Low-phosporous nickel-coated carbon microcoils : Controlling microstructure through an electroless plating process

Carbon microcoils (CMCs) have been coated with a nickel-phosphorus (Ni-P) film using an electroless plating process, with sodium hypophosphite as a reducing agent in an alkaline bath. CMC composites have potential applications as microwave absorption materials. The morphology, elemental composition and phases in the coating layer of the CMCs and Ni-coated CMCs were investigated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), respectively. The effects of process parameters such as pH, temperature and coating time of the plating bath on the phosphorus content and deposition rate of the electroless Ni-P coating were studied. The results revealed that a continuous, uniform and low-phosphorous nickel coating was deposited on the surface of the CMCs for 20 min at pH 9.0, plating bath temperature 70 °C. The as-deposited coatings with approximately 4.5 wt.% phosphorus were found to consist of a mix of nano- and microcrystalline phases. The mean particle size of Ni-P nanoparticles on the outer surface of the CMCs was around 11.9 nm. The deposition rate was found to moderately increase with increasing pH, whereas, the phosphorous content of the deposit exhibited a significant decrease. Moreover, the material of the coating underwent a phase transition between an amorphous and a crystalline structure. The thickness of the deposit and the deposition rate may be controlled through careful variation of the coating time and plating bath temperature.

Structural evolution of nanocrystalline silicon thin films synthesized in high-density, low-temperature reactive plasmas

Silicon thin films with a variable content of nanocrystalline phase were deposited on single-crystal silicon and glass substrates by inductively coupled plasma-assisted chemical vapor deposition using a silane precursor without any hydrogen dilution in the low substrate temperature range from 100 to 300 °C. The structural and optical properties of the deposited films are systematically investigated by Raman spectroscopy, x-ray diffraction, Fourier transform infrared absorption spectroscopy, UV/vis spectroscopy, scanning electron microscopy and high-resolution transmission electron microscopy. It is shown that the structure of the silicon thin films evolves from the purely amorphous phase to the nanocrystalline phase when the substrate temperature is increased from 100 to 150 °C. It is found that the variations of the crystalline fraction fc, bonded hydrogen content CH, optical bandgap ETauc, film microstructure and growth rate Rd are closely related to the substrate temperature. In particular, at a substrate temperature of 300 °C, the nanocrystalline Si thin films of our interest feature a high growth rate of 1.63nms-1, a low hydrogen content of 4.0at.%, a high crystalline fraction of 69.1%, a low optical bandgap of 1.55eV and an almost vertically aligned columnar structure with a mean grain size of approximately 10nm. It is also shown that the low-temperature synthesis of nanocrystalline Si thin films without any hydrogen dilution is attributed to the outstanding dissociation ability of the high-density inductively coupled plasmas and effective plasma-surface interactions during the growth process. Our results offer a highly effective yet simple and environmentally friendly technique to synthesize high-quality nanocrystalline Si films, vitally needed for the development of new-generation solar cells and other emerging nanotechnologies.

Polymer-mediated synthesis of γ-Fe2O3 nano-particles

Nano-particles of γ-Fe2O3 were synthesized by reacting polyethylene oxide–FeCl3 complex with NH4OH. These were characterized by X-ray diffraction (XRD), scanning electron miscroscopy (SEM), selected area electron diffraction (SAED) and transmision electron microscopy (TEM). The average particle size was found to be 10 nm, as determined from the line broadening of the main XRD peak. The crystalline phase was a spinel-type tetragonal structure, which was confirmed from the electron diffraction pattern. The zero field cooled magnetization of samples with varying γ-Fe2O3 content as a function of temperature was measured using a vibrating sample magnetometer. The magnetization curves show a peak at low temperature (15 K) corresponding to the blocking temperature TB. The value of TB was found to decrease with decreasing particle size. The magnetization measurements with respect to field at 5 and 170 K confirmed the transition from superparamagnetic to spin-glass state at TB, as evidenced from the remanence and hysteresis. These results can be explained on the basis of Néel's theory of superparamagnetism as applied to nano-particles.

