Catalysts for H2 production

The research of new catalysts for the hydrogen production described in this thesis was inserted within a collaboration of Department of Industrial Chemistry and Materials of University of Bologna and Air Liquide (Centre de Recherche Claude-Delorme, Paris). The aim of the work was focused on the study of new materials, active and stable in the hydrogen production from methane, using either a new process, the catalytic partial oxidation (CPO), or a enhanced well-established process, the steam methane reforming (SMR). Two types of catalytic materials were examined: 1) Bulk catalysts, i.e. non-supported materials, in which the active metals (Ni and/or Rh) are stabilized inside oxidic matrix, obtained from perovskite type compounds (PVK) and from hydrotalcite type precursors (HT); 2) Structured catalysts, i.e. catalysts supported on materials having high thermal conductivity (SiC and metallic foams). As regards the catalytic partial oxidation, the effect of the metal (Ni and/or Rh), the role of the metal/matrix ratio and the matrix formulation of innovative catalysts obtained from hydrotalcite type precursors and from perovskites were examined. In addition, about steam reforming process, the study was carried out first on commercial type catalysts, examining the deactivation in industrial conditions, the role of the operating conditions and the activity of different type of catalysts. Then, innovative materials bulk (PVK and HT) and structured catalysts (SiC and metallic foam) were studied and a new preparation method was developed.

Application of FTIR microscopy to cultural heritage materials

Research in art conservation has been developed from the early 1950s, giving a significant contribution to the conservation-restoration of cultural heritage artefacts. In fact, only through a profound knowledge about the nature and conditions of constituent materials, suitable decisions on the conservation and restoration measures can thus be adopted and preservation practices enhanced. The study of ancient artworks is particularly challenging as they can be considered as heterogeneous and multilayered systems where numerous interactions between the different components as well as degradation and ageing phenomena take place. However, difficulties to physically separate the different layers due to their thickness (1-200 µm) can result in the inaccurate attribution of the identified compounds to a specific layer. Therefore, details can only be analysed when the sample preparation method leaves the layer structure intact, as for example the preparation of embedding cross sections in synthetic resins. Hence, spatially resolved analytical techniques are required not only to exactly characterize the nature of the compounds but also to obtain precise chemical and physical information about ongoing changes. This thesis focuses on the application of FTIR microspectroscopic techniques for cultural heritage materials. The first section is aimed at introducing the use of FTIR microscopy in conservation science with a particular attention to the sampling criteria and sample preparation methods. The second section is aimed at evaluating and validating the use of different FTIR microscopic analytical methods applied to the study of different art conservation issues which may be encountered dealing with cultural heritage artefacts: the characterisation of the artistic execution technique (chapter II-1), the studies on degradation phenomena (chapter II-2) and finally the evaluation of protective treatments (chapter II-3). The third and last section is divided into three chapters which underline recent developments in FTIR spectroscopy for the characterisation of paint cross sections and in particular thin organic layers: a newly developed preparation method with embedding systems in infrared transparent salts (chapter III-1), the new opportunities offered by macro-ATR imaging spectroscopy (chapter III-2) and the possibilities achieved with the different FTIR microspectroscopic techniques nowadays available (chapter III-3). In chapter II-1, FTIR microspectroscopy as molecular analysis, is presented in an integrated approach with other analytical techniques. The proposed sequence is optimized in function of the limited quantity of sample available and this methodology permits to identify the painting materials and characterise the adopted execution technique and state of conservation. Chapter II-2 describes the characterisation of the degradation products with FTIR microscopy since the investigation on the ageing processes encountered in old artefacts represents one of the most important issues in conservation research. Metal carboxylates resulting from the interaction between pigments and binding media are characterized using synthesised metal palmitates and their production is detected on copper-, zinc-, manganese- and lead- (associated with lead carbonate) based pigments dispersed either in oil or egg tempera. Moreover, significant effects seem to be obtained with iron and cobalt (acceleration of the triglycerides hydrolysis). For the first time on sienna and umber paints, manganese carboxylates are also observed. Finally in chapter II-3, FTIR microscopy is combined with further elemental analyses to characterise and estimate the performances and stability of newly developed treatments, which should better fit conservation-restoration problems. In the second part, in chapter III-1, an innovative embedding system in potassium bromide is reported focusing on the characterisation and localisation of organic substances in cross sections. Not only the identification but also the distribution of proteinaceous, lipidic or resinaceous materials, are evidenced directly on different paint cross sections, especially in thin layers of the order of 10 µm. Chapter III-2 describes the use of a conventional diamond ATR accessory coupled with a focal plane array to obtain chemical images of multi-layered paint cross sections. A rapid and simple identification of the different compounds is achieved without the use of any infrared microscope objectives. Finally, the latest FTIR techniques available are highlighted in chapter III-3 in a comparative study for the characterisation of paint cross sections. Results in terms of spatial resolution, data quality and chemical information obtained are presented and in particular, a new FTIR microscope equipped with a linear array detector, which permits reducing the spatial resolution limit to approximately 5 µm, provides very promising results and may represent a good alternative to either mapping or imaging systems.

