GROWTH OF HIGH-QUALITY GALLIUM-ARSENIDE ON HF-ETCHED SILICON (001) BY CHEMICAL BEAM EPITAXY

HF etching followed by relatively low temperature (almost-equal-to 600-degrees-C) pretreatment is shown to provide a suitable substrate for the heteroepitaxial growth of GaAs on Si(100) by CBE using TEGa and AsH3 as sources. Rutherford backscattering (RBS), photoluminescence (PL), transmission electron microscopy (TEM), and Raman measurements show the low-defect nature of the GaAs epilayer.

Molecular beam epitaxy InAs dot arrays on InGaAs/GaAs

Periodical alignment of the InAs dots along the < 100 > and < 110 > directions was observed on an elastically relaxed InGaAs buffer layer grown at 500 and 450 degrees C, respectively, on the vicinal GaAs(001) substrate. Due to alignment along these directions, the InAs dots were arranged into a quasi-two-dimensional hexagonal lattice. Such a periodical arrangement of InAs dots may be explained in terms of modulation in strain as well as composition along [110] as observed by using cross-sectional transmission electron microscopy.

Influence of semi-insulating InP substrates on InAlAs epilayers grown by molecular beam epitaxy

Tensile-strained InAlAs layers have been grown by solid-source molecular beam epitaxy on as-grown Fe-doped semi-insulating (SI) InP substrates and undoped SI InP substrates obtained by annealing undoped conductive InP wafers (wafer-annealed InP). The effect of the two substrates on InAlAs epilayers and InAlAs/InP type II heterostructures has been studied by using a variety of characterization techniques. Our calculation data proved that the out-diffusion of Fe atoms in InP substrate may not take place due to their low diffusion, coefficient. Double-crystal X-ray diffraction measurements show that the lattice mismatch between the InAlAs layers and the two substrates is different, which is originated from their different Fe concentrations. Furthermore, photoluminescence results indicate that the type II heterostructure grown on the wafer-annealed InP substrate exhibits better optical and interface properties than that grown on the as-grown Fe-doped substrate. We have also given a physically coherent explanation on the basis of these investigations. (C) 2003 Elsevier Science B.V. All rights reserved.

Influence of phosphine flow rate on Si growth rate in gas source molecular beam epitaxy

As reported by other authors, we have also observed that the Si growth rate decreases with increasing phosphine (PH3) flow rate in gas source-Si molecular beam epitaxy using phosphorous (P) as a n-type dopant. Why small quantity PH3 can affect Si growth rate? Up to now, the quantitative characterization of PH3 flow influence on Si growth rate is little known. In this letter, the PH, influence will be analyzed in detail and a model considering strong P surface segregation and its absorption of hydrogen will be proposed to characterize the effect. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of rapid thermal annealing on GaInNAs/GaAs quantum wells grown by plasma-assisted molecular-beam epitaxy

We have studied the effect of rapid thermal annealing (RTA) on GaInNAs/GaAs quantum wells (QWs) grown by molecular-beam epitaxy using a dc plasma as the N source. It was found that RTA at low temperature (LT, 650 degrees C) and high temperature (HT, 900 degrees C) could both improve the QW quality significantly. To clarify the mechanism of quality improvement by RTA, a magnetic field perpendicular to the path of the N plasma flux was applied during the growth of the GaInNAs layers for the sake of comparison. It was found that LT-RTA mainly removed dislocations at interfaces related to the ion bombardment, whereas, HT-RTA further removed dislocations originating from the growth. LT-RTA caused only a slight blueshift of photoluminescence peak wavelength, probably due to defect-assisted interdiffusion of In-Ga at the QW interfaces. The blueshift caused by HT-RTA, on the other hand, was much larger. It is suggested that this is due to the fast defect-assisted diffusion of N-As at the QW interfaces. As defects are removed by annealing, the diffusion of In-Ga at interfaces would be predominant. (C) 2000 American Institute of Physics. [S0003- 6951(00)01535-7].

