Effect of growth interruption on the optical properties of InAs/GaAs quantum dots

The effect of growth interruption (GI) on the optical properties of InAs/GaAs quantum dots was investigated by cw and time-resolved photoluminescence (PL). It is found that this effect depends very much on the growth conditions, in particular, the growth rate. In the case of low growth rate, we have found that the GI may introduce either red-shift or blue-shift in PL with increase of the interruption lime, depending on the InAs thickness. The observed red shift in our 1.7 monolayer (ML) sample is attributed to the evolution of the InAs islands during the growth interruption. While the blue-shift in the 3 ML sample is suggested to be mainly caused by the strain effect. In addition, nearly zero shift was observed for the sample with thickness around 2.5 ML, (C) 1999 Elsevier Science Ltd. All rights reserved.

Optical properties of ZnSxTe1-x mixed crystals

The Raman scattering and the photoluminescence (PL) of ZnSxTe1-x mixed crystals grown by MBE, covering the entire composition range (0 less than or equal to x<1), were investigated. The results of Raman studies show that the phonons in ZnSxTe1-x mixed crystals display two-mode behavior. In addition, photoluminescence spectra obtained in backscattering and edge-emission geometries, reflection spectra and the temperature dependence of the photoluminescence of ZnSxTe1-x from 10 to 300K were employed to find out the origins of PL emissions in ZnSxTe1-x with different x values, The results indicate that the emission bands, for the samples with small x values, can be related to the band gap transitions or a shallow level emission center, while for the samples with large x values, they are designated to strong radiative recombinations of Te isoelectronic centers.

Optical properties of Ge self-organized quantum dots in Si

Small-size, high-density, and vertical-ordering Ge quantum dots are observed in strained Si/Ge short-period superlattices grown on Si(001) at low growth temperature by molecular-beam epitaxy. The photoluminescence (PL) peak position, the strong PL at room temperature, and the high exciton binding energy suggest an indirect-to-direct conversion of the Ge quantum dots. This conversion is in good agreement with the theoretical prediction. The characteristic of absorption directly indicates this conversion. The tunneling of carriers between these quantum dots is also observed. [S0163-1829(98)03515-2].

Influence of rapid thermal annealing on the optical properties of gallium nitride grown by gas-source molecular-beam epitaxy

Raman scattering, photoluminescence (PL), and nuclear reaction analysis (MA) have been employed to investigate the effects of rapid thermal annealing (RTA) on GaN films grown on sapphire (0001) substrates by gas-source molecular-beam epitaxy, The Raman spectra showed the presence of the E-2 (high) mode of GaN and shift of this mode from 572 to 568 cm(-1) caused by annealing. The results showed that RTA has a significant effect on the strain relaxation caused by the lattice and thermal expansion misfit between the GaN epilayer and the substrate. The PL peak exhibited a blueshift in its energy position and a decrease in the full width at half maximum after annealing, indicating an improvement in the optical quality of the film. Furthermore, a green luminescence appeared after annealing and increased in intensity with increasing annealing time. This effect was attributed to H concentration variation in the GaN film, which was measured by NRA. A high H concentration exists in as-grown GaN, which can neutralize the deep level, and the H-bonded complex dissociates during RTA, This leads to the appearance of a luminescent peak in the PL spectrum. (C) 1998 American Institute of Physics.

Linear and nonlinear intersubband optical properties in a step quantum well with an applied electric field

Within the framework of the effective-mass envelope-function theory, the field-dependent intersubband optical properties of a Al0.4Ga0.6As/Al0.2Ga0.8As/GaAs step quantum well are investigated theoretically based on the periodic boundary condition. A very large Stark shift occurs when the lowest subband electron remains confined to the small well while the higher subband electron confined to the big well. The optical nonlinearity in a step well due to resonant intersubband transition (ISBT) is analyzed using a density-matrix approach. The second-harmonic generation coefficient chi(2 omega)((2)) and nonlinear optical rectification chi(0)((2)) have also been investigated theoretically. The results show that the ISBT in a step well can generate very large second order optical nonlinearities, chi(0)((2)) and chi(2 omega)((2)) can be tuned by the electric field over a wide range.

Electronic, structural, and optical properties of crystalline yttria

The electronic structure of crystalline Y2O3 is investigated by first-principles calculations within the local-density approximation (LDA) of the density-functional theory. Results are presented for the band structure, the total density of states (DOS), the atom-and orbital-resolved partial DOS. effective charges, bond order, and charge-density distributions. Partial covalent character in the Y-O bonding is shown, and the nonequivalency of the two Y sites is demonstrated. The calculated electronic structure is compared with a variety of available experimental data. The total energy of the crystal is calculated as a function of crystal volume. A bulk modulus B of 183 Gpa and a pressure coefficient B' of 4.01 are obtained, which are in good agreement with compression data. An LDA band gap of 4.54 eV at Gamma is obtained which increases with pressure at a rate of dE(g)/dP = 0.012 eV/Gpa at the equilibrium volume. Also investigated are the optical properties of Y2O3 up to a photon energy of 20 eV. The calculated complex dielectric function and electron-energy-loss function are in good agreement with experimental data. A static dielectric constant of epsilon(O)= 3.20 is obtained. It is also found that the bottom of the conduction band consists of a single band, and direct optical transition at Gamma between the top of the valence band and the bottom of the conduction band may be symmetry forbidden.

