Intense upconversion and infrared emissions in Er3+;Yb3+ codoped Lu2 Si O5 and (Lu0.5 Gd0.5)2 Si O5 crystals

High optical quality Lu2SiO5 (LSO) and (Lu0.5Gd0.5)(2)SiO5 (LGSO) laser crystals codoped with Er3+ and Yb3+ have been fabricated by the Czochralski method. Intense upconversion (UC) and infrared emission (1543 nm) are observed under excitation of 975 nm. The luminescence processes are explained and the emission efficiencies are quantitatively obtained by measuring the UC efficiency and calculating the emission cross section. The temperature-dependent optical properties of the crystals are also investigated. Our study indicates that Er3+-Yb3+ : LSO and Er3+-Yb3+: LGSO crystals are promising gain media for developing the solid-state 1.5 mu m optical amplifiers and tunable UC lasers. (c) 2008 American Institute of Physics.

Characterization of m-plane ZnO thin film on gamma-LiAlO2 (100) substrate by metal-organic chemical vapor deposition

Non-polar (1 (1) over bar 00)m-plane ZnO thin film has been prepared on gamma-LiAlO2 (100)substrate via the low pressure metal organic chemical vapor deposition. Obvious intensity variation of the E-2 mode in the polarized Raman spectra and the absorption edge shift in the polarized optical transmission spectra indicate that the m-plane film exhibits optical anisotropy, which have applications in certain optical devices, such as the UV modulator and polarization-dependent beam switch. From the atomic force microscopy images, highly-oriented uniform-sized grains of rectangular shape were observed. (c) 2008 Elsevier B.V. All rights reserved.

Simulation of growth process of thin film on non-planar substrate

In (2 + 1) dimension, growth process of thin film on non-planar substrate in Kuramoto-Sivashinsky model is studied with numerical simulation approach. 15 x 15 semi-ellipsoids arranged orderly on the surface of substrate are used to represent initial rough surface. The results show that at the initial stage of growth process, the surface morphology of thin film appears to be grid-structure, and the interface width constantly decreases with the growth time, then reaches minimum. However, the grid-structure becomes ambiguous, and granules of different sizes distribute evenly on the surface of thin film with the increase of growth time. Thereafter, the average size of granules and the interface width gradually increase, and the surface morphology of thin film presents fractal properties. The numerical results of height-height correlation functions of thin film verify the surface morphology of thin film to be fractal for a longer growth time. By fitting of the height-height correlation functions of thin film with different growth times, the growth process is described quantitatively. (c) 2004 Elsevier B.V. All rights reserved.

Modelling analysis of influence of substrate surface defect on optical characteristics of single-layer coating

A simple and practical model is used to analyse the influence of substrate surface defect on the optical characteristics of a single-layer coating. A single-layer coating is prepared and its optical properties are fitted. Some explanations for the origin of the transition layer are presented. It is concluded that there is a transition layer forming between the substrate and coating, which is attributed to substrate surface defects, and its refractive index change is nearly of linearity.

Influence of Cr interlayer on the structure and optical properties of Ag films on glass substrate by magnetron sputtering

Optical properties and microstructure of Ag film on glass substrate with Cr intermediate layer were studied by using spectrophotometer and XRD. The spectra results showed that introducing Cr intermediate layer reduced the surface roughness and promoted the reflectivity of Ag film. The XRD analysis showed that the crystalline grains increased and the stress decreased. The adhesion was also improved by using the tape test method. (c) 2006 Published by Elsevier B.V.

Mo原子溅射能量对Mo／Si薄膜微结构的影响

用磁控溅射法制备了Mo／Si薄膜，用AFM和XRD分别研究了Mo原子的溅射能量不同时，Mo／Si薄膜表面形貌和晶相的变化。通过比较发现，随着Mo原子溅射能量的增大，Mo／Si薄膜表面粗糙度增加，Mo和Si的特征X射线衍射峰也越来越强，并且Mo膜层和Si膜层之间生成了Mo-Si2。Mo原子的溅射能量是诱导非晶Si结晶和MoSi2生成的主要原因。

Theoretical analysis of optical properties of dielectric coatings dependence on substrate subsurface defects

A model for refractive index of stratified dielectric substrate was put forward according to theories of inhomogeneous coatings. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. Both the surface layer (separated into N-1 sublayers of uniform thickness) and subsurface layer (separated into N-2 sublayers of uniform thickness), whose refractive indices have different statistical distributions, are equivalent to inhomogeneous coatings, respectively. And theoretical deduction was carried Out by employing characteristic matrix method of optical coatings. An example of mathematical calculation for optical properties of dielectric coatings had been presented. The computing results indicate that substrate subsurface defects can bring about additional bulk scattering and change propagation characteristic in thin film and Substrate. Therefore, reflectance, reflective phase shift and phase difference of an assembly of coatings and substrate deviate from ideal conditions. The model will provide some beneficial theory directions for improving optical properties of dielectric coatings via substrate surface modification. (c) 2005 Elsevier B.V. All rights reserved.

Theoretical analysis of influence of substrate microdefects on polarized light properties of dielectric coatings

A model for refractive index of stratified dielectric substrate was presented according to inhomogeneous coatings theories. The substrate was divided into surface layer, subsurface layer and bulk layer along the normal direction of its surface. The former two layers were equivalent to inhomogeneous coatings. Theoretical deduction was executed by employing the characteristic matrix method of optical coatings, and one mathematical calculation example was presented. The results indicate that reflectance, reflective phase shift and phase difference of polarized light deviate from ideal conditions. It shows that substrate microdefects can induce volume scattering and change propagation characteristic of light both in coatings and substrate. (c) 2005 Elsevier GmbH. All rights reserved.

不同膜层数的Mo/Si多层膜的表界面粗糙度和软X射线反射率

用磁控溅射法制备了顶层分别是Mo膜层和Si膜层的两个系列的Mo/Si多层膜，它们的周期厚度相同但是膜层数各不相同。Mo/Si多层膜的周期厚度和界面粗糙度由小角X射线衍射（SAXRD）曲线拟和得到。用原子力显微镜测量了Mo/Si多层膜的表面粗糙度。在国家同步辐射实验室测量了Mo/Si多层膜的软X射线反射率。通过理论和试验研究，发现Mo/Si多层膜的软X射线反射率主要由周期数和界面粗糙度决定，表面粗糙度对Mo/Si多层膜的软X射线反射率影响较小。

Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

研究扩散屏障层对Mo/Si多层膜软X射线反射率影响的模拟

在特定波长下,用四层结构模型模拟了Mo/Si多层膜的软X射线反射率.研究了扩散屏障层dMo-on-Si和dSi-on-Mo对Mo/Si多层膜软X射线反射率的影响.研究发现,扩散屏障层并不总是损害Mo/Si多层膜的光学性能,通过合理设计dMo-on-Si和dSi-on-Mo厚度,增加dMo-on-Si与dSi-on-Mo的比值,也能提高多层膜的软X射线反射率.