Effect of rapid thermal annealing on InGaAs/GaAs quantum wells

We have studied the effect of rapid thermal annealing (RTA) on highly strained InGaAs/GaAs quantum wells by using photoluminescence (PL) and double-crystal X-ray diffraction (DCXRD) measurements. It is found that a distinct additional PL emission peak can be observed for the annealed samples. This PL emission possesses features similar to the PL emission from InGaAs/GaAs quantum dots (QDs) with the same indium content. It is proposed that this emission stems from QDs, which were formed during the annealing process. This formation is attributed to the favorable diffusion due to the inhomogeneous strain distribution in the InGaAs layer intersurface. The DCXRD measurements also confirm that the dominant relaxation is strain enhanced diffusion under the low annealing temperatures. (C) 2000 Elsevier Science B.V. All rights reserved.

InAs self-assembled nanostructures grown on InP(001)

The 6-period stacked layers of self-assembled InAs quasi-quantum wires(qQWRs) and quantum dots(QDs) embedded into InAlAs on InP(001) substrates have been prepared by solid molecular beam epitaxy. The structures are characterized by atomic force microscopy(AFM) and transmission electron microscopy(TEM). From AFM we have observed for the first time that InAs qQWRs and QDs coexist, and we explained this phenomenon from the view of the energy related to the islands. Cross-sectional TEM shows that InAs qQWRs are vertically aligned every other layer along the growth direction [001], which disagrees with conventional vertical self-alignment of InAs QDs on GaAs substrate.

Strain and photoluminescence characterization of cubic (In,Ga)N films grown on GaAs(001) substrates

Cubic InxGa1-xN films were successfully grown on GaAs(001) substrates by metalorganic chemical-vapor deposition. The values of x content ranging from 0.10 to 0.24 obtained at different growth conditions were measured by double-crystal x-ray diffraction (XRD). The perpendicular and parallel elastic strain of the In0.2Ga0.8N layer, epsilon(perpendicular to)=0.4% and epsilon(parallel to)=-0.4% for GaN and epsilon(perpendicular to)=0.37% and epsilon(parallel to)=-0.37% for InGaN, respectively, were derived using the XRD measurements. The inhomogeneous strain and the average grain size of the In0.2Ga0.8N/GaN films were also studied by XRD. Photoluminescence spectra were used to measure the optical characterization of the InxGa1-xN thin films with different In composition, and the near-band-edge emission dependence of cubic InxGa1-xN on the x value is nearly linear with In content x less than or equal to 0.24. (C) 2000 American Institute of Physics. [S0021-8979(00)03908-6].

Optical properties of InAs self-organized quantum dots in n-i-p-i GaAs superlattices

The optical properties of InAs quantum dots in n-i-p-i GaAs superlattices are investigated by photoluminescence (PL) characterization. We have observed an anomalously large blueshift of the PL peak and increase of the PL linewidth with increasing excitation intensity, much smaller PL intensity decrease, and faster PL peak redshift with increasing temperature as compared to conventional InAs quantum dots embedded in intrinsic GaAs barriers. The observed phenomena can all be attributed to the filling effects of the spatially separated photogenerated carriers. (C) 2000 American Institute of Physics. [S0003-6951(00)03515-4].

Anomaly of the current self-oscillation frequency in the sequential tunneling of a doped GaAs/AlAs superlattice

An anomalous behavior of the current self-oscillation frequency is observed in the dynamic de voltage bands, emerging from each sawtoothlike branch of the current-voltage characteristic of a doped GaAs/A1As superlattice in the transition process from static to dynamic electric field domain formations. Varying the applied de voltage at a fixed temperature, we find that the frequency increases while the averaged current decreases. Inside each voltage band, the frequency has a strong voltage dependence in the temperature range where the averaged current changes with the applied de voltage. This dependence can be understood in terms of motion of the system along a limit cycle.