Cluster-derived Gold/Iron catalysts for environmental applications

During the last years we assisted to an exponential growth of scientific discoveries for catalysis by gold and many applications have been found for Au-based catalysts. In the literature there are several studies concerning the use of gold-based catalysts for environmental applications and good results are reported for the catalytic combustion of different volatile organic compounds (VOCs). Recently it has also been established that gold-based catalysts are potentially capable of being effectively employed in fuel cells in order to remove CO traces by preferential CO oxidation in H2-rich streams. Bi-metallic catalysts have attracted increasing attention because of their markedly different properties from either of the costituent metals, and above all their enhanced catalytic activity, selectivity and stability. In the literature there are several studies demostrating the beneficial effect due to the addition of an iron component to gold supported catalysts in terms of enhanced activity, selectivity, resistence to deactivation and prolonged lifetime of the catalyst. In this work we tried to develop a methodology for the preparation of iron stabilized gold nanoparticles with controlled size and composition, particularly in terms of obtaining an intimate contact between different phases, since it is well known that the catalytic behaviour of multi-component supported catalysts is strongly influenced by the size of the metal particles and by their reciprocal interaction. Ligand stabilized metal clusters, with nanometric dimensions, are possible precursors for the preparation of catalytically active nanoparticles with controlled dimensions and compositions. Among these, metal carbonyl clusters are quite attractive, since they can be prepared with several different sizes and compositions and, moreover, they are decomposed under very mild conditions. A novel preparation method was developed during this thesis for the preparation of iron and gold/iron supported catalysts using bi-metallic carbonyl clusters as precursors of highly dispersed nanoparticles over TiO2 and CeO2, which are widely considered two of the most suitable supports for gold nanoparticles. Au/FeOx catalysts were prepared by employing the bi-metallic carbonyl cluster salts [NEt4]4[Au4Fe4(CO)16] (Fe/Au=1) and [NEt4][AuFe4(CO)16] (Fe/Au=4), and for comparison FeOx samples were prepared by employing the homometallic [NEt4][HFe3(CO)11] cluster. These clusters were prepared by Prof. Longoni research group (Department of Physical and Inorganic Chemistry- University of Bologna). Particular attention was dedicated to the optimization of a suitable thermal treatment in order to achieve, apart from a good Au and Fe metal dispersion, also the formation of appropriate species with good catalytic properties. A deep IR study was carried out in order to understand the physical interaction between clusters and different supports and detect the occurrence of chemical reactions between them at any stage of the preparation. The characterization by BET, XRD, TEM, H2-TPR, ICP-AES and XPS was performed in order to investigate the catalysts properties, whit particular attention to the interaction between Au and Fe and its influence on the catalytic activity. This novel preparation method resulted in small gold metallic nanoparticles surrounded by highly dispersed iron oxide species, essentially in an amorphous phase, on both TiO2 and CeO2. The results presented in this thesis confirmed that FeOx species can stabilize small Au particles, since keeping costant the gold content but introducing a higher iron amount a higher metal dispersion was achieved. Partial encapsulation of gold atoms by iron species was observed since the Au/Fe surface ratio was found much lower than bulk ratio and a strong interaction between gold and oxide species, both of iron oxide and supports, was achieved. The prepared catalysts were tested in the total oxidation of VOCs, using toluene and methanol as probe molecules for aromatics and alchols, respectively, and in the PROX reaction. Different performances were observed on titania and ceria catalysts, on both toluene and methanol combustion. Toluene combustion on titania catalyst was found to be enhanced increasing iron loading while a moderate effect on FeOx-Ti activity was achieved by Au addition. In this case toluene combustion was improved due to a higher oxygen mobility depending on enhanced oxygen activation by FeOx and Au/FeOx dispersed on titania. On the contrary ceria activity was strongly decreased in the presence of FeOx, while the introduction of gold was found to moderate the detrimental effect of iron species. In fact, excellent ceria performances are due to its ability to adsorb toluene and O2. Since toluene activation is the determining factor for its oxidation, the partial coverage of ceria sites, responsible of toluene adsorption, by FeOx species finely dispersed on the surface resulted in worse efficiency in toluene combustion. Better results were obtained for both ceria and titania catalysts on methanol total oxidation. In this case, the performances achieved on differently supported catalysts indicate that the oxygen mobility is the determining factor in this reaction. The introduction of gold on both TiO2 and CeO2 catalysts, lead to a higher oxygen mobility due to the weakening of both Fe-O and Ce-O bonds and consequently to enhanced methanol combustion. The catalytic activity was found to strongly depend on oxygen mobility and followed the same trend observed for catalysts reducibility. Regarding CO PROX reaction, it was observed that Au/FeOx titania catalysts are less active than ceria ones, due to the lower reducibility of titania compared to ceria. In fact the availability of lattice oxygen involved in PROX reaction is much higher in the latter catalysts. However, the CO PROX performances observed for ceria catalysts are not really high compared to data reported in literature, probably due to the very low Au/Fe surface ratio achieved with this preparation method. CO preferential oxidation was found to strongly depend on Au particle size but also on surface oxygen reducibility, depending on the different oxide species which can be formed using different thermal treatment conditions or varying the iron loading over the support.

