Effects of surface treatment on sapphire substrates

The influence of mechanical polishing, chemo-mechanical polishing (CMP), as well as CMP and subsequent chemical etching on the properties of sapphire substrate surfaces has been studied. The sapphire substrates have been investigated by means of polarizing microscopy, atomic force microscopy (AFM). X-ray diffraction rocking curves (XRCs) and micro-Raman spectroscopy. The results show that CMP with subsequent chemically etching yields the best-quality sapphire substrate surfaces. (C) 2004 Elsevier B.V. All rights reserved.

Fabrication and characterization of GaN-based LEDs grown on nanopatterned sapphire substrates

Sapphire substrates were nanopatterned by dry (inductively coupled plasma, ICP) etching to improve the performance of GaN-based light-emitting diodes (LEDs). GaN-based LEDs on nanopatterned sapphire substrates (NPSS) were fabricated by metal organic chemical vapor deposition (MOCVD). The characteristics of LEDs fabricated on NPSS prepared by dry etching were studied. The light output power and wall-plug efficiency of the LEDs fabricated on NPSS were greater than those of the conventional LEDs fabricated on common planar sapphire substrates when the injection currents were the same. The LEDs on NPSS and common planar sapphire substrates have similar I-V characteristics.

Improvement of the performance of GaN-based LEDs grown on sapphire substrates patterned by wet and ICP etching

Sapphire substrates patterned by a selective chemical wet and an inductively coupled plasma (ICP) etching technique was proposed to improve the performance of GaN-based light-emitting diodes (LEDs). GaN-based LEDs were fabricated on sapphire substrates through metal organic chemical vapor deposition (MOCVD). The LEDs fabricated on the patterned substrates exhibit improved device performance compared with the conventional LED fabricated on planar substrates when growth and device fabricating conditions were the same. The light output powers of the LEDs fabricated on wet-patterned and ICP-patterned substrates were about 37% and 17% higher than that of LEDs on planar substrates at an injection current of 20 mA, respectively. The enhancement is attributable to the combination of the improvement of GaN-based epilayers quality and the improvement of the light extraction efficiency. (c) 2008 Elsevier Ltd. All rights reserved.

Fabrication of nano-patterned sapphire substrates and their application to the improvement of the performance of GaN-based LEDs

Nano-patterned sapphire substrates (NPSSs) were fabricated by a chemical wet etching technology using nano-sized SiO2 as masks. The NPSS was applied to improve the performance of GaN-based light emitting diodes (LEDs). GaN-based LEDs on NPSSs were grown by metal organic chemical vapour deposition. The characteristics of LEDs grown on NPSSs and conventional planar sapphire substrates were studied. The light output powers of the LEDs fabricated on NPSSs were considerably enhanced compared with that of the conventional LEDs grown on planar sapphire substrates.

Enhancement of the light output power of InGaN/GaN light-emitting diodes grown on pyramidal patterned sapphire substrates in the micro- and nanoscale

Sapphire substrates were patterned by a chemical wet etching technique in the micro- and nanoscale to enhance the light output power of InGaN/GaN light-emitting diodes (LEDs). InGaN/GaN LEDs on a pyramidal patterned sapphire substrate in the microscale (MPSS) and pyramidal patterned sapphire substrate in the nanoscale (NPSS) were grown by metalorganic chemical vapor deposition. The characteristics of the LEDs fabricated on the MPSS and NPSS prepared by wet etching were studied and the light output powers of the LEDs fabricated on the MPSS and NPSS increased compared with that of the conventional LEDs fabricated on planar sapphire substrates. In comparison with the planar sapphire substrate, an enhancement in output power of about 29% and 48% is achieved with the MPSS and NPSS at an injection current of 20 mA, respectively. This significant enhancement is attributable to the improvement of the epitaxial quality of GaN-based epilayers and the improvement of the light extraction efficiency by patterned sapphire substrates. Additionally, the NPSS is more effective to enhance the light output power than the MPSS. (c) 2008 American Institute of Physics.

