The fabrication of GaN-based nanopillar light-emitting diodes

InGaN/GaN multiple quantum well-based light-emitting diode (LED) nanopillar arrays were fabricated using Ni self-assembled nanodots as etching mask. The Ni nanodots were fabricated with a density of 6 x 10(8)-1.5 x 10(9) cm(-2) and a dimension of 100-250 nm with varying Ni thickness and annealing duration time. Then LED nanopillar arrays with diameter of approximately 250 nm and height of 700 nm were fabricated by inductively coupled plasma etching. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence (PL) intensity is achieved for the nanopillars and a blueshift as well as a decrease in full width at half maximum of the PL peak are also observed. The method of additional chemical etching was used to remove the etching-induced damage. Then nano-LED devices were further completed using a planarization approach to deposit p-type electrode on the tips of nanopillars. The current-voltage curves of both nanopillars and planar LED devices are measured for comparison.

CHANNELING ALIGNMENT FOR EPITAXIAL LIGHT-MASS FILM ON HEAVY-MASS SUBSTRATE

A simple procedure for obtaining a background-free backscattering spectrum of a light-mass film on a heavy-mass substrate by a normal incidence/grazing exit geometry has been described. Using this method such films can be aligned rapidly and accurately, and the impurity or defect information on the films can be obtained without need for realignment. Example is given from MeV Li-3+ analysis of a deposited film of Si on a single crystal substrate of yttria-stabilized, cubic zirconia.

POLARIZATION OF HOT PHOTOLUMINESCENCE IN QUANTUM-WELLS AND HEAVY-LIGHT HOLE MIXING

Hot electrons excited from the valence band by linearly polarized laser light are characterized by certain angular distributions in momenta. Owing to such angular distributions in momenta, the photoluminescence from the hot electrons shows a certain degree of polarization. A theoretical treatment of this effect observed in the photoluminescence in quantum wells is given, showing that the effect depends strongly on heavy and light hole mixing. The very large disparity between the experimentally observed and theoretically expected values of the degree of polarization in the hot-electron photoluminescence suggests the presence of random quasielastic scattering. The effects of such additional scattering and the presence of a perpendicular magnetic field are incorporated into the theory. it is shown that the measurements of the degree of polarization observed in the hot electron photoluminescence, with and without an applied perpendicular magnetic field can serve to determine the time constants for both LO-phonon inelastic and random quasielastic scattering. As an example, these time constants are determined for the experiments reported in the literature.

GAAS/GAALAS GRADED INDEX SEPARATE CONFINEMENT SINGLE QUANTUM-WELL SINGLE-MODE WAVE-GUIDE ELECTROABSORPTION LIGHT-MODULATOR

A GaAs/GaAlAs graded-index separate confinement single quantum well heterostructure single-mode ridge waveguide electroabsorption modulator was fabricated and investigated. For the modulator with a quantum well width of 100 angstrom and device length of 700-mu-m, an on/off ratio of 29.7 dB and estimated absorption insertion loss of 3 dB were obtained for TE polarised light with wavelength 8650 angstrom, and for TM polarisation the on/off ratio was 28.5 dB. With a switching voltage of 1 V, an on/off ratio of 15 dB was achieved. Photocurrent spectra exhibited a red shift of 600 angstrom of the absorption edge when the voltage applied to the PIN diode was varied from 0.5 to -7 V. The corresponding shift of the room temperature exciton peak energy was 96 meV.

BACKGATING AND LIGHT SENSITIVITY IN GAAS METAL-SEMICONDUCTOR FIELD-EFFECT TRANSISTORS

Three different types of GaAs metal-semiconductor field effect transistors (MESFET) by employing ion implantation, molecular beam epitaxy (MBE) and low-temperature MBE (LT MBE) techniques respectively were fabricated and studied in detail. The backgating (sidegating) measurement in the dark and in the light were carried out. For the LT MBE-GaAs buffered MESFETs, the output resistance R(d) and the peak transconductance g(m) were measured to be above 50 k Omega and 140 mS/mm, respectively, and the backgating and light sensitivity were eliminated. A theoretical model describing the light sensitivity in these kinds of devices is given. and good agreement with experimental data is reached.