Untersuchung der Ordnung und Diffusion von Polymerdispersionen bei ihrer Verfilmung

Im Rahmen dieser Arbeit wurde die, für industrielle Applikationen sehr wichtige, Trocknung und Verfilmung von Latexdispersionen untersucht. Unter der Verfilmung wird in diesem Zusammenhang allgemein der Übergang einer Polymerdispersion in einen transparenten, mechanisch stabilen Polymerfilm während ihrer Trocknung verstanden. Für die Untersuchungen wurden schwerpunktmäßig Streumethoden verwendet. Die Untersuchungen haben gezeigt, daß die Streuung eine besonders geeignete Methode zur Untersuchung der Verfilmung ist, die in Abhängigkeit des beobachteten Streuvektorbereichs, der verwendeten Strahlung, der Probenpräparation und des resultierenden Kontrasts eine Vielzahl unterschiedlicher Informationen über die Verfilmung in ihren verschiedenen Phasen liefert. Von besonderem Interesse war es, den prinzipiellen Verlauf der Verfilmung bei den heterogen trocknenden Reinacrylatlatices zu untersuchen. Dazu wurde mit Hilfe der Röntgenultrakleinwinkelstreuung gezielt der Zustand der Partikel in den einzelnen Phasen der heterogen trocknenden Proben beobachtet. Mit Hilfe der Neutronenkleinwinkelstreuung konnte das Verhalten des Emulgators während der Verfilmung und dessen Verteilung im resultierenden Film genauer untersucht werden. Die Röntgenkleinwinkelstreuung erlaubte eine eingehende Untersuchung der Kristallisation des Emulgators im trockenen Film. Geeignete Kontrastierung durch gezielte Deuterierung ermöglichte die Untersuchung des Comonomereinflusses auf die Interdiffusion von Latexpartikeln mit Neutronenkleinwinkelstreuung. Aus den Meßergebnissen wurde ein Modell zur heterogenen Trocknung von Latexdispersionen entwickelt, das den Ablauf der Verfilmung in einem konsistenten Bild zusammenfaßt.

Strukturelle und molekulare Charakterisierung des Asialoglykoprotein-Rezeptors aus humaner Leber

Der Asialoglykoprotein-Rezeptor (ASGPR) vermittelt als integraler Bestandteil der Leberzellmembran die Endozytose von zirkulierenden Asialoglykoproteinen. Ziele dieser Arbeit waren proteinchemische Untersuchungen von funktionellem ASGPR aus humaner Leber aufgrund einer verbesserten Präparationsmethode und die rekombinante Darstellung der beiden Untereinheiten H1 und H2. In der denaturierenden SDS-PAGE erschienen H1 und H2 überwiegend als Monomere bei 46 und 50kD; nach Deglykosylierung ergaben sich Banden bei 34 und 32kD, wonach der Glykosidanteil etwa 28% beträgt. In der nicht-denaturierenden Größenausschluß-Chromatographie wurden im nativen ASGPR ausschließlich Trimere und Dimere gefunden. In Gegenwart von 2-Mercaptoethanol konnten funktionell eine aktive von einer nicht-aktiven Fraktion getrennt werden, wobei H2 in der nicht-aktiven Fraktion angereichert war, während sich H1 zu etwa gleichen Teilen in beiden Fraktionen befand. Durch zweidimensionale Auftrennung des deglykosylierten Rezeptors wurden auf Proteinebene vier Isoformen von H1 und zwei von H2 mit unterschiedlichen pI-Werten identifiziert. Der Vergleich von funktionellem ASGPR aus normaler Leber und den hepatischen Tumorzellinien HepG2 und Huh7 in der SDS-PAGE brachte Größenunterschiede von etwa sechs und vier Kilodalton hervor. Bei H1 konnte dies auf einen höheren Glykosylierungsgrad zurückgeführt werden, während H2 auch nach Behandlung mit N-GlykosidaseF ein größeres Molekulargewicht aufwies. Ein Antikörper gegen das Insertionspeptid im cytoplasmatischen Bereich einer Splice-Variante von H2 zeigte eine deutlich erhöhte Expression von H2 mit Insertion in Huh7-Zellen gegenüber natürlichem ASGPR. Da bisherige Kenntnisse über den humanen ASGPR vorwiegend aus kultivierten Hepatomzelllinien stammen, scheinen sie nicht ohne weiteres auf die Situation in normaler Leber übertragbar. Die Präparation von funktionellem H1 aus transfizierten cos7- und 293-Zellen führte zum gleichen Bandenmuster wie beim natürlichen ASGPR. Mit einem Enzymimmunoassay wurde die Eignung von rekombinantem H1 zur Detektion von Antikörpern gegen ASGPR in 177 von 178 Patientenseren gezeigt. Da durch Präinkubation mit rekombinantem Antigen die Reaktivität mit natürlichem Rezeptor inhibiert werden konnte, trägt H1 hauptsächlich die antigenen Stellen des ASGPR.

