Phase transformations and metastable phase equilibria in Al-Ge alloy

In this paper the results of a detailed investigation on the metastable phase relations in undercooled as well as rapidly solidified Al---Ge alloys containing 2–50 at.% Ge are reported. Data obtained on the structure and morphology of phases enable us to arrive at the phase relations and transformation processes occurring in undercooled and rapidly quenched melts of this system. These results are explained with the help of a metastable phase diagram consisting of a peritectic and eutectic reaction involving metastable phases.

Origin of anomalous photoinduced transformations in amorphous Ge-based chalcogenide thin films

Anomalous photoinduced transformations in amorphous Ge-based chalcogenide thin films are established as being due to photochemical modification of the surfaces, by photoemission studies. Mass measurements indicate that the giant thickness reduction on irradiation is predominantly due to the loss of material as a result of photogenerated volatile high vapor pressure oxide fractions on the surface. This extrinsic contribution contradicts the models of the phenomenon proposed so far, which are based purely on intrinsic structural transformations.

XPS and XAES studies of surface segregation and oxidation of Cu-Ge alloy

Surface segregation of Ge is seen in the Cu-5at%Ge alloy with an activation enthalpy equal to 17 kJ/mol. Oxidation of the alloy in the temperature range 400 to 600 K shows the formation of Cu2O and GeO which on further heating in vacuum at 650 K converts to GeO2 with the reduction of Cu2O to Cu.

Evidence for a new metastable crystalline compound in Ge---Te system

Pressure dependence of the electrical resistivity of bulk, melt quenched GexTe100−x glasses (15 less-than-or-equals, slant x less-than-or-equals, slant 28) has been studied up to 8GPa pressure. All the glasses exhibit a sharp, discontinuous glass to crystal transition under pressure. The high pressure crystalline phases are identified to have a face centered cubic structure. The value of the cell constant is 0.779nm for 15 less-than-or-equals, slant x less-than-or-equals, slant 17, 0.642nm for x=20 and 0.55lnm for 22 ≤ x ≤ 28 samples respectively. The cell constants of the high pressure crystalline phases suggest the possible existance of a new metastable crystalline compound in the Ge---Te system with F.C.C. structure and cell constant equal to 1.109nm as reported by Moore et al.

Plan Krivorogskogo okruga Kazankovskogo raĭona na uchastok kolfonda Nº 35 otgranichennogo v pori︠a︡dke ustroĭstva kolonizat︠s︡ionnogo fonda 8ĭ partieĭ po ustroĭstvu kolfondov na i︠u︡ge Ukrainy sogolasno plana zemleustroitelʻnykh rabot na 1926 god

Digital image

A study of the deformation slip lines in quenched and aged Al-2% Ge alloy

Optical microscopy has been employed to observe the slip lines in deformed Al-2% Ge alloy samples. Slip lines have been observed in the as-quenched, partially-aged, fully-aged and over-aged states. The lines tend to traverse fairly straight paths in the case of quenched and partially-aged conditions. Fully-aged samples also reveal such straight running lines when tested at low-temperatures. However, the density of the lines generally decreases as the peak-aged state is approached. These results are in agreement with the idea that thermally activated shearing of the precipitates is occurring in the alloy aged up to peak-hardness. The irregular lines for the over-aged specimens support the view that the moving dislocations by-pass the precipitates during deformation. The influence of test-temperature on the appearance of slip traces has been briefly examined.

Rapid quenching and glass formation in chalcogenide glasses: Preparation and properties of Ge-As-Te glasses over an extended composition ranges

In Ge-As-Te system, the glass forming region determined by normal melt quenching method has two regions (GFR I and GFR II) separated by few compositions gap. With a simple laboratory built twin roller apparatus, we have succeeded in preparing Ge7.5AsxTe92.5-x glasses over extended composition ranges. A distinct change in T-g is observed at x = 40, exactly at which the separation of the glass forming regions occur indicating the changes in the connectivity and the rigidity of the structural network. The maximum observed in glass transition (T-g) at x = 55 corresponding to the average coordination number (Z(av)) = 2.70 is an evidence for the shift of the rigidity percolation threshold (RPT) from Z(av) = 2.40 as predicted by the recent theories. The glass forming tendency (K-gl) and Delta T (=T-c-T-g) is low for the glasses in the GFR I and high for the glasses in the GFR II.

Defects in the IFT-B component IFT172 cause Jeune and Mainzer-Saldino syndromes in humans

Intraflagellar transport (IFT) depends on two evolutionarily conserved modules, subcomplexes A (IFT-A) and B (IFT-B), to drive ciliary assembly and maintenance. All six IFT-A components and their motor protein, DYNC2H1, have been linked to human skeletal ciliopathies, including asphyxiating thoracic dystrophy (ATD; also known as Jeune syndrome), Sensenbrenner syndrome, and Mainzer-Saldino syndrome (MZSDS). Conversely, the 14 subunits in the IFT-B module, with the exception of IFT80, have unknown roles in human disease. To identify additional IFT-B components defective in ciliopathies, we independently performed different mutation analyses: candidate-based sequencing of all IFT-B-encoding genes in 1,467 individuals with a nephronophthisis-related ciliopathy or whole-exome resequencing in 63 individuals with ATD. We thereby detected biallelic mutations in the IFT-B-encoding gene IFT172 in 12 families. All affected individuals displayed abnormalities of the thorax and/or long bones, as well as renal, hepatic, or retinal involvement, consistent with the diagnosis of ATD or MZSDS. Additionally, cerebellar aplasia or hypoplasia characteristic of Joubert syndrome was present in 2 out of 12 families. Fibroblasts from affected individuals showed disturbed ciliary composition, suggesting alteration of ciliary transport and signaling. Knockdown of ift172 in zebrafish recapitulated the human phenotype and demonstrated a genetic interaction between ift172 and ift80. In summary, we have identified defects in IFT172 as a cause of complex ATD and MZSDS. Our findings link the group of skeletal ciliopathies to an additional IFT-B component, IFT172, similar to what has been shown for IFT-A.

