A comparison of photoluminescence properties of InGaAs GaAs quantum dots with a single quantum well

Variable temperature photoluminescence (PL) measurements for In0.3Ga0.7As(6 nm)/GaAs(34 nm) quantum dot superlattices with a period of 20 and an In0.3Ga0.7As(6 nm)/GaAs(34 nm) reference single quantum well have been conducted. It is found that the temperature dependence is different between the quantum dots and the reference single quantum well. The PL peak energy of the single quantum well decreases faster than that of the quantum dots with increasing temperature. The PL peak energy for the InGaAs/GaAs quantum dots closely follows the InAs band gap in the temperature range from 11 to 170 K, while the PL peak energy for the InGaAs/GaAs quantum well closely follows the GaAs band gap. In comparison with InAs/GaAs quantum dots, the InGaAs/GaAs quantum dots are more typical as a zero-dimensional system since the unusual PL results, which appear in the former, are not obvious for the latter. (C) 1999 American Institute of Physics. [S0021-8979(99)08615-6].

Photoluminescence study on coarsening of self-assembled InAlAs quantum dots on GaAs (001)

Red-emission at similar to 640 nm from self-assembled In0.55Al0.45As/Al0.5Ga0.5As quantum dots grown on GaAs substrate by molecular beam epitaxy (MBE) has been demonstrated. We obtained a double-peak structure of photoluminescence (PL) spectra from quantum dots. An atomic force micrograph (AFM) image for uncapped sample also shows a bimodal distribution of dot sizes. From the temperature and excitation intensity dependence of PL spectra, we found that the double-peak structure of PL spectra from quantum dots was strongly correlated to the two predominant quantum dot families. Taking into account quantum-size effect on the peak energy, we propose that the high (low) energy peak results from a smaller (larger) dot family, and this result is identical with the statistical distribution of dot lateral size from the AFM image.

Photoluminescence properties of nitrogen-doped ZnSe epilayers

The photoluminescence (PL) properties of nitrogen-doped ZnSe epilayers grown on semi-insulating GaAs(100) substrates by MBE using a rf-plasma source for N doping were investigated. The PL peak which can be related to N acceptor was observed in the PL spectra of ZnSe:N smaples. At 10K, as the excitation power density increases, the energy of donor-acceptor pair(DAP) emission shows a blue-shift and its intensity tends to saturate. As the temperature increases over a range from 10K to 300K, the relative PL intensity of donor bound exciton to that of the acceptor bound exciton increases due to the transfer between two bound excitons.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Quantitative analysis of excitonic photoluminescence in nitrogen-doped ZnSe epilayers

We have investigated the photoluminescence (PL) properties of nitrogen-doped ZnSe epilayers grown by molecular beam epitaxy using a nitrogen radio frequency-plasma source. The PL data shows that the relative intensity of the donor-bound exciton (I-2) emission to the acceptor-bound exciton (I-1) emission strongly depends on both the excitation power and the temperature. This result is explained by a thermalization model of the bound exciton which involved in the capture and emission between the neutral donor bound exciton, the neutral acceptor bound exciton and the free exciton. Quantitative analysis with the proposed mechanism is in good agreement with the experimental data. (C) 1999 American Institute of Physics. [S0021-8979(99)09102-1].

Pressure behaviour of photoluminescence from InAs submonolayer in GaAs matrix

We have investigated the dependence on hydrostatic pressure of the photoluminescence of an InAs submonolayer embedded in a GaAs matrix at 15 K and for pressure up to 8 GPa. Strong InAs-related emissions are observed in all three samples at ambient pressure. The temperature dependence of the emission intensity for these Peaks can be well characterized by the thermal activation of excitons from the InAs layer to the GaAs matrix. With increasing pressure, the InAs-related peaks shift to. higher energies. The pressure coefficients of these peaks are very close to that of the free exciton in bulk GaAs. Some weak peaks observed at pressures above 4.2 GPa are attributed to indirect transitions involving X states in the InAs layer. These results are similar to the pressure behaviour observed in the InAs/GaAs monolayer structures. A group of new lines has been observed in the spectra when pressure is increased beyond 2.5 GPa, which is attributed to the N isoelectronic traps in the GaAs matrix.

Photoluminescence properties of SiGe/Si single wells with fluctuating structural parameters

Photoluminescence properties of SiGe/Si single wells with fluctuating structural parameters are studied. Four SiGe/Si single wells have been grown on Si(001) at 750 degrees C by disilane and solid Ge molecular beam epitaxy with varied disilane cracking-temperatures. Intense NP and TO-phonon replicas are detected up to 70 K in the photoluminescence spectra and the activation energy of the thermal quenching of the photoluminescence is 28 +/- 4 meV. The high growth temperature and purposeful introduction of fluctuation of structural parameters may be responsible for the improvement of the thermal quenching property.

Structure and photoluminescence of InGaAs self-assembled quantum dots grown on InP(001)

Molecular beam epitaxy has been used for growing InGaAs self-assembled quantum dots (QDs) in InAlAs on an InP(001) substrate. Nominal deposition of 9.6 monolayers of In0.9Ga0.1As results in QDs of similar to 6.5 nm high with an areal density of 3.3 X 10(11) cm(-2). Conspicuous bimodal size distribution is identified, and is responsible for the observed QDs photoluminescence (PL) emission with two peaks at 0.627 and 0.657 eV. Good agreement is achieved between the observed PL peak energies and calculated results. (C) 1999 American Institute of Physics. [S00218979(99)00101-2].

