Síntese e caracterização dielétrica de filmes finos de Bi3NbO7 obtidos pelo método dos precursores poliméricos

Bi3NbO7 thin films were prepared by the polymeric precursor method. The precursor solutions were prepared with excess of bismuth ranging from 0% to 10% and the pH was controlled to be maintained between 8 and 9. This control was done by adding to the solution niobium and ethylene glycol. The final solution was clear and free of precipitation. After obtaining the precursor solution, has begun the process of characterization of powders with thermogravimetry (TG), differential thermal analysis and X-ray analysis (XRD). The films were obtained by the polymeric precursors, the method is advantageous because it is simple, and low cost involves steps and controlled stoichiometry. The films were annealed and characterized by XRD and SEM and also characterized according to their dialectics properties. We observed that the best results were obtained when the film is thermally at 800 ° C for two hours and 860 ° C for two hour. Under these conditions we obtain Bi3NbO7 thin films with good homogeneity, uniform distribution of the grains, but with the formation of secondary phase, which does not occur in treatments with lower temperature. The dielectric characterization showed that the produced film showed good characteristics with high dielectric constant and low loss

Síntese por reação em estado sólido de pós cerâmicos multifuncionais à base de CaCu3Ti4O12 modificados com estrôncio

The study of ceramic materials is constantly evolving, especially in research related to advanced ceramics. Once these have many applications, this paper relates to synthesis by solid state reaction of calcium copper titanate (CCTO) ceramic material means doping with strontium. The powders were characterized using thermal analysis techniques such as TG (thermogravimetry), DTA (differencial thermal analysis), dilatometry, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The compositions have submitted weight loss at around 6% with respect to carbonates used, and was attributed a temperature of 950° C to perform the calcination according to thermogravimetric analysis. After the process of calcination and milling, the particles presented approximately spherical shapes and high percentages of substitution Ca2+ with Sr2+ was evident by the presence of necks between to particles due to the milling calcination. Analyses with Energy Dispersive Spectroscopy (EDS) showed stoichiometries in different samples very similar to the theoretical stoichiometry

Estudo do comportamento térmico e reológico de amidos na conformação cerâmica de compostos multicamada com alumina, titanato de alumínio e dióxido de titânio

The project aims to develop ceramic compounds with gradients of the mechanical properties, using the molding technique with commercial starches. To understand the process of interaction between starch and ceramic powders, the proposed methodology involves viscometry tests (up to 200 °C). Viscometric assays were carried out with slurries of alumina, titania and aluminum titanate with potato starch, cassava and corn. The specimens were tested for dilatometry, thermomechanical, thermal shock, mechanical and characterization by SEM. The ceramic powders and starches were analyzed using the optical microscope to measure the size of these. It was made of th kinetics of starch gelatinization and titania with the cornstarch in theoptical microscope to observe how the grains of starch behaved in welling

Desenvolvimento de filmes finos de Bi3NbO7 pelo método dos precursores poliméricos em diferentes eletrodos óxidos

Technology always advances and thus the device miniaturization and improved performance, besides multifunctionality, they become extremely necessary. A wave of research on the area tends to grow in number and importance in today's market, it is necessary to search for new materials, new applicability of the existing ones and new processes for increasingly cheaper costs. Dielectric materials are considered a key element in this sector being the main electrical properties its high dielectric constant and low dielectric loss. The Polymeric Precursor Method appears as a good alternative because is a low cost, simple process with controlled stoichiometry. In this method, two steps were performed. In a first step, the precursor solution was decomposed into powders and in a second step the precursor solution was converted in thin films. In this work, was used the polymeric precursor methods to get thin films where they were heat treated and characterized by XRD, SEM and AFM. We have obtained Bi3NbO7 thin films with good homogeneity and uniform distribution of grains were noted. We observed that the best condition to obtain the tetragonal phase is annealing the film at high temperatures for a longer soaking time and with excess of bismuth. Several oxides electrodes were evaluated aiming to obtain textured dielectric thin films

Síntese e caracterização de filmes finos de ferrita de bismuto dopados com cálcio visando aplicação em memórias de múltiplos estados