Effect of indium doping on the electrical switching behaviour of Ge-Te glasses

Bulk Ge15Te85-xInx (1 <= x <= 11) series of glasses have been found to exhibit a threshold switching behaviour for an input current of 2 mA. An initial decrease is seen in the switching voltages (V-T) with the addition of indium, which is due to the higher metallicity of indium. An increase is seen in V-T above 3 at.% of indium, which proceeds until 8 at.%, with a change in slope (lower to higher) seen around 7 at.%. Beyond x = 8, a reversal in trend is exhibited in the variation of V-T, with a well-defined minimum around x = 9 at.%. Based on the composition dependence of V-T, it is proposed that Ge15Te85-xInx glasses exhibit an extended rigidity percolation threshold. The composition, x = 3, at which the V-T starts to increase and the composition, x = 7, at which a slope change is exhibited correspond to the onset and completion, respectively, of the extended stiffness transition. Thermal studies and photoconductivity e85-xInx glasses. In addition, the minimum seen in V-T at x = 9 is associated with the chemical threshold (CT) of this glassy system.

Electrical switching and in situ Raman scattering studies on the set-reset processes in Ge-Te-Si glass

Bulk Ge15Te83Si2 glass has been found to exhibit memory-type switching for 1 mA current with a threshold electric field of 7.3 kV/cm. The electrical set and reset processes have been achieved with triangular and rectangular pulses, respectively, of 1 mA amplitude. In situ Raman scattering studies indicate that the degree of disorder in Ge15Te83Si2 glass is reduced from off to set state. The local structure of the sample under reset condition is similar to that in the off state. The Raman results are consistent with the switching results which indicate that the Ge15Te83Si2 glass can be set and reset easily. (C) 2007 American Institute of Physics.

Evidence for a thermally reversing window in bulk Ge-Te-Si glasses revealed by alternating differential scanning calorimetry

Experiments on Ge15Tc85-xSix glasses (2 <= x <= 12) using alternating differential scanning calorimetry (ADSC) indicate that these glasses exhibit one glass transition and two crystallization reactions upon heating. The glass transition temperature has been found to increase almost linearly with silicon content, in the entire composition tie-line. The first crystallization temperature (T-cl) exhibits an increase with silicon content for x<5; T-cl remains almost a constant in the composition range 5 < x <= 10 and it increases comparatively more sharply with silicon content thereafter. The specific heat change (Delta C-p) is found to decrease with an increase in silicon content, exhibiting a minimum at x=5 (average coordination number, (r) = 2.4); a continuous increase is seen in Delta C-p with silicon concentration above x = 5. The effects seen in the variation with composition of T-cl and Delta C-p at x=5, are the specific signatures of the mean-field stiffness threshold at (r) = 2.4. Furthermore, a broad trough is seen in the enthalpy change (Delta H-NR), which is indicative of a thermally reversing window in Ge15Te85-xSix glasses in the composition range 2 <= x <= 6 (2.34 <= (r) <= 2.42).

Low-temperature Er3+ emission in Ge-S-Ga glasses excited by host absorption

The photoluminescence (PL) of a series of (GeS2)(80)(Ga2S3)(20) glasses doped with different amounts of Er (0.17, 0.35, 0.52, 1.05 and 1.39 at.%) at 77 and 4.2 K has been studied. The influence of the temperature on the emission cross-section of the PL bands at -> 1540, 980 and 820 nm under host excitation has been defined. A quenching effect of the host photoluminescence has been established from the compositional dependence of the PL intensity. It has been found that the present Er3+-doped Ge-S-Ga glasses posses PL lifetime values about 3.25 ms. (C) 2007 Elsevier B.V. All rights reserved.

Structure and bonding of MCB5H7 and its sandwiched dimer CB5H6M–MCB5H6 (M = Si, Ge, Sn): Isomer stability and preference for slip distorted structure

We find sandwiched metal dimers CB5H6M–MCB5H6 (M = Si, Ge, Sn) which are minima in the potential energy surface with a characteristic M–M single bond. The NBO analysis and the M–M distances (Å) (2.3, 2.44 and 2.81 for M = Si, Ge, Sn) indicate substantial M–M bonding. Formal generation of CB5H6M–MCB5H6 has been studied theoretically. Consecutive substitution of two boron atoms in B7H−27 by M (Si, Ge, Sn) and carbon, respectively followed by dehydrogenation may lead to our desired CB5H6M–MCB5H6. We find that the slip distorted geometry is preferred for MCB5H7 and its dehydrogenated dimer CB5H6M–MCB5H6. The slip-distortion of M–M bond in CB5H6M–MCB5H6 is more than the slip distortion of M–H bond in MCB5H7. Molecular orbital analysis has been done to understand the slip distortion. Larger M–M bending (CB5H6M–MCB5H6) in comparison with M–H bending (MCB5H7) is suspected to be encouraged by stabilization of one of the M–M π bonding MO’s. Preference of M to occupy the apex of pentagonal skeleton of MCB5H7 over its icosahedral analogue MCB10H11 has been observed.