GdxSi grown with mass-analyzed low energy dual ion beam epitaxy technique

Semiconducting gadolinium silicide GdxSi samples were prepared by mass-analyzed low-energy dual ion beam epitaxy technique. Auger electron spectroscopy depth profiles indicate that the gadolinium ions are implanted into the single-crystal silicon substrate and formed 20 nm thick GdxSi film. X-ray double-crystal diffraction measurement shows that there is no new phase formed. The XPS spectra show that one type of silicon peaks whose binding energy is between that of silicide and silicon dioxide, and the gadolinium peak of binding energy is between that of metal Gd and Gd2O3. All of these results indicate that an amorphous semiconductor is formed. (C) 2002 Elsevier Science B.V. All rights reserved.

MnSi similar to 1.73 grown on silicon with mass-analyzed low energy dual ion beam epitaxy technique

Semiconducting manganese silicide, Mn27Si47 and Mn15Si26, were obtained using mass-analyzed low energy dual ion beam epitaxy technique, Auger electron spectroscopy depth profiles showed that some of the Mn ions were deposited on single-crystal silicon substrate and formed a 37.5 nm thick Mn film, and the other Mn ions were successfully implanted into the Si substrate with the implantation depth of 618 nm. Some samples were annealed in the atmosphere of flowing N-2 at 840 degreesC. X-ray diffraction measurements showed that the annealing was beneficial to the formation of Mn27Si47 and Mn15Si26 (C) 2001 Published by Elsevier Science B.V.

Ion bombardment as the initial stage of diamond film growth

It is believed that during the initial stage of diamond film growth by chemical-vapor deposition (CVD), ion bombardment is the main mechanism in the bias-enhanced-nucleation (BEN) process. To verify such a statement, experiments by using mass-separated ion-beam deposition were carried out, in which a pure carbon ion beam, with precisely defined low energy, was selected for investigating the ion-bombardment effect on a Si substrate. The results are similar to those of the BEN process, which supports the ion-bombardment-enhanced-nucleation mechanism. The formation of sp(3) bonding is based on the presumption that the time of stress generation is much shorter than the duration of the relaxation process. The ion-bombarded Si is expected to enhance the CVD diamond nucleation density because the film contains amorphous carbon embedded with nanocrystalline diamond and defective graphite. (C) 2001 American Institute of Physics.

Structural study of YSi1.7 layers formed by channeled ion beam synthesis

High quality YSi1.7 layers (chi(min) of Y is 3.5%) have been formed by 60 keV Y ion implantation in Si (111) substrates to a dose of 1.0 x 10(17)/cm(2) at 450 degrees C using channeled ion beam synthesis (CIBS). It shows that, compared to the conventional nonchanneled ion beam synthesis, CIBS is beneficial in forming YSi1.7 layers with better quality due to the lower defect density created in the implanted layer. Rutherford backscattering/channeling and x-ray diffraction have been used to study the structure and the strain of the YSi1.7 layers. The perpendicular and parallel elastic strains of the YSi1.7 epilayer are e(perpendicular to) = -0.67% +/- 0.02% and e(parallel to) = +1.04% +/- 0.08%. The phenomenon that a nearly zero mismatch of the YSi1.7/Si (111) system results in a nonpseudomorphic epilayer with a rather large parallel strain relative to the Si substrate (epsilon(parallel to) = +1.09%) is explained, and the model is further used to explain the elastic strain of epitaxial ErSi1.7 and GdSi1.7 rare-earth silicides. (C) 1998 American Vacuum Society.

Identification of induced reaction during XPS depth profile measurements of CeO2/Si films grown by ion beam epitaxy

An anomalous behavior was observed in X-ray photoelectron Spectroscopy (XPS) depth profile measurements conducted on CeO2/Si epilayers grown by ion beam epitaxy (IBE): the signals of Ce3+ and Ce4+ co-exist, and the ratio between them increases during the etching time and then tends to maintain a constant level before increasing again. The results of X-ray Diffraction (XRD), Auger Electron Spectroscopy (AES), and Rutherford Back-Scattering (RES) measurements proved that the reduction chemical reaction of CeO2 is induced by ion-etching. (C) 1998 Elsevier Science Ltd. All rights reserved.