Interaktions- und Aggregationsverhalten von Nanopartikeln in Blutserum

Das Interesse an nanopartikulären Wirkstoffsystemen steigt sowohl auf universitärer als auch auf industrieller Seite stetig an. Da diese Formulierungen meist intravenös verabreicht werden, kommt es folglich zu einem direkten Kontakt der Nanopartikel mit den Blutbestandteilen. Adsorption von Plasma Proteinen kann eine deutliche Veränderung der charakteristischen Eigenschaften des Systems induzieren, was dann Wirkungsweise sowie Toxizität stark beinflussen kann. Derzeit findet die Charakterisierung nanopartikulärer Wirkstoffsysteme vor der in vivo Applikation in Pufferlösungen mit physiologischem Salzgehalt statt, es ist jedoch kaum etwas bekannt über deren Wechselwirkungen mit komplexen Proteinmischungen wie sie im Blutserum oder –plasma vorliegen. rnMittels dynamischer Lichtstreuung (DLS) wurde eine einfache und reproduzierbare Methode entwickelt um die Aggregatbildung zwischen Nanopartikeln, Polymeren oder verschiedenen Wirkstoff-Konjugaten in humanem Blutserum zu untersuchen. Die Anwendbarkeit dieser Methode wurde durch Untersuchung verschiedener potentieller Nanotherapeutika (z.B. Polystyrol-Nanokapseln, Liposomen, amphiphile Blockcopolymere und Nanohydrogele) bezüglich ihrer Aggregation in humanem Blutserum mittels DLS gezeigt und teilweise mit aktuellen in vivo Experimenten verglichen. rnDarüber hinaus wurden größeneinheitliche Liposomen, basierend auf Disteraoylphosphatidylcholin, Cholesterol und einem Spermin-Tensid, hergestellt. Die Einkapselung von siRNA ist, je nach Präparationsmethode, mit Einkapselungseffizienzen von 40-75% möglich. Nach detaillierter Charakterisierung der Liposomen wurden diese ebenfalls bezüglich ihres Aggregationsverhaltens in humanem Blutserum untersucht. Unbeladene Liposomen aggregieren nicht mit Komponenten des Serums. Je nach Beladungsprotokoll können aggregierende sowie nicht aggregierende Liposomen-siRNA Komplexe hergestellt werden. rnWeiterhin wurden, zur Identifikation der Aggregation induzierenden Serumkomponenten, verschiedenen Serumsfraktionierungstechniken erfolgreich angewendet. Albumin, IgG, und Lipoproteine (VLDL, LDL) sowie verschiedene Proteinmischungen konnten isoliert und für weitere Aggregationsstudien mittels DLS verwendet werden. Für einige ausgesuchte Systeme konnten die Interaktionspartner identifiziert werden. rnDie Korrelation des Aggregationsverhaltens mit den strukturellen sowie funktionellen Eigenschaften der untersuchten Nanopartikel führt zu dem generellen Ergebnis, dass leicht negativ und leicht positiv bis neutrale Partikel eine geringe Tendenz zur Aggregation in Serum haben. Auch zwitterionische Substanzen zeigen eine hohe Serumstabilität. Hingegen aggregieren stark positiv und negativ geladene Partikel vermehrt.rn