Improvement of the photoluminescence from gallium nitride layers grown by MBE with an additional incident indium flux

The effect of using an indium flux during the MBE growth of GaN layers was investigated. The properties of these layers were studied using electron probe microanalysis, secondary ion mass spectroscopy, photoluminescence and cathodoluminescence. The optical properties of the GaN layers are shown to improve as compared with undoped GaN layers grown under nominally the same conditions but without an additional indium flux.

Microstructure and photoluminescence of a-SiOx : H

Two strong photoluminescence (PL) bands in the spectral range of 550-900 nm have been observed at room temperature from a series of a-SiOx:H films fabricated by plasma-enhanced chemical vapor deposition (PECVD) technique. One is composed of a main band in the red-light region and a shoulder; the other is located at about 850 nm, only found after 1170 degrees C annealing in N-2 atmosphere. In conjunction with infrared (IR) and micro-Raman spectra, it is thought that the two PL bands are associated with a-Si clusters in the SiOx network and nanocrystalline silicon in SiO2, respectively.

Photoluminescence enhancement of porous silicon by organic cyano compounds

A pronounced photoluminescence enhancement on chemically oxidized porous silicon was induced by a series of organic cyano compounds including 1,2-dicyanoethylene (CE), 1,3-dicyanobenzene (1,3-CB), 1,4-dicyanobenzene (1,4-CB), 1-cyanonaphthalene (1-CN), and 9-cyanoanthracene (9-CA). Photoluminescence enhancement effects were reversible for all compounds studies in this work. A dependence of photoluminescence enhancement on the steric effect and the electronic characteristics of these compounds and the structure of the porous silicon substrates were analyzed in terms of the photoluminescence enhancing factors. Surface chemical composition examined by Fourier transform infrared (FTIR) spectra demonstrated that the surface Si-H bonds were not changed and no new luminescent compounds were formed on porous silicon surface during adsorption of cyano compounds. A mechanism based on induced surface states acting as radiative recombination centers by cyano compounds adsorption was suggested.

Photovoltage and photoreflectance spectroscopy of InAs/GaAs self-organized quantum dots

We present a detailed study of the interband excitonic transitions of InAs/GaAs self-organized quantum dots (QDs) based on photovoltage (PV) photoreflectance (PR) and photoluminescence (PL) spectroscopy. At room temperature, the interband absorption transitions of QDs have been observed by using PV spectrum, which clearly exhibits four well-resolved excitonic absorption peaks. The absorption line shape is Gaussian-like. Furthermore, the corresponding excitonic transitions are also observed in PR experiment at 77 K. The first derivative of a Gaussian profile can fit the experimental data well. (C) 1998 American Institute of Physics. [S0003-6951(98)00743-8]

Effects of growth interruption on self-assembled InAs/GaAs islands

The effect of growth interruption on the InAs deposition and its subsequent growth as self-assembled island structures, in particular the material transport process of the InAs layers has been investigated by photoluminescence and transmission electron microscopy measurements. InAs material in structures with only coherent islands transfers from the wetting layer to the formed islands and the growth interruption causes a red shift of PL peak energy. On the other hand, the PL peak shifts to higher energy in structures containing simultaneously coherent and noncoherent islands with dislocations. In this case, the noncoherent islands capture InAs material from the surrounding wetting layer as well as coherent islands, which casues a reduction in the size of these islands. The variations in the PL intensity and line width are also discussed. (C) 1998 Elsevier Science B.V. All rights reserved.

Photoluminescence investigation of GaInP/GaAs multiple quantum wells grown on (001) and (311) B GaAs surfaces by gas source molecular beam epitaxy

Photoluminescence (PL) investigation was carried out on GaInP/GaAs multiple quantum wells structures grown on (001) and (311) B surfaces of GaAs by gas source molecular beam epitaxy. Superlattice structures of GaAs/GaInP grown on (001) GaAs substrate were also studied in comparison. Deep-level luminescence was seen to dominate the PL spectra from the quantum wells and superlattice structures that were grown on (001) GaAs substrate. In contrast, superior optical properties were exhibited in the same structures grown on (311) B GaAs surfaces. The results suggested that GaAs/GaInP quantum well structures on (311) B oriented substrates could efficiently suppress the deep-level emissions, result in narrower PL peaks indicating smooth interfaces. (C) 1998 American Institute of Physics.

Annealing behaviors of photoluminescence from SiOx : H

The strong photoluminescence (PL) of SiOx:H prepared by plasma enhanced chemical vapor deposition has been systematically studied in conjunction with infrared and micro-Raman spectra. We have found that each PL spectrum is comprised of two Gaussian components, a main band and a shoulder. The main band might originate from amorphous silicon clusters embedded in die SiOx network, and its redshift with annealing temperature is due to expansion of the silicon clusters. The shoulder remains at about 835 nm in spite of the annealing temperature and possibly comes from luminescent defect centers. The enhanced PL spectra after 1170 degrees C annealing are attributed to the quantum confinement effects of nanocrystalline silicon embedded in the SiO2 matrix. (C) 1998 American Institute of Physics.