Defect evolution and accompanied change of electrical properties during the GaN growth by metalorganic chemical vapor deposition

The defect evolution and its correlation with electrical properties of GaN films grown by metalorganic chemical vapor deposition are investigated. It is found that the dislocation density decreases gradually during the growth process, and the dislocation reduction rate in the island coalescence process is especially rapid. The changes in electron mobility of GaN with the increase of growth time are mainly dependent on the dislocations acting as scattering centers. Furthermore, the variation of carrier concentration in GaN may be related with the point defects and their clusters. The quality of GaN could be improved by suitably increasing the film thickness. (C) 2009 Elsevier B.V. All rights reserved.

Influence of penetrating V-pits on leakage current of GaN based p-i-n UV detector

The leakage mechanism of GaN-based p-i-n (p-AlGaN/i-GaN/n-GaN) UV detector has been investigated. With the same dislocation density, devices made from material with higher density of V-pits on surface produce larger leakage current. SEM images show that some V-pits penetrate into i-GaN layer, sometimes even the n-GaN layer. If p-ohmic contact metal (Ni/Au) deposits in the V-pits, Schottky contact would be formed at the interface of metal and i-GaN, or form ohmic contact at the interface of metal and n-GaN. The existence of parallel Schottky junction and ohmic contact resistance enhances the leakage current greatly.

Effect of trimethylgallium flow on the structural and optical properties of InGaN/GaN multiple quantum wells

InGaN/GaN multiple quantum wells (MQWs) are grown by metal-organic chemical vapour deposition on (0001) sapphire substrates. Triple-axis X-ray diffraction (TXRD) and photoluminescence (PL) spectra are used to assess the influence of trimethylgallium (TMGa) flow on structural defects, such as dislocations and interface roughness, and the optical properties of the MQWs. In this paper, a method, involving an ! scan of every satellite peak of TXRD, is presented to measure the mean dislocation density of InGaN/GaN MQWs. The experimental results show that under certain conditions which keep the trimethlyindium flow constant, dislocation density and interface roughness decrease with the increase of TMGa flow, which will improve the PL properties. It can be concluded that dislocations, especially edge dislocations, act as nonradiative recombination centres in InGaN/GaN MQWs. Also noticed is that changing the TMGa flow has more influence on edge dislocations than screw dislocations.

Effect of the N/Al ratio of AlN buffer on the crystal properties and stress state of GaN film grown on Si(111) substrate

The effect of the N/Al ratio of AlN buffers on the optical and crystal quality of GaN films, grown by metalorganic chemical vapor deposition on Si(111) substrates, has been investigated. By optimizing the N/Al ratio during the AlN buffer, the threading dislocation density and the tensile stress have been decreased. High-resolution X-ray diffraction exhibited a (0002) full-width at half-maximum as low as 396 acrsec. The variations of the tensile stress existing in the GaN films were approved by the redshifts of the donor bound exiton peaks in the low-temperature photoluminescence measurement at 77 K. (C) 2003 Elsevier B.V. All rights reserved.

Stress evolution influenced by oxide charges on GaN metal-organic chemical vapor deposition on silicon-on-insulator substrate

GaN epilayers have been deposited on silicon-on-insulator (SOI) and bulk silicon substrates. The stress transition thickness and the initial compressive stress of a GaN epilayer on the SOI substrate are larger than those on the bulk silicon substrate, as shown in in situ stress measurement results. It is mainly due to the difference of the three-dimensional island density and the threading dislocation density in the GaN layer. It can increase the compressive stress in the initial stage of growth of the GaN layer, and helps to offset the tensile stress generated by the lattice mismatch.

Enhanced performance of p-GaN by Mg delta doping

The electrical and structural properties of Mg delta-doped GaN epilayers grown by MOCVD were investigated. Compared to uniform Mg-doping GaN layers, it has been shown that the delta-doping (delta-doping) process could suppress the dislocation density and enhance the p-type performance. The influence of pre-purge step on the structural properties of GaN was also investigated. The hole concentration of p-GaN decreases when using a pre-purge step. These results can be explained convincingly using a simple model of impurity incorporation under Ga-free growth condition. (C) 2007 Elsevier B.V. All rights reserved.

Influence of defects in n(-)-GaN layer on the responsivity of Schottky barrier ultraviolet photodetectors

The influence of defects on the responsivity of GaN Schottky barrier ultraviolet photodetectors with n(-)-GaN/n(+)-GaN layer structures is investigated. It is found that employing undoped GaN instead of Si-doped GaN as the n(-)-GaN layer brings about a higher responsivity due to a lower Ga vacancy concentration. On the other hand, the dislocations may increase the recombination of electron-hole pairs and enhance the surface recombination in the photodetectors. Employing undoped GaN and reducing the dislocation density in the n(-)-GaN layer are necessary to improve the responsivity of Schottky barrier photodetectors. (c) 2007 American Institute of Physics.

Strain evolution in GaN layers grown on high-temperature AlN interlayers

The strain evolution of the GaN layer grown on a high-temperature AlN interlayer with GaN template by metal organic chemical vapor deposition is investigated. It is found that the layer is initially under compressive strain and then gradually relaxes and transforms to under tensile strain with increasing film thickness. The result of the in situ stress analysis is confirmed by x-ray diffraction measurements. Transmission electron microscopy analysis shows that the inclination of edge and mixed threading dislocations rather than the reduction of dislocation density mainly accounts for such a strain evolution. (c) 2006 American Institute of Physics.