The increasing demand for electro-electronic devices, with high performance and multi-functional and the rapid advances of the nanotechnology require the development of new methods and techniques for the production and characterization of nanostructure materials and phenomenological models to describe/to predict some of its properties. The demand for multifunctionality requires, at least, new materials, that can integrate ferroelectric and magnetic properties of high technological interest. Inside of this context, multiferroics material can be considered suitable to integrate two or more physical properties of high technological interest. It can also provides new challenges in the processes of synthesis of new materials, and development of new devices with controlling and simulation of its physical properties and modeling. For this Calcium (Ca)-doped bismuth ferrite (BiFeO3) thin films prepared by using the polymeric precursor method (PPM) were characterized by X-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM), transmission electron microscopy (TEM), polarization and piezoelectric measurements.In order to study the behavior and determine which are the most important parameters to achieve the optimal property to be applied to a multiferroic materials

Effects of the addition of ions barium on the structural and electrical properties of PZT ceramic

Lead zirconate titanate, with Zr/Ti ratio of 53/47 was prepared by the polymeric precursor method. It was investigated the barium (II) modification at 0.0, 0.2, 0.4 and 0.6 mol% in substitution to the lead (II) cation in A site of perovskite structure. The powder samples were characterized by XRD and the diffraction patterns were used to Rietveld refinement. The percentages of tetragonal and rhombohedral phases and a systematic study of the effect of barium (II) on the morphology and the dielectric properties of PZT were carried out. The results showed that the tetragonal phase is favored and the ceramic density is improved with the barium (II) insertion. The Curie temperature (Tc) is increased besides the slight reduction of dielectric constant (Kc).

Métodos de identificação e redução de modelos para atenuação de vibrações em estruturas inteligentes

Pós-graduação em Engenharia Mecânica - FEIS

Controle ativo de estruturas reticuladas utilizando atuadores de pilha de pzt

Pós-graduação em Engenharia Mecânica - FEIS

Obtenção e caracterização de nanoestruturas puras e dopadas a base de 'TI''O'IND.2' para a aplicação em fotocatálise

Pós-graduação em Química - IQ

Avaliação da capacidade de vedamento e pH do tampão apical com cimento Portland branco acrescido de radiopacificadores convencionais

The Portland cement has shown similar biological properties to calcium hydroxide, but its radiopacity is lower. Therefore, the addition of materials that minimize this deficiency should be considered. OBJECTIVE: To evaluate the apical sealing ability and pH of a white Portland cement added of several radiopacifying agents. MATERIAL AND METHODS: Forty bovine roots with incomplete apices were selected, and the foraminal openings were standardized to PM 720G bur. After the external root sealing, an apical intracanal barrier 10.0 mm thick was executed with the white Portland cement powder, pure or added of a radiopacifying agent (iodoform, zinc oxide or bismuth subnitrate), and distilled water (0.37 mL). The apical roots were immersed 24h in water in humid atmosphere, and after that they were immersed 24h in 2% Rhodamine B, under vacuum. In sequence, the roots were longitudinally sectioned, the root fragments were photographed, the images were digitalized and the apical infiltration was measured by the Image Tool program. The pH solutions were also evaluated, in 24h and 48h and 7 and 30 days. Data were submitted to Anova test. RESULTS: The zinc oxide solution has the lowest apical infiltration in relation to the other groups (p < 0.05). The pH behavior varied during the analysis, and in the period of 24h all groups showed the highest values (p < 0.05). CONCLUSION: The type of radiopacifying agent used interferes in the sealing ability of the apical barrier, and zinc oxide showed to be the most beneficial one. The pH varies according to the period of analysis, and the highest values were obtained in the first 24h (p < 0.05).