Liquid crystalline cellulose derivatives for mirrorless lasing

In this thesis cholesteric films made of liquid crystalline cellulose derivatives with improved optical properties were prepared. The choice of the solvent, hydrogen bond influencing additives, the synthetic realization of a very high degree of substitution on the cellulosic polymer and the use of mechanical stirring at the upper concentration limit of the liquid crystalline range were the basis for an improved alignment of the applied cellulose tricarbamates. In combination with a tuned substrate treatment and film preparation method, cholesteric films were obtained, with optical properties that were theoretically predicted and only known from low molecular weight liquid crystals so far. Subsequent polymerization allowed a permanent fixing of the alignment and the fabrication of free standing and insensitive films.rnThe incorporation of inorganic nanorods into the cholesteric host material was mediated with tailored block copolymers, available via controlled radical polymerization methods. In addition to the shape match between the rodlike mesogens of the host and the nanorods it was possible to increase the miscibility of both materials. Nevertheless, the size of the nanorods, in comparison to the mesogens, in these densely packed liquid crystalline phases as well as their long equilibration times were the reasons for phase separation. Nanorods are, in principle, valuable substitutes for organics, but their utilization in cellulosic CLC was not to be combined with a high quality alignment of the cholesteric structure.rnA swelling process of polymerized films in a dye solution or dissolving dyes in non-polymerized CLC was used for incorporation of the organic chromophores. With the first method the CLC could be aligned and polymerized without any disturbance due to dye molecules. The optical properties of dye and CLC were matched, with regard to mirrorless lasing devices. The dye was optically excited and laser emission supported by the cholesteric cavity was obtained. The polarization and wavelength of the emitted radiation as well as its bandwidth, the obtained interference pattern and threshold behavior of the emission proofed the feedback mechanism that was not believed to be realizable in liquid crystalline polymers. rnUtilization of a microfluidic co-flow injection device enabled us to transfer the properties of cellulosic CLC from the planar film shape to spherical micrometer sized particles. The pure material yielded particles with distorted mesogen alignment similar to films prepared by capillary flow. Dilution of the CLC with a solvent that migrated into the carrier phase during particle preparation provided the basis for particles with well ordered areas. rnAlthough cellulose derivatives were known for their liquid crystalline behavior for decades and synthesized in mass production, their application as feedback material was affected by bad optical properties. In comparison to low molar mass compounds, the low degree of order in the CLC phase was the cause. With the improved material, defined lasing emission was shown and characterized. Derivatives of cellulose are desirable materials, because, as a renewable resource, they are available in large amounts for a low price and need only simple derivatization reactions. The fabrication of CLC films with tunable lasing emission, for which this thesis can provide a starting point, is in good agreement with today's requirements of modern technology and its miniaturization.rn

The fabrication and application of semi-crystalline and thermoset-thermoplastic composite colloidal particles with well-defined microstructures

Die Zielsetzung der Arbeit besteht darin, neue Ansätze zur Herstellung strukturierter Kompositpartikel in wässrigem Medium zu entwickeln, welche als die Bildung genau definierter heterogener Strukturen in Kolloidsystemen angesehen werden können. Im Allgemeinen wurden zwei verschiedene Herangehensweisen entwickelt, die sich aufgrund des Ursprungs der gebildeten heterogenen Strukturen unterscheiden: Heterogenität oder Homogenität. Der Erste Ansatz basiert auf der Aggregation heterogener Phasen zur Bildung strukturierter Kolloidpartikel mit Heterogenität in der zugrunde liegenden Chemie, während der Zweite Ansatz auf der Bildung heterogener Phasen in Kolloidpartikeln aus homogenen Mischungen heraus durch kontrollierte Phasenseparation beruht.rnIm Detail beschäftigt sich der erste Teil der Dissertation mit einer neuen Herstellungsmethode für teilkristalline Komposit-Kolloidpartikel mit hoher Stabilität basierend auf der Aggregation flüssiger Monomertropfen an teilkristalline Polyacrylnitrilpartikel. Nach der Aggregation wurden hochstabile Dispersionen bestehend aus strukturierten, teilkristallinen Kompositpartikeln durch freie radikalische Polymerisation erhalten, während ein direktes Mischen der PAN Dispersionen mit Methacrylat-Polymerdispersionen zur unmittelbaren Koagulation führte. In Abhängigkeit von der Glastemperatur des Methacrylatpolymers führt die anschließende freie radikalische Polymerisation zur Bildung von Rasberry oder Kern-Schale Partikeln. Die auf diese Weise hergestellten Partikel sind dazu in der Lage, kontinuierliche Filme mit eingebetteten teilkristallinen Phasen zu bilden, welche als Sauerstoffbarriere Anwendung finden können.rnDer zweite Teil der Dissertation beschreibt eine neue Methode zur Herstellung strukturierter Duroplast-Thermoplast Komposit-Kolloidpartikel. Die Bildung eines Duroplastnetzwerks mit einer thermoplastischen Hülle wurde in zwei Schritten durch verschiedene, separate Polymerisationsmechanismen erreicht: Polyaddition und freie radikalische Polymerisation. Es wurden stabile Miniemulsionen erhalten, welche aus Bisphenol-F basiertem Epoxidharz, Phenalkamin-basiertem Härter und Vinlymonomere bestehen. Sie wurden durch Ultraschall mit nachfolgender Härtung bei verschiedenen Temperaturen als sogenannte Seed-Emulsionen hergestellt. Weitere Vinylmonomere wurden hinzugegeben und nachfolgend polymerisiert, was zur Bildung von Kern-Schale, beziehungsweise Duroplast-Thermoplast Kolloidpartikeln führte. Dabei findet in beiden Fällen zwischen der duroplastischen und der thermoplastischen Phase eine chemisch induzierte Phasenseparation statt, welche essenziell für die Bildung heterogener Strukturen ist. Die auf diese Weise hergestellten Kompositpartikel sind dazu in der Lage, transparente Filme zu bilden, welche unter geeigneten Bedingungen deutlich verbesserte mechanische Eigenschaften im Vergleich zu reinen Duroplastfilmen bereitstellen.rn