Phase transitions and gravity

Einstein's gravitational field is non-minimally coupled to a self-interacting scalar field in the presence of radiation. Such a theory can give rise to a phase transition associated with a change of sign of the gravitational “constant”. In our approach, the criterion for stability is formulated in terms of an effective potential, the phase-transition takes place due to temperature dependence of the scalar self-interaction coupling constant.

Pressure-Induced transitions in amorphous TlxSe100-x alloys

The electrical resistivity of bulk semiconducting amorphous TlxSe100-x alloys with 0 ≤ x ≤ 25 has been investigated up to a pressure of 14 GPa and down to liquidnitrogen temperature by use of a Bridgman anvil device. All the glasses undergo a discontinuous pressure-induced semiconducting-to-metal transition. X-ray diffraction studies on the pressure-recovered samples show that the high-pressure phase is the crystalline phase. The pressure-induced crystalline products are identified to be a mixture of Se having a hexagonal structure with a = 4·37 Aring and c = 4·95 Aring and TlSe having a tetragonal structure with a = 8·0 Aring and c = 7·0 Aring

Impurity states in Sb-doped amorphous semiconductors

A systematic investigation of the effects of antimony dopant on the electronic transport properties of amorphous (GeSe3.5)100−xSbx under high pressure (up to 120 kbar) has been carried out down to liquid-nitrogen temperature for the first time. Differential thermal analysis and x-ray diffraction methods were used for the characterization of freshly prepared and pressure-quenched materials which indicated the presence of structural phase transition in both GeSe3.5 and (GeSe3.5)100−xSbx around 105 kbar pressure. Electrical transport data revealed the strong compositional dependence of the electronic conduction process. A distinct kink in the conductivity temperature plot at pressures>15 kbar was observed in the Sb-doped compositions indicating the presence of different conduction processes. An attempt has been made to interpret the pressure-induced effect in the transport properties of these glasses considering the possible presence of both thermally activated conduction in the extended states and hopping process in the localized tail states. However, the interpretation of the transport data is not straightforward and the pressure dependence of the thermoelectric power will be needed to complete the picture. Journal of Applied Physics is copyrighted by The American Institute of Physics.

Metallization and crystallization of semiconducting amorphous Ga20Te80 alloy under high pressure

Pressure and temperature dependence of the electrical resistivity of amorphous Ga20Te80 alloy is reported for the first time. The alloy undergoes a pressure induced amorphous semiconductor-to-crystalline metal phase transition at 6.5 ± 0.5 GPa. The high pressure crystalline phase is a mixture of Te and GaTe3 phases.

Pressure-induced electronic and structural transformations in bulk gese2 glass

The pressure dependence of the electrical of the electrical resistivity of bulk GeSe2 glass shows a semiconductor-to-metal transition at 7 GPa pressure. The high pressure phase is examined using he x-ray diffractometer and is found to be crystalline, with a face-centered cubic structure having a =4.06A. The electrical conductivity has also been studied as a function of temperature at various pressures.

Pressure induced effects in bulk amorphous n-type semiconductors(GeSe3.5)100âxBix

The effect of pressure on the electrical resistivity of amorphous n-type (GeSe3.5)100�xBix been studied in a Bridgeman anvil system up to a pressure of 90 kbar down to liquid nitrogen temperature. A continuous amorphous semiconductor to metal-like solid transition in the undoped GeSe3.5 is observed at room temperature. Incorporation of Bi in the GeSe3.5 network is found to significantly disturb the behaviour of the resistivity with pressure. With increasing Bi concentration a much broader variation in resistivity with pressure is observed. The temperature dependence of the resistivity and activation energy at different pressures is also measured and they are found to be composition dependent. Results are discussed in the light of the Phillips Model of ordered clusters in chalcogenide semiconductors.

Mixed valency in the high-temperature phases of transition metal molybdates,AMoO4 (A=Fe, Co, Ni)

Transition metal molybdates of the formulaAMoO4 whereA=Fe, Co or Ni exhibit a first-order phase transition between 670K–970K. An investigation of the lowtemperature (lt) and high-temperature (ht) phases by x-ray photoelectron spectroscopy, x-ray absorption spectroscopy, magnetic susceptibility and other physical methods shows that the phase transition is associated with a valence change of the typeA 2++Mo6+αA 3++Mo5+ in the cases of iron and cobalt molybdates.