The field emission properties of nonpolar a-plane n-type GaN films grown on nano-patterned sapphire substrates

Si-doped nonpolar a-plane GaN films were grown on nanopatterned sapphire substrates by a low-pressure metal organic chemical vapor deposition (MOCVD) system. The structure, morphology and field emission properties of the sample were studied by means of high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM), and field emission measurement. The XRD analysis shows that the sample is a nonpolar a-plane (11 (2) over bar0) GaN film. The field emission measurement shows that the nonpolar GaN films exhibit excellent field emission properties with a threshold emission field of as low as 10 V/mu m at a current density of 0.63 mu A/cm(2), and a high field emission current density of 74 mA/cm(2) at an applied field of 24 V/mu m. Moreover, the Fowler-Nordheirn plot of the sample fits a near linear relation. (C) 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Growth of nonpolar a-plane GaN on nano-patterned r-plane sapphire substrates

Sapphire substrates were nano-patterned by inductive coupled plasma etching process. Nonpolar a-plane GaN films were grown on planar and nano-patterned r-plane sapphire substrates by metal organic chemical vapor deposition. The anisotropic characteristic and the crystalline quality of the a-plane GaN films were studied through XRD rocking curves. The cross section and surface morphologies of the a-plane GaN films were studied using SEM and AFM measurements, respectively. The crystal quality and surface flatness of the nonpolar a-plane GaN were greatly improved through the usage of the nano-patterned r-plane sapphire substrates. (C) 2008 Elsevier B.V. All rights reserved.

Improved DC and RF performance of AlGaN/GaN HEMTs grown by MOCVD on sapphire substrates

High-quality AlGaN/GaN high electron mobility transistor (HEMT) structures were grown by metalorganic chemical vapor deposition (MOCVD) on 2-in. sapphire substrates. Two-dimensional electron gas (2DEG) mobility of 1410 cm(2)/Vs and concentration of 1.0X10(13) CM-2 are obtained at 295 K from the HEMT structures, whose average sheet resistance and sheet resistance uniformity are measured to be about 395 Omega/sq and 96.65% on 2-in. wafers, respectively. AlGaN/GaN HEMTs with 0.8 mu m gate length and 0.2 mm gate width were fabricated and characterized using the grown HEMT structures. Maximum current density of 0.9 A/ mm, peak extrinsic transconductance of 290 mS/mm, unity cutoff frequency (f(T)) of 20 GHz and maximum oscillation frequency (f(max) of 46 GHz are achieved. These results represent significant improvements over the previously fabricated devices with the same gate length, which are attributed to the improved performances of the MOCVD-grown HEMT structures. (c) 2005 Elsevier Ltd. All rights reserved.

Luminescence properties of multi-layer InGaN quantum dots grown on C- and R-plane sapphire substrates

In this study, we report comparative luminescence properties of multi-layer InGaN quantum dots grown on C- and R-plane sapphire substrates by metal organic chemical vapor deposition (MOCVD). High-density InGaN quantum dots (QDs) are formed on GaN templates by decreasing the growth temperature and increasing the adatom hopping-barrier through surface passivation. Atomic force microscopy (AFM) has been employed to estimate the size and height of these dots. Photoluminescence (PL) spectra recorded from (1120) InGaN QDs/(1102) sapphire show much stronger emission intensity compared to spectra recorded from (0001) InGaN QDs/(0001) sapphire. Due to the absence of strong spontaneous polarization and piezoelectric field, such (1150) InGaN QDs in the active layers would lead to high efficiency light emitting devices. (c) 2005 Elsevier B.V. All rights reserved.

ZnO nanostructures grown on AlN/sapphire substrates by MOCVD

ZnO nanorods and nanotubes are successful synthesized on AlN/sapphire substrates by metal-organic chemical vapour deposition (MOCVD). The different morphology and structure properties of ZnO nanorods and nanotubes are found to be allected by the AlN under-layer. The photoluminescence spectra show the optical properties of the ZnO nanorods and nanotubes, in which a blueshift of UV emission is observed and is attributed to the surface effect.