Mechanism of induced reaction during XPS depth profile measurements of CeO2/Si films grown by ion beam epitaxy

In a search for the mechanism of the induced reduction reaction that occurred in X-ray photoelectron Spectroscopy (XPS) depth profiles measured experimentally on CeO2/Si epilayers grown by ion beam epitaxy (IBE), several possibilities have been checked. The first possibility, that the X-ray induces the reaction, has been ruled out by experimentation. Other possible models for the incident-ion induced reaction, one based on short-range interaction (direct collision) and the other based on long-range potential accompanied with the incident-ions, have been tested by simulation on computer. The results proved that the main mechanism is the former, not the latter. (C) 1998 Elsevier Science Ltd. All rights reserved.

Fabrication of Nano-structured VOx Film by Low Temperature Ion Beam Sputtering and Reductive Annealing

VOx thin films have been fabricated by low temperature ion beam sputtering and post reductive annealing process. Semiconductor-metal phase transition is observed for the film annealed at 400 degrees C for 2 hours. The film also shows a polycrystal structure with grain size from 50nm to 150nm. The VOx thin films fabricated by this process have a TCR up to -2.7% at room temperature. Our results indicate a promising fabrication method of the nano-structured VOx film with relatively high TCR and semiconductor-metal phase transition.

A DUAL ION-BEAM EPITAXY SYSTEM

The design and characteristics of a dual ion beam epitaxy system (DIBE) are discussed. This system is composed of two beam lines, each providing a mass-separated ion beam converging finally with the other into the target chamber. The ions are decelerated and deposited on a substrate which can be heated to a temperature of 800-degrees-C. Currents of a few hundred microamperes are available for both beams and the deposit energies are in the range from tens to 1000 eV. The pressure of the target chamber during processing is about 7 x 10(-6) Pa. Preliminary experiments have proved that compound semiconductor materials such as GaN can be synthesized using the DIBE system.

X-ray-diffraction study of quasipseudomorphic ErSi1.7 layers formed by channeled ion-beam synthesis

ErSi1.7 layers with high crystalline quality (chi(min) of Er is 1.5%) have been formed by 90 keV Er ion implantation to a dose of 1.6X10(17)/cm(2) at 450 degrees C using channeled implantation. The perpendicular and parallel elastic strain e(perpendicular to)=-0.94%+/-0.02% and e(parallel to)=1.24%+/-0.08% of the heteroepitaxial erbium silicide layers have been measured with symmetric and asymmetric x-ray reflections using a double-crystal x-ray diffractometer. The deduced tetragonal distortion e(T(XRD))=e(parallel to)-e(perpendicular to)=2.18%+/-0.10%, which is consistent with the value e(T(RBS))2.14+/-0.17% deduced from the Rutherford backscattering and channeling measurements. The quasipseudomorphic growth of the epilayer and the stiffness along a and c axes of the epilayer deduced from the x-ray diffraction are discussed.

High-Power and High-Efficiency 650nm-Band AlGaInP Visible Laser Diodes Fabricated by Ion Beam Etching

High power and high-slope efficiency 650nm band real-refractive-index ridge waveguide AlGaInP laser diodes with compressive strained MQW active layer are formed by pure Ar ion beam etching process.Symmetric laser mesas with high perpendicularity,which are impossible to obtain by traditional wet etching method due to the use of a 15°-misoriented substrate,are obtained by this dry etching method.Laser diodes with 4μm wide,600μm long and 10%/90% coat are fabricated.The typical threshold current of these devices is 46mA at room temperature,and a stable fundamental-mode operation over 40mW is obtained.Very high slope efficiency of 1.4W/A at 10mW and 1.1W/A at 40mW are realized.