Effects of edge dislocations and intentional Si doping on the electron mobility of n-type GaN films

The effects of dislocations and Si doping on the electrical properties of n-type GaN grown by metal organic chemical vapor deposition (MOCVD) are investigated. It is found that both electron mobility and carrier concentration are strongly influenced by edge dislocations. A moderate Si doping during the GaN growth improves the electron mobility, but the best doping effect depends on the dislocation density of the sample. High quality about 4-mu m-thick MOCVD-grown GaN film with a room temperature electron mobility as high as 1005 cm(2)/V s is obtained by optimizing growth conditions. (c) 2006 American Institute of Physics.

Role of edge dislocations in enhancing the yellow luminescence of n-type GaN

We investigate the origin of yellow luminescence in n-type GaN. It is found that the relative intensity of yellow luminescence increases as the full width at half maximum of the x-ray diffraction rocking curve at the (102) plane increases. This indicates that the yellow luminescence is related to the edge dislocation density. In addition, the relative intensity of yellow luminescence is confirmed to increase with increasing Si doping for the high quality GaN we have obtained. We propose that the yellow luminescence is effectively enhanced by the transition from donor impurities such as Si to acceptors around the edge dislocations in n-type GaN. (c) 2006 American Institute of Physics.

Comparison of space- and ground-grown Ce: Bi12SiO20 single crystals

Ce doped Bi12SiO20 single crystals were grown either on board of the Chinese Spacecraft-Shenzhou No.3 (SZ-3) or on the ground at the same conditions with the exception of microgravity. The surface morphology of crystals clearly showed significant differences between the space- and ground-grown portions. The space- and ground-grown crystals have been measured by X-ray rocking curve, Cc concentration distribution in growth direction, dislocation density, absorption spectrums. These results show that the compositional homogeneity and structural perfection of Ce doped crystal grown in space are obviously improved.

Defects in GaN films grown on Si(111) substrates by metal-organic chemical vapour deposition

We report the transmission-electron microscopy study of the defects in wurtzitic GaN films grown on Si(111) substrates with AIN buffer layers by the metal-organic chemical vapour deposition method. The In0.1Ga0.9N/GaN multiple quantum well (MQW) reduced the dislocation density by obstructing the mixed and screw dislocations passing through the MQW. No evident reduction of the edge dislocations density by the MQW was observed. It was found that dislocations with screw component can be located at the boundaries of sub-grains slightly in-plane misoriented.

Microstructure of GaN films grown on Si(111) substrates by metalorganic chemical vapor deposition

We report the transmission electron microscopy (TEM) study of the microstructure of wurtzitic GaN films grown on Si(I I I) substrates with AlN buffer layers by metalorganic chemical vapor deposition (MOCVD) method. An amorphous layer was formed at the interface between Si and AlN when thick GaN film was grown. We propose the amorphous layer was induced by the large stress at the interface when thick GaN was grown. The In0.1Ga0.9N/GaN multiple quantum well (MQW) reduced the dislocation density by obstructing the mixed and screw dislocations from passing through the MQW. But no evident reduction of the edge dislocations by the MQW was observed. It was found that dislocations located at the boundaries of grains slightly in-plane misoriented have screw component. Inversion domain is also observed. (C) 2003 Elsevier B.V. All rights reserved.

Investigation of GaN layer grown on Si(111) substrate using an ultrathin AlN wetting layer

High-quality GaN epilayers were grown on Si (1 1 1) substrate by metalorganic chemical vapor deposition. The growth process was featured by using an ultrathin AlN wetting layer (WL) in combination with a low-temperature (LT) GaN nucleation layer (NL). The full-width at half-maximum (FWHM) of the X-ray rocking curve for the GaN (0 0 0 2) diffraction was 15 arcmin. The dislocation density estimated from TEM investigation was found to be of the order of 10(9)cm(-2). The FWHM of the dominant band edge emission peak of the GaN was measured to be 47 meV by photoluminescence measurement at room temperature. The ultrathin AlN WL was produced by nitridation of the aluminium pre-covered substrate surface. The reflection high-energy electron diffraction showed that the AlN WL was wurtzite and the surface morphology was like the nitridated surface of sapphire by the atomic force microscopy measurement. X-ray photoelectron spectroscopy measurement showed that Si and SixNy at a certain concentration were intermixed in the AlN WL. This study suggests that by employing an appropriate WL combined with a LT NL, high-quality heteroepitaxy is achievable even with large mismatch. (C) 2002 Elsevier Science B.V. All rights reserved.

Structural characterization of cubic GaN grown on GaAs(001) substrates

Structural characteristics of cubic GaN epilayers grown on GaAs(001) were studied using X-ray double-crystal diffraction technique. The structure factors of cubic GaN(002) and (004) components are approximately identical. However, the integrated intensities of the rocking curve for cubic (002) components are over five times as those of (004) components. The discrepancy has been interpreted in detail considering other factors. In the conventional double crystal rocking curve, the peak broadening includes such information caused by the orientation distribution (mosaicity) and the distribution of lattice spacing. These two kinds of distributions can be distinguished by the triple-axis diffraction in which an analyser crystal is placed in front of the detector. Moreover, the peak broadening was analysed by reciprocal lattice construction and Eward sphere. By using triple-axis diffraction of cubic (002) and (113) components, domain size and dislocation density were estimated. The fully relaxed lattice parameter of cubic GaN was determined to be about 0.451 +/- 0.001nm.