Hydrogen ion and calcium releasing of MTA Fillapex® and MTA-based formulations

MTA is composed of various metal oxides, calcium oxide and bismuth. It has good biological properties and is indicated in cases of endodontic complications. Several commercial formulations are available and further studies are necessary to evaluate these materials. Objective: To evaluate pH and calcium releasing of MTA Fillapex® compared with gray and white MTA. Material and methods: Gray and white MTA (Angelus) and MTA Fillapex® (Angelus) were manipulated and placed into polyethylene tubes and immersed in distilled water. The pH of these solutions was measured at 24 hours, 7 days and 14 days. Simultaneously, at these same aforementioned periods, these materials' calcium releasing was quantified, through atomic absorption spectrophotometry. The results were submitted to ANOVA, with level of significance at 5%. Results: Concerning to pH, the materials present similar behaviors among each other at 24 hours (p > 0.05). At 7 and 14 days, MTA Fillapex® provided significantly lower pH values than the other materials (p < 0.05). Regarding to calcium releasing, at 24 hours and 7 days, MTA Fillapex® provided lower releasing than the other materials (p < 0.05). After 14 days, differences were found between MTA Fillapex® and gray MTA (p < 0.05). Conclusion: All materials showed alkaline pH and calcium releasing, with significantly lower values for MTA Fillapex® sealer.

Compressive strength and setting time of MTA and portland cement associated with different radiopacifying agents

The aim of this study was to evaluate the compressive strength and setting time of MTA and Portland cement (PC) associated with bismuth oxide (BO), zirconium oxide (ZO), calcium tungstate (CT), and strontium carbonate (SC). Methods. For the compressive strength test, specimens were evaluated in an EMIC DL 2000 apparatus at 0.5 mm/min speed. For evaluation of setting time, each material was analyzed using Gilmore-type needles. The statistical analysis was performed with ANOVA and the Tukey tests, at 5% significance. Results. After 24 hours, the highest values were found for PC and PC + ZO. At 21 days, PC + BO showed the lowest compressive strength among all the groups. The initial setting time was greater for PC. The final setting time was greater for PC and PC + CT, and MTA had the lowest among the evaluated materials (< 0.05). Conclusion. The results showed that all radiopacifying agents tested may potentially be used in association with PC to replace BO.

Ph and antimicrobial activity of portland cement associated with different radiopacifying agents

The aim of this study was to evaluate the antimicrobial activity and pH changes induced by Portland cement (PC) alone and in association with radiopacifiers. Methods. The materials tested were pure PC, PC + bismuth oxide, PC + zirconium oxide, PC + calcium tungstate, and zinc oxide and eugenol cement (ZOE). Antimicrobial activity was evaluated by agar diffusion test using the following strains: Micrococcus luteus, Streptococcus mutans, Enterococcus faecalis, Pseudomonas aeruginosa, and Candida albicans. After 24 hours of incubation at 37°C, inhibition of bacterial growth was observed and measured. For pH analysis, material samples (n=10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 12, 24, 48, and 72 hours, the pH of the solutions was determined using a pH meter. Results. All microbial species were inhibited by the cements evaluated. All materials composed of PC with radiopacifying agents promoted pH increase similar to pure Portland cement. ZOE had the lowest pH values throughout all experimental periods. Conclusions. All Portland cement-based materials with the addition of different radiopacifiers (bismuth oxide, calcium tungstate, and zirconium oxide) presented antimicrobial activity and pH similar to pure Portland cement.

Calcium silicate-based cements associated with micro-and nanoparticle radiopacifiers: physicochemical properties and bioactivity

The aim of this study was to evaluate the physicochemical properties and bioactivity of two formulations of calcium silicate-based cements containing additives (CSCM) or resin (CSCR), associated with radiopacifying agents zirconium oxide (ZrO2) and niobium oxide (Nb2O5) as micro- and nanoparticles; calcium tungstate (CaWO4); and bismuth oxide (Bi2O3). MTA Angelus was used as control. Methods. Surface features and bioactivity were evaluated by scanning electron microscopy and the chemical composition by energy dispersive X-ray spectrometry (EDS-X). Results. CSCM and CSCR presented larger particle sizes than MTA. Hydroxyapatite deposits were found on the surface of some materials, especially when associated with the radiopacifier with ZrO2 nanoparticles. All the cements presented calcium, silicon, and aluminum in their composition. Conclusion. Both calcium silicate-based cements presented composition and bioactivity similar to MTA when associated with the radiopacifiers evaluated.