Kinetic modeling of N incorporation in GaInNAs growth by plasma-assisted molecular-beam epitaxy

We have studied the growth of GaInNAs by a plasma-assisted molecular-beam epitaxy (MBE). It was found that the N-radicals were incorporated into the epitaxial layer like dopant atoms. In the range of 400-500 degrees C, the growth temperature (T-g) mainly affected the crystal quality of GaInNAs rather than the N concentration. The N concentration dropped rapidly when T-g exceeded 500 degrees C. Considering N desorption alone is insufficient to account for the strong falloff of the N concentration with T-g over 500 degrees C, the effect of thermally-activated N surface segregation must be taken into account. The N concentration was independent of the arsenic pressure and the In concentration in GaInNAs layers, but inversely proportional to the growth rate. Based on the experimental results, a kinetic model including N desorption and surface segregation was developed to analyze quantitatively the N incorporation in MBE growth. (C) 2000 American Institute of Physics. [S0003-6951(00)00928-1].

Influence of rapid thermal annealing on the optical properties of gallium nitride grown by gas-source molecular-beam epitaxy

Raman scattering, photoluminescence (PL), and nuclear reaction analysis (MA) have been employed to investigate the effects of rapid thermal annealing (RTA) on GaN films grown on sapphire (0001) substrates by gas-source molecular-beam epitaxy, The Raman spectra showed the presence of the E-2 (high) mode of GaN and shift of this mode from 572 to 568 cm(-1) caused by annealing. The results showed that RTA has a significant effect on the strain relaxation caused by the lattice and thermal expansion misfit between the GaN epilayer and the substrate. The PL peak exhibited a blueshift in its energy position and a decrease in the full width at half maximum after annealing, indicating an improvement in the optical quality of the film. Furthermore, a green luminescence appeared after annealing and increased in intensity with increasing annealing time. This effect was attributed to H concentration variation in the GaN film, which was measured by NRA. A high H concentration exists in as-grown GaN, which can neutralize the deep level, and the H-bonded complex dissociates during RTA, This leads to the appearance of a luminescent peak in the PL spectrum. (C) 1998 American Institute of Physics.

Identification of induced reaction during XPS depth profile measurements of CeO2/Si films grown by ion beam epitaxy

An anomalous behavior was observed in X-ray photoelectron Spectroscopy (XPS) depth profile measurements conducted on CeO2/Si epilayers grown by ion beam epitaxy (IBE): the signals of Ce3+ and Ce4+ co-exist, and the ratio between them increases during the etching time and then tends to maintain a constant level before increasing again. The results of X-ray Diffraction (XRD), Auger Electron Spectroscopy (AES), and Rutherford Back-Scattering (RES) measurements proved that the reduction chemical reaction of CeO2 is induced by ion-etching. (C) 1998 Elsevier Science Ltd. All rights reserved.

Influence of AlN Buffer Thickness on GaN Grown on Si(111) by Gas Source Molecular Beam Epitaxy with Ammonia

Hexagonal GaN is grown on a Si(111) substrate with AlN as a buffer layer by gas source molecular beam epitaxy (GSMBE) with ammonia. The thickness of AlN buffer is changed from 9 to 72 nm. When the thickness of AlN buffer is 36 nm, the surface morphology and crystal quality of GaN is optimal. The in-situ reflection high energy electron diffraction (RHEED) reveals that the transition to a two-dimensional growth mode of AlN is the key to the quality of GaN. However, the thickness of AlN buffer is not so critical to the residual in-plane tensile stress in GaN grown on Si(111) by GSMBE for AlN thickness between 9 to 72 nm.

Influence of V/III ratio on the structural and photoluminescence properties of In0.52AlAs/In0.53GaAs metamorphic high electron mobility transistor grown by molecular beam epitaxy

A series of metamorphic high electron mobility transistors (MMHEMTs) with different V/III flux ratios are grown on GaAs (001) substrates by molecular beam epitaxy (XIBE). The samples are analysed by using atomic force microscopy (AFM), Hall measurement, and low temperature photoluminescence (PL). The optimum V/III ratio in a range from 15 to 60 for the growth of MMHEMTs is found to be around 40. At this ratio, the root mean square (RMS) roughness of the material is only 2.02 nm; a room-temperature mobility and a sheet electron density are obtained to be 10610.0cm(2)/(V.s) and 3.26 x 10(12)cm(-2) respectively. These results are equivalent to those obtained for the same structure grown on InP substrate. There are two peaks in the PL spectrum of the structure, corresponding to two sub-energy levels of the In0.53Ga0.47 As quantum well. It is found that the photoluminescence intensities of the two peaks vary with the V/III ratio, for which the reasons are discussed.

