being removed from the growth system to air, the sample was first annealed at 850 degrees C for 30 min, and then was investigated by cross-sectional transmission electron microscopy and Rutherford backscattering spectroscopy. It is shown that the 5000-Angstrom Ge0.24Si0.76 thick over layer is perfect, and most of the threading dislocations are located in the embedded thin Si layer and the lower 1000-Angstrom Ge0.24Si0.76 layer. The relaxation ratio of the over layer is deduced to be 0.8 from Raman spectroscopy.

Microstructure of SiOx : H films prepared by plasma enhanced chemical vapor deposition

The micro-Raman spectroscopy and infrared (IR) spectroscopy have been performed for the study of the microstructure of amorphous hydrogenated oxidized silicon (alpha-SiOx,:H) films prepared by Plasma Enhanced Chemical Vapor Deposition technique. It is found that a-SiOx:H consists of two phases: an amorphous silicon-rich phase and an oxygen-rich phase mainly comprised of HSi-SiO2 and HSi-O-3. The Raman scattering; results exhibit that the frequency of TO-like mode of amorphous silicon red-shifts with decreasing size of silicon-rich region. This is related to the quantum confinement effects, similar to the nanocrystalline silicon.

Initial stages of GaN/GaAs (100) growth by metalorganic chemical vapor deposition

We have investigated the growth of GaN buffers by metalorganic chemical vapor deposition (MOCVD) on GaAs (100) substrates. Atomic force microscope (AFM) and reflection high-energy electron diffraction (RHEED) were employed to study the dependence of the nucleation on the growth temperature, growth rate, annealing effect, and growth time. A two-step growth sequence must be used to optimize and control the nucleation and the subsequent growth independently. The size and distribution of islands and the thickness of buffer layers have a crucial role on the quality of GaN layers. Based on the experimental results, a model was given to interpret the formation of hexagonal-phase GaN in the cubic-phase GaN layers. Using an optimum buffer layer, the strong near-band emission of cubic GaN with full-width at half maximum (FWHM) value as small as 5.6 nm was observed at room temperature. The background carrier concentration was estimated to be in the range of 10(13) similar to 10(14) cm(-3).

Room-temperature optical transitions in Mg-doped cubic GaN/GaAs(100) grown by metalorganic chemical vapor deposition

The mechanism of room-temperature optical transitions in a Mg-doped cubic GaN epilayer grown on GaAs(100) by metalorganic chemical vapor deposition has been investigated. By examining the dependence of photoluminescence on the excitation intensity (which varied over four orders) at room temperature, four different emissions with different origins were identified. A blue emission at similar to 3.037 eV was associated with a shallow Mg acceptor, while three different lower-energy emissions at similar to 2.895, similar to 2.716, and similar to 2.639 eV were associated with a deep Mg complex. In addition to a shallow acceptor at E congruent to 0.213 eV, three Mg-related deep defect levels were also found at around 215, 374, and 570 meV (from the conduction band). (C) 2000 American Institute of Physics. [S0021-8979(00)01904-6].

Stability investigation of cubic GaN films grown by metalorganic chemical vapor deposition on GaAs (001)

The thermal stability of cubic-phase GaN (c-GaN) films are investigated by photoluminescence (PL) and Raman scattering spectroscopy. C-GaN films are grown on GaAs (001) substrates by metalorganic chemical vapor deposition. PL measurements show that the near-band-edge emissions in the as-grown GaN layers and thermally treated samples are mainly from c-GaN. No degradation of the optical qualities is observed after thermal annealing. Raman scattering spectroscopy shows that the intensity of the E-2 peak from hexagonal GaN grains increases with annealing temperature for the samples with poor crystal quality, while thermal annealing up to 1000 degrees C has no obvious effect on the samples with high crystal quality. (C) 1999 American Institute of Physics. [S0003-6951(99)04719-1].

Enhanced hydrogen desorption from Si sites during low-temperature Si1-xGex growth by disilane and solid-Ge molecular beam epitaxy

A phenomenological model is proposed to explain quantitatively the interesting compositional dependence on the Ge incorporation rate during low-temperature growth of Si1-xGex by disilane and solid-Ge molecular beam epitaxy, based on enhanced hydrogen desorption from Si sites due to the presence of Ge atoms. The hydrogen desorption rate constant for disilane on Si sites is fitted to an exponential function of Ge incorporation rate and a possible physical explanation is discussed. Simulated results are in excellent agreement with experimental data. (C) 1999 American Institute of Physics. [S0021-8979(99)02109-X].