Farming strategy of African smallholder farmers in transition from traditional to alternative agriculture : the case of the Nupe in central Nigeria

It is worthwhile to understand farming strategies of smallholder farmers in sub-Saharan Africa, especially those of farmers who are in transition from traditional to alternative agriculture in terms of adoption of innovative technologies. In a case study of inland valleys in central Nigeria, we investigated the farming strategy of Nupe farmers who have a long-term tradition of wet rice cultivation and indigenous methods of land preparation for soil, water and weed management. In this region, a new method of land preparation has recently been introduced along with a recommendation to use improved seeds and chemical fertilizers. Our findings reveal that Nupe farmers directly sow traditional seeds and apply a marginal amount of fertilizer to paddy plots prepared by labor-saving methods on drought-prone hydromorphic valley fringes and flood-susceptible valley bottoms, whereas they preferentially transplanted improved seedlings and applied a relatively large quantity of fertilizer to paddy fields prepared by a labor-intensive and mechanized method on a valley position where they can access to optimum water condition (less risky against the drought and flood).

Unsaturated polyester-poly(epsilon-caprolactone) hybrid nanocomposites: Thermal-mechanical properties

This paper reports on the thermal behavior and mechanical properties of nanocomposites based on unsaturated polyester resin (UP) modified with poly(ɛ-caprolactone) (PCL) and reinforced with an organically modified clay (cloisite 30B). To optimize the dispersion of 30B and the mixing of PCL in the UP resin, two different methods were employed to prepare crosslinked UP–PCL-30B hybrid nanocomposites. Besides, two samples of poly(ɛ-caprolactone) of different molecular weight (PCL2: Mn = 2.103g.mol−1 and PCL50: Mn = 5.104g.mol−1) were used at several concentrations (4, 6, 10 wt%). The 30B concentration was 4 wt% in all the nanocomposites. The morphology of the samples was studied by scanning electron microscopy (SEM). The analysis of X-ray patterns reveals that intercalated structures have been found for all ternary nanocomposites, independently of the molecular weight, PCL concentration and the preparation method selected. A slight rise of the glass transition temperature, Tg, is observed in UP/PCL/4%30B ternary nanocomposites regarding to neat UP. The analysis of the tensile properties of the ternary (hybrid) systems indicates that UP/4%PCL2/4%30B nanocomposite improves the tensile strength and elongation at break respect to the neat UP while the Young modulus remains constant