Strong resonant intersubband magnetopolaron effect in heavily modulation-doped GaAs/AlGaAs single quantum wells at high magnetic fields

Electron cyclotron resonance (CR) has been studied in magnetic fields up to 32 T in two heavily modulation-delta-doped GaAs/Al0.3Ga0.7As single quantum well samples. Little effect on electron CR is observed in either sample in the region of resonance with the GaAs LO phonons. However, above the LO-phonon frequency energy E-LO at B > 27 T, electron CR exhibits a strong avoided-level-crossing splitting for both samples at energies close to E-LO + (E-2 - E-1), where E-2, and E-1 are the energies of the bottoms of the second and the first subbands, respectively. The energy separation between the two branches is large, reaching a minimum of about 40 cm(-1) around 30.5 T for both samples. This splitting is due to a three-level resonance between the second LI, of the first electron subband and the lowest LL of the second subband plus an LO phonon. The large splitting in the presence: of high electron densities is due to the absence of occupation (Pauli-principle) effects in the final states and weak screening for this three-level process. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

Experimental determination of local Strain effect on InAs/GaAs self-organized quantum dots

The energy barrier at InAs/GaAs interface due to the built-in strain in self-organized system has been determined experimentally. Such a barrier has been predicted by previous theories. From the deep-level transient spectroscopy (DLTS) measurements, we have obtained the electron and hole energy levels of quantum dots E-e(QD-->GaAs) = 0.13 eV and E-h(QD-->GaAs) = 0.09 eV relative to the bulk unstrained GaAs band edges E-c and E-v. DLTS measurements have also provided evidence to the existence of the capture barriers of quantum dots for electron E-eB = 0.30 eV and hole E-hB = 0.26 eV. The barriers can be explained by the apexes appearing in the interface between InAs and GaAs caused by strain. Combining the photoluminescence results, the band structures of InAs and GaAs have been determined.

Infrared absorption efficiency in AlAs/AlxGa1-xAs type-II multiple-quantum-well structure grown on (211) GaAs substrate

We have made a normal incidence high infrared absorption efficiency AlAs/Al0.55Ga0.45As multiple-quantum-well structure grown on (211) GaAs substrates by molecular beam epitaxy (MBE). A strong infrared absorption signal at 11.6 mu m due to the transition of the ground state to the first excited state, and a small signal at 6.8 mu m due to the transition from the ground state to continuum. were observed. A 45 degrees tilted incidence measurement was also performed on the same sample for the comparison with a normal incidence measurement. Both measurements provide important information about the quantum well absorption efficiency. Efficiencies which evaluate the absorption of electric components perpendicular and parallel to the well plane are eta(perpendicular to) = 25% and eta(parallel to) = 88%, respectively. The total efficiency is then deduced to be eta = 91%. It is apparent that the efficiency eta(parallel to) dominates the total quantum efficiency eta Because an electron in the (211) AlAs well has a small effective mass (m(zx)* or m(zy)*), the normal incidence absorption coefficient is expected to be higher:than that grown on (511) and (311) substrates. Thus, in the present study, we use the (211) substrate to fabricate QWIP. The experimental results indicate the potential of these novel structures for use as normal incidence infrared photodetectors.

The investigations on semi-insulating GaAs by surface photovoltaic spectroscopy

The surface photovoltage (SPV) effect induced by the defect states in semi-insulating (SI) GaAs was studied. The PV response below the band edge was measured at room temperature with a de optical biasing. The spectra were found to be strongly dependent on the surface recombination and were attributed to formation of the carrier concentration gradient near the surface region, showing that SPV is a very sensitive and nondestructive technique for characterizing the surface quality of the SI-GaAs wafers.

Temperature dependence of the optical properties of InAs/GaAs self-organized quantum dots with bimodal size distribution

In this work we report the optical and microscopic properties of self-organized InAs/GaAs quantum dots grown by molecular beam epitaxy on (1 0 0) oriented GaAs substrates. A distinctive double-peak feature of the PL spectra from quantum dots has been observed, and a bimodal distribution of dot sizes has also been confirmed by scanning tunneling microscopy (STM) image for uncapped sample. The power-dependent photoluminescence (PL) study demonstrates that the distinctive PL emission peaks are associated with the ground-state emission of islands in different size branches. The temperature-dependent PL study shows that the PL quenching temperature for different dot families is different. It is shown that the coupling between quantum dots plays a key role in unusual temperature dependence of QD photoluminescence. In addition, we have tuned the emission wavelength of InAs QDs to 1.3 mu m at room temperature. (C) 2000 Elsevier Science B.V. All rights reserved.