A composition dependent thermal behavior of GexSe35-xTe65 glasses

Alternating differential scanning calorimetric (ADSC) studies have been performed to understand the thermal behavior of bulk GexSe35-xTe65 glasses (17 <= x <= 25); it is found that the glasses with x <= 20 exhibit two crystallization exotherms (T-c1 & T-c2). On the other hand, those with x >= 20.5, show a single crystallization reaction upon heating. The exothermic reaction at T-c1 has been found to correspond to the partial crystallization of the glass into hexagonal Te and the reaction at T-c2 is associated with the additional crystallization of rhombohedral Ge-Te phase. The glass transition temperature of GexSe35-xTe65 glasses is found to show a linear but not-steep increase, indicating a progressive, but a gradual increase in network connectivity with Ge addition. It is also found that T-c1 of GexSe35-xTe65 glasses with x <= 20, increases progressively with Ge content and eventually merges with T-c2 at x approximate to 20.5 (< r > = 2.41); this behavior has been understood on the basis of the reduction in Te-Te bonds of lower energy and increase in Ge-Te bonds of higher energy, with increasing Ge content. Apart from the interesting composition dependent crystallization, an anomalous melting behavior is also exhibited by the GexSe35-xTe65 glasses.

Gel growth and dielectric studies of K. Rb and Cs perchlorates

Single crystals of K, Rb and Cs perchlorates have been grown by the counter diffusion of the respective ions and CIO4 through the gel medium. Studies on nucleation, growth kinetics, morphological aspects and purity are discussed in this paper. The dielectric constant, ~b, as well as loss measured along the longest axis, exhibits an anomaly at the transition temperature, Tt, in all the three crystals. It is found that the peak values of Tt are approximately 800, 100 and 53 in K, Rb and Cs perchlorates, respectively. The dielectric anomaly and the large value of c b in the cubic phase are discussed in terms of the degree of disorder of the CIO~ group and the possible contribution from defects.

Temperature dependence of chlorine NQR in 2-chloro 5-nitrobenzoic acid and 4-chloro 3-nitrobenzoic acid

Temperature dependence of chlorine nuclear quadrupole resonance in 2-chloro 5-nitrobenzoic acid and 4-chloro 3-nitrobenzoic acid has been investigated in the region 77° K to room temperature. No phase transition has been observed. The results are analysed to obtain the torsional frequencies and their temperature dependence. A nonlinear temperature dependence is obtained for the torsional frequencies.

Heterojunctions between amorphous and crystalline niobium oxide with enhanced photoactivity for selective aerobic oxidation of benzylamine to imine under visible light

The formation of heterojunctions between two crystals with different band gap structures, acting as a tunnel for the unidirectional transfer of photo-generated charges, is an efficient strategy to enhance photocatalytic performance in semiconductor photocatalysts. The heterojunctions may also promote the photoactivity in the visible-light-response of any surface complex catalysts by influencing the transfer of photo-generated electrons. Herein, Nb2O5 microfibers, with a high surface area of interfaces between an amorphous phase and crystalline phase, were designed and synthesised by the calcination of hydrogen-form niobate while controlling the crystallization The photoactivity of these microfibers towards selective aerobic oxidation reactions was investigated. As predicted, the Nb2O5 microfibres containing heterojunctions exhibited the highest photoactivity. This could be due to the band gap difference between the amorphous phase and the crystalline phase, which shortened the charge mobile distance and improved the efficiency.

Quantum phase analysis of 1D superconducting quantum dot lattice using extended Bose-Hubbard model

We have obtained the quantum phase diagram of a one-dimensional superconducting quantum dot lattice using the extended Bose-Hubbard model for different commensurabilities. We describe the nature of different quantum phases at the charge degeneracy point. We find a direct phase transition from the Mott insulating phase to the superconducting phase for integer band fillings of Cooper pairs. We predict explicitly the presence of two kinds of repulsive Luttinger liquid phases, besides the charge density wave and superconducting phases for half-integer band fillings. We also predict that extended range interactions are necessary to obtain the correct phase boundary of a one-dimensional interacting Cooper system. We have used the density matrix renormalization group method and Abelian bosonization to study our system.