Catalisadores Ni/MgO-SiO2 aplicados na reação de reforma a vapor de glicerol

Catalisadores de Ni (10% em massa) suportado em matrizes mistas MgO-SiO2 foram aplicados na reação de reforma a vapor de glicerol. Os efeitos do teor de MgO como aditivo e do método de preparação foram avaliados frente às propriedades físico-químicas e texturais dos materiais; assim como à atividade, seletividade, estabilidade e formação de carbono na reforma a vapor do glicerol. Os catalisadores foram preparados com diferentes teores mássicos de MgO (10%, 30% e 50%) sobre SiO2 comercial, utilizando processo via seca (mistura física) e via úmida (impregnação sequencial com diferentes solventes: água, etanol e acetona). Foram utilizadas as técnicas de caracterização de espectroscopia de energia dispersiva de raios X, fisissorção de nitrogênio, difratometria de raios X, termogravimetria, difratometria de raios X in situ com O2, redução a temperatura programada com H2, difratometria de raios X in situ com H2, dessorção a temperatura programada com H2 e microscopia eletrônica de varredura. Foi observado que o Ni(II) interage de forma variada com os suportes com diferentes teores de MgO, e que a polaridade do solvente de impregnação utilizado no processo de preparação influencia as propriedades dos catalisadores. A fim de verificar a atividade, seletividade e deposição de carbono; os catalisadores foram testados na reação de reforma a vapor de glicerol a 600oC, por um período de 5h e razão molar água:glicerol de 12:1. Após as reações, os catalisadores foram novamente submetidos às análises de termogravimetria, difratometria de raios X e microscopia eletrônica de varredura, visando a caracterização dos depósitos de carbono obtidos durante o processo catalítico. Os catalisadores de matrizes mistas se mostraram ativos e apresentaram seletividades similares para os produtos gasosos CH4, CO e CO2, além de um alto rendimento em H2. Observou-se que a adição de MgO no suporte, aumentou a dispersão do Ni(II) no material, que por sua vez, influenciou na quantidade de carbono depositado ao longo da reação. A polaridade do solvente de impregnação também teve influência na dispersão metálica, sendo que, quanto menor a polaridade do solvente, maior foi a dispersão obtida no catalisador, e menor a deposição de carbono na reação. O material que apresentou o melhor desempenho catalítico frente ao rendimento de H2 e à deposição de carbono, foi o catalisador preparado com 30% de MgO com etanol como solvente de impregnação.

NaOH and KOH for preparing activated carbons used in energy and environmental applications

Alkaline hydroxides, especially sodium and potassium hydroxides, are multi-million-ton per annum commodities and strong chemical bases that have large scale applications. Some of them are related with their consequent ability to degrade most materials, depending on the temperature used. As an example, these chemicals are involved in the manufacture of pulp and paper, textiles, biodiesels, soaps and detergents, acid gases removal (e.g., SO2) and others, as well as in many organic synthesis processes. Sodium and potassium hydroxides are strong and corrosive bases, but they are also very stable chemicals that can melt without decomposition, NaOH at 318ºC, and KOH at 360ºC. Hence, they can react with most materials, even with relatively inert ones such as carbon materials. Thus, at temperatures higher than 360ºC these melted hydroxides easily react with most types of carbon-containing raw materials (coals, lignocellulosic materials, pitches, etc.), as well as with most pure carbon materials (carbon fibers, carbon nanofibers and carbon nanotubes). This reaction occurs via a solid-liquid redox reaction in which both hydroxides (NaOH or KOH) are converted to the following main products: hydrogen, alkaline metals and alkaline carbonates, as a result of the carbon precursor oxidation. By controlling this reaction, and after a suitable washing process, good quality activated carbons (ACs), a classical type of porous materials, can be prepared. Such carbon activation by hydroxides, known since long time ago, continues to be under research due to the unique properties of the resulting activated carbons. They have promising high porosity developments and interesting pore size distributions. These two properties are important for new applications such as gas storage (e.g., natural gas or hydrogen), capture, storage and transport of carbon dioxide, electricity storage demands (EDLC-supercapacitors-) or pollution control. Because these applications require new and superior quality activated carbons, there is no doubt that among the different existing activating processes, the one based on the chemical reaction between the carbon precursor and the alkaline hydroxide (NaOH or KOH) gives the best activation results. The present article covers different aspects of the activation by hydroxides, including the characteristics of the resulting activated carbons and their performance in some environment-related applications. The following topics are discussed: i) variables of the preparation method, such as the nature of the hydroxide, the type of carbon precursor, the hydroxide/carbon precursor ratio, the mixing procedure of carbon precursor and hydroxide (impregnation of the precursor with a hydroxide solution or mixing both, hydroxide and carbon precursor, as solids), or the temperature and time of the reaction are discussed, analyzing their effect on the resulting porosity; ii) analysis of the main reactions occurring during the activation process, iii) comparative analysis of the porosity development obtained from different activation processes (e.g., CO2, steam, phosphoric acid and hydroxides activation); and iv) performance of the prepared activated carbon materials on a few applications, such as VOC removal, electricity and gas storages.

Organic distributed feedback laser to monitor solvent extraction upon thermal annealing in solution-processed polymer films

Solution-processed polymer films are used in multiple technological applications. The presence of residual solvent in the film, as a consequence of the preparation method, affects the material properties, so films are typically subjected to post-deposition thermal annealing treatments aiming at its elimination. Monitoring the amount of solvent eliminated as a function of the annealing parameters is important to design a proper treatment to ensure complete solvent elimination, crucial to obtain reproducible and stable material properties and therefore, device performance. Here we demonstrate, for the first time to our knowledge, the use of an organic distributed feedback (DFB) laser to monitor with high precision the amount of solvent extracted from a spin-coated polymer film as a function of the thermal annealing time. The polymer film of interest, polystyrene in the present work, is doped with a small amount of a laser dye as to constitute the active layer of the laser device and deposited over a reusable DFB resonator. It is shown that solvent elimination translates into shifts in the DFB laser wavelength, as a consequence of changes in film thickness and refractive index. The proposed method is expected to be applicable to other types of annealing treatments, polymer-solvent combinations or film deposition methods, thus constituting a valuable tool to accurately control the quality and reproducibility of solution-processed polymer thin films.