Solid-phase crystallization and dopant activation of amorphous silicon films by pulsed rapid thermal annealing

An improved pulsed rapid thermal annealing method has been used to crystallize amorphous silicon films prepared by PECVD. The solid-phase crystallization and dopant activation process can be completed with time-temperature budgets such as 10 cycles of 60-s 550 degrees C thermal bias/l-s 850 degrees C thermal pulse. A mean grain size more than 1000 Angstrom and a Hall mobility of 24.9 cm(2)/V s are obtained in the crystallized films. The results indicate that this annealing method possesses the potential for fabricating large-area and good-quality polycrystalline silicon films on low-cost glass substrate. (C) 1998 Elsevier Science B.V. All rights reserved.

Influence of rapid thermal annealing on the optical properties of gallium nitride grown by gas-source molecular-beam epitaxy

Raman scattering, photoluminescence (PL), and nuclear reaction analysis (MA) have been employed to investigate the effects of rapid thermal annealing (RTA) on GaN films grown on sapphire (0001) substrates by gas-source molecular-beam epitaxy, The Raman spectra showed the presence of the E-2 (high) mode of GaN and shift of this mode from 572 to 568 cm(-1) caused by annealing. The results showed that RTA has a significant effect on the strain relaxation caused by the lattice and thermal expansion misfit between the GaN epilayer and the substrate. The PL peak exhibited a blueshift in its energy position and a decrease in the full width at half maximum after annealing, indicating an improvement in the optical quality of the film. Furthermore, a green luminescence appeared after annealing and increased in intensity with increasing annealing time. This effect was attributed to H concentration variation in the GaN film, which was measured by NRA. A high H concentration exists in as-grown GaN, which can neutralize the deep level, and the H-bonded complex dissociates during RTA, This leads to the appearance of a luminescent peak in the PL spectrum. (C) 1998 American Institute of Physics.

Effects of annealing treatment on the formation of CO2 in ZnO thin films grown by metal-organic chemical vapor deposition

Post-growth annealing was carried out on ZnO thin films grown by metal-organic chemical vapor deposition (MOCVD). The grain size of ZnO thin film increases monotonically with annealing temperature. The ZnO thin films were preferential to c-axis oriented after annealing as confirmed by Xray diffraction (XRD) measurements. Fourier transformation infrared transmission measurements showed that ZnO films grown at low temperature contains CO2 molecules after post-growth annealing. A two-step reaction process has been proposed to explain the formation mechanism of CO2, which indicates the possible chemical reaction processes during the metal-organic chemical vapor deposition of ZnO films.

A study of indium incorporation in In-rich InGaN grown by MOVPE

InGaN/GaN heterostructures have been deposited onto (0 0 0 1) sapphire by our home-made low pressure MOVPE with different growth parameters. It has been noted that the indium incorporation depends by a complex way on a number of factors. In this work, the effect of substrate temperature, trimethylindium input flow and V/III ratio on the indium incorporation has been investigated. Finally, by optimizing the growth parameters, we made a series of single-phase InGaN samples with indium content from 10% up to 45%.

GROWTH OF GASB AND GAASSB IN THE SINGLE-PHASE REGION BY MOVPE

GaSb layers are grown on GaSb substrates; the effects of input partial pressure of trimethylantimony and the V/III ratio are studied. A model of the MOVPE phase diagram for the growth of GaSb and GaAsxSb1-x is developed which assumes thermodynamic equilibrium to be established at the solid-vapor interface.

PHYSICAL VAPOR TRANSPORT AND CRYSTAL-GROWTH OF GESEXTE1-X SOLID-SOLUTIONS

Physical vapor transport studies of GeSe(x)Te1 - x (x = 0.1, 0.2, 0.3, and 0.4) solid solutions demonstrated, that individual, large single crystals of these materials can be grown in closed ampoules. A compositional analysis of the grown crystals revealed, that the mass transport (crystal growth) process under steady-state conditions is pseudo-congruent and controlled by diffusion processes in the source material. From these experiments, the degree of non-stoichiometry (Ge-vacancy concentrations) of GeSe(x)Te1 - x single crystals could be estimated. The effects of the cubic to rhombohedral phase transformation during cooling on the microstructure and morphology of the grown mixed crystals are observed. This work provides the basis for subsequent defect studies and electrical measurements on these crystals.