Growth and characterization of strained superlattices delta-GaNxAs1-x/GaAs by molecular beam epitaxy

A series of superlattices delta-GaNxAs1-x/GaAs were grown by a DC plasma-N-2-assisted molecular beam epitaxy. The evolution of the surface reconstruction during the growth has been studied with the use of in situ reflection high-energy electron diffraction. The superlattices have been characterized by high-resolution X-ray diffraction measurements. Distinct satellite peaks indicate that the superlattices are of good quality. The N compositions in strained GaNxAs1-x monolayers are obtained from the dynamical simulations of the measured X-ray diffraction patterns. The periodicity fluctuations of N composition are obtained from a kinematical method dependent on the broadening of the satellite peaks of the X-ray diffraction. (C) 2000 Elsevier Science B.V. All rights reserved.

Self-ordering of quasi-quantum wire in InAlAs/AlGaAs multilayer nanostructure and its optical anisotropy

Self-ordering of quasi-quantum wires in multilayer InAlAs/AlGaAs nanostructures grown by molecular beam epitaxy is identified. The chain-like structures along the [1 (1) over bar 0] Of direction formed by coalescence of quantum dots were observed. The photoluminescence of the nanostructures is partially polarized along the [1 (1) over bar 0] direction. The polarization ratio depends on the wavelength and the maximum polarization is on the lower energy side. The maximum polarization increases from 0.32 at 10 K to 0.53 at 100 K, and the energy position of maximum polarization moves near to PL peak with increasing temperature. They are all related to the existence of isolated islands and quasi-quantum wires in our sample. This result provides a novel approach to produce narrow quantum wires. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of arsenic precipitates on Fermi level in GaAs grown by molecular-beam epitaxy at low temperature

A simple model is presented to discuss the effect of As precipitates on the Fermi level in GaAs grown by molecular-beam epitaxy at low temperature (LT-GaAs). This model implements the compensation between point defects and the depletion of arsenic precipitates. The condition that the Fermi level is pinned by As precipitates is attained. The shifts of the Fermi level in LT-GaAs with annealing temperature are explained by our model. Additionally, the role of As precipitates in conventional semi-insulating GaAs is discussed. (C) 2000 American Institute of Physics. [S0021-8979(00)09905-9].

Photoluminescence study of InAlAs quantum dots grown on differently oriented surfaces

We reported the optical properties of self-assembled In0.55Al0.45As quantum dots grown by molecular beam epitaxy on (001) and (n11)A/B(n = 3,5)GaAs substrates. Two peaks were observed in the photoluminescence (PL) spectra from quantum dots in the (001) substrate and this suggested two sets of quantum dots different in size. For quantum dots in the high-index substrates, the PL spectra were related to the atomic-terminated surface (A or B substrate). The peaks for the B substrate surfaces were in the lower energy position than that for the (001) and A type. In addition, quantum dots in the B substrate have comparatively high quantum efficiency. These results suggested that high-index B-type substrate is more suitable for the fabrication of quantum dots than (001) and A-type substrates at the same growth condition. (C) 2000 American Vacuum Society. [S0734-211X(00)04701-6].

Methods to tune the electronic states of self-organized InAs/GaAs quantum dots

After capping InAs islands with a thin enough GaAs layer, growth interruption has been introduced. Ejected energy of self-organized InAs/GaAs quantum dots has been successfully tuned in a controlled manner by changing the thickness of GaAs capping layer and the time of growth interruption and InAs layer thickness. The photoluminescence (PL) spectra showing the shift of the peak position reveals the tuning of the electronic states of the QD system. Enhanced uniformity of Quantum dots is observed judging from the decrease of full width at half maximum of FL. Injection InAs/GaAs quantum dot lasers have been fabricated and performed on various frequencies. (C) 2000 Published by Elsevier Science B.V. All rights reserved.