A comparison of pseudo-ternary diagrams of aqueous mixtures of Quil A, cholesterol and phospholipid prepared by lipid-film hydration and dialysis

Pseudo-ternary diagrams for Quil A, phospholipid (phosphatidylcholine (PC) or phosphatidylethanolamine (PE)) and cholesterol were established in order to identify combinations that result in the formation of immune-stimulating complex (ISCOM) matrices and other colloidal structures produced by these three components in aqueous systems following lipid-film hydration or dialysis (methods that can be used to produce ISCOMs). In addition, the effect of equilibration time (1 month at 4degreesC) on the structures formed by the various combinations of the three components was investigated. Depending on the ratio of Quil A, cholesterol and phospholipid, different colloidal particles, including ISCOM matrices, liposomes and ring-like micelles, were found irrespective of the preparation method used. In contrast, worm-like micelles were only observed in systems prepared by lipid-film hydration. For samples prepared by dialysis, ISCOM matrices were predominantly found near the Quil A apex of the pseudo-ternary diagram (> 50% Quil A). On the other hand, for samples prepared by lipid-film hydration, ISCOM matrices were predominantly found near the phospholipid apex of the pseudo-ternary diagram (> 50% phospholipid). The regions in the pseudo-ternary diagrams in which ISCOM matrices were observed increased following an extended equilibration time, particularly for samples prepared by lipid-film hydration. Differences were also observed between pseudoternary diagrams prepared using either PE or PC as phospholipids.

Synthesis and characterisation of pillared clay catalysts for hydro-cracking of heavy liquid fuels

A range of chromia pillared montmorillonite and tin oxide pillared laponite clay catalysts, as well as new pillared clay materials such as cerium and europium oxide pillared montmorillonites were synthesised. Methods included both conventional ion exchange techniques and microwave enhanced methods to improve performance and/or reduce preparation time. These catalytic materials were characterised in detail both before and after use in order to study the effect of the preparation parameters (starting material, preparation method, pillaring species, hydroxyl to metal ratio etc.) and the hydro cracking procedure on their properties. This led to a better understanding of the nature of their structure and catalytic operation. These catalysts were evaluated with regards to their performance in hydrocracking coal derived liquids in a conventional microbomb reactor (carried out at Imperial College). Nearly all catalysts displayed better conversions when reused. The chromia pillared montmorillonite CM3 and the tin oxide pillared laponite SL2a showed the best "conversions". The intercalation of chromium in the form of chromia (Cr203) in the interlayer clearly increased conversion. This was attributed to the redox activity of the chromia pillar. However, this increase was not proportional to the increase in chromium content or basal spacing. In the case of tin oxide pillared laponite, the catalytic activity might have been a result of better access to the acid sites due to the delaminated nature of laponite, whose activity was promoted by the presence of tin oxide. The manipulation of the structural properties of the catalysts via pillaring did not seem to have any effect on the catalysts' activity. This was probably due to the collapse of the pillars under hydrocracking conditions as indicated by the similar basal spacing of the catalysts after use. However, the type of the pillaring species had a significant effect on conversion. Whereas pillaring with chromium and tin oxides increased the conversion exhibited by the parent clays, pillaring with cerium and europium oxides appeared to have a detrimental effect. The relatively good performance of the parent clays was attributed to their acid sites, coupled with their macropores which are able to accommodate the very high molecular mass of coal derived liquids. A microwave reactor operating at moderate conditions was modified for hydro cracking coal derived liquids and tested with the conventional catalyst NiMo on alumina. It was thought that microwave irradiation could enable conversion to occur at milder conditions than those conventionally used, coupled with a more effective use of hydrogen. The latter could lead to lower operating costs making the process cost effective. However, in practice excessive coke deposition took place leading to negative total conversion. This was probably due to a very low hydrogen pressure, unable to have any hydro cracking effect even under microwave irradiation. The decomposition of bio-oil under microwave irradiation was studied, aiming to identify the extent to which the properties of bio-oil change as a function of time, temperature, mode of heating, presence of char and catalyst. This information would be helpful not only for upgrading bio-oil to transport fuels, but also for any potential fuel application. During this study the rate constants of bio-oil's decomposition were calculated assuming first order kinetics.