High-Saturation-Power and High-Speed Ge-on-SOI p-i-n Photodetectors

Ge-on-silicon-on-insulator p-i-n photodetectors were fabricated using an ultralow-temperature Ge buffer by ultrahigh-vacuum chemical vapor deposition. For a detector of 70-mu m diameter, the 1-dB small-signal compression power was about 110.5 mW. The 3-dB bandwidth at 3-V reverse bias was 13.4 GHz.

Fabrication of Silicon-Based Template-Assisted Nanoelectrode Arrays and Ohmic Contact Properties Investigation

A convenient fabrication technology for large-area, highly-ordered nanoelectrode arrays on silicon substrate has been described here, using porous anodic alumina (PAA) as a template. The ultrathin PAA membranes were anodic oxidized utilizing a two-step anodization method, from Al film evaporated on substrate. The purposes for the use of two-step anodization were, first, improving the regularity of the porous structures, and second reducing the thickness of the membranes to 100 similar to 200 nm we desired. Then the nanoelectrode arrays were obtained by electroless depositing Ni-W alloy into the through pores of PAA membranes, making the alloy isolated by the insulating pore walls and contacting with the silicon substrates at the bottoms of pores. The Ni-W alloy was also electroless deposited at the back surface of silicon to form back electrode. Then ohmic contact properties between silicon and Ni-W alloy were investigated after rapid thermal annealing. Scanning electron microscopy (SEM) observations showed the structure characteristics, and the influence factors of fabrication effect were discussed. The current voltage (I-V) curves revealed the contact properties. After annealing in N-2 at 700 degrees C, good linear property was shown with contact resistance of 33 Omega, which confirmed ohmic contacts between silicon and electrodes. These results presented significant application potential of this technology in nanosize current-injection devices in optoelectronics, microelectronics and bio-medical fields.

INVESTIGATION OF POROUS SILICON BY SCANNING-TUNNELING-MICROSCOPY AND ATOMIC-FORCE MICROSCOPY

The size and distribution of surface features of porous silicon layers have been investigated by scanning tunneling and atomic force microscopy. Pores and hillocks down to 1-2 nm size were observed, with their shape and distribution on the sample surface being influenced by crystallographic effects. The local density of electronic states show a strong increase above 2 eV, in agreement with recent theoretical predictions.

QUANTITATIVE-ANALYSIS OF INXGA1-XAS BY AUGER-ELECTRON SPECTROSCOPY

Quantitative Auger electron spectroscopy analysis for the ternary system InGa1-xAs grown by molecular-beam epitaxy has been studied. The relative sensitivity factors are determined by with an internal reference element. The matrix correction factor for In relative to Ga was shown to be 1.08. No preferential sputtering of As for the ternary compounds was found, and the sputter correction factor, K(s)InGa is 0.75. The results are compared with that measured by the x-ray double-crystal diffraction analysis, electron probe microanalysis, and Auger analysis without matrix and sputter corrections.

EFFECT OF A SI LAYER ON THE SUPERCONDUCTIVE PROPERTIES OF A BIPBSRCACUO THIN-FILM

The Pb-doped BiSrCaCuO superconducting films were grown by the single source mixed evaporation technique. The microbridges of dimensions 50 mum x 40 mum were fabricated by standard photolithography technologies. Si films with a thickness of 2500 angstrom were deposited on the microbridge area surfaces of BiPbSrCaCuO superconducting films by rf-magnetron sputtering. A greatly lowered zero resistance temperature of the microbridge area of the BiPbSrCaCuO film after Si sputtering was found. A non-linear effect of the current-voltage (I-V) characteristics at 78 K was shown. The high-frequency capacitance-voltage (C-V) curve of this structure at 78 K was symmetrical with the maximum capacitance at V = 0, and the capacitance decreased with increasing applied bias voltage. Afl experimental results are discussed.