Polarized Raman scattering studies of nonpolar a-plane GaN films grown on r-plane sapphire substrates by MOCVD

Nonpolar (1120) a-plane GaN thin films were grown on r-plane (1102) sapphire substrates by low-pressure metal organic chemical vapor deposition (MOCVD). The stress characteristics of the a-plane GaN films were investigated by means of polarized Raman scattering spectra in backscattering configurations. The experimental results show that there are strong anisotropic in-plane stresses within the epitaxial a-plane GaN films by calculating the corresponding stress tensors. The temperature dependence of Raman scattering spectra was studied in the range from 100 K to 550 K. The measurements reveal that the Raman phonon frequencies decrease with increasing temperature. The temperature at which nonpolar a-plane GaN films are strain free is discussed. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Growth and characterization of 0.8-mu m gate length AlGaN/GaN HEMTs on sapphire substrates

AlGaN/GaN high electron mobility transistor (HEMT) structures were grown on 2 inch sapphire substrates by MOCVD, and 0.8-mu m gate length devices were fabricated and measured. It is shown by resistance mapping that the HEMT structures have an average sheet resistance of approximately 380 Omega/sq with a uniformity of more than 96%. The 1-mm gate width devices using the materials yielded a pulsed drain current of 784 mA/mm at V-gs=0.5 V and V-ds=7 V with an extrinsic transconductance of 200 mS/mm. A 20-GHz unity current gain cutoff frequency (f(T)) and a 28-GHz maximum oscillation frequency (f(max)) were obtained. The device with a 0.6-mm gate width yielded a total output power of 2.0 W/mm (power density of 3.33 W/mm) with 41% power added efficiency (PAE) at 4 GHz.

Epitaxial growth and characterization of SiC on C-plane sapphire substrates by ammonia nitridation

The growth of SiC epilayers on C-face (0 0 0 1) sapphire (alpha-Al2O3) has been performed using CVD method. We found that the quality of SiC epilayers has been improved through the nitridation of substrates by exposing them to ammonia ambient, as compared to growth on bare sapphire substrates. The single crystallinity of these layers was verified by XRD and double crystal XRD measurements. Atomic force microscopy was used to evaluate the surface morphology. Infrared reflectivity and Raman scattering measurement were carried out to investigate the phonon modes in the grown SiC. Detailed Raman analysis identified the 6H nature of the as-grown SiC films. (C) 2002 Elsevier Science B.V. All rights reserved.

In situ doping of 3C-SiC grown on (0001) sapphire substrates by LPCVD

The heteroepitaxial growth of n-type and p-type 3C-SiC on (0001) sapphire substrates has been performed with a supply of SiH4+C2H4+H-2 system by introducing ammonia (NH3) and diborane (B2H6) precursors, respectively, into gas mixtures. Intentionally incorporated nitrogen impurity levels were affected by changing the Si/C ratio within the growth reactor. As an acceptor, boron can be added uniformly into the growing 3C-SiC epilayers. Nitrogen-doped 3C-SiC epilayers were n-type conduction, and boron-doped epilayers were p-type and probably heavily compensated.

High-efficiency GaN-based blue LEDs grown on nano-patterned sapphire substrates for solid-state lighting - art. no. 684103

Nano-patterning sapphire substrates technique has been developed for nitrides light-emitting diodes (LEDs) growths. It is expected that the strain induced by the lattice misfits between the GaN epilayers and the sapphire substrates can be effectively accommodated via the nano-trenches. The GaN epilayers grown on the nano-patterned sapphire substrates by a low-pressure metal organic chemical vapor deposition (MOCVD) are characterized by means of scanning electron microscopy (SEM), high-resolution x-ray diffraction (HRXRD) and photoluminescence (PL) techniques. In comparison with the planar sapphire substrate, about 46% increment in device performance is measured for the InGaN/GaN blue LEDs grown on the nano-patterned sapphire substrates.