Reversible regeneration of molybdenum carbonyl species on an alumina thin film

The thin alumina film-supported metallic molybdenum model catalyst was prepared by thermal decomposition of MO(CO)6, and CO chemisorption on the catalyst was investigated in-situ by thermal desorption spectroscopy (TDS) and X-ray photoelectron spectroscopy (XPS). The results showed that a molybdenum-carbonyl-like species was formed on the alumina surface at low temperature by high coordination of CO with the surface metallic molybdenum nanoparticles, indicating a reversible regeneration of molybdenum carbonyl on the alumina surface. CO chemisorption on the model catalyst surface caused the Mo 3d XPS peak to shift toward higher binding energy. The formed molybdenum carbonyl species appeared at about 240 K in the TDS. The supported metallic molybdenum nanoparticles were quite different from the bulk molybdenum in chemical properties, which indicated a prominent particle-size effect of the clusters.

The formation of nanotubes and nanocoils of molybdenum disulphide

This work reports the successful realization of MoS2 nanotubes by a novel intercalation chemistry and hydrothermal treatment. An inorganic-organic precursor of hexadecylamine (HDA) and molybdenum disulphide (MoS2) were used in synthesizing the nanocomposite comprising laminar MoS2 with HDA intercalated in the interlaminar spacing. The formation of MoS2 nanotubes occurred during hydrothermal treatment (HT) by a self-organized rolling mechanism. The nanotubes were observed to have dimensions 2-12 µm in length and inner diameters typically in the range of 25-100 nm. We also report the formation of amorphous nanocoils of MoS2 obtained during similar procedures.

Functionalization of lamellar molybdenum disulphide nanocomposite with gold nanoparticles

This work explores the functionalization of an organic-inorganic MoS2 lamellar compound, prepared by a Chemical Liquid Deposition Method (CLD), that has an interlamellar distance of ~5.2 nm, using clusters of gold nanoparticles. The gold nanoparticles have a mean diameter of 1.2 nm, a stability of ~85 days, and a zeta potential measured to be ζ = -6.8 mV (solid). The nanoparticles are localized in the hydrophilic zones, defined by the presence of amine groups of the surfactant between the lamella of MoS2. SEM, TEM, EDAX and electron diffraction provide conclusive evidence of the interlamellar insertion of the gold nanoparticles in the MoS2.

Pressure induced anisotropy of electrical conductivity in polycrystalline molybdenum disulfide

Anisotropic specimens of MoS2 are obtained by pressing the microcrystalline powder into special die. This inelastic compression results in a rearrangement of the disulfide micro platelets observed by Atomic Force Microscopy and reflected in the macroscopic anisotropy in electrical conductivity in these samples. The conductivity measured parallel and perpendicular to the direction of applied pressure exhibits an anisotropy factor of ∼10 at 1 GPa. This behaviour of the conductivity as a function of applied pressure is explained as the result of the simultaneous influence of a rearrangement of the micro platelets in the solid and the change of the inter-grain distances.

Molybdenum hexacarbonyl and DBU reduction of nitro compounds under microwave irradiation

An ethanolic mixture of molybdenurn hexacarbonyl and DBU mediates the reduction of nitroarenes to the corresponding anilines in excellent yields in 15-30 minutes under microwave irradiation.

Electron impact ionization of hydrogen-like molybdenum ions

The electron impact ionization cross sections of hydrogen-like molybdenum ions were measured with an electron beam ion trap at the electron energies of 49.4, 64.4 and 79.6 keV The results are 2.82(22) x 10(-23), 3.13(29) x 10(-23) and 3.23(51) x 10(-23) cm(2), respectively. These results are compared with the experimental results measured previously. The agreement with the results obtained with, scaling formulae is also discussed.