STUDY ON PREPARATION OF GAN AND COSI2 EPITAXIAL-FILMS BY MASS ANALYZED LOW-ENERGY DUAL ION-BEAM EPITAXY

The Mass Analyzed Low Energy Dual Ion Beam Epitaxy (MALE-DIBE) system has been designed and constructed in our laboratory. We believe that the system, which was installed and came into full operation in 1988, is the first facility of this kind. With our system we have carried out studies, for the first time, on compound synthesis of GaN and CoSi2 epitaxial thin films. RHEED and AES results show that GaN films, which were deposited on Si and sapphire substrates, are monocrystalline and of good stoichiometry. To our knowledge, GaN film heteroepitaxially grown on Si. which is more lattice-mismatched than GaN on sapphire, has not been reported before by other authors. RBS and TEM investigations indicated a rather good crystallinity of CoSi2 with a distinct interface between CoSi2 and the Si substrate. The channelling minimum yield chi(min) from the Co profile is approximately 4%. The results showed that the DIBE system with simultaneous arrival of two beams at the target is particularly useful in the formation of novel compounds at a relatively low substrate temperature.

INDIUM OHMIC CONTACTS TO N-ZNSE

The reaction between an indium over layer and high purity MBE grown n-ZnSe chlorine doped (2x 10(18) cm-3) epilayers has been investigated using X-ray diffraction, Rutherford backscattering spectroscopy, X-ray photoelectron and Auger electron spectroscopy, and by electrical function tests (I-V and C-V). Good ohmic contacts were formed after annealing at 250 or 300-degrees-C for a few minutes in forming gas. Annealing at lower or higher temperatures resulted in higher resistance or rectifying contacts. The data show that no compounds were formed at the interface; instead In appeared to diffuse into the ZnSe. High surface doping densities appear to allow an ohmic contact, but the electrical data suggest that compensation effects are also very significant in the formation of the contact. These effects must be considered for successful formation of the ohmic contact.

STUDY OF TI/LNP INTERFACE BY PES

The interface of Ti/InP(110) was studied by X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS). It is evident that deposition of Ti on the surface of InP(110) at room temperature introduced a break of the In-P bond and a diffusion of In atoms into the Ti film. The interaction of Ti and P occurred at a temperature of 350-degrees-C.

INTERFACIAL REACTIONS IN THE CO/SI/GAAS AND SI/CO/GAAS SYSTEMS

The interfacial reactions between thin films of cobalt and silicon and (100)-oriented GaAs substrates in two configurations, Co/Si/GaAs and Si/Co/GaAs, were studied using a variety of techniques including Auger electron spectroscopy, x-ray diffraction, and transmission electron microscopy. The annealing conditions were 200, 300, 400, 600-degrees-C for 30 min, and rapid thermal annealing for 15 s. It was found that Si layer in the Co/Si/GaAs system acts as a barrier at the interface between Co and GaAs when annealed up to 600-degrees-C. The interfacial reaction between Co and Si is faster than that between Co and GaAs in the system of Si/Co/GaAs. The sequence of compound formation for the two metallizations studied (Co/Si/GaAs and Si/Co/GaAs) depends strongly on the sample configuration as well as the layer thickness of Si and Co (Co/Si atomic ratio). From our results, it is promising to utilize Co/Si/GaAs multilayer film structure to make a CoSi2/GaAs contact, and this CoSi2 may offer an alternative to the commonly used W silicides as improved gate metallurgies in self-aligned metal-semiconductor field effect transistor (MESFET) technologies.

DELINEATION OF DEFECTS IN SIMOX STRUCTURES USING A CHEMICAL ETCHING TECHNIQUE

Residual defects in the overlayer of fully annealed SIMOX material have been studied by means of a chemical etching technique. The etching procedure has been calibrated and an optimum recipe is reported. Observations using optical microscopy and transmission electron microscopy have been used to quantify the defect densities and good agreement between the two techniques has been established, confirming that the optimised chemical etching process can be used with confidence to determine the dislocation density for values < 10(7) cm-2.

DIRECT ION-BEAM DEPOSITION OF CARBON-FILMS ON SILICON IN THE ION ENERGY-RANGE OF 15-500 EV

Direct ion beam deposition of carbon films on silicon in the ion energy range of 15-500 eV and temperature range of 25-800-degrees-C has been studied. The work was carried out using mass-separated C+ and CH3+ ions under ultrahigh vacuum. The films were characterized with x-ray photoelectron spectroscopy, Raman spectroscopy, transmission electron microscopy, and transmission electron diffraction analysis. In the initial stage of the deposition, carbon implanted into silicon induced the formation of silicon carbide, even at room temperature. Further carbon ion bombardment then led to the formation of a carbon film. The film properties were sensitive to the deposition temperature but not to the ion energy. Films deposited at room temperature consisted mainly of amorphous carbon. Deposition at a higher temperature, or post-deposition annealing, led to the formation of microcrystalline graphite. A deposition temperature above 800-degrees-C favored the formation of microcrystalline graphite with a preferred orientation in the (0001) direction. No evidence of diamond formation in these films was observed.