Optimization of metamorphic InGaAs quantum wells on GaAs grown by molecular beam epitaxy

We investigate the molecular beam epitaxy growth of metamorphic InxGa(1-x)As materials (x up to 0.5) on GaAs substrates systematically. Optimization of structure design and growth parameters is aimed at obtaining smooth surface and high optical quality. The optimized structures have an average surface roughness of 0.9-1.8 nm. It is also proven by PL measurements that the optical properties of high indium content (55%) InGaAs quantum wells are improved apparently by defect reduction technique and by introducing Sb as a surfactant. These provide us new ways for growing device quality metamorphic structures on GaAs substrates with long-wavelength emissions.

Evolution of surface morphology and photoluminescence characteristics of 1.3-mu m In0.5Ga0.5As/GaAs quantum dots grown by molecular beam epitaxy

Evolution of surface morphology and optical characteristics of 1.3-mu m In0.5Ga0.5As/GaAs quantum dots (QDs) grown by molecular beam epitaxy (MBE) are investigated by atomic force microscopy (AFM) and photoluminescence (PL). After deposition of 16 monolayers (ML) of In0.5Ga0.5As, QDs are formed and elongated along the [110] direction when using sub-ML depositions, while large size InGaAs QDs with better uniformity are formed when using ML or super-ML depositions. It is also found that the larger size QDs show enhanced PL efficiency without optical nonlinearity, which is in contrast to the elongated QDs.

GaAs-Based Metamorphic Long-Wavelength InAs Quantum Dots Grown by Molecular Beam Epitaxy

A bilayer stacked InAs/GaAs quantum dot structure grown by molecular beam epitaxy on an In0.05Ga0.95As metamorphic buffer is investigated. By introducing a InGaAs Sb cover layer on the upper InAs quantum dots (QDs) layers, the emission wavelength of the QDs is extended successfully to 1.533 mu m at room temperature, and the density of the QDs is in the range of 4 x 10(9) -8 x 10(9) cm(-2). Strong photoluminescence (PL) intensity with a full width at half maximum of 28.6 meV of the PL spectrum shows good optical quality of the bilayer QDs. The growth of bilayer QDs on metamorphic buffers offers a useful way to extend the wavelengths of GaAs-based materials for potential applications in optoelectronic and quantum functional devices.

Growth and characterization of GaInNAs by molecular beam epitaxy using a nitrogen irradiation method

We propose an innovative technique, making use of the In segregation effect, referred as the N irradiation method, to enhance In-N bonding and extend the emission wavelength of GaInNAs quantum wells (QWs). After the formation of a complete In floating layer, the growth is interrupted and N irradiation is initiated. The majority of N atoms are forced to bond with In atoms and their incorporation is regulated independently by the N exposure time and the As pressure. The effect of the N exposure time and As pressure on the N incorporation and the optical quality of GaInNAs QWs were investigated. Anomalous photoluminescence (PL) wavelength red shifts after rapid thermal annealing (RTA) were observed in the N-irradiated samples, whereas a normal GaInNAs sample revealed a blue shift. This method provides an alternative way to extend the emission wavelength of GaInNAs QWs with decent optical quality. We demonstrate light emission at 1546 nm from an 11-nm-thick QW, using this method and the PL intensity is similar to that of a 7-nm-thick GaInNAs QW grown at a reduced rate. (C) 2008 Elsevier B.V. All rights reserved.

Annealing study of carrier concentration in gradient-doped GaAs/GaAlAs epilayers grown by molecular beam epitaxy

We measured the carrier concentration distribution of gradient-doped GaAs/GqAlAs epilayers grown by molecular beam epitaxy before and after annealing at 600 degrees C, using electrochemical capacitance voltage profiling, to investigate the internal variation of transmission-mode GaAs photocathodes arising from the annealing process. The results show that the carrier concentration increased after annealing. As a result, the total band-bending energy in the gradient-doped GaAs emission layer increased by 25.24% after annealing, which improves the pbotoexcited electron movement toward the surface. On the other hand, the annealing process resulted in a worse carrier concentration discrepancy between the GaAs and the GaAlAs, which causes a lower back interface potential barrier, decreasing the amount of high-energy photoelectrons. (C) 2009 Optical Society of America