Effect of noncoherent islands on the optical properties of the 1.3 mu m InAs/GaAs quantum dots during rapid thermal annealing

The effect of thermal annealing of InAs/GaAs quantum dots (QDs) with emission wavelength at 1.3 mu m have been investigated by photoluminescence (PL) and transmission electron microscopy (TEM measurements. There is a dramatic change in the A spectra when the annealing temperature is raised up to 800 degrees C: an accelerated blushifit of the main emission peak of QDs together with an inhomogeneous broadening of the linewidth. The TEM images shows that the lateral size of normal QDs decreases as the annealing temperature is increased, while the noncoherent islands increase their size and densit. A small fraction of the relative large QDs contain dislocations when the annealing temperature increases up to 800 degrees C. The latter leads to the strong decrease of the PL intensity.

Optical properties of inGaAs/GaAs quantum wells grown by Sb-assisted molecular beam epitaxy

It is found that both methods using either continuous Sb supply or pre-deposition of a very thin Sb layer are efficient for the Sb-assisted molecular beam epitaxy growth of highly strained InGaAs/GaAs quantum wells (QWs). The emission of QWs is extended to long wavelength close to 1.25 mu m with high luminescence efficiency at room temperature. The influence of rapid thermal annealing (RTA) on the photoluminescence intensity critically depends on the annealing temperature and duration for highly strained QWs. A relatively low RTA temperature of 700 degrees C with a short duration of 10 s is suggested for optimizing the annealing effect. (c) 2005 Elsevier B.V. All rights reserved.

Optical properties and electrical bistability of CdS nanoparticles synthesized in dodecanethiol

We reported the synthesis of CdS semiconductor nanoparticles using a simple one-pot reaction by thermolysis of cadmium acetylacetonate in dodecanethiol. Optical measurements of the as-obtained CdS nanoparticles revealed that their optical properties were closely related to surface effects. Based upon the cocktail of poly (N-vinylcarbazole) (PVK) and CdS nanoparticles, a bistable device was fabricated by a simple solution processing technique. Such a device exhibited a remarkable electrical bistability, which was attributed to the electric field-assisted charge transfer between PVK and the CdS nanoparticles capped by dodecaethiol. The conduction mechanism changed from an injection-controlled current to a bulk-controlled one during switching from OFF-state to ON-state.

Effects of Hydrogen Plasma Treatment on the Electrical and Optical Properties of ZnO Films: Identification of Hydrogen Donors in ZnO

Wurtzite ZnO has many potential applications in optoelectronic devices, and the hydrogenated ZnO exhibits excellent photoelectronic properties compared to undoped ZnO; however, the structure of H-related defects is still unclear. In this article, the effects of hydrogen-plasma treatment and subsequent annealing on the electrical and optical properties of ZnO films were investigated by a combination of Hall measurement, Raman scattering, and photoluminescence. It is found that two types of hydrogen-related defects, namely, the interstitial hydrogen located at the bond-centered (H-BC) and the hydrogen trapped at a O vacancy (H-O), are responsible for the n-type background conductivity of ZnO films. Besides introducing two hydrogen-related donor states, the incorporated hydrogen passivates defects at grain boundaries. With increasing annealing temperatures, the unstable H-BC atoms gradually diffuse out of the ZnO films and part of them are converted into H-O, which gives rise to two anomalous Raman peaks at 275 and 510 cm(-1). These results help to clarify the relationship between the hydrogen-related defects in ZnO described in various studies and the free carriers that are produced by the introduction of hydrogen.

Optical properties of Mn+ doped GaAs

The above work was supported by the national Basic Research Program of China (2006cb604904, 2006cb604908), the hi-tech R & D program of China (2006aa03z0408, 2006aa03z0404), the scientific research Fund of Central South University of Forstry and Technology.

Tunable optical properties of nano-Au on vanadium dioxide

The optical properties of Au nanoparticles deposited on thermochromic thin films of VO2 are investigated using spectroscopy. A localized modification on the transmittance spectrum of VO2 film is formed due to the presence of Au nanoparticles which exhibit localized surface plasmon resonance (LSPR) in the visible-near IR region. The position of the modification wavelength region shows a strong dependence on the Au mass thickness and shifts toward the red as it increases. On the other hand, it was found that the LSPR of Au nanoparticles can be thermally tunable because of the thermochromism of the supporting material of VO2. The LSPR wavelength, lambda(SPR), shifts to the blue with increasing temperature, and shifts back to the red as temperature decreases. A fine tuning is achieved when the temperature is increased in a stepwise manner.

Nonlinear optical properties of semiconductor quantum wells under intense terahertz radiation

The nonlinear optical properties of semiconductor quantum wells driven by intense in-plane terahertz electric fields are investigated theoretically by employing the extended semiconductor Bloch equations. The dynamical Franz-Keldysh effect of the optical absorption near the band edge is analyzed with Coulomb correlation among the carriers included. The in-plane terahertz field induces a variety of behavior in the absorption spectra, including terahertz replicas of the (dark) 2p exciton and terahertz sidebands of the 1s exciton. The dependence of these interesting features on the intensity, frequency, and phase of the terahertz field is explored in detail.