CONSTRUCTION AND APPLICATIONS OF A DUAL MASS-SELECTED LOW-ENERGY ION-BEAM SYSTEM

A direct ion beam deposition system designed for heteroepitaxy at a low substrate temperature and for the growth of metastable compounds has been constructed and tested. The system consists of two mass-resolved low-energy ion beams which merge at the target with an incident energy range 50-25 000 eV. Each ion beam uses a Freeman ion source for ion production and a magnetic sector for mass filtering. While a magnetic quadrupole lens is used in one beam for ion optics, an electrostatic quadrupole lens focuses the other beam. Both focusing approaches provide a current density more than 100-mu-A/cm2, although the magnetic quadrupole gives a better performance for ion energies below 200 eV. The typical current of each beam reaches more than 0.3 mA at 100 eV, with a ribbon beam of about 0.3-0.5 x 2 cm2. The target is housed in an ultrahigh vacuum chamber with a base pressure of 1 x 10(-7) Pa and a typical pressure of 5 x 10(-6) Pa when a noncondensable beam like argon is brought into the chamber. During deposition, the target can be heated to 800-degrees-C and scanned mechanically with an electronic scanning control unit. The dual beam system has been used to grow GaN using a Ga+ and a N+ beam, and to study the oxygen and hydrogen ion beam bombardment effects during carbon ion beam deposition. The results showed that the simultaneous arrival of two beams at the target is particularly useful in compound formation and in elucidation of growth mechanisms.

PHOTOLUMINESCENCE AND SURFACE PHOTOVOLTAIC SPECTRA OF STRAINED INP ON GAAS

A high energy shift of the band-band recombination has been observed in the photoluminescence (PL) spectra of the strained InP epilayer on GaAs by metalorganic chemical vapor deposit. The strain determined by PL peak is in good agreement with calculated thermal strain. The surface photovoltalic spectra gives the information about energy gap, lattice mismatching, and composition of heteroepilayers, diffusion length, surface, and interface recombination velocity of minority carriers of heteroepitaxy layers.

CERIUM SILICIDE FORMATION IN THIN CE SI MULTILAYER FILMS

Alternating layers of Si(200 angstrom thick) and Ce(200 angstrom thick) up to 26 layers altogether were deposited by electron evaporation under ultrahigh vacuum conditions on Si(100) substrate held at 150-degrees-C. Isothermal, rapid thermal annealing has been used to react these Ce-Si multilayer films. A variety of analytical techniques has been used to study these multilayer films after annealing, and among these are Auger electron spectroscopy, Rutherford backscattering, X-ray diffraction, and high resolution transmission electron microscopy. Intermixing of these thin Ce-Si multilayer films has occurred at temperatures as low as 150-degrees-C for 2 h, when annealed. Increasing the annealing temperature from 150 to 400-degrees-C for 1 h, CeSi2 forms gradually and the completion of reaction occurs at approximately 300-400-degrees-C. During the formation of CeSi2 from 150-400-degrees-C, there is some evidence for small grains in the selected area diffraction patterns, indicating that CeSi2 crystallites were present in some regions. However, we have no conclusive evidence for the formation of epitaxial CeSi2 layers, only polycrystals were formed when reacted in the solid phase even after rapid thermal anneal at 900-degrees-C for 10 s. The formation mechanism has also been discussed in combining the results of the La-Si system.

PHOTOEMISSION-STUDY OF THE INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AL AND HYDROGENATED AMORPHOUS SI

Using photoemission spectroscopy and Auger electron spectroscopy, the interfacial formation process and the reactions between Al and hydrogenated amorphous Si are probed, and annealing behaviors of the Al/a-Si:H system are investigated as well. It is found that a three-dimensional growth of Al metal clusters which includes reacted Al and non-reacted metal Al occurs at the initial Al deposition time, reacted Al and Si alloyed layers exist in the Al/a-Si:H interface, and non-reacted Al makes layer-by-layer growth forming a metal Al layer on the sample surface. The interfacial reactions and element interdiffusion of Al/a-Si:H are promoted under the vacuum annealing.